1. Introduction
Mechanical processes including grinding, hard turning, and burnishing belong to finishing operations, which are mainly intended to form surface layer (SL) properties e.g., surface roughness, residual stresses [
1,
2,
3,
4,
5,
6,
7]. In traditional manufacturing processes, the finishing operation of tools and machine parts, of which hardness after heat treatment is higher than 45 HRC and even 60 HRC, is often grinding. For several decades in many industries, e.g., automotive, bearing, molds and dyes manufacturing, processes of grinding are gradually replaced by so-called “hard machining” (HM). Not always, however, does HM meet the requirements for the expected surface quality. The method to overcome these technological barriers is burnishing, which is applied both to the turned and milled surfaces [
8].
Prevey [
9] reports that static burnishing (e.g., rolling and sliding burnishing) provides significantly improved properties of SL compared to dynamic burnishing (shot peening). Static burnishing enables control of the depth of plastic deformation, while shot peening generates a large dislocation density in the SL due to the high degree of work-hardening, which results in unstable residual stress state. Sliding burnishing, whose specificity is the use of tools made of diamond or of similar superhard materials with a very low sliding friction on metals, may be used for treatment of the hardest steels and alloys [
10].
Thermo-chemical treatment, such as nitriding or sulphonitriding, is another type of operation widely used in industrial conditions based on the diffusion change of the chemical composition of SL in order to obtain the required functional properties of a workpiece [
11,
12,
13,
14,
15]. In this process, a nitrided layer is achieved, as in the case of the classical nitriding method. However, it should be noted that in the ε zone, iron sulphides are produced, which are decisive at the exploitation stage since they separate the friction surfaces and reduce their adhesion. This allows one to obtain low friction as well as high wear and abrasion resistance. This type of chemical heat treatment gives the opportunity to modify selected properties of SL in a wide range by controlling the process parameters. Production of the right amount of iron sulphide in the ε phase is extremely important in this case. Gas sulfonitriding is the final process, and therefore parts are not subjected to any additional mechanical treatment. The thickness of such layers is usually from 0.1 mm to 0.4 mm, depending on the type of material, process parameters, and application of these elements. The method of gas sulfonitriding can be used to treated elements made of low-, medium-, and high-alloy steels as well as tool steels.
Figure 1 schematically shows two basic variants of SL structure along with their division into individual zones, which are possible to obtain after gas sulfonitriding [
16,
17].
The complex structure of sulfonitrided layers may have two functions. Firstly, reducing the adhesion affinity of frictional pair elements and diminishing the shear strength of surface irregularities and possible galling. Secondly, it provides increased hardness of the SL, which allows transfer of pressure in the contact zone. Sulfonitrided layers achieved on alloy steels (variant b) are characterized by high hardness in the nitride compounds zone (up to 1300 HV) and in the zone of internal nitriding (from 1200 to 500 HV). Therefore, they can be used in friction nodes loaded with high pressure, sometimes even of linear and point character.
2. Materials and Methods
The aim of the experimental program presented in this paper is to assess the impact of commonly used mechanical processes, such as a pre-sulphonitriding treatment, on SL properties of two types of P/M tool steels. Our studies included, in particular:
Microstructure analysis by scanning and optical microscope,
X-ray diffraction analysis,
Micro-hardness measurements of cross-sectional SL,
3D surface roughness measurements,
Evaluation of dynamic friction and wear resistance against Al2O3 and 19MnB4 steel pins.
The nominal chemical compositions of the two grades are presented in
Table 1. The main difference between these materials is the content of C, N, and W. First of all, Vancron 40 contains 1.8% N and 3.7% W, as well as 1.1% C. By contrast, Vanadis 8 is characterized by higher concentrations of C and lack of N and W. The content of other chemical elements is at a similar level.
Samples from both steels were cut and heat treated as indicated in
Table 2. The final macrohardness after the heat treatment was 64 ± 1 HRC and 62 ± 1 HRC, respectively, for the Vanadis 8 and Vancron 40 tool steels. Afterwards, two various paths of surface modification were employed:
Grinding–sulphonitriding (G-SN),
Hard turning–slide burnishing with 130 N force–sulphonitriding (T-B130-SN).
Front face grinding with cBN (cubic boron nitride) wheels with resinous bond was carried out on a 3E642 type universal tool grinder. The following parameters were used: Peripheral speed of the wheel vs. = 16 m/s; table feed speed vf = 210 mm/min; working engagement ae = 0.02 mm, grit size = B126. Turning process was applied to PCBN (polycrystalline cubic boron nitride) cutting inserts with commercial names NP-DCGW11T302GA2 BC020 by using a constant feed f = 0.07 mm/rev. and the cutting depth ap = 0.2 mm. Cutting speeds were different: vc = 100 m/min for Vanadis 8 and vc = 160 m/min for Vancron 40. Furthermore, slide diamond burnishing of our tool steels in the quenched state was carried out using diamond tools at the following parameters: F = 130 N, f = 0.02 mm/rev., and v = 100 m/min. The applied burnishing force allowed the reduction of surface roughness after turning and the plastic deformation of the surface layer of investigated tool steels in the hardened condition—without abrasive wear of the burnishing ending tip. These tools with tips in the shape of spherical caps were designed, and are currently produced, at our Institute. High pressure–high temperature (HT-HP) Bridgman type apparatus was used to obtain diamond composites with ceramic bonding phase, namely Ti
3SiC
2. Compacts were sintered at the pressure of 8.0 ± 0.2 GPa and at 1800 ± 50 °C for 30 s. Subsequently, their spherical shapes were formed by electrical discharge machining (EDM) [
18,
19].
