Power Production and Degradation of Pesticide Wastewater Through Microbial Fuel Cells with the Modified Activated Carbon Air Cathode by Hollow-Carbon and Carbon-Encapsulated Structures
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Molecules
Volume 30
Issue 4
10.3390/molecules30040820
molecules-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

S- and N-Co-Doped Carbon-Nanoplate-Encased Ni Nanoparticles Derived from Dual-Ligand-Assembled Ni-MOFs as Efficient Electrocatalysts for the Oxygen Evolution Reaction

by
Huijuan Han
1,*,
Yalei Zhang
1,
Chunrui Zhou
1,
Haixin Yun
1,
Yiwen Kang
1,
Kexin Du
1,
Jianying Wang
2,
Shujun Chao
3,* and
Jichao Wang
1,*
1
School of Chemistry and Chemical Engineering, Henan Institute of Science and Technology, Xinxiang 453003, China
2
Henan Provincial Ecological Environment Monitoring and Safety Center, Department of Ecology and Environment of Henan Province, Zhengzhou 450046, China
3
Xinxiang Engineering Technology Research Center of Functional Medical Nanomaterials, School of Basic Medical Sciences, Xinxiang Medical University, Xinxiang 453003, China
*
Authors to whom correspondence should be addressed.
Molecules 2025, 30(4), 820; https://doi.org/10.3390/molecules30040820
Submission received: 11 December 2024 / Revised: 25 January 2025 / Accepted: 4 February 2025 / Published: 10 February 2025
(This article belongs to the Special Issue Innovations in Metal–Organic Frameworks: Their Synthesis, Properties and Multifaceted Applications)
Browse Figures
Versions Notes

Abstract

:
To achieve the “double carbon” goal, it is urgent to reform the energy system. The oxygen evolution reaction (OER) is a vital semi-reaction for many new energy-storage and conversion devices. Metal nanoparticles embedded in heteroatom-doped carbon materials prepared by the pyrolyzing of metal–organic frameworks (MOFs) have been a key route to obtain high-performance electrochemical catalysts. Herein, a nanocatalyst embedding Ni nanoparticles into S- and N-co-doped carbon nanoplate (Ni NPs@SN-CNP) has been synthesized by pyrolysis of a Ni-MOF precursor. The prepared Ni NPs@SN-CNP exhibits superior oxygen evolution performance with an overpotential of 256 mV to attain 10 mA cm−2 and a low Tafel slope value of 95 mV dec−1. Moreover, a self-assembled overall-water-splitting cell with Ni NPs@SN-CNP/NF||Pt-C/NF achieves a low potential of 1.56 V at 10 mA cm−2 and a high cycling stability for at least 10 h. The improvement in this performance is benefit from its large surface area, unique morphology, and the nanostructure of the electrocatalyst. This study presents a novel and simple approach to designing high-performance OER catalysts.

1. Introduction

Because of the environmental pollution and energy shortage, all the countries in the world began to study solar energy, hydrogen energy, wind energy, and ocean energy instead of the traditional fossil fuels [1,2,3]. During these new energies, hydrogen energy is the most promising to solve the problems of environmental pollution and resource shortage of secondary energy, therefore it has been paid more and more attention by people [4,5,6]. In the existing hydrogen production technology, electrolyzed water is a relatively mature technology for hydrogen production. The oxygen evolution reaction (OER) is the critical half reaction and needs more efficient electrocatalysts [7,8,9]. So, looking for the high efficiency and low cost of the electrode material is the main factor that affects the efficiency and energy consumption of electrolyzed water [10,11].
At present, the main electrode materials are precious metals and their oxides (Ru, Ir, IrO2, RuO2, etc.) [12,13,14]. However, whether precious metals or their oxides, the anode polarization is serious under strong alkaline conditions, and it is easy for the electrode to be corroded. Also, the reserves are limited and the price is high [15,16,17,18]. Therefore, it is committed to the use of non-precious metals instead of precious metals electrocatalysts for OER [19,20,21]. Transition metals such as Co, Ni, Fe, and their oxide materials, as well as Fe-Ni-, Ni-Mo-, Cu-Ni-alloy electrodes synthesized by introducing Ni(OH)2 onto Ni can greatly reduce overpotential of oxygen reaction and exhibit great OER performance comparable to that of noble metal catalysts [22,23,24,25,26].
However, these transition metals still face pulverization issues due to particle aggregation, low conductivity, and instability [27,28]. To overcome these obstacles, metal–organic frameworks (MOFs) with special structural properties and changes in its internal structure have been used as precursors or sacrificial templates for synthesizing single-metal oxide/sulfide nanoparticles embedded in heteroatom-doped nanoporous carbon through thermal decomposition [29,30,31,32,33]. For example, Ni-Co-based sulfide nanoparticles homogeneously embedded in N- and S-co-doped porous carbon by a one-step sulfurization and carbonization of Ni-substituted ZIF-67 simultaneously [34]. Sun et al. reported 2D Ni-Fe-MOFs (2,5-thiophene dicarboxylic acid as ligand) with high efficiency of water splitting and solar-water splitting [35]. Lin et al. reported 2D N-doped Ni-Ni3S2@carbon nanoplates (Py-1.5@SNC600) using 4,4′-bipyridine as an organic precursor for an enhanced OER electrocatalyst [36]. These reported catalysts are usually prepared by using single-ligand MOFs as precursors.
But it still faces significant challenges in achieving precise, controllable, and repeatable doping of the carbon network with heteroatoms. In this paper, we successfully obtain a multi-hole nitrogen- and sulfur-co-doped nickel-carbon material derived in situ from the dual-ligand nickel MOF through pyrolysis in an inert gas environment. The introduction of heteroatoms such as N and S in the textural properties of C can effectively modify the electrochemical behaviors and wettability of an electrode. The research results show the Ni NPs@SN-CNP exhibits superior oxygen evolution performance and a large surface area (271.9 m2 g−1) due to the synergistic effect between Ni nanoparticles and S- and N-co-doped hierarchical carbon. Furthermore, the unique morphology, nanostructure, and appropriate doping level of heteroatoms of the electrocatalyst are also important factors contributing to its superior performance. The Ni NPs@SN-CNP catalyst exhibits enhanced OER performance by combining the beneficial characteristics of NPs, SN-CNP, and the combination of NPs and SN-CNP. The higher performance of Ni NPs@SN-CNP comes from its large surface area, more catalytic sites, electron transfer, and shorten mass pathway. This work offers a new and cost-effective approach to fabricating electrocatalysts with excellent performance for the OER.

