Search Results (60)

Melt-spun Fe_70−xPd₃₀Ga_x ribbons (x = 1 and 3 at.% Ga) were heat-treated at 1223 K for 1 h and 2 h and characterized by X-ray diffraction, scanning electron microscopy, differential scanning calorimetry, magnetometry, and magnetoelastic measurements. Increasing Ga content decreases thermodynamic equilibrium temperature from 292.0 K (1 at.% Ga) to 283.5 K (3 at.% Ga) in as-prepared ribbons. Extended heat treatment then shifts it to 288.0 K and 264.5 K, respectively, and promotes Fe-rich precipitation. Fine precipitates at 1 h preserve a large transformable matrix fraction and introduce microstructural heterogeneity that governs variant mobility and domain-wall pinning; prolonged annealing triggers coalescence, depleting the matrix and reducing both the transformation heat and the magnetoelastic response. Kissinger analysis yields apparent activation energies of 338 kJmol⁻¹ (1 at.% Ga) and 228 kJmol⁻¹ (3 at.% Ga), confirming that higher Ga content lowers the transformation energy barrier. The magnetostrictive response depends on annealing: 1 h-annealed samples exhibit field-induced variant reorientation and saturation magnetostriction of ~60 ppm at 200 K, whereas 2 h-annealed samples approach volume-conserving behavior. Coercivity scales with precipitate density, with Ga3-2h showing anomalously soft magnetic behavior following coalescence. Thermally induced precipitation thus emerges as a route to simultaneously control microstructure, transformation kinetics, magnetoelastic response, and magnetic behavior in ferromagnetic shape memory alloys. Full article

Ni-Mn-Sn-based ferromagnetic shape memory alloys (FSMAs) are multifunctional materials that are promising for solid-state refrigeration applications based on the magnetocaloric effect (MCE) and elastocaloric effect (eCE). However, a combination of excellent multi-caloric properties, suitable operating temperatures, and mechanical properties cannot be well achieved in these materials, posing a challenge for their practical application. In this work, we systematically study the phase transformations and magnetic properties of Ni_50−xMn₃₈Sn₁₂Cu_x (x = 0, 2, 3, 4, 5, and 6) and Ni_50−yMn₃₈Sn₁₂Fe_y (y = 0, 1, 2, 3, 4, and 5) alloys, and the magnetic-structural phase diagrams of these alloy systems are reported. The influences of the fourth-element doping on the phase transitions and magnetic properties of the alloys are elucidated by first-principles calculations. This work demonstrates that the fourth-element doping of Ni-Mn-Sn-based FSMA is effective in developing multicaloric refrigerants for practical solid-state refrigeration. Full article

Fe-~30 at.%Pd is a ferromagnetic shape memory alloy (SMA) with a reversible thermoelastic fcc-fct phase transformation. The advantage of adding a small amount of Indium to Fe-Pd SMAs is, among other things, the upward shift of the transformation temperatures, which allows us to maintain the material in the martensitic state (fct structure) at room temperature. In this work, we study the microstructure and the magnetic properties of nominally Fe67.6-Pd32-In0.4 (at.%) melt-spun ribbons. Energy-dispersive spectroscopy analysis showed a certain level of non-uniformity of Indium distribution in the as-spun ribbon. However, the attempt to homogenize the ribbon by annealing at 1273 K for 120 h resulted in an unfavoured structural change to bct martensite. Magneto strains induced by a 9 kOe magnetic field reached over 400 ppm for certain field orientations, which is around four times more than the magneto strains of near-binary Fe-Pd shape memory alloys. Full article

Solid-state refrigeration based on elastocaloric materials (eCMs) requires reversibility and repeatability. However, the intrinsic intergranular brittleness of ferromagnetic shape memory alloys (FMSMAs) limits fatigue life and, thus, is the crucial bottleneck for its industrial applications. Significant cyclic stability of elastocaloric effects (eCE) via 53% porosity in Ni-Fe-Ga FMSMA has already been proven. Here, Ni-Fe-Ga foams (single-/hierarchical pores) with high porosity of 64% and 73% via tailoring the material’s architecture to optimize the eCE performances are studied. A completely reversible superelastic behavior at room temperature (297 K) is demonstrated in high porosity (64–73%) Ni-Fe-Ga foams with small stress hysteresis, which is greatly conducive to durable fatigue life. Consequentially, hierarchical pore foam with 64% porosity exhibits a maximum reversible ∆T_ad of 2.0 K at much lower stress of 45 MPa with a large COP_mat of 34. Moreover, it shows stable elastocaloric behavior (ΔT_ad = 2.0 K) over >300 superelastic cycles with no significant deterioration. The enhanced eCE cyclability can be attributed to the pore hierarchies, which remarkably reduce the grain boundary constraints and/or limit the propagation of cracks to induce multiple stress-induced martensitic transformations (MTs). Therefore, this work paves the way for designing durable fatigue life FMSMAs as promising eCMs by manipulating the material architectures. Full article

