Fabrication and Characterization of Piezoelectric PEO/SF/BaTiO₃ Scaffolds for Cardiac Tissue Engineering

The existence of an intrinsic electrical platform responsible for the formation and transmission of impulses is essential, especially in cardiac tissue. However, most cardiac tissue made from biodegradable polymeric materials lacks conductive characteristics; this delays regional conduction, potentially causing arrhythmias. This study proposes a conductive polyethylene oxide (PEO)/silk fibroin (SF)-based material conjugated with conductive nanoparticles as a cardiac patch to fix any infarcted heart part. A new composite of PEO/15 wt%SF/0.2 wt%BaTiO₃ was prepared and characterized in vitro. The obtained patches were characterized by conventional Bragg-platinum-conductive action (XRD), FTIR spectroscopy, Raman spectra, and thermogravimetric analysis. A PiezoTester device was used to evaluate the piezoelectric properties. The produced samples of 500 μm thickness were assessed in tapping mode. The applied load was selected to be as low as possible, and the frequencies were adjusted to simulate the heartbeats, ranging from 10 to 100 Hz. The results showed that a maximum of around 1100 mV was obtained at a load of 20 N. A maximum of about 80 mV was received at an applied force of 1 N and a frequency of 100 Hz, which matches the electricity generated by the human heart. The cytotoxicity effect of prepared films was tested against AC16 cells using microculture tetrazolium assay (MTT). The pristine PEO cell viability either was not affected by adding SF or slightly decreased. However, the cell viability dramatically increased by adding BaTiO₃ to the PEO/SF composites. The confocal microscope images proved that the cells showed a spread morphology. The cells adhered to the PEO membranes and demonstrated a well-spread morphology. Overall, our study suggests that the PEO/SF/BaTiO₃ composite can be a promising cardiac patch material for repairing infarcted heart tissue, as it is conductive, has good mechanical properties, and is biocompatible.