We report the synthesis and multifunctional characterization of copper-reinforced Ba_0.85Sr_0.15TiO₃ (BST) ceramic composites with Cu contents ranging from 0 to 40 wt%, prepared by a sol–gel route and densified using spark plasma sintering (SPS). X-ray diffraction and FT-IR analyses confirm the coexistence of cubic and tetragonal BST phases, while Cu remains as a chemically separate metallic phase without detectable interfacial reaction products. Microstructural observations reveal abnormal grain growth induced by localized liquid-phase-assisted sintering and progressive Cu agglomeration at higher loadings. Scanning electron microscopy reveals abnormal grain growth, with the average BST grain size increasing from approximately 3.1 µm in pure BST to about 5.2 µm in BST–Cu40% composites. Optical measurements show a continuous reduction in the effective optical bandgap (apparent absorption edge) from 3.10 eV for pure BST to 2.01 eV for BST–Cu40%, attributed to interfacial electronic states, defect-related absorption, and enhanced scattering rather than Cu lattice substitution. Electrical characterization reveals a percolation threshold at approximately 30 wt% Cu, where AC conductivity and dielectric permittivity reach their maximum values. Impedance spectroscopy and equivalent-circuit analysis demonstrate strong Maxwell–Wagner interfacial polarization, yielding a maximum permittivity of ~1.2 × 10⁵ at 1 kHz for BST–Cu30%. At higher Cu contents, conductivity and permittivity decrease due to disrupted Cu connectivity and increased porosity. These findings establish BST–Cu composites as tunable ceramic–metal systems with enhanced dielectric and optical responses, demonstrating potential for specialized high-capacitance decoupling applications where giant permittivity is prioritized over low dielectric loss. Full article

Bone regeneration relies on the coordinated interplay between mechanical and biological cues. Piezoelectric composites, capable of converting mechanical strain into electrical signals, offer a promising approach to stimulate osteogenesis. This study aimed to develop and characterize polycaprolactone (PCL) and barium titanate (BaTiO₃) composite scaffolds fabricated through thermally induced phase separation (TIPS), and to systematically evaluate the effects of polymer concentration and ceramic incorporation on scaffold morphology, porosity, mechanical properties, and cytocompatibility were systematically evaluated. The resulting scaffolds exhibited a highly porous, interconnected architecture, with 9% PCL formulation showing the most uniform morphology and consistent mechanical and biological behavior. Incorporation of BaTiO₃ did not alter pore structure or compromise cytocompatibility but slightly enhanced stiffness and surface uniformity. SEM-based image analysis confirmed homogeneous BaTiO₃ dispersion across all formulations. MTT assays and confocal microscopy demonstrated robust pre-osteoblast adhesion and spreading, particularly on denser composite scaffolds, confirming that the inclusion of BaTiO₃ supports a favorable environment for cell proliferation. Overall, optimizing polymer concentration and ceramic dispersion enables fabrication of structurally coherent, cytocompatible scaffolds. The findings establish structure–property–biology relationships that serve as a baseline for future investigations into the electromechanical behavior of PCL/BaTiO₃ scaffolds and their potential to promote osteogenic differentiation under physiological loading. Full article

The investigation of environmentally friendly, Pb-free ceramic dielectric materials with excellent energy storage capability represents a fundamental yet challenging research direction for the development of next-generation high-power capacitors. In this study, linear dielectric Ca_0.7La_0.2(Mg_1/3Nb_2/3)O₃ was added into [0.65BaTiO₃–0.35(Na_0.5Bi_0.5)TiO₃] to form a solid solution. The introduction of Ca_0.7La_0.2(Mg_1/3Nb_2/3)O₃ modified the crystal structure, enhanced insulation performance and breakdown strength, and reduced hysteresis loss. These improvements collectively contributed to higher energy storage density and efficiency (η). The ceramic pellet with the optimal 10 mol% Ca_0.7La_0.2(Mg_1/3Nb_2/3)O₃ demonstrated a higher retrievable energy density (~3.40 J cm⁻³) and efficiency (~81%) at a breakdown strength of 340 kV cm⁻¹ compared to BaTiO₃-based ferroelectric ceramics. The sample also exhibited good stability across a temperature range of 30–90 °C and a frequency range of 0.5–300 Hz. Thus, the as-prepared ceramics sample exhibited significant potential for pulsed power device applications. Full article

