Influence of Dentine Pre-Treatment by Sandblasting with Aluminum Oxide in Adhesive Restorations. An In Vitro Study
Abstract
:1. Introduction
2. Materials and Methods
2.1. Study Design
- Group 1 (TEST): sandblasting with aluminum oxide particles (50 μm), etching treatment with 37% orthophosphoric acid (ENA Etch-Micerium), application of the adhesive (Prime & Bond—Etch & Rinse Adhesive-DENTSPLY) and a layer of composite (ENAMEL plus HRi-Micerium).
- Group 2 (CONTROL): etching with 37% orthophosphoric acid (ENA Etch-Micerium), application of the adhesive (Prime & Bond—Etch & Rinse Adhesive-DENTSPLY) and a layer of composite (ENAMEL plus HRi-Micerium).
2.2. Sample Preparation
2.3. Mechanical Test
2.4. Scanning Electron Microscope (SEM) Test
2.5. Statistical Analysis
3. Results
4. Discussion
5. Conclusions
Author Contributions
Funding
Conflicts of Interest
References
- Samorodnitzky-Naveh, G.R.; Geiger, S.B.; Levin, L. Patients’ satisfaction with dental esthetics. J. Am. Dent. Assoc. 2007, 1386, 805–808. [Google Scholar] [CrossRef] [PubMed]
- Sinjari, B.; D’Addazio, G.; Traini, T.; Varvara, G.; Scarano, A.; Murmura, G.; Caputi, S. A 10-year retrospective comparative human study on screw-retained versus cemented dental implant abutments. J. Biol. Regul. Homeost. Agents 2019, 33, 787–797. [Google Scholar] [PubMed]
- Pjetursson, B.E.; Valente, N.A.; Strasding, M.; Zwahlen, M.; Liu, S.; Sailer, I. A systematic review of the survival and complication rates of zirconia-ceramic and metal-ceramic single crowns. Clin. Oral Implant. Res. 2018, 29, 199–214. [Google Scholar] [CrossRef] [Green Version]
- Van den Breemer, C.R.; Özcan, M.; Pols, M.R.; Postema, A.R.; Cune, M.S.; Gresnigt, M.M. Adhesion of resin cement to dentin: Eects of adhesive promoters, immediate dentin sealing strategies, and surface conditioning. Int. J. Esthet. Dent. 2019, 14, 52–63. [Google Scholar] [PubMed]
- Munaga, S.; Chitumalla, R.; Kubigiri, S.K.; Rawtiya, M.; Khan, S.; Sajjan, P. Effects of saliva contamination on the shear bond strength of a new self-etch adhesive system to dentin. J. Conserv. Dent. 2014, 17, 31–34. [Google Scholar] [CrossRef]
- Mojon, P.; Kaltio, R.; Feduik, D.; Hawbolt, E.B.; MacEntee, M.I. Short-term contamination of luting cements by water and saliva. Dent. Mater. 1996, 12, 83–87. [Google Scholar] [CrossRef]
- Zhou, W.; Liu, S.; Zhou, X.; Hannig, M.; Rupf, S.; Feng, J.; Peng, X.; Cheng, L. Modifying Adhesive Materials to Improve the Longevity of Resinous Restorations. Int. J. Mol. Sci. 2019, 20, 723. [Google Scholar] [CrossRef] [PubMed] [Green Version]
- Van Meerbeek, B.; De Munck, J.; Yoshida, Y.; Inoue, S.; Vargas, M.; Vijay, P.; Van Landuyt, K.; Lambrechts, P.; Vanherle, G. Buonocore memorial lecture. Adhesion to enamel and dentin: Current status and future challenges. Oper. Dent. 2003, 28, 215–235. [Google Scholar] [PubMed]
- Karadas, M.; Çağlar, İ. The effect of Er: YAG laser irradiation on the bond stability of self-etch adhesives at different dentin depths. Lasers Med Sci. 2017, 32, 967–974. [Google Scholar] [CrossRef] [Green Version]