Finally, after the above-mentioned types of mechanical processes, samples were immediately sulpho-nitrided, under the following conditions: 520 °C/5 h. This technology has been prescribed as one of the operations in the design and manufacturing of tools, dyes, etc.
The X-ray diffraction (XRD) measurements were performed with a PANalytical Empyrean diffractometer (PANalytical B.V., Almelo, Netherlands) using copper radiation (λCu = 1.5406 Å). The phase analyses were performed using the ICDD PDF-4 + 2018 files.
Metallographic structures were observed with a scanning electron microscope (JEOL type JSM-6460LV, JEOL Ltd., Akishima, Tokyo, Japan) equipped with an INCA EDS (energy dispersive X-ray spectrometer) and INCA wavelength dispersive spectroscopy (WDS). An optical Carl Zeiss Axiovert 100A microscope (Carl Zeiss AG, Oberkochen, Baden-Württemberg, Deutschland) was also used to observe cross-sections of the SL samples.
Vickers microhardness HV was determined using a FM 7 tester from Future Tech. Corp., Kawasaki, Japan. Microindentations were made using a 100 g load. On each specimen, 3 measurements were performed at various distances below the surface in order to obtain a representative average hardness value.
3D surface roughness parameters were measured using a TOPO 01 laboratory profilometer, developed at our Institute. It was equipped with a 1 mm measuring head, a diamond tip with a radius of 2 μm, and a cone angle of 90°. Data analysis and surface topography were developed in Mountain Map v.7 by Digital Surf.
The abrasive wear resistance was evaluated by well-known pin-on-disc method [
20,
21]. More information about the mechanical tester and how the measurements were conducted have been provided in earlier papers [
22,
23]. The tests were carried out three times without a lubricant at room temperature. Applied test conditions are given in
Table 3 and samples are shown in
Figure 2. For each sample, two tests using different diameters of the sliding circle 7 mm and 11 mm were made, respectively, for Al
2O
3 and 19MnB4 steel pins. It should be noted that for both pins, the same sliding speed was used to avoid a negative impact on the dynamic friction. Moreover, due to the faster wear of steel pins, the shorter sliding distance was used. Dynamic friction µ and wear rate Ws were calculated by well-known standard formulas also reported in [
22].
3. Results
In
Figure 3a, microstructures of investigated steels after heat treatment are shown: Vancron 40 on the left and Vanadis 8 on the right. In both cases, we see carbide particles within a fine-tempered martensite matrix. Differences are seen in the color of observed carbides. In order to determine their type, X-ray diffraction analysis were performed; see
Figure 3b. The black line corresponds to the Vancron 40 steel steel and the microstructure of contains two types of carbides, such as MC and M
6C, whereas, the blue line corresponds to the Vanadis 8 steel and its microstructure consists only of MC type carbides. According to Jurči [
24], excellent wear resistance is ensured by a high amount of carbides, among which the MC particles play a dominant role.
Microstructure changes in the SL of samples after the application of two various paths of surface modification (G-SN and T-B130-SN) were also studied. The optical images of cross-sectional micrographs for both tool steels are presented in
Figure 4 and
Figure 5. For Vancron 40, the total thickness of the SL comprising the sulfurized zone as well the nitrogen compound zone and a diffusion layer in the G-SN variant reached ≈160 µm (
Figure 4a), but for the specimen that had been turned and burnished before sulfonitriding, the thickness of such a layer was slightly smaller (
Figure 4b). For Vanadis 8, the corresponding values were very similar; see
Figure 5a,b. Meanwhile, the thickness of the sulfurized zone near the surface in case of Vancron 40 steel samples was thicker after G-SN. An opposite effect was found for the Vanadis 8 steel. An example of the etched cross section of the sulfurized and nitrided compound zones recorded on the scanning electron microscope is also provided in
Figure 5. Differences in the thickness of sub-surface zones recorded on cross-sections of the surface layer of both steel samples were related to their chemical composition. The difference between C content and elements, such as N and W (see
Table 1), could affect the rate of diffusion. Finally, it should be added that after mechanical processes, all samples were subjected to sulphonitriding treatment in one process.
Selected results, including X-ray diffraction analysis with phase composition determined in the SL of samples after combined mechanical processes with the chemical heat-treatment operation (sulfonitriding), are presented in
Figure 6 and
Figure 7 as well as in
Table 4 and
Table 5. For both steels, the same phases (Fe
3N, FeS) were found after the two processes applied. No significant differences in their concentrations were found.