2. Results and Discussion

2.1. Structure and Morphology of the Ni NPs@SN-CNP

The synthesis process of Ni NPs@SN-CNP is illustrated in Figure 1. The preparation of Ni NPs@SN-CNP involved a two-step method. Firstly, the MOF was obtained by a solvothermal method. Ni(NO3)2·6H2O, 4,4′-bipyridine, thiophene-2,5-dicarboxylate, and distilled water were mixed together, and the mixture was heated in an autoclave at 105 °C for 3 days. Granulated green crystals were obtained. For comparison, the Ni-MOFs were separately pyrolyzed at 500 °C, 600 °C, 700 °C, and 800 °C for 180 min each. The resulting products were represented as Ni-MOF-500, Ni NPs@SN-CNP, Ni-MOF-700, and Ni-MOF-800, respectively. The electrochemical test results reveal that the Ni NPs@SN-CNP shows the best electrochemical catalytic performance among the four resulting products. And, in the course of the pyrolysis process, the Ni (II) was reduced to metallic nickel and the ligand was carbonated under N2 atmosphere. XPS data will demonstrate the presence of pyridinic N and pyridine-N-oxide.
From the XRD pattern (Figure 2), it can be seen that after pyrolysis of Ni-MOFs at 500 °C, 600 °C, 700 °C, and 800 °C, only three nickel phase diffraction peaks were exhibited (JCPDS card no. 65-2865) and located at 44.3°, 51.6°, and 75.9°, respectively. This phenomenon indicates the only crystalline species observed are related to metallic Ni in the four samples, demonstrating that the Ni-MOFs decomposes into metallic Ni at different pyrolysis temperatures.
The microstructure and morphology of the as synthesized Ni NPs@SN-CNP catalyst was characterized by a Field-Emission Scanning Electron Microscope (FESEM, Scios 2 HiVac, FEI, Hillsboro, OR, USA). Figure 3a shows that a lot of long ribbon are piling up together to form a flower-like structure. The inset of Figure 3b indicates that the average width of the carbon ribbon is 120 nm. Figure 3b shows that the surface of the ribbon is rough. Figure 3c–h shows the TEM image of Ni NPs@SN-CNP and the corresponding elemental mapping analysis, respectively. Figure 3h shows that it could be confirmed that the Ni, O, N, S, and C element are uniformly distributed, which indicates that N and S elements are doped successfully in the Ni NPs@SN-CNP. Figure 3i shows the atom percentage of the C, Ni, O, S, and N is 54.5%, 28.3%, 9.1%, 6.5%, and 1.6%.
Figure 4a,b is the TEM images of the Ni NPs@SN-CNP catalyst. As can be seen from Figure 4a, the width of the carbon ribbon is 120 nm or so. From Figure 4b, there are many nanoparticles in the carbon ribbon. It is evident that the metallic Ni is surrounded by the carbon. The inset of Figure 4b indicates that the average diameter of the nickel nanoparticles is around 3 nm which can be further confirmed by HRTEM (Figure 4c). Additionally, the lattice spacings of 0.204 nm detected in the HRTEM image are consistent with the (111) planes of metallic Ni. The ring patterns observed from the SAED image in Figure 4 can further prove it. The results are consistent with the XRD observation. The smaller metallic nickel nanoparticles that are buried in carbon can well-prevent themselves by oxidation.
To further ascertain the elemental composition and chemical states of the Ni NPs@SN-CNP catalyst, the XPS was used. The XPS full spectrum (Figure 5a) of Ni NPs@SN-CNP shows that there are Ni 2p, C 1s, O 1s, N 1s, and S 2p. And the relative atomic percentages of Ni, C, N, S, and O are 11.63, 69.4, 6.33, 4.9, and 7.73 in this Ni NPs@SN-CNP catalyst. Figure 5b–f shows the deconvoluted spectrums of Ni 2p, C 1s, N 1s, S 2p, and O 1s in the Ni NPs@SN-CNP catalyst. The Ni 2p spectrum (Figure 5b) consists of the main peak of Ni0 (852.1 eV), the other two peaks of the Ni ion are at 855.6 and 869.6 eV. The two peaks at 861.5 and 874.8 eV are satellite peaks of the Ni ion [37,38]. In composite materials, Ni NPs often reveal a partial oxidation since the samples need to be briefly handled in air to be introduced into the XPS instrument.
As shown in Figure 5c, there are three peaks in the C 1s spectrum. The peaks located at 284.9 eV and 285.8 eV. 284.6 eV correspond to C-S, C-N, and sp2-hybridized C=C bonds, respectively [39,40].
N 1s spectrum (Figure 5d) shows the presence of two states of N in Ni NPs@SN-CNP, including graphitic-N at 401.1 eV and pyridinic-N at 398.0 eV, both of which were reported to be active sites of OER [41,42,43,44].
From Figure 5e, the S 2p XPS spectra of the Ni NPs@SN-CNP can be fitted into two peaks. The peaks at 163.8 eV and 165.3 eV are attributed to S 2p3/2 and S 2p1/2, respectively. Their present peak area ratio is 2:1 [43]. These results confirm that carbon is co-doped with S and N, enhancing the electrocatalytic performance of the catalyst by incorporating additional active sites. The O 1s XPS spectra (Figure 5f) exhibits three peaks at 532.5 eV, 531.4 eV, and 530.7 eV, ascribed to C-O, C-OH, and C=O, respectively.
The N2 adsorption–desorption isotherm can be used to verify the surface area and porosity of the Ni NPs@SN-CNP. As shown in Figure 6a–d, the isotherms are of typical type IV, and their surface areas are 182.8 m2 g−1 (Ni-MOF-500), 271.9 m2 g−1 (Ni NPs@SN-CNP), 169.8 m2 g−1 (Ni-MOF-700), and 169.3 m2 g−1 (Ni-MOF-800). Figure 6e–h shows that their pore sizes are centered at 10.3 nm, 11.7 nm, 14.1 nm, 17.7 nm (Ni-MOF-500), 3.0 nm, 5.7 nm (Ni NPs@SN-CNP), 3.5 nm (Ni-MOF-700), and 1.7 nm and 2.3nm (Ni-MOF-800), indicating that after calcination, the surface area of the material increases to varying degrees, and there are mesopores present in the material. The calcination at high temperature would cause the structure of MOF to collapse and the agglomerate of Ni NPs, thus seriously decreasing surface area and catalytic activity. The good catalytic performance of Ni NPs@SN-CNP can be attributed to its large surface area and mesoporous structure, which exposes abundant catalytic active sites to improve catalytic efficiency.

