A non-axisymmetric laser-tungsten inert gas (TIG) heat source was designed to join Mg–Al dissimilar metals with pure Zn filler at a series of welding speeds (500–900 mm/min). Laser and TIG heat sources respectively acted on Al and Mg base...
In order to clarify the microstructural evolution and the mechanical property of dissimilar friction stir-welded joints of ZK60 and Mg-4.6Al-1.2Sn-0.7Zn magnesium alloys, two types of arrangement with ZK60 at advancing side (AS) or retreating side (R...
In this study, a penetration-controlled friction stir welding (FSW) technique was employed to lap weld dissimilar Al/Mg alloys, incorporating a Zn interlayer. The joint’s microstructure, interfacial reaction, and phase composition were analyzed...
Based on the idea of alloying welding seams, a series of Zn–xAl filler metals was calculated and designed for joining Mg/Al dissimilar metals by gas tungsten arc (GTA) welding. An infrared thermography system was used to measure the temperature of th...
The vacuum brazing of dissimilar Al 7075 and Al–25 Si alloy was investigated. The brazing filler was copper foil with a thickness of 20 μm, and the brazing temperature was 560 °C held for 10 min. The average shear strength of the brazed...
The use of a Zn/Ag–Cu–Zn/Zn multi-interlayer was observed to avoid the formation of Mg–Al binary intermetallic compounds (IMCs), which cause embrittlement and low strength of bonding when dissimilar metals such as Mg/Al are joined u...
There is limited research on dissimilar joints of RE-containing Mg alloys and Al alloys, and the diffusion of elements is fundamental for the properties of Mg/Al interfaces. In this study, samples were manufactured by magnetic pulse welding (MPW) wit...
Diffusion bonding with an interlayer is considered an effective means of obtaining Mg/Al dissimilar alloy joints. However, at low temperatures, it is often impossible to simultaneously achieve joints between the interlayer and Mg/Al under the same bo...
This study aims to explore the effects of various pre- and post-weld heat treatments (PWHTs) on the microstructural and mechanical properties of dissimilar aluminium alloys, namely AA7075 and AA2024, joined through rotary friction welding. The joints...
Dissimilar 7075-T6 and 6061-T6 aluminum alloy joints were fabricated using pulsed metal inert gas (P-MIG) welding with ER5356 filler wire. The effects of welding current (224 A, 234 A, and 244 A) on macro-morphology, microstructure, mechanical proper...