Impact of Notches on Additively Manufactured Inconel 718 Tensile Performance

This study was completed in effort to characterize the notch sensitivity of additively manufactured (AM) Inconel 718 produced by laser powder bed fusion (L-PBF). Three different root radii on V-notched test specimens and smooth specimens were evaluated under tensile conditions for specimens built in vertical and horizontal orientations. Both the total axial strain and localized notch diametral strain were measured. Finite element analysis (FEA) was completed on each specimen geometry to confirm the actual strain measurements near the notch. Test results showed the tensile strength of the notched specimens were larger than the tensile strength values of the smooth specimens. These tensile results equate to a notch-sensitivity ratio (NSR) greater than one, indicating that the L-PBF Inconel 718 material is a notch-strengthened material. It is suspected that the notch strengthening is a result of increased triaxial stress produced near the notch tip causing added material constraints, resulting in higher strength values for the notched specimens. Fractography analysis was completed on the various fracture surfaces and identified a dominate ductile failure mode within all of the specimens; however, the amount of ductility reduced with smaller notch root radii. While this study provides the initial notch responses of the L-PBF Inconel 718, further research must be completed in regard to the impact of notches on more complex loading behaviors, such as fatigue and stress-rupture conditions.