Ultrahigh-temperature ceramic composites based on hafnium diboride have a wide range of applications, including as components for high-speed aircraft and energy generation and storage devices. Consequently, developing methodologies for their fabrication and studying their properties are of paramount importance, in particular in using them as an electrode material for energy storage devices with increased oxidation resistance. This study investigates the behavior of ceramic composites based on the HfB₂-HfO₂-SiC system, obtained using 15 vol% Ti₂AlC MAX-phase as a sintering component, under the influence of subsonic flow of dissociated air. It was determined that incorporating the modifying component (Ti₂AlC) altered the composition of the silicate melt formed on the surface during ceramic oxidation. This modification led to the observation of a protective antioxidant function. Consequently, liquation was observed in the silicate melt layer, resulting in the formation of spherical phase inhomogeneities in its volume with increased content of titanium, aluminum, and hafnium. It is hypothesized that the increase in the high-temperature viscosity of this melt prevents it from being carried away in the form of drops, even at a surface temperature of ~1900–2000 °C. Despite the established temperature, there is no sharp increase in its values above 2400–2500 °C. This is due to the evaporation of silicate melt from the surface. In addition, the electrochemical behavior of the obtained material in a liquid electrolyte medium (KOH, 3 mol/L) was examined, and it was shown that according to the value of electrical conductivity and specific capacitance, it is a promising electrode material for supercapacitors. Full article

The titanium matrix composites (TMCs) fabricated via Directed Energy Deposition (DED) effectively overcome the issue of coarse columnar grains typically observed in additively manufactured titanium alloys. In this study, systematic annealing heat treatments were applied to in situ (TiB + TiC)/Ti-6Al-4V composites to refine the microstructure and tailor mechanical properties. The results reveal that the plate-like α phase in the as-deposited composites gradually transforms into an equiaxed morphology with increasing annealing temperature and holding time. Notably, when the annealing temperature exceeds 1000 °C, significant coarsening of the TiC phase is observed, while the TiB phase remains morphologically stable. Annealing promotes decomposition of acicular martensite and stress relaxation, leading to a reduction in hardness compared to the as-deposited state. However, the reticulated distribution of the TiB and TiC reinforcement phases contributes to enhanced tensile performance. Specifically, the as-deposited composite achieves a tensile strength of 1109 MPa in the XOY direction, representing a 21.6% improvement over the as-cast counterpart, while maintaining a ductility of 2.47%. These findings demonstrate that post-deposition annealing is an effective strategy to regulate microstructure and achieve a desirable balance between strength and ductility in DED-fabricated titanium matrix composites. Full article

After reviewing the state of the art of the fluorination of inorganic solid electrolytes, an application of gas/solid fluorination is given and how it can be processed. Garnet-type oxide has been chosen. These oxides with an ideal structure of chemical formula A₃B₂(XO₄)₃ are mainly known for their magnetic and dielectric properties. Certain garnets may have a high enough Li⁺ ionic conductivity to be used as solid electrolyte of lithium ion battery. The surface of LLZO may be changed in contact with the moisture and CO₂ present in the atmosphere that results in a change of the conductivity at the interface of the solid. LiOH and/or lithium carbonate are formed at the surface of the garnet particles. In order to allow for handling and storage under normal conditions of this solid electrolyte, surface fluorination was performed using elemental fluorine. When controlled using mild conditions (temperature lower or equal to 200 °C, either in static or dynamic mode), the addition of fluorine atoms to LLZO with Li_6,4Al_0,2La₃Zr₂O₁₂ composition is limited to the surface, forming a covering layer of lithium fluoride LiF. The effect of the fluorination was evidenced by IR, Raman, and NMR spectroscopies. If present in the pristine LLZO powder, then the carbonate groups disappear. More interestingly, contrary to the pristine LLZO, the contents of these groups are drastically reduced even after storage in air up to 45 days when the powder is covered with the LiF layer. Surface fluorination could be applied to other solid electrolytes that are air sensitive. Full article