2.2. OER Performance

Using a typical three-electrode system to assess the OER performance of catalysts in N2-saturated 1 M KOH, as shown in Figure 7a,d, the OER LSV curves and corresponding overpotentials at 10 mA cm−2 (η10,OER) are for Ni-MOF (328 mV), Ni-MOF-500 (336 mV), Ni NPs@SN-CNP (256 mV), Ni-MOF-700 (328 mV), Ni-MOF-800 (362 mV), and RuO2 (225 mV). Ni NPs@SN-CNP has a slightly higher η10,OER than commercial RuO2 and lower than Ni-MOF, Ni-MOF-500, Ni-MOF-700, and Ni-MOF-800, exhibiting superior OER performance, demonstrating that 600 °C is the optimal pyrolysis condition for Ni-MOF. Figure 7b shows that the Ni NPs@SN-CNP exhibits a lower Tafel slope value (95 mV dec−1) than Ni-MOF (104 mV dec−1), Ni-MOF-500 (137 mV dec−1), Ni-MOF-700 (144 mV dec−1), and Ni-MOF-800 (134 mV dec−1), and is closer to commercial RuO2 (67 mV dec−1). η10,OER and Tafel slope of the Ni NPs@SN-CNP is also comparable to those reported for some non-precious metal catalysts, such as Ni10-CoS2 (304 mV, 98 mV dec−1) [45], Ni(OH)2@CoB (320 mV, 94 mV dec−1) [24], Ni-BTC (390 mV, 114 mV dec−1) [46], Fe-Ni·MOFNSS (258 mV, 40.8 mV dec−1) [47], CoNi-ZIF-67@Ti3C2TX (275 mV, 65 mV dec−1) [48], and Ni-MOF@Fe-MOF (265 mV, 82 mV dec−1) [49]. These results suggest that Ni NPs@SN-CNP possesses the fast OER kinetics [50,51], which demonstrates that Ni NPs@SN-CNP has excellent OER performance. From the electrochemical impedance spectroscopy curves (Figure 7c) it can be observed that the intercept of materials is arranged in ascending order as follows: RuO2, Ni NPs@SN-CNP, Ni-MOF-500, Ni-MOF, Ni-MOF-800, and Ni-MOF-700. The small semi-circular diameter and closeness to RuO2 of Ni NPs@SN-CNP reflects the small interfacial transfer resistance during the catalytic process, facilitating electron transfer, which is in accord with the results of the faster charge transfer in the OER process and the smaller Tafel slope value [52].
Stability is an important parameter that determines the practicality of OER electrocatalysts, thus, we evaluated the stability of the Ni NPs@SN-CNP in 1 M KOH solution. As can be seen in Figure 7e, after 24 h of continuous durability testing at a current density of 10 mA cm−2, there was no deactivation of the catalyst. To further confirm the stability of the Ni NPs@SN-CNP, we conducted LSV analysis on a before and after stability test of Ni NPs@SN-CNP. As shown in Figure 7f, there is a negligible increase (10 mV) in overpotential after 24 h of cycling. The figures inserted in Figure 7e,f are TEM and XRD diagrams of Ni NPs@SN-CNP after stability testing, respectively, showing there is no agglomeration and material change after stability testing. The above results all indicate the excellent stability of Ni NPs@SN-CNP, providing reference for the development of stable catalysts.
Based on the excellent OER performance of Ni NPs@SN-CNP, we fabricated a two-electrode system by using Pt-C/NF as the cathode and Ni NPs@SN-CNP/NF as the anode for overall water splitting in 1 M KOH. From Figure 8a, it can be clearly seen that H2 and O2 emerge from the Pt-C/NF electrode and Ni NPs@SN-CNP/NF electrode, respectively. The Ni NPs@SN-CNP/NF||Pt-C/NF cell only needs 1.56 V to achieve 10 mA cm−2, which is comparable to some reported catalysts, such as Ru/Ni3Se4Ni(OH)2/NF (1.51 V) [15], Co0.67Ni0.33P/C (1.59 V) [53], CoFeZr oxides (1.63 V) [29], and FeCoP2@NPPC (1.60 V) [30]. In addition, the assembled two-electrode system remained stable after 10 h of being i-t treated at the potential of 10 mA cm−2 (Figure 8b), indicating the good stability of Ni NPs@SN-CNP.