The magnetic domain structures and martensite microstructures of porous Ni₂MnGa Heusler alloys with various circle-shaped and ellipse-shaped pores were systematically studied by the phase field method. The magnetization curves and magnetic field-induced strains (MFIS) at the external field were determined. A mesoscopic mechanism was proposed for simulation to reveal the influence of the pores on the microstructures and the MFIS of porous magnetic shape memory alloy. The stress concentration effect and the recovery strain of the porous alloy are studied. The results indicate the MFIS value increases when ellipse-shaped pores elongate along the twin boundary. The effects of porosity and pore size on MFIS for porous Ni-Mn-Ga alloys with randomly distributed pores were also explored. The present study is of guiding significance for understanding the role played by pores on the MFIS and may provide a possible way to adjust the functional properties of ferromagnetic shape memory alloys. Full article

Solid-state refrigeration technology is expected to replace conventional gas compression refrigeration technology because it is environmentally friendly and highly efficient. Among various solid-state magnetocaloric materials, Ni-Mn-based ferromagnetic shape memory alloys (SMAs) have attracted widespread attention due to their multifunctional properties, such as their magnetocaloric effect, elastocaloric effect, barocaloric effect, magnetoresistance, magnetic field-induced strain, etc. Recently, a series of in-depth studies on the thermal effects of Ni-Mn-based magnetic SMAs have been carried out, and numerous research results have been obtained. It has been found that poor toughness and cyclic stability greatly limit the practical application of magnetic SMAs in solid-state refrigeration. In this review, the influences of element doping, microstructure design, and the size effect on the strength and toughness of Ni-Mn-based ferromagnetic SMAs and their underlying mechanisms are systematically summarized. The pros and cons of different methods in enhancing the toughness of Ni-Mn-based SMAs are compared, and the unresolved issues are analyzed. The main research directions of Ni-Mn-based ferromagnetic SMAs are proposed and discussed, which are of scientific and technological significance and could promote the application of Ni-Mn-based ferromagnetic SMAs in various fields. Full article

Ferromagnetic shape memory alloys (FSMAs), which are potential candidates for future technologies (i.e., actuators in robots), have been paid much attention for their high work per volume and rapid response as external stimulation, such as a magnetic field, is imposed. Among all the FSMAs, the Ni–Mn–Ga-based alloys were considered promising materials due to their appropriate phase transformation temperatures and ferromagnetism. Nevertheless, their intrinsic embrittlement issue and sluggish twin motion due to the inhibition of grain boundaries restrict their practicability. This study took advantage of the single-crystal Ni–Mn–Ga cube/silicone rubber composite materials to solve the two aforementioned difficulties. The single-crystal Ni–Mn–Ga cube was prepared by using a high-temperature alloying procedure and a floating-zone (FZ) method, and the cubes were verified to be the near-{100}_p Ni–Mn–Ga alloy. Various room temperature (RT) curing silicone rubbers were utilized as matrix materials. Furthermore, polystyrene foam particles (PFP) were used to provide pores, allowing a porous silicone rubber matrix. It was found that the elastic modulus of the silicone rubber was successfully reduced by introducing the PFP. Additionally, the magnetic field-induced martensite variant reorientation (MVR) was greatly enhanced by introducing a porous structure into the silicone rubber. The single-crystal Ni–Mn–Ga cube/porous silicone rubber composite materials are considered to be promising materials for applications in actuators. Full article

To meet the great requirements of future technologies, such as robots, single-crystal (SC) Ni-Mn-Ga alloys and their composites were designed and investigated in this study. Ferromagnetic shape memory alloys (FSMAs) are promising materials for applications in high-speed actuators, which are core components of robots; however, there are some issues of embrittlement and small deformation strain. Therefore, in this work, we first prepared SC Ni-Mn-Ga alloys for fundamental investigations of the shape deformations under the application of different fields (e.g., compressive and magnetic fields). Second, the SC Ni-Mn-Ga alloys were integrated with polymers of epoxy resin or silicone rubber to solve the embrittlement problem. The obvious two-stage yielding and sudden intensifying of the magnetization both suggest martensite variant reorientation (MVR) under the compressive and magnetic fields, respectively. Micro-computed tomography (μCT) and an X-ray diffractometer were utilized for the observations of shape deformation brought about by the MVR of the SC Ni-Mn-Ga particles in the polymer matrix. Clear MVR and shape deformation could be found in the compressed composites. Full article