- Fang, M.; Liu, R.; Xiao, Y.; Li, F.; Wang, D.; Hou, R.; Chen, J. Biomodification to dentin by a natural crosslinker improved the resin-dentin bonds. J. Dent. 2012, 40, 458–466. [Google Scholar] [CrossRef]
- De Munck, J.; Van Landuyt, K.; Peumans, M.; Poitevin, A.; Lambrechts, P.; Braem, M.; Van Meerbeek, B. A critical review of the durability of adhesion to tooth tissue: Methods and results. J. Dent. Res. 2005, 84, 118–132. [Google Scholar] [CrossRef] [PubMed]
- Bortolotto, T.; Bahillo, J.; Richoz, O.; Hafezi, F.; Krejci, I. Failure analysis of adhesive restorations with SEM and OCT: From marginal gaps to restoration loss. Clin. Oral Investig. 2015, 19, 1881–1890. [Google Scholar] [CrossRef] [PubMed] [Green Version]
- D’Addazio, G.; Santilli, M.; Rollo, M.L.; Cardelli, P.; Rexhepi, I.; Murmura, G.; Husain, N.A.; Sinjari, B.; Traini, T.; Özcan, M.; et al. Fracture Resistance of Zirconia-Reinforced Lithium Silicate Ceramic Crowns Cemented with Conventional or Adhesive Systems: An In Vitro Study. Materials 2020, 13, 2012. [Google Scholar] [CrossRef] [PubMed]
- Alshaikh, K.H.; Hamama, H.H.H.; Mahmoud, S.H. Effect of smear layer deproteinization on bonding of self-etch adhesives to dentin: A systematic review and meta-analysis. Restor. Dent. Endod. 2018, 43, e14. [Google Scholar] [CrossRef] [PubMed]
- Stencel, R.; Kasperski, J.; Pakieła, W.; Mertas, A.; Bobela, E.; Barszczewska-Rybarek, I.; Chladek, G. Properties of Experimental Dental Composites Containing Antibacterial Silver-Releasing Filler. Materials 2018, 11, 1031. [Google Scholar] [CrossRef] [PubMed] [Green Version]
- Santos, M.J.; Bapoo, H.; Rizkalla, A.S.; Santos, G.C. Effect of dentin-cleaning techniques on the shear bond strength of self-adhesive resin luting cement to dentin. Oper. Dent. 2011, 36, 512–520. [Google Scholar] [CrossRef] [Green Version]
- Coli, P.; Alaeddin, S.; Wennerberg, A.; Karlsson, S. In vitro dentin pretreatment: Surface roughness and adhesive shear bond strength. Eur. J. Oral Sci. 1999, 107, 400–413. [Google Scholar] [CrossRef]
- Magne, P.; So, W.S.; Cascione, D. Immediate dentin sealing supports delayed restoration placement. J. Prosthet. Dent. 2007, 98, 166–174. [Google Scholar] [CrossRef]
- Shawkat, E.S.; Shortall, A.C.; Addison, O.; Palin, W.M. Oxygen inhibition and incremental layer bond strengths of resin composites. Dent. Mater. 2009, 11, 1338–1346. [Google Scholar] [CrossRef]
- Sinjari, B.; D’Addazio, G.; Murmura, G.; Di Vincenzo, G.; Semenza, M.; Caputi, S.; Traini, T. Avoidance of interaction between impression materials and tooth surface treated for immediate dentin sealing: An in-vitro study. Materials 2019, 12, 3454. [Google Scholar] [CrossRef] [Green Version]
- Sinjari, B.; D’Addazio, G.; Xhajanka, E.; Caputi, S.; Varvara, G.; Traini, T. Penetration of Different Impression Materials into Exposed Dentinal Tubules during the Impression Procedure. Materials 2020, 13, E1321. [Google Scholar] [CrossRef] [PubMed] [Green Version]