3. Materials and Methods

3.1. Material

Ni(NO3)2·6H2O, 2, 5-thiophenedicarboxylic acid, 4,4′-bipyridine, and N,N-dimethylformamide were provided by Aladdin Industrial Corporation (Shanghai, China). In this work, all chemical reagents were analytical grade and do not need further purification before use.

3.2. Synthesis of Ni-MOFs

In a typical synthesis procedure for Ni-MOFs, Ni(NO3)2.6H2O (0.2908 g), 4,4′-bipyridine (0.1562 g), and 2, 5-thiophenedicarboxylic acid (0.1722 g) were slowly added to a mixed solvent of dimethylformamide (10 mL) and distilled water (10 mL), then the turbid liquid was ultrasonicated for 30 min. Subsequently, after 3 days of continuous heating at 105 °C, filtering and washing with acetone and anhydrous ethanol several times, the bright green Ni-MOFs were synthesized.

3.3. Synthesis of Ni NPs@SN-CNP

A total of 0.3 g of the Ni-MOFs were placed into a porcelain boat and calcine in it under a N2 atmosphere at 600 °C for 3 h with a heating rate of 5 °C/min. The black Ni NPs@SN-CNP powder catalysts were obtained by natural cooling to room temperature.
As comparison, the products obtained by pyrolyzing Ni-MOFs as precursors at different temperatures (500 °C, 700 °C, 800 °C) were labeled as Ni-MOF-500, Ni-MOF-700, and Ni-MOF-800, respectively.

3.4. Characterizations

The surface chemical qualities of the composites were measured by X-ray photoelectron spectroscopy (XPS, 250XI, Thermofisher Scientific, Waltham, MA, USA). The structure information of the catalysts was revealed by X-ray diffractometer (XRD, D8 Advance A25, Bruker, Karlsruhe, Germany). The morphology and size data of Ni NPs@SN-CNP can be displayed by transmission electron microscope (TEM, JEM-2100, JEOL, Tokyo, Japan). The surface area and pore size distribution of the catalysts were obtained by using specific surface and pore size analysis instrument (BET, 3H-2000PS2, BeiShiDe Instrument-S&T, Beijing, China). All reagents were purchased from commercial sources and used without further treatment, unless otherwise indicated.

3.5. Electrochemical Measurements

The homogeneous suspension of catalyst was prepared by mixing 2 mg of catalyst or Pt-C, 1mg carbon black, 15 µL of 5wt% Nafion perfluorinated resin solution, and 485 µL of anhydrous ethanol, and the mixture was ultrasonically dispersed for approximately 30 min. Next, 25.6 µL of the suspension was uniformly dropped onto a glassy carbon RDE, which was ultrasonic cleaned with acetone and anhydrous ethanol for 10 min, respectively. The capacity of the catalyst was 0.815 mg cm−2. For comparison, the commercial RuO2-modified electrode was followed by the above-mentioned procedure. Before conducting OER testing, N2 is introduced into the solution for 30 min to achieve a N2-saturated 1 M KOH electrolyte, and N2 is continuously introduced during the testing progress.
Electrochemical tests were all performed on a CHI 760E electrochemical workstation, utilizing N2-saturated 1 M KOH as the electrolyte. A glassy carbon RDE loaded with catalyst was used as the working electrode, and the Hg/HgCl2 electrode (saturated KCl) and platinum wire were utilized as the reference electrode and counter electrode, respectively. Convert all measured potentials into reversible hydrogen electrode potentials (RHE) based on the Nernst equation:
E (RHE) = E (SCE) + 0.0591 × pH + 0.244
The LSV (linear sweep voltammetry) tests were conducted at a potential of −0.1 V to 1 V and a scan rate of 5 mV s−1. Before conducting LSV testing, all catalyst samples must undergo 40 cycles of CV testing at a potential of 0 V to 0.7 V and a scan rate of 50 mV s−1 for activation. The Nyquist curves were obtained at a potential of 1.56 V vs. RHE, and a frequency range from 10−1 to 105 Hz. The stability test was conducted by chronopotentiometry (i-t) at a potential of 10 mA cm−2 for 24 h. The current density is calculated based on the area of the glassy carbon RDE (0.1256 cm−2).
Before overall water splitting test, the cathode and anode were fabricated as follows: 377 µL of homogeneous suspension of commercial Pt-C and Ni NPs@SN-CNP were uniformly dropped onto two nickel foam (NF) with a diameter of 0.6 cm, and after drying serve them as the cathode and anode for overall water splitting, respectively. The mass loading is about 2 mg cm−2. The LSV curve of overall water splitting was conducted at a range of 0.4 V to 2.0 V and a scan rate of 1 mV s−1.

4. Conclusions

In summary, we use a simple method for fabricating a multi-hole nitrogen- and sulfur-co-doped nickel-carbon material derived in situ from the nickel MOF through pyrolysis in an inert gas environment. The prepared Ni NPs@SN-CNP exhibits superior oxygen evolution performance with an overpotential of 256 mV at 10 mA cm−2 and a small Tafel slope of 95 mV dec−1. In addition, when operated continuously in an alkaline 1 M KOH for more than 24 h, the electrocatalyst exhibits excellent performance and stability. More importantly, the self-assembled NPs@SN-CNP/NF||Pt-C/NF water-splitting cell also displays high performance. This performance enhancement is attributed to high specific surface area, unique morphological structure, moderate doping of heteroatoms, and the nanoscale structure. In this paper, we present a simple and economical idea to fabricate carbon-based composite materials embedded with nickel doped with S and N without extra S and N sources using Ni-MOF precursors for electrocatalysis.

