Ti-based alloys are accessible for use in the human body due to their good mechanical properties, corrosion resistance, and biocompatibilities. These main properties of alloys are important criteria for choosing biomedical implants for human bones or...
Mo–Si–B alloys have attracted considerable research interest during the last several decades due to their high melting points, excellent high-temperature strength and relatively good oxidation resistance. However, insufficient room-temper...
Considering the future trends of biomaterials, current studies are focused on the corrosion resistance and the mechanical properties of new materials that need to be considered in the process of strengthening alloys with additive non-toxic elements....
The effect of phase composition and morphology on high-temperature strength in the compression of Fe-Al-Si-based iron aluminides manufactured by casting was investigated. The structure and high-temperature strength in the compression of three alloys&...
Titanium alloys are used in medical devices due to their mechanical properties, but also for their corrosion resistance. The natural passivation of titanium-based biomaterials, on the surface of which a dense and coherent film of nanometric thickness...
The amorphous AlTiCrFeMoSi high entropy alloy (HEA) coating with high hardness (11.88 GPa) is successfully deposited on T91 substrate by the magnetron sputtering method. Both T91 steel and as−deposited AlTiCrFeMoSi coating samples are exposed t...
Thermal expansion measurements were used to characterize phase transformations in metastable β-Ti alloys (Ti15MoxSi) without and with various Si additions (where x = 0, 0.5, 1.0, 1.5, and 2 in wt.%) during linear heating at two heating rates of...
The effects of different brazing processes on the interfacial microstructure and shear strength of TiZrHfNbMo high-entropy alloy (HEAS) and Si3N4 ceramic brazed joints were studied. There is no obvious defect in a brazed TiZrHfNbMo HEAS/AgCuTi/Si3N4...
In this paper, the isothermal compressive behavior of Ti-6.5Al-3.5Mo-1.5Zr-0.3Si titanium alloy was investigated on a Gleeble-3500 simulator in the temperature range from 1073 to 1373 K at an interval of 50 K (while the phase transus temperature is a...
The mechanical properties and electrochemical behavior of two new titanium alloys, Ti20Mo7Zr and Ti20Mo7Zr0.5Si, are investigated in this paper. The alloys have been manufactured by vacuum arc remelting (VAR) technique and studied to determine their...
The use of joints fabricated from dissimilar titanium alloys allows the design of structures with local properties tailored to different service requirements. To develop welded structures for aerospace applications, particularly under critical loadin...
Dissimilar joints between Ti-6Al-4V (Ti-64) and Ti-6Al-2Sn-4Zr-2Mo-0.1Si (Ti-6242) were manufactured using linear friction welding. The weld quality, in terms of the microstructure and mechanical properties, was investigated after stress relief annea...
The aim of this paper is to conduct an experimental study in order to obtain a roughness (Ra) prediction model for dry end-milling (with an AlTiCrSiN PVD-coated tool) of the Co–28Cr–6Mo and Co–20Cr–15W–10Ni biomedical alloys, a model that can contrib...
In this study we present a series of light-weight (6.24 to 6.42 g/cm3), Ti-rich Mo-Si-Ti alloys (≥40 at.% nominal Ti content) with the hitherto best combination of pesting and creep resistance at 800 and 1200 °C, respectively. This has been ac...
This paper presents the microstructural characteristics and mechanical properties of linear friction-welded (LFWed) Ti-6Al-2Sn-4Zr-2Mo-0.1Si (Ti-6242) in as-welded (AWed) and stress relief-annealed (SRAed) conditions. The weld center (WC) of the AWed...
The quality and properties of metal powders are essential for powder metallurgical (PM) processes in general and for additive manufacturing (AM) processing routes in particular. Thus, a variety of atomization technologies were established meeting the...
The main purpose of this research is to evaluate the mechanical characteristics and biocompatibility of two novel titanium alloys, Ti15Mo7ZrxSi (x = 0, 0.5, 0.75, 1). These samples had already undergone grinding, polishing, cutting, and chipping. Ele...