- Nishimura, K.; Nikaido, T.; Foxton, R.M.; Tagami, J. Effect of air-polishing on dentin adhesion of a self-etching primer bonding system. Dent. Mater. 2005, 24, 59–65. [Google Scholar] [CrossRef] [PubMed] [Green Version]
- Sinjari, B.; D’Addazio, G.; Bozzi, M.; Santilli, M.; Traini, T.; Murmura, G.; Caputi, S. SEM Analysis of Enamel Abrasion after Air Polishing Treatment with Erythritol, Glycine and Sodium Bicarbonate. Coatings 2019, 9, 549. [Google Scholar] [CrossRef] [Green Version]
- Frankenberger, R.; Lohbauer, U.; Tay, F.R.; Taschner, M.; Nikolenko, S.A. The effect of different air-polishing powders on dentin bonding. J. Adhes. Dent. 2007, 9, 381–389. [Google Scholar] [PubMed]
- Powers, J.M.; O’Keefe, K.L.; Pinzon, L.M. Factors affecting in vitro bond strength of bonding agents to human dentin. Odontology 2003, 91, 1–6. [Google Scholar] [CrossRef]
- Franca, F.M.G.; Santos, A.J.S.; Lovadino, J.R. Influence of air abrasion and Long-Term storage on the bond strength of Self-etching adhesives to dentin. Oper. Dent. 2007, 32, 217–224. [Google Scholar] [CrossRef]
- Anja, B.; Walter, D.; Nicoletta, C.; Marco, F.; Pezelj Ribarić, S.; Ivana, M. Influence of air abrasion and sonic technique on microtensile bond strength of one-step self-etch adhesive on human dentin. Sci. World J. 2015, 2015, 368745. [Google Scholar] [CrossRef] [Green Version]
- Motisuki, C.; Monti Lima, L.; Emi Sanabe, M.; Jacques, P.; Santos-Pinto, L. Evaluation of the microtensile bond strength of composite resin restoration in dentin prepared with different sizes of aluminum oxide particles, using the air abrasion system. Minerva Stomatol. 2006, 55, 611–618. [Google Scholar]
- Arola, D. Fatigue testing of biomaterials and their interfaces. Dent. Mater. 2017, 33, 367–381. [Google Scholar] [CrossRef]
- Soappman, M.J.; Nazari, A.; Porter, J.A.; Arola, D. A comparison of fatigue crack growth in resin composite, dentin and the interface. Dent. Mater. 2007, 23, 608–614. [Google Scholar] [CrossRef]
- Meira, J.B.C.; Ballester, R.Y.; Lima, R.G.; Martins de Souza, R.; Driemeier, L. Geometrical aspects on bi-material microtensile tests. J. Braz. Soc. Mech. Sci. Eng. 2005, 27, 310–313. [Google Scholar] [CrossRef] [Green Version]
- De Munck, J.; Luehrs, A.K.; Poitevin, A.; Van Ende, A.; Van Meerbeek, B. Fracture toughness versus micro-tensile bond strength testing of adhesive-dentin interfaces. Dent. Mater. 2013, 29, 635–644. [Google Scholar] [CrossRef] [PubMed]
- Scarano, A.; Murmura, G.; Sinjiari, B.; Sollazzo, V.; Spinelli, G.; Carinci, F. Analysis and structural examination of screw loosening in oral implants. Int. J. Immunopathol. Pharm. 2011, 24, 77–81. [Google Scholar] [CrossRef] [PubMed]
- Chaiyabutr, Y.; Kois, J.C. “The effects of tooth preparation cleansing protocols on the bond strength of self-adhesive resin luting cement to contaminated dentin. Oper. Dent. 2008, 33, 556–563. [Google Scholar] [CrossRef] [PubMed]