Author Contributions

H.H.: methodology, validation, formal analysis, and resources; Y.Z.: writing—original draft preparation, software, and data curation; C.Z. and H.Y.: writing—review and editing; Y.K., K.D. and J.W. (Jianying Wang): investigation; H.H., S.C. and J.W. (Jichao Wang): conceptualization, supervision, project administration, and funding acquisition. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by National Natural Science Foundation of China (No. 51802082), Training Program for Young Backbone Teachers in Higher Education Institutions in Henan Province (No. 2024GGJS101).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Data are contained within the article.

Conflicts of Interest

The authors declare no conflicts of interest.

References

  1. Niu, Z.; Lu, Z.; Qiao, Z. Robust Ru-VO2 bifunctional catalysts for all-pH overall water splitting. Adv. Mater. 2024, 36, 2310690. [Google Scholar] [CrossRef] [PubMed]
  2. Zhang, B.; Zheng, Y.; Ma, T. Designing MOF nanoarchitectures for electrochemical water splitting. Adv. Mater. 2021, 33, 2006042. [Google Scholar] [CrossRef]
  3. Lima, G.M.; Belchior, F.N.; Villena, J.E.N. Hybrid electrical energy generation from hydropower, solar photovoltaic and hydrogen. Int. J. Hydrogen Energy 2024, 53, 602–612. [Google Scholar] [CrossRef]
  4. Cheng, C.C.; Ting, Y.C.; Yen, F.Y. Synergistic Mo and W single atoms co-doped surface hydroxylated NiFe oxide as bifunctional electrocatalysts for overall water splitting. Appl. Catal. B-Environ. 2024, 358, 124356. [Google Scholar] [CrossRef]
  5. Yang, Y.; Zhu, C.; Zhang, Y. Construction of Co3O4/Fe2O3 nanosheets on nickel foam as efficient electrocatalyst for the oxygen evolution reaction. J. Phys. Chem. Solids 2021, 148, 109680. [Google Scholar] [CrossRef]
  6. Wang, Y.; Wang, T.; Zhang, R. CuO@CoFe layered double hydroxide core–shell heterostructure as an efficient water oxidation electrocatalyst under mild alkaline conditions. Inorg. Chem. 2020, 59, 9491–9495. [Google Scholar] [CrossRef]
  7. Yang, Y.; Yu, Y.; Li, J. Engineering ruthenium-based electrocatalysts for effective hydrogen evolution reaction. Nanomicro Lett. 2021, 13, 160. [Google Scholar] [CrossRef] [PubMed]
  8. Lin, X.; Chen, D.; Qiu, X. Lignin-metal supramolecular framework strategy of self-healing carbon-coated CoRu alloy nanocatalyst for efficient overall water splitting. Adv. Energy Mater. 2024, 14, 2303442. [Google Scholar] [CrossRef]
  9. Ma, Y.; Lu, Z.A.; Li, S. In situ growth of amorphous Fe(OH)3 on nickel nitrate hydroxide nanoarrays for enhanced electrocatalytic oxygen evolution. ACS. Appl. Mater. 2020, 12, 12668–12676. [Google Scholar] [CrossRef]
  10. Ahmad, F.; Rafiq, K.; Najam, T. Metal-organic frameworks for electrocatalytic water-splitting: Beyond the pyrolysis. Int. J. Hydrogen Energy 2023, 48, 35075–35111. [Google Scholar] [CrossRef]
  11. Hao, J.; Luo, W.; Wang, S. Discharge-induced enhancement of the oxygen evolution reaction. Angew. Chew. Int. Ed. 2021, 60, 20042–20048. [Google Scholar] [CrossRef] [PubMed]
  12. Bhuvanendran, N.; Park, C.W.; Su, H. Multifunctional Pt3Rh–Co3O4 alloy nanoparticles with Pt-enriched surface and induced synergistic effect for improved performance in ORR, OER, and HER. Environ. Res. 2023, 229, 115950. [Google Scholar] [CrossRef] [PubMed]
  13. Shaikh, J.S.; Rittiruam, M.; Saelee, T. Ru tailored hydrous cobalt phosphate as a rational approach for high-performance alkaline oxygen evolution reaction. Mater. Today Chem. 2022, 26, 101267. [Google Scholar] [CrossRef]
  14. You, H.; Wu, D.; Si, D. Monolayer NiIr-layered double hydroxide as a long-lived efficient oxygen evolution catalyst for seawater splitting. J. Am. Chem. Soc. 2022, 144, 9254–9263. [Google Scholar] [CrossRef]
  15. Guo, X.; Li, J.; Meng, F. Ru nanoparticles modified Ni3Se4/Ni(OH)2 heterostructure nanosheets: A fast kinetics boosted bifunctional overall water splitting electrocatalyst. J. Colloid Interface Sci. 2024, 663, 847–855. [Google Scholar] [CrossRef]
  16. Zhou, G.; Wang, P.; Li, H. Spin-state reconfiguration induced by alternating magnetic field for efficient oxygen evolution reaction. Nat. Commun. 2021, 12, 4827. [Google Scholar] [CrossRef]
  17. Qian, Q.; Li, Y.; Liu, Y. Ambient fast synthesis and active sites deciphering of hierarchical foam-like trimetal–organic framework nanostructures as a platform for highly efficient oxygen evolution electrocatalysis. Adv. Mater. 2019, 31, 1901139. [Google Scholar] [CrossRef] [PubMed]
  18. Huang, J.; Sheng, H.; Ross, R.D. Modifying redox properties and local bonding of Co3O4 by CeO2 enhances oxygen evolution catalysis in acid. Nat. Commun. 2021, 12, 3036. [Google Scholar] [CrossRef] [PubMed]
  19. Pan, S.; Ma, Z.; Yang, W. Magnesium incorporation activates perovskite cobaltites toward efficient and stable electrocatalytic oxygen evolution. Mater. Rep. Energy 2023, 3, 100212. [Google Scholar] [CrossRef]
  20. Sun, H.; Xu, X.; Fei, L. Electrochemical oxidation of small molecules for energy-saving hydrogen production. Adv. Energy Mater. 2024, 14, 2401242. [Google Scholar] [CrossRef]
  21. Wu, Z.P.; Lu, X.F.; Zang, S.Q. Non-noble-metal-based electrocatalysts toward the oxygen evolution reaction. Adv. Funct. Mater. 2020, 30, 1910274. [Google Scholar] [CrossRef]
  22. Fan, J.; Chang, X.; Li, L. Synthesis of CoMoO4 nanofibers by electrospinning as efficient electrocatalyst for overall water splitting. Molecules 2023, 29, 7. [Google Scholar] [CrossRef] [PubMed]
  23. Li, X.; Wang, T.; Wang, C. An advanced flower-like Co-Ni/PI-CNT film electrocatalyst for oxygen evolution reaction. J. Alloys Compd. 2017, 729, 19–26. [Google Scholar] [CrossRef]
