Aluminum matrix composites provide an ideal solution for lightweight brake disks, but conventional casting processes are prone to crack initiation due to inhomogeneous reinforcement dispersion, gas porosity, and inadequate toughness. To break the conventional trade-off between high wear resistance and low toughness of brake disks, this study fabricated a bimetallic structure of SiC_p/Al–Fe–V–Si aluminum matrix composite and cast ZL101 alloy using friction stir lap welding (FSLW). Then, the microstructural evolution, mechanical properties, and tribological behavior of the FSLW joints were studied by XRD, SEM, TEM, tensile testing, and tribological tests. The results showed that the FSLW process homogenized the distribution of SiC particle reinforcements in the SiC_p/Al–Fe–V–Si composites. The Al₁₂(Fe,V)₃Si heat-resistant phase was not decomposed or coarsened, and the mechanical properties were maintained. The FSLW process refined the grains of the ZL101 aluminum alloy through recrystallization and fragmented eutectic silicon, improving elongation to 22%. A metallurgical bond formed at the joint interface. Tensile fracture occurred within the ZL101 matrix, demonstrating that the interfacial bond strength exceeded the alloy’s load-bearing capacity. In addition, the composites exhibited significantly enhanced wear resistance after FSLW, with their wear rate reduced by approximately 40% compared to the as-received materials, which was attributed to the homogenized SiC particle distribution and the activation of an oxidative wear mechanism. Full article

Bio-based polyurethane asphalt binder (PUAB) derived from castor oil (CO) is environmentally friendly and exhibits extended allowable construction time. However, CO imparts inherently poor mechanical performance to bio-based PUAB. To address this limitation, attapulgite (ATT) with fibrous nanostructures was incorporated. The effects of ATT on bio-based PUAB were systematically investigated, including cure kinetics, rotational viscosity (RV) evolution, phase-separation microstructures, dynamic mechanical properties, thermal stability, and mechanical performance. Experimental characterization employed Fourier transform infrared spectroscopy, Brookfield viscometry, laser scanning confocal microscopy, dynamic mechanical analysis, thermogravimetry, and tensile testing. ATT incorporation accelerated the polyaddition reaction conversion between isocyanate groups in polyurethane (PU) and hydroxyl groups in ATT. Paradoxically, it reduced RV during curing, prolonging allowable construction time proportionally with clay content. Additionally, ATT’s compatibilizing effect decreased bitumen particle size in PUAB, with scaling proportionally with clay loading. While enhancing thermal stability, ATT lowered the glass transition temperature and damping properties. Crucially, 1 wt% ATT increased tensile strength by 71% and toughness by 62%, while maintaining high elongation at break (>400%). The cost-effectiveness and significant reinforcement capability of ATT make it a promising candidate for producing high-performance bio-based PUAB composites. Full article

This study investigates the effect of hemp shive granulometry on the thermal conductivity and microstructure of hemp–lime composites. Three distinct particle size fractions—fine, medium, and coarse—were characterized using high-resolution image analysis to determine geometric parameters such as Feret diameters, circularity, and elongation. Composite mixtures with varying binder-to-shive and water-to-shive ratios were prepared and compacted at a consistent level to isolate the influence of aggregate granulometry on thermal performance. Results demonstrate a clear inverse relationship between particle size and thermal conductivity, with coarse fractions reducing thermal conductivity by up to 7.6% compared to fine fractions. Composite density was also affected, decreasing with increasing particle size, confirming the impact of granulometry on pore structure and packing density. However, binder content exhibited the most significant effect on thermal conductivity, with a 20% increase observed for higher binder-to-shive ratios irrespective of shive size. The study further establishes that a 15 g sample size (~2400 particles) provides sufficient statistical accuracy for granulometric characterization using image analysis. These findings provide critical insights for optimizing hemp–lime composites for enhanced thermal insulation performance, supporting sustainable construction practices by informing material formulation and processing parameters. Full article