Background/Objectives: Barium titanate (BaTiO₃)-based nanocarriers have emerged as versatile and promising platforms for targeted drug delivery, owing to their unique combination of biocompatibility, piezoelectric and ferroelectric properties, as well as responsiveness to external stimuli. These multifunctional ceramic nanoparticles can be precisely engineered to enable spatiotemporally controlled release of therapeutic agents, triggered by physical stimuli such as ultrasound, light, magnetic fields, temperature changes, and pH variations. Such an approach enhances treatment efficacy while reducing systemic side effects. Methods: This review provides a comprehensive overview of the latest advancements in the development and biomedical application of BaTiO₃-based nanocarriers. Special emphasis is placed on modern synthesis strategies, surface functionalization methods, and the integration of BaTiO₃ with other functional nanomaterials to create hybrid systems with improved therapeutic performance. Key challenges in clinical translation are also discussed, including biocompatibility assessment, biodistribution, and regulatory requirements. Conclusions: BaTiO₃-based nanocarriers show promise as materials well suited for advanced biomedical applications. The paper concludes with an outline of future research directions aimed at optimizing these advanced nanosystems for precision and personalized medicine, with applications in oncology, anti-infective therapy, and regenerative medicine. Full article

The interest in synthesizing new dielectric materials is caused by their potential application in various electronic and sensor devices as well as in a large variety of electronic components. The present work reports the synthesis of glasses in the Na₂O/Al₂O₃/BaO/ZrO₂/TiO₂/B₂O₃/SiO₂ system prepared by melt-quenching. These glasses were then crystallized to glass–ceramics by a controlled thermal treatment. X-ray diffraction experiments reveal the precipitation of Ba₂TiSi₂O₈ (fresnoite) and BaTiO₃, which probably forms a BaZr_xTi_1−xO₃ solid solution. The microstructure is studied by scanning electron microscopy and shows the presence of mulberry-shaped, crystallized structures with a densely-branching morphology. Microcomputed X-ray tomography is used to gather information on the volume fraction and average size of the crystallized volume as an effect of the applied temperature–time schedule. Longer annealing times lead to a higher volume fraction and increasing average size of the crystallization structures obtained. The dielectric properties analyzed by impedance spectroscopy are insulating and show relatively high dielectric constants ≥ 100 and moderate loss tangent values at 10 kHz. Full article

Lead-free ceramic materials have been widely studied since dielectric capacitors became a key component for energy storage. In this work, we adopted defect dipole engineering and improved the energy storage performance of barium zirconate titanate (BZT) ceramics by doping them with MnO₂. With the increase in Mn content, the hysteresis loop changed from a conventional loop to a pinned hysteresis loop, resulting in a decrease in remnant polarization (P_r). When x = 0.02, the recoverable energy storage density (W_rec) reached 0.1561 J/cm² @ 40 kV/cm, a 59% increase from undoped BZT. Further, XPS and EPR analyses confirmed that many oxygen vacancies were generated. We also performed SEM and TEM characterization and observed the microstructures. These results are consistent with theories suggesting that the formation of the pinned hysteresis loop is attributable to oxygen vacancies and defect dipoles. Full article

Flexible electronics is an applicative field in continuous expansion. This article addresses the requirements of this domain regarding eco-friendly and flexible components from a renewable chitosan polysaccharide that is progressively reinforced with barium titanate nanoparticles. Ultrafine ceramic powder was produced by the coprecipitation method, and the resulting phase composition and morphology were investigated by X-ray diffraction and transmission electron microscopy, together with the perovskite structure of the spherical nanoparticles. FTIR studies were conducted to elucidate the interactions between the two constituting phases of the composites. The filler dispersion in the matrix was checked by scanning electron microscopy. The rheological percolation threshold was compared with that extracted from electrical measurements. The thermal behavior was assessed by thermogravimetry and differential scanning calorimetry. The dielectric properties as a function of frequency and applied electric field were investigated, and the results are discussed in terms of extrinsic contributions. The current results demonstrate a straightforward method for producing tunable flexible structures. Full article