  24. Lu, J.; Ji, S.; Kannan, P. Hydrophilic Ni(OH)2@CoB nano-chains with shell-core structure as an efficient catalyst for oxygen evolution reaction. J. Alloys Compd. 2020, 844, 156129. [Google Scholar] [CrossRef]
  25. Wan, Z.; Guo, X.; Jiang, J. Modulating nickel-iron active species via dealloying to boost the oxygen evolution reaction. Dalton Trans. 2024, 53, 2065–2072. [Google Scholar] [CrossRef] [PubMed]
  26. Li, Y.D.; Mou, C.L.; Ma, W.L. Nano-TiO2 anchored onto 2D Cu–Ni bimetallic MOF as a heterojunction for highly-efficient OER overpotential reduction. New J. Chem. 2024, 48, 2979–2991. [Google Scholar] [CrossRef]
  27. Wu, R.; Wang, D.P.; Rui, X. In-situ formation of hollow hybrids composed of cobalt sulfides embedded within porous carbon polyhedra/carbon nanotubes for high-performance lithium-ion batteries. Adv. Mater. 2015, 27, 3038–3044. [Google Scholar] [CrossRef] [PubMed]
  28. Wang, Q.; Zou, R.; Xia, W. Facile synthesis of ultrasmall CoS2 nanoparticles within thin N-doped porous carbon shell for high performance lithium-ion batteries. Small 2015, 11, 2511–2517. [Google Scholar] [CrossRef]
  29. Chen, B.; Li, R.; Ma, G. Cobalt sulfide/N, S codoped porous carbon core–shell nanocomposites as superior bifunctional electrocatalysts for oxygen reduction and evolution reactions. Nanoscale 2015, 7, 20674–20684. [Google Scholar] [CrossRef] [PubMed]
  30. Xu, X.; Sun, H.; Jiang, S.P. Modulating metal–organic frameworks for catalyzing acidic oxygen evolution for proton exchange membrane water electrolysis. SusMat 2021, 1, 460–481. [Google Scholar] [CrossRef]
  31. Chen, B.; Ma, G.; Kong, D. Atomically homogeneous dispersed ZnO/N-doped nanoporous carbon composites with enhanced CO2 uptake capacities and high efficient organic pollutants removal from water. Carbon 2015, 95, 113–124. [Google Scholar] [CrossRef]
  32. Jin, H.; Wang, J.; Su, D. In situ cobalt–cobalt oxide/N-doped carbon hybrids as superior bifunctional electrocatalysts for hydrogen and oxygen evolution. J. Am. Chem. Soc. 2015, 137, 2688–2694. [Google Scholar] [CrossRef] [PubMed]
  33. Torad, N.L.; Hu, M.; Ishihara, S. Direct synthesis of MOF-derived nanoporous carbon with magnetic Co nanoparticles toward efficient water treatment. Small 2014, 10, 2096–2107. [Google Scholar] [CrossRef] [PubMed]
  34. Chen, B.; Ma, G.; Zhu, Y. Metal-organic-framework-derived bi-metallic sulfide on N, S-codoped porous carbon nanocomposites as multifunctional electrocatalysts. J. Power Sources 2016, 334, 112–119. [Google Scholar] [CrossRef]
  35. Sun, Y.; Ding, S.; Xu, S. Metallic two-dimensional metal-organic framework arrays for ultrafast water splitting. J. Power Sources 2021, 494, 229733. [Google Scholar] [CrossRef]
  36. Lin, Y.; Chen, G.; Wan, H. 2D free-standing nitrogen-doped Ni-Ni3S2@ carbon nanoplates derived from metal–organic frameworks for enhanced oxygen evolution reaction. Small 2019, 15, 1900348. [Google Scholar] [CrossRef] [PubMed]
  37. Zheng, Y.; Zhang, G.; Zhang, P. Structural investigation of metallic Ni nanoparticles with N-doped carbon for efficient oxygen evolution reaction. Chem. Eng. J. 2022, 429, 132122. [Google Scholar] [CrossRef]
  38. Öztürk, S.; Xiao, Y.X.; Dietrich, D. Nickel nanoparticles supported on a covalent triazine framework as electrocatalyst for oxygen evolution reaction and oxygen reduction reactions. Beilstein J. Nanotechnol. 2020, 11, 770–781. [Google Scholar] [CrossRef] [PubMed]
  39. Huang, H.C.; Shown, I.; Chang, S.T. Pyrolyzed cobalt corrole as a potential non-precious catalyst for fuel cells. Adv. Funct. Mater. 2012, 22, 3500–3508. [Google Scholar] [CrossRef]
  40. Qiao, J.; Xu, L.; Ding, L. Using pyridine as nitrogen-rich precursor to synthesize Co-NS/C non-noble metal electrocatalysts for oxygen reduction reaction. Appl. Catal. 2012, 125, 197–205. [Google Scholar] [CrossRef]
  41. Zhao, Y.; Nakamura, R.; Kamiya, K. Nitrogen-doped carbon nanomaterials as non-metal electrocatalysts for water oxidation. Nat. Commun. 2013, 4, 2390. [Google Scholar] [CrossRef] [PubMed]
  42. Yin, J.; Qiu, Y.; Yu, J. Onion-like graphitic nanoshell structured Fe–N/C nanofibers derived from electrospinning for oxygen reduction reaction in acid media. Electrochem. Commun. 2013, 30, 1–4. [Google Scholar] [CrossRef]
  43. Ai, W.; Luo, Z.; Jiang, J. Nitrogen and sulfur codoped graphene: Multifunctional electrode materials for high-performance Li-ion batteries and oxygen reduction reaction. Adv. Mater. 2014, 26, 6186–6192. [Google Scholar] [CrossRef] [PubMed]
  44. Liu, R.; Wu, D.; Feng, X. Nitrogen-doped ordered mesoporous graphitic arrays with high electrocatalytic activity for oxygen reduction. Angew. Chem. Int. Ed. 2010, 14, 2565–2569. [Google Scholar] [CrossRef]
  45. Mathankumar, M.; Karthick, K. In situ decorated Ni metallic layer with CoS2-layered thin films via a layer-by-layer strategy using pulsed laser deposition for enhanced electrocatalytic OER. Inorg. Chem. 2021, 60, 8946–8957. [Google Scholar] [CrossRef] [PubMed]
  46. Shreyanka, S.N.; Theerthagiri, J.; Lee, S.J. Multiscale design of 3D metal–organic frameworks (M−BTC, M: Cu, Co, Ni) via PLAL enabling bifunctional electrocatalysts for robust overall water splitting. Chem. Eng. J. 2022, 446, 137045. [Google Scholar] [CrossRef]
  47. Pan, C.; Liu, Z.; Huang, M. 2D iron-doped nickel MOF nanosheets grown on nickel foam for highly efficient oxygen evolution reaction. Appl. Surf. Sci. 2020, 529, 147201. [Google Scholar] [CrossRef]