Gaucher disease (GD) is an autosomal recessive disorder caused by the deficient activity of the lysosomal enzyme glucocerebrosidase (GCase). Although enzyme replacement therapy (ERT) remains the standard of care for non-neuropathic GD patients, its high cost significantly limits accessibility. To enhance production efficiency, we developed a lentiviral system encoding a codon-optimized GCase gene driven by the human elongation factor 1a (hEF1α) promoter for stable production in human cell lines. A functional lentiviral vector, LV_EF1α_GBA_Opt, was generated at a titer of 7.88 × 10⁸ LV particles/mL as determined by qPCR. Six transduction cycles were performed at a multiplicity of infection of 30–50. The transduced heterogeneous human cell population showed GCase-specific activity of 307.5 ± 53.49 nmol/mg protein/h, which represents a 3.21-fold increase compared to wild-type 293FT cells (95.58 ± 16.5 nmol/mg protein/h). Following single-cell cloning, two clones showed specific activity of 763.8 ± 135.1 and 752.0 ± 152.1 nmol/mg/h (clones 15 and 16, respectively). These results show that codon optimization, a lentiviral delivery system, and clonal selection together enable the establishment of stable human cell lines capable of producing high levels of biologically active, synthetic recombinant GCase in vitro. Further studies are warranted for the functional validation in GD patient-derived fibroblasts and animal models. Full article

This article presents the results of studies of the degradation of the structure and mechanical properties of the core materials BN-350 fast neutron and research WWR-K reactors required to justify the service life extension of early-generation power and research reactors. Extending the service life of nuclear reactors is a modern problem, since most operating reactors are early-generation reactors that have exhausted their design lifespan. The possibility of extending the service life is largely determined by the condition of the structural materials of the nuclear facility, i.e., their residual resources must ensure safe operation of the reactor. For the SAV-1 alloy, the structural material of the WWR-K reactor, studies were conducted on witness samples which were in the active zone during its operation for 56 years. It was found that yield strength and tensile strength of the irradiated SAV-1 alloy decreased by 24–48%, and relative elongation decreased by ~2% compared to the unirradiated alloy. Inside the grains and along their boundaries, there were particles of secondary phases enriched with silicon, which is typical for aged aluminum alloys. For irradiated structural steels of power reactors, studied at 350–450 C, hardening and a damping nature of creep were revealed, caused by dispersion hardening and the Hall–Petch effect. Full article

High-density polyethylene (HDPE) is a widely used polymer known for its excellent mechanical properties and chemical resistance. This study investigated the impact of incorporating varying percentages of nano-graphene particles (NGP) into HDPE on its thermal, mechanical, and tensile properties. Differential scanning calorimetry (DSC) analysis revealed that the addition of NGP enhanced the thermal stability and crystallization behavior of HDPE, with optimal performance observed at a 5% NGP concentration. Mechanical property evaluations indicated that small additions of NGP initially reduced zero-shear viscosity from 114,667 Pa·s to 44,045 Pa·s at 1% NGP, but higher concentrations improved the material’s rigidity and strength, with the best results at 3% NGP, where the flexural modulus reached 980 MPa. Tensile tests showed that while small amounts of NGP may decrease tensile strength from 26.4 MPa to 23.5 MPa at 1% NGP, higher concentrations significantly enhanced these properties, with tensile strength at break reaching 27 MPa and tensile elongation peaking at 20.8% at 7% NGP. The findings highlight the potential of NGP to enhance the performance of HDPE composites, making them suitable for a wide range of industrial applications. These enhanced composites are particularly important for the bottling industry, where improved material properties can lead to lighter, stronger, and more efficient packaging solutions. Full article