The disposal of olive mill wastewater (OMWW) poses significant environmental challenges due to its high content of phytotoxic and pollutant compounds. This study aims to explore the chemical composition of OMWW derived from various olive varieties (Buža, Buža puntoža, Istarska bjelica, Leccino, and Rosinjola) and assess its antifungal potential against phytopathogenic fungi from the Botryosphaeriaceae family. OMWW samples were analyzed for their physicochemical properties, phenolic composition via LC-MS/MS, and antifungal activity against Botryosphaeria dothidea (Moug. ex Fr.) Ces. & De Not., Diplodia mutila (Fr.) Fr., D. seriata De Not., Dothiorella iberica A.J.L. Phillips, J. Luque & A. Alves, Do. sarmentorum (Fr.) A.J.L. Phillips, Alves & Luque, and Neofusicoccum parvum (Pennycook & Samuels) Crous, Slippers & A.J.L. Phillips. Antifungal efficacy was tested at varying concentrations, alongside the phenolic compounds hydroxytyrosol and vanillic acid. Antifungal activity varied across fungal species and OMWW concentrations. Lower OMWW concentrations inhibited mycelial growth in some pathogens, while higher concentrations often had a stimulatory effect. Among the OMWW treatments, Leccino and Buža showed the most significant antifungal activity against species from the Botryosphaeriaceae family. The results demonstrated significant variability in OMWW composition, with Istarska bjelica exhibiting the highest concentrations of phenolic compounds, sugars, dry matter, and carbon and nitrogen content. The results also highlight the impact of acidification on the phenolic profile of OMWW. Treatment with HCl significantly altered the concentration of individual phenolic compounds, either enhancing their release or contributing to their degradation. Among the two compounds, vanillic acid showed greater efficacy than hydroxytyrosol. In addition, microorganisms isolated from OMWW, including Bacillus velezensis Ruiz-Garcia et al., Rhodotorula mucilaginosa (A. Jörg.) F.C. Harrison, Nakazawaea molendiniolei (N. Cadez, B. Turchetti & G. Peter) C. P. Kurtzman & C. J. Robnett, and Penicillium crustosum Thom, demonstrated antagonistic potential against fungal pathogens, with B. velezensis showing the strongest inhibitory effect. The greatest antagonistic effect against fungi was observed with the species Do. Iberica. The findings highlight the potential of OMWW as a sustainable alternative to chemical fungicides, simultaneously contributing to the management of waste and protection of plants through circular economy principles. Full article

A SiO₂-Al₂O₃-B₂O₃-CaO-MgO-Na₂O glass-based protective lubricant coating was developed for Ti-6Al-4V alloy forging, featuring a fully non-toxic formulation. The coating consisted of a composite glass matrix formed by blending two phases with distinct softening temperatures, extending its operational window to 700–950 °C. The composite glass showed initial softening at 700 °C and complete melting at 800 °C, with contact angle measurements confirming superior wettability (θ < 90°) across the forging range (800~950 °C). With an increase in temperature, the surface tension of the composite glass melt decreased, and subsequently, the wettability of the composite glass melt was significantly improved. XRD revealed that the uncoated Ti-6Al-4V formed a 22 μm thick rutile TiO₂ scale with a porous structure and interfacial cracks, while the coated sample retained an amorphous glass layer with no TiO₂. Cross-sectional SEM showed a crack-free, poreless interface with strong metallurgical bonding, in contrast to the uncoated sample’s spalled oxide layer. EDS showed minimal oxygen diffusion of the glass coating into the substrate. Ring upsetting tests showed that the coating reduced friction from 0.5–0.7 to 0.3 (50–57% decrease). Collectively, the glass protective lubricant coating showed good performance in terms of protection and lubrication. Full article

This study systematically investigates the effects of heat treatment at 800–1000 °C on the microstructure and mechanical properties of 10 wt.% TiB₂@Ti/AlCoCrFeNi_2.1 eutectic high-entropy alloy matrix composites (EHEAMCs) prepared by vacuum hot-pressing sintering. The results show that the materials consist of FCC, BCC, TiB₂, and Ti phases, with a preferred orientation of the (111) crystal plane of the FCC phase. As the temperature increases, the diffraction peak of the BCC phase separates from the main FCC peak and its intensity increases, while the diffraction peak positions of the FCC and BCC phases shift at small angles. This is attributed to the diffusion of TiB₂@Ti from the grain boundaries into the matrix, where the Ti solid solution increases the lattice constant of the FCC phase. Microstructural observations reveal that the eutectic region transforms from lamellar to island-like structures, and the solid solution zone narrows. With increasing temperature, the Ti concentration in the solid solution zone increases, while the contents of elements such as Ni decrease. Element diffusion is influenced by binary mixing enthalpy, with Ti and B tending to solidify in the FCC and BCC phase regions, respectively. The mechanical properties improve with increasing temperature. At 1000 °C, the average hardness is 579.2 HV, the yield strength is 1294 MPa, the fracture strength is 2385 MPa, and the fracture strain is 19.4%, representing improvements of 35.5% and 24.9% compared to the as-sintered state, respectively, without loss of plasticity. The strengthening mechanisms include enhanced solid solution strengthening due to the diffusion of Ti and TiB₂, improved grain boundary strength due to the diffusion of alloy elements to the grain boundaries, and synergistic optimization of strength and plasticity. Full article