Figure 8 show the microhardness results for the SL of samples previously treated by our two processes. The micro hardness was measured from the surface into the depth of the material on the cross section of the samples. In the case of Vancron 40 steel, it can be seen that slightly higher values (about 5%) were obtained for the SL of samples after the combining process of G-SN. In this variant, the thickness of the upper layer with increased hardness was determined to 230 µm. Only at a distance of 80 μm from the surface, slightly lower values were found. An analogous comparison for Vanadis 8 steel samples indicates that up to a depth of 110 um of SL, a similar trend was found. Meanwhile, deeper towards the core, the opposite effect occurs. Higher values were determined for the samples after the three-stage process.
3D topographies of sample surfaces for both investigated tool steels are presented in
Figure 9 and
Figure 10. For Vancron 40 steel samples, lower values of selected parameters were found after the G-SN variant. Comparing the roughness parameter Sa (arithmetical mean height), a two-fold change was found. In connection to the other parameters, the changes are not so significant. In the case of Vanadis 8 steel, slightly lower values were obtained for samples subjected to T-B130-SN treatment.
Given the nature of the typical wear of tool steels used in cold forming processes, two types of pins as counterbodies were applied for tribological tests. An Al
2O
3 ceramic ball was selected to determine abrasion resistance, whereas pins made of low-carbon 19MnB4 steel with the addition of boron were used to determine adhesive resistance. The volume of material removed was significantly different, both for the depth and the width of achieved wear tracks. Example of two profiles of such traces for Vanadis 8 tool steel samples after tests with our types of counterbodies are shown in
Figure 11. A 3D view of 3 × 3 mm area is presented for one of them.
Taking into account the differences observed in the wear traces, counterbodies were also evaluated. About 40-fold higher wear of pins made of 19MnB4 steel compared to Al
2O
3 ceramic pins was found; examples of such results are shown in
Figure 12. It is worth mentioning that the width of wear found on the counterbodies corresponds to the width of wear traces measured on the sample. In the case of ceramic pins, the width is ≈1.3 mm, whereas for steel pins, it amounts to more than 4 mm.
Wear rates and dynamic friction values determined for our steels after pin-on-disc tests against 19MnB4 pins are shown in
Figure 13 and
Figure 14. It should be noted that minor changes in wear rates for samples subjected to different processes of SL modification are found; this applies to both steels. Differences between T-B130-SN and G-SN variants amount to 2% and 3%, respectively, for Vancron 40 and Vanadis 8 steels. This is related to the much lower hardness of the 19MnB4 steel pin relative to the sample. Taking into account results of dynamic friction for samples of Vancron 40 steel, lower values were observed after G-SN variant; see
Figure 13b. The 2-fold higher surface roughness of samples (
Figure 9b) may explain such a result. For Vanadis 8 steel samples, a very similar trend and values of dynamic friction are observed. In case of this steel, similar surface topography was obtained after both variants of surface modification were applied.
Deposits of pin material on the sample’s surface were the dominating features on the wear tracks created after pin-on-disc tests using 19MnB4 steel pins. Examples of SEM images of wear traces on Vanadis 8 steel samples are shown in
Figure 15. Large deposits of material built up on the disc surface in the G-SN variant appeared. Only a little transfer of pin material on the sample surface was observed after three stage process. Unlubricated sliding wear tests of D2 steel (sample) and AISI 1018 steel (pin) pairs with more than a twice higher hardness of samples, carried out by Okonkwo et al. [
25], indicate that the material adhesion was also the dominant mechanism for the ambient temperature wear tests.
On the other hand, wear rates and dynamic friction values determined for Al
2O
3 pins are shown in
Figure 16 and
Figure 17. Application of the T-B130-SN variant was beneficial for abrasion resistance of both steels. A significant increase in wear resistance has been achieved compared to the G-SN variant. It reached 30% and 37%, respectively, for Vancron 40 and Vanadis 8 tool steels. Moreover, a simple comparison between examined steels subjected to three-stage process points to more than 50% increase of abrasion wear resistance of Vanadis 8 steel. The type of carbides in the microstructure is undoubtedly one of the explanations for these results. Compressive residual stress is another factor that could affect such a result. According to previous studies, a homogenization of stress state to the isotropic (σ
1 = σ
2) compression after application of the sequential technology (e.g., turning–burnishing–nitriding) was observed, contributing to increased wear resistance. More information on this subject can be found in an earlier paper [
26].
Finally, SEM micrographs of wear tracks created in pin-on-disc tests against Al
2O
3 pins for samples of Vanadis 8 steel are shown in
Figure 18. Images and chemical analysis reveal a much smaller deposition of pin material on the sample surface in the case of T-B130-SN variant. Taking into account the main wear mechanisms, the abrasive wear dominates in this case. Furthermore, some differences of S and N content in the wear tracks were observed—it is related to their depth created after tests.