Due to an oversight, the data of the last column “Vs” in
Table 1 was missing in the original version of this article [
1].
Table 1.
Glass composition, density, molar volume, molecular weight, longitudinal and shear ultrasonic wave velocities of (AlF3)x-(ZnO)y-(TeO2)z glasses. The pure TeO2 glass is included for comparison.
Table 1.
Glass composition, density, molar volume, molecular weight, longitudinal and shear ultrasonic wave velocities of (AlF3)x-(ZnO)y-(TeO2)z glasses. The pure TeO2 glass is included for comparison.
| Glass sample | Composition (mol%) | Density (kg·m−3) | Molar volume (cm3/mol) | Molar weight (g/mol) | Vl | Vs |
|---|
| AlF3 x | ZnOy | TeO2z | (m s−1) |
|---|
| Pure | 0 | 0 | 100 | 4806 | 33.21 | 159.61 | 3435 | 2115 |
| A1 | 0 | 10 | 90 | 5098 | 29.77 | 151.77 | 3324 | 2030 |
| A2 | 1 | 9 | 90 | 5023 | 30.22 | 151.80 | 3316 | 1979 |
| A3 | 3 | 7 | 90 | 5018 | 30.26 | 151.84 | 3364 | 2013 |
| A4 | 5 | 5 | 90 | 4963 | 30.61 | 151.92 | 3393 | 2038 |
| A5 | 7 | 3 | 90 | 4846 | 31.36 | 151.97 | 3424 | 2068 |
| A6 | 9 | 1 | 90 | 4779 | 31.81 | 152.02 | 3435 | 2075 |
| B1 | 0 | 15 | 85 | 5102 | 28.98 | 147.86 | 3307 | 2024 |
| B2 | 1 | 14 | 85 | 5075 | 29.14 | 147.89 | 3334 | 1987 |
| B3 | 5 | 10 | 85 | 4990 | 29.66 | 148.00 | 3409 | 2057 |
| B4 | 8 | 7 | 85 | 4898 | 30.23 | 148.07 | 3480 | 2123 |
| B5 | 12 | 3 | 85 | 4799 | 30.88 | 148.19 | 3486 | 2129 |
| B6 | 14 | 1 | 85 | 4756 | 31.65 | 150.53 | 3488 | 2134 |
| C1 | 0 | 20 | 80 | 5136 | 28.03 | 143.96 | 3296 | 1995 |
| C2 | 2 | 18 | 80 | 5124 | 28.1 | 143.98 | 3353 | 2009 |
| C3 | 5 | 15 | 80 | 5074 | 28.4 | 144.10 | 3398 | 2026 |
| C4 | 10 | 10 | 80 | 4950 | 28.33 | 140.23 | 3471 | 2100 |
| C5 | 15 | 5 | 80 | 4792 | 28.4 | 136.09 | 3528 | 2145 |
| C6 | 19 | 1 | 80 | 4743 | 30.45 | 144.42 | 3542 | 2174 |
We apologize for any inconvenience this may have caused.