GTD 111 has been employed in first-stage blades in different gas turbines. The study of microstructural evolution is essential for the lifetime assessment and development of turbine blades. The microstructural stability of a 130 MW gas turbine first-stage blade at 800 °C was studied. The microstructure’s evolution was analyzed using scanning electron microscopy (SEM), transmission electron microscopy (TEM), and thermodynamic calculation. As thermal exposure time increases, the shape of γ′ precipitates changes from square to spherical. During thermal exposure, MC particles formed and coarsened along the grain boundaries, and primary MC carbide decomposed into the η phase and M₂₃C₆. The stability of MC carbide at the grain boundaries was lower than that within the grains. MC carbide precipitated at the grain boundaries tends to grow along the boundaries and eventually forms elongated carbide. High-resolution transmission electron microscopy (HRTEM) images indicate that the orientation of the γ′ precipitate changes during the coarsening process. The GTD 111 alloy can be deformed through dislocation shearing at 800 °C. The hardness value initially increases, then decreases with further exposure, which is related to the reduced precipitation strengthening by γ′ precipitates and the reduction in the hardness of the γ matrix. Full article

In this study, solid particle erosion tests were conducted to evaluate the resistance of AISI 4340 (EN24) and 8620 alloy steels against silicon carbide (SiC). These steels were selected due to their high hardness, yield strength (σ_y), ultimate tensile strength (σ_uts) and elongation (%), which are significant parameters, influencing wear resistance. An erosion rig based on the ASTM G76-95 standard was used to perform the testing. Tests were carried out using different impact angles, 30°, 45°, 60° and 90°, with a particle velocity of 24 ± 2 m/s. The abrasive flow rate was 0.7 ± 0.5 g/min and the temperature was between 35 °C and 40 °C. Characterization techniques such as SEM were employed to identify the chemical composition of AISI 4340 and AISI 8620 steels and optical microscopy to determine the morphology of SiC abrasive particles. In addition, the SiC particle size was between 350 and 450 µm; it was determined by the particle size distribution technique. SEM micrographs were obtained to classify the wear mechanisms, characterized by micro-cutting, micro-ploughing, grooves, pitting actions and embedded particles on the surface at 30° and 90°. The results showed that AISI 8620 steel exhibited higher erosion resistance than AISI 4340 steel. Finally, AFM was used to evaluate the roughness variations before and after erosion tests, specifically in the central zone of the wear scars at 30° and 90° for both materials. Full article

This work systematically investigates the Zn-content-dependent phase evolution (1–12 at.%) and its correlation with mechanical properties in as-cast Mg–2Y–xZn alloys. A sequential phase transformation is observed with the Zn content increasing: the microstructure evolves from X-phase dominance (1–2 at.% Zn) through W-phase formation (3–6 at.% Zn) to I-phase emergence (12 at.% Zn). Optimal mechanical performance is attained in the 2 at.% Zn-containing alloy, with measured tensile properties reaching 239 MPa UTS and 130 MPa YS, while maintaining an elongation of 12.62% prior to its gradual decline at higher Zn concentrations. Crystallographic analysis shows that the most significant strengthening effect of the X-phase originates from its coherent orientation relationship with the α-Mg matrix and the development of deformation-induced kink bands. Meanwhile, fine W-phase particles embedded within the X-phase further enhance alloy performance by suppressing X-phase deformation, revealing pronounced synergistic strengthening between the two phases. Notably, although both the I-phase and W-phase act as crack initiation sites during deformation, their coexistence triggers a competitive fracture mechanism: the I-phase preferentially fractures to preserve the structural integrity of the W-phase, effectively mitigating crack propagation. These dynamic interactions of second phases during plastic deformation—synergistic strengthening and competitive fracture—provide a novel strategy and insights for designing high-performance Mg–RE–Zn alloys. Full article

Flexible strain sensors, fabricated from high-elongation polymers and conductive filler particles, are proving an essential tool in the study of biomechanics using wearable technology. It has been previously shown that the resistive response of such composites, relative to the amount of conductive filler material, can be reasonably modeled using a standard percolation-type model. Once a certain critical fraction of filler material is reached, a conductive network across the sample is established and resistance rapidly decreases. However, modeling the more subtle resistance changes that occur while deforming the sensors during operation is more nuanced. Conductivity across the network of particles is dominated by tunneling mechanisms at the interfaces between the filler materials. Small changes in strain at these interfaces lead to relatively large, but nevertheless continuous, changes in local resistance. By assigning some arbitrary value of resistance as a dividing line between ‘low’ and ‘high’ resistance, one might model the piezoresistive behavior using a standard percolation model. But such an assumption is likely to lead to low accuracy. Our alternative approach is to divide the range of potential resistance values into several bins (rather than the usual two bins) and apply a relatively novel multi-state percolation theory. The performance of the multi-state percolation model is assessed using a random resistor model that is assumed to provide the ground truth. The model is applied to predict resistance response with both changes in relative amount of conductive filler (i.e., to help design the initial unstrained sensor) and with applied strain (for an operating sensor). We find that a multi-state percolation model captures the behavior of the simulated composite sensor in both cases. The multicomponent percolation theory becomes more accurate with more divisions/bins of the resistance distribution, and we found good agreement with the simulation using between 10 and 20 divisions. Full article