The new mineral achyrophanite (K,Na)₃(Fe³⁺,Ti,Al,Mg)₅O₂(AsO₄)₅ was found in high-temperature sublimates of the Arsenatnaya fumarole at the Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. It is associated with aphthitalite-group sulfates, hematite, alluaudite-group arsenates (badalovite, calciojohillerite, johillerite, nickenichite, hatertite, and khrenovite), ozerovaite, pansnerite, arsenatrotitanite, yurmarinite, svabite, tilasite, katiarsite, yurgensonite, As-bearing sanidine, anhydrite, rutile, cassiterite, and pseudobrookite. Achyrophanite occurs as long-prismatic to acicular or, rarer, tabular crystals up to 0.02 × 0.2 × 1.5 mm, which form parallel, radiating, bush-like, or chaotic aggregates up to 3 mm across. It is transparent, straw-yellow to golden yellow, with strong vitreous luster. The mineral is brittle, with (001) perfect cleavage. D_calc is 3.814 g cm^–3. Achyrophanite is optically biaxial (+), α = 1.823(7), β = 1.840(7), γ = 1.895(7) (589 nm), 2V (meas.) = 60(10)°. Chemical composition (wt.%, electron microprobe) is: Na₂O 3.68, K₂O 9.32, CaO 0.38, MgO 1.37, MnO 0.08, CuO 0.82, ZnO 0.48, Al₂O₃ 2.09, Fe₂O₃ 20.42, SiO₂ 0.12, TiO₂ 7.35, P₂O₅ 0.14, V₂O₅ 0.33, As₂O₅ 51.88, SO₃ 1.04, and total 99.40. The empirical formula calculated based on 22 O apfu is Na_1.29K_2.15Ca_0.07Mg_0.34Mn_0.01Cu_0.11Zn_0.06Al_0.44Fe³⁺_2.77Ti_1.00Si_0.02P_0.02S_0.14V_0.04As_4.90O₂₂. Achyrophanite is orthorhombic, space group P222₁, a = 6.5824(2), b = 13.2488(4), c = 10.7613(3) Å, V = 938.48(5) ų and Z = 2. The strongest reflections of the PXRD pattern [d,Å(I)(hkl)] are 5.615(59)(101), 4.174(42)(022), 3.669(31)(130), 3.148(33)(103), 2.852(43)(141), 2.814(100)(042, 202), 2.689(29)(004), and 2.237(28)(152). The crystal structure of achyrophanite (solved from single-crystal XRD data, R = 4.47%) is unique. It is based on the octahedral-tetrahedral M-T-O pseudo-framework (M = Fe³⁺ with admixed Ti, Al, Mg, Na; T = As⁵⁺). Large-cation A sites (A = K, Na) are located in the channels of the pseudo-framework. The achyrophanite structure can be described as stuffed, with the defect heteropolyhedral pseudo-framework derivative of the orthorhombic Fe³⁺AsO₄ archetype. The mineral is named from the Greek άχυρον, straw, and φαίνομαι, to appear, in allusion to its typical straw-yellow color and long prismatic habit of crystals. Full article

Aluminide coatings on nickel-based superalloys were synthesized via a high-temperature “clean” low-activity vapor-phase process. This process is environmentally friendly and meets manufacturers’ environmental protection requirements. Hence, it fulfils the Industry 4.0 requirements, where the reduction of environmental impact in the industrial sector is a key issue. Surface morphology, cross-section microstructure, and phase composition of the coatings were studied and compared by using an optical microscope and a scanning electron microscope (SEM) equipped with an energy dispersive spectroscope (EDS) and X-ray diffraction (XRD). Bare and coated superalloys’ lifetime was evaluated and compared via air exposure at 1100 °C. High-temperature low-activity aluminizing of the IN713, IN625, and CMSX4 superalloys enabled the obtainment of the desirable β-NiAl phase. The highest nickel content in the chemical composition of the IN713 superalloy among the investigated superalloys resulted in the highest aluminide coatings’ thickness. Moreover, the higher refractory elements concentration in the IN625 and CMSX4 superalloys than that in the IN713 superalloy may contribute to a thinner aluminide coatings’ thickness. Refractory elements diffused to the surface of the superalloy and formed carbides or intermetallic phases, which impeded outward nickel diffusion from the substrate to the surface and thereby inhibited coating growth. The obtained coatings fulfilled the requirements of ASTM B 875. Despite the fact that the coating formed on IN713 was thicker than that formed on IN625, the lifetime of both coated superalloys was comparable. Oxidation resistance of the aluminide coatings formed on the IN713 and IN625 superalloys makes them the favored choice for gas turbine applications. Full article