In this study, magnetostriction measurements were performed on the ferromagnetic Heusler alloy, Ni₂MnGa_0.88Cu_0.12, which is characterized by the occurrence of the martensitic phase and ferromagnetic transitions at the same temperature. In the austenite and martensite phases, the alloy crystallizes in the L2₁ and D0₂₂-like crystal structure, respectively. As the crystal structure changes at the martensitic transition temperature (T_M), a large magnetostriction due to the martensitic and ferromagnetic transitions induced by magnetic fields is expected to occur. First, magnetization (M-H) measurements are performed, and metamagnetic transitions are observed in the magnetic field of μ₀H = 4 T at 344 K. This result shows that the phase transition was induced by the magnetic field under a constant temperature. Forced magnetostriction measurements (ΔL/L) are then performed under a constant temperature and atmospheric pressure (P = 0.1 MPa). Magnetostriction up to 1300 ppm is observed around T_M. The magnetization results and magnetostriction measurements showed the occurrence of the magnetic-field-induced strain from the paramagnetic austenite phase to the ferromagnetic martensite phase. As a reference sample, we measure the magnetostriction of the Ni₂MnGa-type (Ni₅₀Mn₃₀Ga₂₀) alloy, which causes the martensite phase transition at T_M = 315 K. The measurement of magnetostriction at room temperature (298 K) showed a magnetostriction of 3300 ppm. The magnetostriction of Ni₂MnGa_0.88Cu_0.12 is observed to be one-third that of Ni₅₀Mn₃₀Ga₂₀ but larger than that of Terfenol-D (800 ppm), which is renowned as the giant magnetostriction alloy. Full article

Terahertz absorbers have been extensively investigated by researchers due to their applications in thermophotovoltaic energy conversion and sensors, but a key factor limiting their development is the lack of vital and versatile materials. Ferromagnetic shape memory alloys (FSMAs) offer a novel remedy for tunable metamaterials due to their brilliant recovery of deformation, remote control, and transient response. In this study, we propose a tunable absorber based on magnetic field tuning, consisting of Ni–Mn–Sn ferro-magnetic shape memory alloy films in fractal geometry and optically excited Si plates. Numerical analysis shows that the proposed absorber has an absorbance bandwidth of 1.129 THz above 90% between 1.950 THz and 3.079 THz. The absorber geometry can be regulated by an external magnetic field, allowing dynamic switching between broadband and narrowband absorption modes, the latter showing an ultra-narrow bandwidth and a high-quality factor Q of ~25.8. The proposed terahertz absorber has several advantages over current state-of-the-art bifunctional absorbers, including its ultra-thin structure of 10.39 μm and an additional switching function. The absorption can be continuously tuned from 90% to 5% when the light-excited silicon plate is transferred from the insulator state to the metal state. This study presents a promising alternative strategy for developing actively regulated and versatile terahertz-integrated devices. Full article

We present the design, simulation, and characterization of a magnetic shape-memory alloy (MSMA) film actuator that transitions from bistable switching to resonant self-actuation when subjected to a stationary heat source. The actuator design comprises two Ni-Mn-Ga films of 10 µm thickness integrated at the front on either side of an elastic cantilever that moves freely between two heatable miniature permanent magnets and, thus, forms a bistable microswitch. Switching between the two states is induced by selectively heating the MSMA films above their Curie temperature Tc. When continuously heating the permanent magnets above Tc, the MSMA film actuator exhibits an oscillatory motion in between the magnets with large oscillation stroke in the frequency range of 50–60 Hz due to resonant self-actuation. A lumped-element model (LEM) is introduced to describe the coupled thermo-magnetic and magneto-mechanical performance of the actuator. We demonstrate that this performance can be used for the thermomagnetic energy generation of low-grade waste heat (T < 150 °C) with a high power output per footprint in the order of 2.3 µW/cm². Full article

High-speed actuators are greatly required in this decade due to the fast development of future technologies, such as Internet-of-Things (IoT) and robots. The ferromagnetic shape memory alloys (FSMAs), whose shape change could be driven by applying an external magnetic field, possess a rapid response. Hence, these materials are considered promising candidates for the applications of future technologies. Among the FSMAs, the Ni-Mn-Ga-based materials were chosen for their large shape deformation strain and appropriate phase transformation temperatures for near-room temperature applications. Nevertheless, it is widely known that both the intrinsic brittleness of the Ni-Mn-Ga alloy and the constraint of shape deformation strain due to the existence of grain boundaries in the polycrystal inhibit the applications. Therefore, various Ni-Mn-Ga-based composite materials were designed in this study, and their shape deformation behaviors induced by compressive or magnetic fields were examined by the in situ micro CT observations. In addition, the dependence of the martensite variant reorientation (MVR) on the crystallographic directions was also investigated. It was found that most of the MVRs are active within the magnetic field range applied in the regime of the <100>_p, <110>_p, and <111>_p of the single-crystal {100}_p Ni-Mn-Ga cubes. Full article