This study investigates the industrial potential of red gypsum (RG), a major by-product of titanium dioxide (TiO₂) production, for the development of thermoplastic polypropylene (PP)-based composites via melt extrusion, targeting agricultural applications. Prior to compounding, RG was thermally treated at approximately 200 °C to remove residual moisture and chemically bound water, resulting in its anhydrous form (CaSO₄). PP/RG composites were then formulated with RG loadings up to 20 wt.%, employing stearic acid (SA) as a compatibilizer. The resulting materials were thoroughly characterized and successfully processed through industrial-scale injection molding up to 250 °C. Morphological and FTIR analyses confirmed the role of SA in enhancing both filler dispersion and interfacial adhesion between RG and the PP matrix. SEM images revealed finer and more uniformly distributed RG particles, resulting in a reduced loss of ductility and elongation at break typically associated with filler addition. Specifically, the Young’s Modulus increased from 1.62 GPa (neat PP) up to 3.21 GPa with 20 wt.% RG and 0.6 wt.% SA. The addition of 0.6 wt.% SA also helped limit the reduction in stress at break from 46.68 MPa (neat PP) to 34.05 MPa and similarly mitigated the decrease in Charpy impact energy, which declined slightly from 2.66 kJ/m² (neat PP) to 2.24 kJ/m² for composites containing 20 wt.% RG. Preliminary phytotoxicity was assessed using germination tests on Lepidium sativum L. seeds. Eluates from both untreated and SA-treated RG powders resulted in germination indices below 80%, indicating phytotoxicity likely due to high sulfate ion concentrations. In contrast, eluates from composite pellets exhibited germination indices equal to or exceeding 100%, demonstrating the absence of phytotoxic effects. These results highlight the suitability of the developed composites for applications in floriculture and horticulture. The optimized composite pellets were successfully processed via injection molding to manufacture plant pots, which exhibited a dark brown coloration, confirming the effective pigmenting function of RG. These results demonstrate the potential of red gypsum to serve both as a functional filler and pigment in PP composites, providing a sustainable alternative to iron oxide pigments and promoting the valorization of industrial waste through resource recovery. Full article

This study developed sustainable biocomposites composed of polylactic acid (PLA) and surface-treated pineapple core powder (PACP), fabricated via extrusion and fused deposition modelling (FDM). PACP loadings of 1–3 vol% were combined after chemical modification with NaOH and silane to improve interfacial bonding. Particle morphology showed increased porosity and surface roughness following treatment. The melt flow index (MFI) increased from 31.56 to 35.59 g/10 min at 2 vol% PACP, showing improved flowability. Differential scanning calorimetry (DSC) showed the emergence of cold crystallization (T_cc ~121 °C) and an increase in crystallinity from 35.7% (neat PLA) to 47.3% (2 vol% PACP). Thermogravimetric analysis showed only slight decreases in T₅ and T_max, showing the thermal stability. The mechanical testing of extruded filaments showed increased modulus (1463 to 1518 MPa) but a decrease in tensile strength and elongation. For the 3D-printed samples, elongation at break increased slightly at 1–2 vol% PACP, likely because of the improvement in interlayer fusion. Though, at 3 vol% PACP, the mechanical properties declined, consistent with filler agglomeration observed in SEM. Overall, 2 vol% PACP offered the optimal balance between printability, crystallinity, and mechanical performance. These results reveal the possibility of PACP as a value-added biowaste filler for eco-friendly PLA composites suitable for extrusion and 3D printing applications. Full article