This study systematically investigates the effects of various direct aging (DA) treatments on the residual stress, mechanical properties, and microstructure of laser powder bed fusion (LPBF) fabricated TiB₂/AlSi7Mg composites. The results demonstrate that during aging at 120 °C, the hardness exhibits a typical age-hardening behavior. The residual stress relief rate increased to 45.1% after 336 h, although the stress relief rate significantly diminished over time. Increasing the aging temperature effectively enhanced residual stress removal efficiency, with reductions of approximately 40% and 62% observed after aging at 150 °C for 4 h and 190 °C for 8 h, respectively. Regarding mechanical properties, aging at 150 °C for 4 h resulted in an optimal synergy in yield strength (YS = 358 MPa) and elongation (EL = 9.2%), followed by aging at 190 °C for 8 h with YS of 320 MPa and EL of 7.0%. Microstructural analysis revealed that low temperature aging promotes the formation of nanoscale Si precipitates, which enhance strength through the Orowan mechanism. In contrast, high temperature annealing disrupts the metastable cellular structure, leading to the loss of strengthening effects. This work provides fundamental insights for effective residual stress management and performance optimization of LPBF Al–Si–Mg alloys. Full article

A novel bioactive glass–ceramic was developed using biogenic hydroxyapatite (BHA) synthesized from Rapana venosa (Black Sea) shells and monocalcium phosphate monohydrate [Ca(H₂PO₄)₂·H₂O] via solid-state synthesis. The prepared batches were obtained by combining BHA with SiO₂, B₂O₃, and Na₂O, melted at 1200 °C and melt-quenched in water to form glass–ceramic materials. Dense biogenic hydroxyapatite-based ceramics were successfully sintered at 1200 °C (2 h hold) using a 25 mass % sintering additive composed of 35 mass % B₂O₃, 45 mass % SiO₂, 10 mass % Al₂O₃, and 10 mass % Na₂O. Structural characterization was carried out using X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM). The resulting materials consisted of a well-defined crystalline hydroxyapatite phase [Ca₁₀(PO₄)₆(OH)₂] alongside an amorphous phase. In samples with increased SiO₂ and reduced B₂O₃ content (composition 3), a finely dispersed Na₃Ca₆(PO₄)₅ crystalline phase appeared, with a reduced presence of hydroxyapatite. Bioactivity was assessed in simulated body fluid (SBF) after 10 and 20 days of immersion, confirming the material’s ability to support apatite layer formation. The main structural units SiO₄, PO₄, and BO₃ are interconnected through Si–O–Si, B–O–B, P–O–P, and mixed Si–O–Al linkages, contributing to both structural stability and bioactivity. Full article

A Cl-rich annitic mica is present in zones in taxitic gabbro–dolerite enriched in base metal sulfides in the eastern portion of the Oktyabrsky deposit in the Norilsk complex (Russia). Other Cl-enriched minerals in the assemblage include hastingsite (4.06 wt.% Cl), ferro-hornblende (2.53 wt.%), and chlorapatite (>6 wt.%). New wavelength-dispersive electron probe analyses reveal compositions with up to 7.75 wt.% Cl, corresponding to the formula K_0.742Na_0.047Ca_0.007)_Σ0.796 (Fe²⁺_2.901Mg_0.078Mn_0.047Ti_0.007Cr_0.003)_Σ3.036 (Si_3.190Al_0.782)_Σ3.972O₁₀ (Cl_1.105OH_0.854F_0.041)_Σ2.000 based on 22 negative charges per formula unit, in which OH(calc.) = 2 − (Cl + F). Unfortunately, the grain size of the Cl-dominant mica precluded a single-crystal X-ray diffraction study even though its EBSD pattern confirms its identity as a member of the Mica group. We present results of a refinement of a crystal from the same mineralized sample containing 0.90(6) apfu Cl [R1 = 7.89% for 3720 unique reflections]. The mica is monoclinic, space group C2/m, a 5.3991(4), b 9.3586(6), c 10.2421(10) Å, β 100.873(9)°, V = 508.22(7) ų, Z = 2. We also describe physical properties and provide a Raman spectrum. Among the mica compositions acquired from the same sample, a high Cl content is correlated with relative enrichment in Si, Mn, and Na and with a depletion in Al, Mg (low Mg#), K, Cr, and Ti. The buildup in Cl in the ore-forming environment is ultimately due to efficient fractional crystallization of the basic magma, with possible contributions from the Devonian metasedimentary sequences that it intruded. Full article