The durability of a metallic biomaterial to withstand weight loss is a key factor in determining its service life and performance. Therefore, it is essential to create biomaterials with high wear resistance to ensure the biomaterial has a long servic...
Low-density materials show promising prospects for industrial application in engineering, and have remained a research hotspot. The ingots of Al15Zr40Ti28Nb12Cr5, Al15Zr40Ti28Nb12Mo5 and Al15Zr40Ti28Nb12Si5 high-entropy alloys were prepared using an...
Tinted plasma electrolytic oxidized (PEO) coatings have been widely applied on the surface of Ti alloys in aerospace field. In this study, a black PEO coating was successfully developed on TC4 alloy, incorporating MoSi2 nanoparticles in situ within t...
As a candidate material for turbine blades in aerospace engines, Nb-Si-based alloys have attracted significant research attention due to their high melting point and low density. However, their poor high-temperature oxidation resistance limits practi...
Refractory metal-based Mo-Si-B alloys have long been considered the most promising candidates for replacing nickel-based superalloys in the aerospace and energy sector due to their outstanding mechanical properties and good oxidation of the Mo-silici...
The microstructural evolution and tensile properties of Ti-3Al-8V-6Cr-4Mo-4Zr titanium alloys with various Si contents were investigated. The results revealed that the addition of trace Si and the presence of Zr induced the formation of (TiZr)6Si3 si...
We studied the microstructures and isothermal oxidation of the Nb-silicide-based alloys Nb-11.5Ti-18Si-5Mo-2W-4.9Sn-4.6Ge-4.5Cr-4.7Al-1Hf (JZ4) and Nb-21Ti-18Si-6.7Mo-1.2W-4.4Sn-4.2Ge-4Cr-3.7Al-0.8Hf (JZ5), calculated their average creep rate for the...
The Nb-silicide-based alloy of near eutectic composition (at.%) Nb-21.1Si-8.3Ti-5.4Mo-4W-0.7Hf (alloy CM1) was studied in the cast and heat-treated (1500 °C/100 h) conditions. The alloy was produced in the form of buttons and bars using three dif...
A novel TiB2-CeO2-modified (Nb,Mo,Cr,W)Si2 coating was prepared on a Nb-5W-2Mo-1Zr alloy substrate using two-step slurry sintering and halide-activated pack cementation to address the limitations of a single NbSi2 coating in meeting the service requi...
In situ synthesized TiB whiskers (TiBw) reinforced Ti-15Mo-3Al-2.7Nb-0.2Si alloys were successfully manufactured by pre-sintering and canned hot extrusion via adding TiB2 powders. During pre-sintering, most TiB2 were reacted with Ti atoms to produce...
The hot deformation behavior of Ti-4Zr-6Al-0.6Si-0.5Mo high-temperature titanium alloy was investigated under temperatures of 800–1100 °C, strain rates of 0.001–1 s−1, and a true strain of 0.5. Flow stress curves under different...
Uniaxial tensile flow properties of a duplex Ti-6.6Al-3.3Mo-1.8Zr-0.29Si alloy in a temperature range from 213 K to 573 K are investigated through crystal plasticity modelling. Experimental results indicate that the initial yield stress of the alloy...
The complex deformation usually involves wide strain-rate change. However, few efforts have been devoted to investigate the effect of strain rate history on the tensile behavior of α + β titanium alloy. In present paper, tensile tests of T...
Structure, gaseous phase hydrogen storage, and electrochemical properties of a series of TiVCrMn-based body-centered-cubic (BCC) alloys with different partial substitutions for Mn with covalent elements (B and Si), transition metals (Ni, Zr, Nb, and...
The typical microstructure of the laser melting deposition (LMD) additive-manufactured Ti-6.5Al-3.5Mo-1.5Zr-0.3Si alloy (TC11) contains the heat-affected bands (HABs), the narrow bands (NBs) and the melting pools (MPs) that formed due to the reheatin...
High-entropy diboride-based (MeB2-based) ceramics are promising high-temperature structural materials because of their excellent mechanical properties, high-temperature stability, and oxidation resistance. In order to achieve low-temperature sinterin...