- Mujdeci, A.; Gokay, O. The effect of airborne-particle abrasion on the shear bond strength of four restorative materials to enamel and dentin. J. Prosthet. Dent. 2004, 92, 245–249. [Google Scholar] [CrossRef]
- Rafael, C.F.; Quinelato, V.; Morsch, C.S.; DeDeus, G.; Reis, C.M. Morphological analysis of dentin surface after conditioninG with two different methods: Chemical and mechanical. J. Contemp. Dent. Pract. 2016, 17, 58–62. [Google Scholar] [CrossRef]
- D’Amario, M.; Piccioni, C.; Di Carlo, S.; De Angelis, F.; Caruso, S.; Capogreco, M. Effect of Airborne Particle Abrasion on Microtensile Bond Strength of Total-Etch Adhesives to Human Dentin. BioMed Res. Int. 2017, 2432536. [Google Scholar] [CrossRef] [Green Version]
- Sudsangiam, S.; van Noort, R. Do dentin bond strength tests serve a useful purpose? J. Adhes. Dent. 1999, 1, 57–67. [Google Scholar]
- Miyazaki, M.; Tsubota, K.; Takamizawa, T.; Kurokawa, H.; Rikuta, A.; Ando, S. Factors affecting the in vitro performance of dentin-bonding systems. Jpn. Dent. Sci. Rev. 2012, 48, 53–60. [Google Scholar] [CrossRef] [Green Version]
- Pongprueksa, P.; De Munck, J.; Karunratanakul, K.; Barreto, B.C.; Van Ende, A.; Senawongse, P.; Van Meerbeek, B. Dentin Bonding Testing Using a Mini-interfacial Fracture Toughness Approach. J. Dent. Res. 2015, 95, 327–333. [Google Scholar] [CrossRef]
- Yahyazadehfar, M.; Ivancik, J.; Majd, H.; An, B.; Zhang, D.; Arola, D. On the Mechanics of Fatigue and Fracture in Teeth. Appl. Mech. Rev. 2014, 66, 030803. [Google Scholar] [CrossRef] [PubMed]
- De Kok, P.; Kleverland, C.J.; Kuijs, R.H.; Öztoprak, M.A.; Feilzer, A.J. Influence of Dentin and Enamel on the Fracture Resistance of Restorations at Several Thicknesses. Am. J. Dent. 2018, 31, 34–38. [Google Scholar] [PubMed]
- Okuda, M.; Pereira, P.N.; Nakajima, M.; Tagami, J.; Pashley, D.H. Long-term durability of resin dentin interface: Nanoleakage vs microtensile bond strength. Oper. Dent. 2002, 27, 289–296. [Google Scholar]
- Los, S.A.; Barkmeier, W.W. Effects of dentin air abrasion with aluminum oxide and hydroxyapatite on adhesive bond strength. Oper. Dent. 1994, 19, 169–175. [Google Scholar] [PubMed]
© 2020 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/).
Share and Cite
Sinjari, B.; Santilli, M.; D’Addazio, G.; Rexhepi, I.; Gigante, A.; Caputi, S.; Traini, T. Influence of Dentine Pre-Treatment by Sandblasting with Aluminum Oxide in Adhesive Restorations. An In Vitro Study. Materials 2020, 13, 3026. https://doi.org/10.3390/ma13133026
Sinjari B, Santilli M, D’Addazio G, Rexhepi I, Gigante A, Caputi S, Traini T. Influence of Dentine Pre-Treatment by Sandblasting with Aluminum Oxide in Adhesive Restorations. An In Vitro Study. Materials. 2020; 13(13):3026. https://doi.org/10.3390/ma13133026
Chicago/Turabian StyleSinjari, Bruna, Manlio Santilli, Gianmaria D’Addazio, Imena Rexhepi, Alessia Gigante, Sergio Caputi, and Tonino Traini. 2020. "Influence of Dentine Pre-Treatment by Sandblasting with Aluminum Oxide in Adhesive Restorations. An In Vitro Study" Materials 13, no. 13: 3026. https://doi.org/10.3390/ma13133026