In recent days, aluminum-based hybrid composites have garnered more interest than monolithic alloys owing to their remarkable properties, encompassing a high strength-to-weight ratio, excellent corrosion resistance, and impressive wear durability. The present study attempts to optimize the multiple wear attribute characteristics of Al6061/SiC/Al₂O₃ hybrid composites using grey and entropy-based VIKOR techniques. The composites were produced by adding equal proportions of SiC/Al₂O₃ (0–12 wt.%) ceramics through the stir-casting process, using an ultrasonication setup. Dry sliding wear experiments were executed with tribometer variants, namely reinforcement content (wt.%), load (N), sliding velocity (v), and sliding distance (SD), following L₂₇ OA. The optimal combination of process variables for achieving high GRG values from grey analysis was found to be A₃-B₃-C₃-D₃. The S/N ratios and ANOVA results for GRG indicated that RF content (wt.%) is the predominant component determining multiple outcomes, followed by sliding distance, load, and sliding velocity. The multi-order regression model formulated for the VIKOR index (Q_i) displayed high significance and more accuracy, with a variance of 0.0216 and a coefficient of determination (R²), and adjusted R² values of 99.60% and 99.14%. Subsequent morphological studies indicated that plowing, abrasion, and adhesion mechanisms are the dominant modes of wear. Full article

This study investigates the influence of the HfB₂ content and sintering method on the mechanical behavior of Ti₂AlC-based composites. Compositions containing 0–10 wt.% HfB₂ are processed via conventional and microwave sintering at 1200 °C for 30 min. X-ray diffraction and scanning electron microscopy analyses have confirmed the formation of the Ti₂AlC and HfB₂ phases, whereas the TiC phase is predominantly observed in samples processed by conventional sintering. The highest hardness (~475 HV) and compressive strength (~450 MPa) are that of the composite containing 5 wt.% HfB₂ associated with a porosity reduction of approximately 10%. These improvements are attributed to the enhanced densification and microstructural refinement achieved via microwave processing. The findings underscore the potential of HfB₂ addition and microwave sintering in tailoring the structure–property relationships of the Ti₂AlC composites, enabling applications at high-temperature filtration, thermal barriers, and self-lubricating components. Full article

B₄C is beneficial for forming a glassy film that is effective at impeding oxygen diffusion and improving the oxidation resistance of coatings at high temperature. The effect of B₄C content on the oxidation resistance of a B₄C-SiO₂–Albite/Al₂O₃ (BSA/AO) double-layer coating by the slurry brushing method at 900 °C was investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) with energy-dispersive spectroscopy (EDS), and differential scanning calorimetry (DSC) with thermogravimetric analysis (TGA) in this work. It is indicated that the composite coating with 20 wt% B₄C exhibits excellent oxidation resistance at high temperature, which shows a mass loss of only 0.11% for the coated carbon block after being exposed to 900 °C for 196 h. This is attributed to the in situ formation of a thin, dense glass layer with good self-healing ability at the interface of the B₄C-SiO₂–Albite/Al₂O₃ composite coating within 1 h and the persistence and stability of the dense glass layer during exposure. The mechanism is discussed in detail. Full article

This study employed a composite method using TiB₂-HfC dual-component additive to prepare AlMgB₁₄ ceramic composite material. The morphology and phase composition of the AlMgB₁₄ ceramic powder were characterized using scanning electron microscopy (SEM) and an X-ray diffractometer (XRD). The phase evolution, microstructure, and mechanical properties of the sintered composite were investigated. The experimental results indicate that the AlMgB₁₄-based composite sintered at 1450 °C exhibited excellent comprehensive properties, with a Vickers hardness of 25.3 GPa, a fracture toughness of 6.9 MPa·m^1/2, a bending strength of 615 MPa, and a density of 3.22 g/cm³. Additionally, a solid solution second phase was observed in the AlMgB₁₄ material. Through a dual-component synergistic composite strategy, this study enhanced the toughness of AlMgB₁₄ material without significantly compromising other properties, providing a new design approach for the development of low-cost, high-performance AlMgB₁₄-based composites. Full article