  48. Wen, Y.; Wei, Z.; Ma, C. MXene boosted CoNi-ZIF-67 as highly efficient electrocatalysts for oxygen evolution. Nanomaterials 2019, 9, 775. [Google Scholar] [CrossRef]
  49. Rui, K.; Zhao, G.; Chen, Y. Hybrid 2D dual-metal–organic frameworks for enhanced water oxidation catalysis. Adv. Funct. Mater. 2018, 28, 1801554. [Google Scholar] [CrossRef]
  50. Jiang, Y.; Cheng, K.; Xie, J. Construction of core-shell NiFe LDH/Co(OH)F amorphous/crystalline heterostructure for synergistically enhanced electrocatalytic water oxidation. J. Alloys Compd. 2024, 1010, 177889. [Google Scholar] [CrossRef]
  51. Chen, Y.; Wu, Y.; Chen, M. Interface engineering of Ni3S2@NiFe-LDH core-shell heterostructure to achieve energy-saving hydrogen production. J. Alloys Compd. 2024, 1010, 177855. [Google Scholar] [CrossRef]
  52. Salman, M.; Qin, H.; Zou, Y. In-situ decoration of NiCo-thiophene based metal-organic framework on nickel foam as an efficient electrocatalyst for oxygen evolution reaction. J. Power Sources 2025, 629, 235942. [Google Scholar] [CrossRef]
  53. Li, G.; Zhao, M.; Yang, F. Size controllable CoNiP nanoparticle supported on porous carbon for highly-efficient electrocatalytic overall water splitting. Int. J. Hydrogen Energy 2025, 105, 1–9. [Google Scholar] [CrossRef]
Molecules 30 00820 g001
Figure 1. Schematic presentation of synthesis process of Ni NPs@SN-CNP.
Figure 1. Schematic presentation of synthesis process of Ni NPs@SN-CNP.
Molecules 30 00820 g001
Molecules 30 00820 g002
Figure 2. XRD pattern of Ni-MOF-500, Ni NPs@SN-CNP, Ni-MOF-700, and Ni-MOF-800.
Figure 2. XRD pattern of Ni-MOF-500, Ni NPs@SN-CNP, Ni-MOF-700, and Ni-MOF-800.
Molecules 30 00820 g002
Molecules 30 00820 g003
Figure 3. (a,b) FESEM images (inset is corresponding size distribution). (c) TEM and (d–h) element distribution images of Ni NPs@SN-CNP. (i) The spectrum of the proportion of the corresponding elements in the Ni NPs@SN-CNP.
Figure 3. (a,b) FESEM images (inset is corresponding size distribution). (c) TEM and (d–h) element distribution images of Ni NPs@SN-CNP. (i) The spectrum of the proportion of the corresponding elements in the Ni NPs@SN-CNP.
Molecules 30 00820 g003
Molecules 30 00820 g004
Figure 4. (a,b) TEM images (inset is corresponding size distribution). (c) High-resolution TEM (HRTEM) of the Ni NPs@SN-CNP. (d) SAED pattern of the Ni NPs@SN-CNP.
Figure 4. (a,b) TEM images (inset is corresponding size distribution). (c) High-resolution TEM (HRTEM) of the Ni NPs@SN-CNP. (d) SAED pattern of the Ni NPs@SN-CNP.
Molecules 30 00820 g004
Molecules 30 00820 g005
Figure 5. (a) XPS survey spectrum of high-resolution (b) Ni 2p, (c) C 1s, (d) N 1s, (e) S 2p, and (f) O 1s for the Ni NPs@SN-CNP.
Figure 5. (a) XPS survey spectrum of high-resolution (b) Ni 2p, (c) C 1s, (d) N 1s, (e) S 2p, and (f) O 1s for the Ni NPs@SN-CNP.
Molecules 30 00820 g005
Molecules 30 00820 g006
Figure 6. (a–d) Nitrogen adsorption–desorption isotherms and (e–h) the corresponding pore size distributions of Ni-MOF-500, Ni NPs@SN-CNP, Ni-MOF-700, and Ni-MOF-800.
Figure 6. (a–d) Nitrogen adsorption–desorption isotherms and (e–h) the corresponding pore size distributions of Ni-MOF-500, Ni NPs@SN-CNP, Ni-MOF-700, and Ni-MOF-800.
Molecules 30 00820 g006
Molecules 30 00820 g007
Figure 7. (a) LSV curves for the OER of Ni-MOF, Ni-MOF-500, Ni NPs@SN-CNP, Ni-MOF-700, Ni-MOF-800, and RuO2 catalysts in N2-saturated 1 M KOH. (b) Tafel plots of Ni-MOF, Ni-MOF-500, Ni NPs@SN-CNP, Ni-MOF-700, Ni-MOF-800, and RuO2 catalysts based on (a). (c) Nyquist plots of the six catalysts. (d) Overpotential of Ni-MOF, Ni-MOF-500, Ni NPs@SN-CNP, Ni-MOF-700, Ni-MOF-800, and RuO2 catalysts in N2-saturated 1 M KOH. (e) i-t curve of Ni NPs@SN-CNP at 1 M KOH and 10 mA/cm−2 of current density (inset: TEM image of Ni NPs@SN-CNP after i-t treated and corresponding size distribution). (f) LSV curves for the OER of Ni NPs@SN-CNP before and after being i-t treated (inset: XRD pattern of Ni NPs@SN-CNP before and after being i-t treated).
Figure 7. (a) LSV curves for the OER of Ni-MOF, Ni-MOF-500, Ni NPs@SN-CNP, Ni-MOF-700, Ni-MOF-800, and RuO2 catalysts in N2-saturated 1 M KOH. (b) Tafel plots of Ni-MOF, Ni-MOF-500, Ni NPs@SN-CNP, Ni-MOF-700, Ni-MOF-800, and RuO2 catalysts based on (a). (c) Nyquist plots of the six catalysts. (d) Overpotential of Ni-MOF, Ni-MOF-500, Ni NPs@SN-CNP, Ni-MOF-700, Ni-MOF-800, and RuO2 catalysts in N2-saturated 1 M KOH. (e) i-t curve of Ni NPs@SN-CNP at 1 M KOH and 10 mA/cm−2 of current density (inset: TEM image of Ni NPs@SN-CNP after i-t treated and corresponding size distribution). (f) LSV curves for the OER of Ni NPs@SN-CNP before and after being i-t treated (inset: XRD pattern of Ni NPs@SN-CNP before and after being i-t treated).
Molecules 30 00820 g007
Molecules 30 00820 g008
Figure 8. (a) The LSV curve of Ni NPs@SN-CNP in 1 M KOH. (Inset: the picture of H2 and O2 emerge from the Pt-C/NF electrode and Ni NPs@SN-CNP/NF electrode, respectively). (b) i-t curve of Ni NPs@SN-CNP at the potential of 10 mA cm−2 in 1 M KOH.
Figure 8. (a) The LSV curve of Ni NPs@SN-CNP in 1 M KOH. (Inset: the picture of H2 and O2 emerge from the Pt-C/NF electrode and Ni NPs@SN-CNP/NF electrode, respectively). (b) i-t curve of Ni NPs@SN-CNP at the potential of 10 mA cm−2 in 1 M KOH.
Molecules 30 00820 g008
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Han, H.; Zhang, Y.; Zhou, C.; Yun, H.; Kang, Y.; Du, K.; Wang, J.; Chao, S.; Wang, J. S- and N-Co-Doped Carbon-Nanoplate-Encased Ni Nanoparticles Derived from Dual-Ligand-Assembled Ni-MOFs as Efficient Electrocatalysts for the Oxygen Evolution Reaction. Molecules 2025, 30, 820. https://doi.org/10.3390/molecules30040820