Magnetic hysteresis is a manifestation of non-equilibrium state of magnetic domain walls trapped in local energy minima. Using two types of experiments we show that, after application of a magnetic field to a ferromagnet, acoustic oscillations excited in the latter can “equilibrate” metastable magnetic domain structure by triggering the motion of domain walls into more stable configurations. Single crystals of archetypal Ni₂MnGa magnetic shape memory alloy in the cubic phase were used in the experiments. The magnetomechanical absorption of ultrasound versus strain amplitude was studied after step-like changes of a polarizing magnetic field. One-time hysteresis was observed in strain amplitude dependences of magnetomechanical internal friction after step-like variations of a polarizing field. We distinguish two ingredients of the strain amplitude hysteresis that are found in the ranges of linear and non-linear internal friction and show qualitatively different behavior for increasing and decreasing applied polarizing fields. The uncovered effect is interpreted in terms of three canonical magnetomechanical internal friction terms (microeddy, macroeddy and hysteretic) and attributed to “triggering” by acoustic oscillations of the irreversible motion of domain walls trapped in the metastable states. To confirm the suggested interpretation we determine the coercive field of magnetization hysteresis through the measurements of the reversible Villari effect. We show that the width of the hysteresis loops decreases when acoustic oscillations in the non-linear range of domain wall motion are excited in the crystal. The observed “equilibration” of the magnetic domain structure by acoustic oscillations is attributed to the periodic stress anisotropy field induced by oscillatory mechanical stress. Full article

The martensitic phase transition and exchange bias effect of the Ni-Mn-based ferromagnetic shape memory alloys (FSMAs) Ni₄₅Co₅Mn₃₇In₁₃ (Ni-Co-Mn-In) films are investigated in this paper. The martensitic transformation properties of the Ni-Co-Mn-In alloy target material are manipulated by the process of electric arc melting, melt-fast quenching, and high-temperature thermal pressure. The Ni-Co-Mn-In alloy films with martensite phase transition characteristics are obtained by adjusting deposition parameters on the (001) MgO substrate, which shows a significant exchange bias (EB) effect at different temperatures. With increasing sputtering power and time, the film thickness increases, resulting in a gradual relaxation of the constraints at the interface between the film and the substrate (the interfacial strain decreases as the increase of thin film thickness), which promotes the martensite phase transition. Between zero-field cooling (ZFC) and field-cooled (FC) curve obvious division zone, the decrease of exchange bias field (H_EB) and coercive force field (H_c) with an increase in test temperature is due to ferromagnetic (FM) interaction begins to dominate, resulting in a reduction of antiferromagnetic (AFM) anisotropy at the interface. The maximal H_EB and H_c reach ~465.7 Oe and ~306.9 Oe at 5 K, respectively. The manipulation of the martensitic transformation and EB effect of the Ni-Co-Mn-In alloy films demonstrates potential application in the field of information and spintronics. Full article

Shape memory alloys, especially ferromagnetic shape memory alloys, are interesting new materials for the manufacturing of stents. Iron–palladium alloys in particular can be used to manufacture self-expanding temporary stents due to their optimum rate of degradation, which is between that of magnesium and pure iron, two metals commonly used in temporary stent research. In order to avoid blood clotting upon the introduction of the stent, they are often coated with anticoagulants. In this study, sulfated pectin, a heparin mimetic, was synthesized in different ways and used as coating on multiple iron–palladium alloys. The static and dynamic prothrombin time (PT) and activated partial thromboplastin time (APTT) of the prepared materials were compared to samples uncoated or coated with polyethylene glycol. While no large differences were observed in the prothrombin time measurements, the activated partial thromboplastin time increased significantly with all alloys coated with sulfated pectin. Aside from that, sulfated pectin synthesized by different methods also caused slight changes in the activated partial thromboplastin time. These findings show that iron–palladium alloys can be coated with anticoagulants to improve their utility as material for temporary stents. Sulfated pectin was characterized by nuclear magnetic resonance (NMR) and Fourier-transform infrared (FTIR) spectroscopy, and the coated alloys by scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDX). Full article