Abstract
Carbon-fiber structural batteries represent a class of multifunctional energy-storage systems that integrate electrochemical energy storage with mechanical load-bearing capability. Unlike conventional batteries, which are mainly evaluated based on cell-level energy density, structural batteries provide new opportunities for system-level weight reduction by reducing inactive structural mass, improving space utilization, and enabling distributed energy storage within integrated structures. In recent years, substantial progress has been achieved in carbon-fiber electrodes, structural electrolytes, laminated devices, electrolyte topology engineering, and fully carbon-fiber structural batteries. Nevertheless, most reported advances have been demonstrated under relatively ideal static testing conditions, while maintaining multifunctional performance under manufacturing and long-term service conditions remains a critical challenge. This review systematically examines the development of carbon-fiber structural batteries from a reliability perspective. First, the system-level motivations and technological evolution are introduced, and existing architectures are categorized according to their integration depth and degree of multifunctional coupling. Carbon-fiber electrodes are then discussed with emphasis on balancing capacity, ion transport, cycling stability, mechanical property retention, interfacial robustness, and manufacturing scalability. Furthermore, structural electrolytes are reviewed from the viewpoint of topology-enabled regulation of ion transport and load transfer, with particular focus on the intrinsic trade-off between ionic conductivity and mechanical modulus. In addition, manufacturing routes and device architectures are analyzed from the perspective of multifunctionality-degrading defects, including voids, dry regions, coating cracks, weak interfaces, and current-collector discontinuities. Finally, retained multifunctionality is used as a reliability-oriented evaluation criterion to examine the preservation of electrochemical, mechanical, interfacial, and safety functions, with particular emphasis on the carbon-fiber-specific failure chain linking interfacial and manufacturing heterogeneities to multifunctionality-degrading defects, coupled-field localization, and damage propagation. This review emphasizes that reliable carbon-fiber structural batteries require application-specific and coordinated optimization of materials, interfaces, electrolyte topology, coupled degradation behavior, and validation protocols.