AMA Style

Han H, Zhang Y, Zhou C, Yun H, Kang Y, Du K, Wang J, Chao S, Wang J. S- and N-Co-Doped Carbon-Nanoplate-Encased Ni Nanoparticles Derived from Dual-Ligand-Assembled Ni-MOFs as Efficient Electrocatalysts for the Oxygen Evolution Reaction. Molecules. 2025; 30(4):820. https://doi.org/10.3390/molecules30040820

Chicago/Turabian Style

Han, Huijuan, Yalei Zhang, Chunrui Zhou, Haixin Yun, Yiwen Kang, Kexin Du, Jianying Wang, Shujun Chao, and Jichao Wang. 2025. "S- and N-Co-Doped Carbon-Nanoplate-Encased Ni Nanoparticles Derived from Dual-Ligand-Assembled Ni-MOFs as Efficient Electrocatalysts for the Oxygen Evolution Reaction" Molecules 30, no. 4: 820. https://doi.org/10.3390/molecules30040820

APA Style

Han, H., Zhang, Y., Zhou, C., Yun, H., Kang, Y., Du, K., Wang, J., Chao, S., & Wang, J. (2025). S- and N-Co-Doped Carbon-Nanoplate-Encased Ni Nanoparticles Derived from Dual-Ligand-Assembled Ni-MOFs as Efficient Electrocatalysts for the Oxygen Evolution Reaction. Molecules, 30(4), 820. https://doi.org/10.3390/molecules30040820