The design of piezoelectric roads is one of the future directions of smart roads. In order to ensure the environmentally friendly and long-lasting use of piezoelectric road materials, lead-free piezoelectric ceramics (barium titanate), polymer piezoelectric materials (polyvinylidene fluoride), and conductive particles (conductive carbon black and graphene) were used to prepare composite piezoelectric materials. The electrical performance was studied by the conductivity, dielectric properties, and piezoelectric properties of the composite materials. Then, the mechanical properties of the composite material were investigated by load compression tests. Finally, the microstructure of the composite materials was studied. The results showed that as the amount of conductive particles increased, the electrical performance was improved. However, further addition of conductive particles led to a decline in the electrical performance. The addition of conductive particles had a minimal effect on the mechanical properties of composite materials. The composite material met road use requirements. The overall structure of the composite materials was compact, with a clear wrapping effect of the polymer, and good interface compatibility. The addition of conductive carbon black and graphene had no significant impact on the structure of the composite materials. Full article

A 3D-printable, ARDUINO-based multipurpose X-ray stage of compact dimensions enabling in situ electric field and temperature-dependent measurements is put into practice and tested here. It can be routinely applied in combination with a technique of structural characterization of materials. Using high-performance X-ray laboratory equipment, two investigations were conducted to illustrate the device’s performance. The lattice characteristics and microstructure evolution of piezoelectric ceramics of barium titanate, BaTiO₃ (BT), and barium calcium zirconate titanate, with compositions of (Ba_0.92Ca_0.08) (Ti_0.95Zr_0.05)O₃ (BC8TZ5), were studied as a function of the applied electric field and temperature. The X-ray stage is amenable as an off-the-shelf device for a diffraction line in a synchrotron. It provides valuable information for poling piezoceramics and subsequent optimization of their performance. Full article

Polymer and ceramic-based composites offer a unique blend of desirable traits for improving dielectric permittivity. This study employs an empirical approach to estimate the dielectric permittivity of composite materials and uses a finite element model to understand the effects of permittivity and filler concentration on mechanical and electrical properties. The empirical model combines the Maxwell-Wagner-Sillars (MWS) and Bruggeman models to estimate the effective permittivity using Barium Titanate (BT) and Calcium Copper Titanate Oxide (CCTO) as ceramic fillers dispersed in a Polydimethylsiloxane (PDMS) polymer matrix. Results indicate that the permittivity of the composite improves with increased filler content, with CCTO/PDMS emerging as the superior combination for capacitive applications. Capacitance and energy storage in the CCTO/PDMS composite material reached 900 nF and 450 nJ, respectively, with increased filler content. Additionally, increased pressure on the capacitive model with varied filler content showed promising effects on mechanical properties. The interaction between BT filler and the polymer matrix significantly altered the electrical properties of the model, primarily depending on the composite’s permittivity. This study provides comprehensive insights into the effects of varied filler concentrations on estimating mechanical and electrical properties, aiding in the development of real-world pressure-based capacitive models. Full article

In this work, the electrocaloric effect (ECE) and electrocaloric strength (ΔT/E) were measured and thermal and dielectric studies were performed on Pb-modified BaTiO₃ (BPT). The saturated hysteresis loops and normal ferroelectric behavior of the ferroelectric ceramics allow the utilization of the indirect method to estimate the electrocaloric properties. The electrocaloric measurements were performed under high (18 kV/cm) versus low (8 kV/cm) electric field conditions. These conditions were chosen to notice and then eliminate an artificial negative electrocaloric effect in the tested ceramics. At the same time, relatively high values of positive electrocaloric temperature change ΔT ($~ 2.19 \mathrm{K}$) and electrocaloric strength ΔT/E ($~$0.27–0.11 K$·$cm/kV) were obtained. Full article

This study presents the dielectric properties of a barium titanate–gadolinium ferrite composite material, obtained through a solid-state reaction method. The aim of this research was to create a composite material with enhanced dielectric properties compared to each individual component, and to investigate the electrical properties of the composites, using impedance spectroscopy. The structural and morphologic properties were analyzed using X-ray diffraction and scanning electron microscopy, respectively. Impedance spectroscopy measurements were performed over a wide frequency range (100–0.1 GHz) and temperature (45–170 °C) to evaluate the electrical behavior of the material. The dielectric relaxations were analyzed using the Havriliak–Negami function, and the key electrical parameters such as relaxation frequency, dielectric strength, and electrical conductivity were extracted. Several relaxation processes were identified, which depend on the mixture of the initial titanate and ferrite materials, and a correlation between structural, morphologic, and electrical properties was exposed. The sample with the highest dielectric constant was the 25 wt% gadolinium ferrite composite, with ε′ close to 240 and loss tangent values below 0.1, affording it the more appropriate composition for energy storage devices such as lead-free dielectric capacitors. Full article