Ti-5Al-4Sn-2Zr-1Mo-0.25Si-1Nb (TA32) titanium alloy is a kind of near α high temperature titanium alloy with great application prospects in aero-engine afterburners and cruise missiles. However, there are still few studies on the microstructure...
This article presents a novel and feasible approach for researching the quantity of the ceramic phase and component optimization in high-temperature titanium alloys with small trace amounts of ceramic phases. Different near-α titanium alloys wi...
TiAl alloys are ideal candidates to replace nickel-based superalloys in aero-engines due to their low density and high specific strength, yet their industrial application is hindered by narrow heat treatment windows and unbalanced mechanical performa...
(AlCrNbSiTiMo)N high-entropy alloy films with different nitrogen contents were deposited on tungsten carbide substrates using a radio-frequency magnetron sputtering system. Two different types of targets were used in the sputtering process: a hot-pre...
Near-α Ti alloys find themselves in advanced aeroengines for applications of up to 600 °C, mainly as compressor components owing to their superior combination of ambient- and elevated-temperature mechanical properties and oxidation resistan...
The oxidation behavior of two ternary Mo-Si-Ti alloys (eutectic Mo-20.0Si-52.8Ti and eutectoid Mo-21.0Si-34.0Ti) was investigated using thermogravimetric analysis at 700 °C, 900 °C, and 1300 °C for 100 h. The eutectic alloy formed a prote...
Ti-based alloys are widely used in medical applications. When implant devices are used to reconstruct disordered bone, prevent bone resorption and enhance good bone remodeling, the Young’s modulus of implants should be close to that of the bone...
Titanium-based alloys are constantly improved to obtain properties suitable for their use. Improving titanium alloys is very important for performing alloys without side effects. In this paper effects of structure, microhardness, and indentation test...
Coating properties and oxidation behaviors of Si pack cementation-coated TZM (Mo-0.5Ti-0.1Zr-0.02C) alloys were investigated in order to understand the stability of the coating layer at high temperatures up to 1350 °C in an ambient atmosphere. Af...
In the present work, we studied the effects of transition metal elements on microstructure evolution and high-temperature mechanical properties via the preparation of new modified alloys with micro-additions of Cr, Ti, V, Zr, Mo, and Mn to address th...
TiMoZrTaSi alloys appertain to a new generation of metallic biomaterials, labeled high-entropy alloys, that assure both biocompatibility as well as improved mechanical properties required by further medical applications. This paper presents the use o...
The designed alloy Ti-10.56%Al-2.08%Zr-0.80%Sn-0.88%Mo-0.51%Si (mol%), modified alloy Ti-10.81%Al-4.80%Zr-1.23%Sn-0.76%Cu-0.35%Si (mol%) and reference alloy Ti-10.52%Al-2.07%Zr-1.1%Sn-0.2%Mo-0.76%Si (mol%) with the same bond order (Bot) value of 3.49...
Owing to the reducing effect of NHx radicals and H species produced in (Ar-N2-H2) expanding plasma, chemical reactions are promoted in thin metal films in contrast with other plasma treatments where the impinging energetic ions play the main role. Mu...
The alloying of Nb5Si3 modifies its properties. Actual compositions of (Nb,TM)5X3 silicides in developmental alloys, where X = Al + B + Ge + Si + Sn and TM is a transition and/or refractory metal, were used to calculate the composition weighted diffe...
The use of titanium and titanium-based alloys in the human body due to their resistance to corrosion, implant ology and dentistry has led to significant progress in promoting new technologies. Regarding their excellent mechanical, physical and biolog...
Ti-based alloy Ti75Zr11Si9Fe5 (At %) and Ti66Zr11Si15Fe5Mo3 (At %) ribbons are fabricated by a single roller spun-melt technique, according to the three empirical rules. Both alloys are found to have a large, supercooled liquid region (ΔTx) bef...
Mo-Ti-Si, Mo-Zr-B, and Mo-Hf-B are promising alloy systems for high-temperature applications as they show higher toughness and higher creep resistance than other Mo-based alloys. Regarding ductility and toughness, the chemical composition of the Mo s...
of 3