Abstract
The temperature and field dependencies of electric conductivities of two types of silicone rubber-based polymers intended for use in high voltage direct current applications are presented and discussed. The conductivities obtained with the standard method by measuring a current through the material sample placed between metallic electrodes in response to the applied voltage are compared with those deduced from the measured potential decay on pre-charged material surface in an open circuit configuration. The measurements were conducted in the range of the applied electric field strength (0.5–5) kV/mm and temperatures ranging from 22 °C to 70 °C. It is shown that the values of the conductivities obtained by the two methods are in agreement and their temperature dependences obey Arrhenius law yielding similar activation energies.