Improving fracture toughness, electrical conductivity, and biocompatibility has consistently presented challenges in the development of artificial bone replacement materials. This paper presents a new strategy for creating high-performance, multifunctional composite ceramic materials by doping graphene oxide (GO), which is known to induce osteoblast differentiation and enhance cell adhesion and proliferation into barium calcium zirconate titanate (BCZT) ceramics that already exhibit good mechanical properties, piezoelectric effects, and low cytotoxicity. Using fast hot-pressed sintering under vacuum conditions, (1 − x)(Ba_0.85Ca_0.15Zr_0.1Ti_0.9)O₃₋xGO (0.2 mol% ≤ x ≤ 0.5 mol%) composite piezoelectric ceramics were successfully synthesized. Experimental results revealed that these composite ceramics exhibited high piezoelectric properties (d₃₃ = 18 pC/N, k_p = 62%) and microhardness (173.76 HV_0.5), meeting the standards for artificial bone substitutes. Furthermore, the incorporation of graphene oxide significantly reduced the water contact angle and enhanced their wettability. Cell viability tests using Cell Counting Kit-8, alkaline phosphatase staining, and DAPI staining demonstrated that the GO/BCZT composite ceramics were non-cytotoxic and effectively promoted cell proliferation and growth, indicating excellent biocompatibility. Consequently, with their superior mechanical properties, piezoelectric performance, and biocompatibility, GO/BCZT composite ceramics show extensive potential for application in bone defect repair. Full article

As consumer electronics and industrial control systems continue to evolve, the operating temperature range of capacitors is gradually increasing. Barium titanate-based ceramic capacitors are widely used in the field of high dielectrics, so temperature-stable barium titanate-based dielectric materials have been a hot research topic in the field of dielectric ceramics. The construction of a core–shell structure by unequal doping is an effective way to obtain temperature-stable dielectric materials. At the same time, this structure retains part of the highly dielectric tetragonal phase, and materials with overall high dielectric constants can be obtained. In this work, we prepared BaTiO₃-xNaNbO₃-0.002Gd₂O₃ (x = 1.0–6.0 mol%) as well as BaTiO₃-0.05NaNbO₃-yGd₂O₃ (y = 0–0.30 mol%) dielectric ceramics. On the basis of high-electronic-bandgap NaNbO₃-modified BaTiO₃ dielectric ceramics, a core–shell structure with a larger proportion of core phase was obtained by further doping the amphiphilic rare-earth oxide Gd₂O₃. By designing this core–shell structure, the temperature stability range of capacitors can be expanded. At a doping level of 5.0 mol% NaNbO₃ and 0.20 mol% Gd₂O₃, the room temperature dielectric constant ε_r = 4266 and dielectric loss tan δ = 0.95% conforms to the X8R standard (from −55 °C to 150 °C, TCC < ±15%); volume resistivity ρ_v = 10,200 GΩ·cm and breakdown strength E_b = 13.5 kV/mm is attained in BaTiO₃-based ceramics. The system has excellent dielectric and insulating properties; it provides a new solution for temperature-stable dielectric ceramics. Full article

An electrothermal analysis for barium-titanate-based ceramics is presented, combining the Heywang–Jonker model for the electric resistivity with a heat dissipation mechanism based on natural convection and radiation in a one-dimensional model on the device level with voltage as the control parameter. Both positive-temperature-coefficient (PTC) and negative temperature coefficient (NTC) effects are accounted for through the double Schottky barriers at the grain boundaries of the material. The problem formulated in this way admits uniform and non-uniform multiple-steady-state solutions that do not depend on the external circuit. The numerical bifurcation analysis reveals that the PTC effect gives rise to several multiplicites above the Curie point, whereas the NTC effect is responsible for the thermal runaway (temperature blowup). The thermal runaway phenomenon as a potential thermal shock could be among the possible reasons for the observed thermomechanical failures (delamination fracture). The theoretical results for the NTC regime and the thermal runaway are in agreement with the experimental flash sintering results obtained for barium titanate, and 3% and 8% yttria-stabilized zirconia. Full article