In this research, novel biocomposite filaments were developed by incorporating coffee silver skin (CSS) waste into polylactic acid (PLA) for use in Fused Filament Fabrication (FFF) technology. CSS was blended with PLA at concentrations of 0, 5, 10, and 15 wt.% to address the waste disposal challenge and produce environmentally friendly composite biofilaments for FFF, supporting circular economic efforts. These filaments have the potential to be used in sustainable prototyping, functional parts, and consumer products. A comprehensive analysis was conducted to examine the effect of printing temperature on dimensional accuracy, melt flow index (MFI), and mechanical properties. Higher printing temperatures and increased CSS content led to larger dimensions due to increased material fluidity, as confirmed by MFI results, which increased from 3.5 g/10 min (0% CSS) to 5.8 g/10 min (15% CSS) at 180 °C, reaching 26.3 g/10 min at 220 °C. Tensile tests on 3D-printed specimens indicated an improvement in elastic modulus with increasing CSS content at lower temperatures (180 °C), rising from 1622 MPa (0% CSS) to 1952 MPa (15% CSS), representing about a 20% increase. However, at higher temperatures, the elastic modulus decreased, possibly due to the poor dispersion and agglomeration of filler particles. Tensile strength generally decreased with CSS addition, especially at higher loadings, while yield elongation remained low (~1.4–1.7%), indicating a more brittle material. The findings also revealed no significant thermal changes with increasing CSS content, and good printability was achieved for all compositions, which was characterized by good layer adhesion, the absence of warping, and the ease of extrusion. Full article

This study investigates the microstructure and mechanical properties of Inconel 718, a nickel-based alloy, reinforced with ceramic phases via additive manufacturing. Two reinforcement strategies were explored: in situ formation of ceramic phases through titanium powder addition, and direct incorporation of Cr₂O₃ and TiO₂ ceramic particles. Both approaches significantly modified the alloy’s microstructure and elemental distribution. The in situ formation method produced leaf-like Ti-rich precipitates (up to 70.13 wt%), while direct ceramic addition suppressed the preferred orientation of the Laves phase and promoted the formation of NbC precipitates. Microhardness increased by 19.4% with titanium addition, compared to a modest 1.3% improvement with direct ceramic addition. Tensile testing revealed that titanium powder enhanced ultimate tensile strength but reduced elongation, whereas direct ceramic addition led to decreases in both strength and ductility. Wear resistance evaluation showed that direct ceramic addition yielded superior performance, evidenced by the lowest friction coefficient (0.514) and smallest wear volume (16,290,782 μm³). These findings demonstrate the effectiveness of ceramic reinforcement strategies in optimizing the mechanical and tribological behavior of additively manufactured Inconel 718, and offer valuable guidance for the development of wear-resistant components such as those used in hydraulic support systems. Full article

This study investigates the factors affecting the mechanical performance of conventional and impulse friction stir welded (FSW and IFSW) AA2024-T351 joints under static and cyclic loading. Emphasis is placed on the influence of fracture-inducing features such as oxide inclusions, constituent particle distributions, crystallographic texture, and precipitation state. A series of IFSW welds produced at varying impulse parameters were compared to conventional FSW welds in terms of microhardness, tensile strength, fatigue life, and Taylor factor distribution. IFSW joints demonstrated a significant improvement in tensile strength and elongation, particularly at higher impulse frequencies. Enhanced material mixing due to the reciprocating tool motion in IFSW resulted in finer particle distribution, more favorable crystallographic texture, and reduced weld pitch, all contributing to increased ductility and strength. Fractographic analyses revealed that fatigue failures primarily initiated in the stir zone, typically at unplasticized metallic inclusions. However, IFSW joints displayed longer fatigue lives, particularly when impulse parameters were optimized. These findings underline the complex interplay of microstructural and textural factors in determining weld performance, highlighting IFSW as a promising technique for enhancing the durability of high-strength aluminum welds. Full article