Next Article in Journal
Insights into SnO2 Nanoparticles Supported on Fibrous Mesoporous Silica for CO Catalytic Oxidation
Next Article in Special Issue
Identifying the Active Phase of RuO2 in the Catalytic CO Oxidation Reaction, Employing Operando CO Infrared Spectroscopy and Online Mass Spectrometry
Previous Article in Journal
Ultra-Low Loading of Iron Oxide and Platinum on CVD-Graphene Composites as Effective Electrode Catalysts for Solid Acid Fuel Cells
Previous Article in Special Issue
CO Oxidation Catalyzed by Au Dispersed on SBA-15 Modified with TiO2 Films Grown via Atomic Layer Deposition (ALD)
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Au Clusters Supported on Defect-Rich Ni-Ti Oxides Derived from Ultrafine Layered Double Hydroxides (LDHs) for CO Oxidation at Ambient Temperature

1
Department of Applied Chemistry for Environment, Graduate School of Urban Environmental Sciences, Tokyo Metropolitan University, 1-1 Minami-osawa, Hachioji, Tokyo 192-0397, Japan
2
Yantai Key Laboratory of Gold Catalysis and Engineering, Shandong Applied Research Center of Gold Nanotechnology (Au-SDARC), School of Chemistry & Chemical Engineering, Yantai University, 30 Qingquan Road, Yantai 264005, China
3
Laboratory of Integrated Function Materials, Center for Advanced Research of Energy and Materials, Faculty of Engineering, Hokkaido University, Kita13 Nishi8, Kita-ku, Sapporo, Hokkaido 060-8628, Japan
*
Author to whom correspondence should be addressed.
Catalysts 2023, 13(8), 1155; https://doi.org/10.3390/catal13081155
Submission received: 29 June 2023 / Revised: 21 July 2023 / Accepted: 23 July 2023 / Published: 26 July 2023

Abstract

:
Ultrafine layered double hydroxides (LDHs) have abundant hydroxy groups at their edge sites, serving as anchor sites for metal NPs. Furthermore, transformation of ultrafine LDHs into mixed metal oxides (MMOs) generates abundant oxygen vacancies, which are advantageous for O2 activation during Au-catalyzed CO oxidation. We used ultrafine Ni-Ti LDHs with low crystallinity or Ni-Ti MMOs supported on SiO2 onto which Au NPs were deposited by deposition–precipitation (DP) and DP–urea (DPU). The catalytic activity of the Au catalysts was significantly affected by the preparation method, with the highest activity obtained by depositing Au onto LDH/SiO2 by DPU, followed by transformation of LDH to MMO (Au/Ni-Ti MMO/SiO2 (LDH-DPU)). The presence of Au on LDHs affected the transformation of LDHs into MMOs, resulting in LDH-DPU having the greatest number of oxygen vacancies in the TiO2 domain in MMOs. Consequently, the adsorbed or the lattice oxygen on the surface of LDH-DPU can be easily utilized for CO oxidation at low temperatures. Moreover, the catalytic activity of LDH-DPU increased with water vapor concentration up to 100% relative humidity at room temperature, suggesting the potential of Au/Ni-Ti MMO/SiO2 as an air purification catalyst.

1. Introduction

The catalytic oxidation of harmful CO to CO2 in air at ambient temperature is a fundamental and important process for air purification. In 1987, Haruta et al. reported that Au nanoparticles (NPs) supported on reducible metal oxides exhibited outstanding catalytic activity for CO oxidation at −70 °C [1]. This discovery sparked extensive research on Au catalysts because other metal catalysts, such as Pd and Pt, required higher temperatures exceeding 100 °C. Since then, tremendous efforts have been devoted to the development of highly active Au catalysts. Because the catalytic performance of Au significantly depends on the size of Au NPs and the type of supports, numerous preparation methods have been developed to deposit small Au particles onto various supports [2,3,4]. Specifically, Au clusters with diameters less than 2 nm are desirable to exhibit high activity. The reaction mechanism of Au-catalyzed CO oxidation has been discussed both experimentally and theoretically [2,4,5,6,7,8]. It is now widely accepted that the active site of Au-catalyzed CO oxidation is Au–support interface. Au works as a CO adsorption sites, and O2 is activated at the oxygen vacancies on the metal oxide supports [4,6,7,8]. Therefore, reducible metal oxides, such as NiO, Co3O4, CeO2, and TiO2, have been frequently used as supports for Au NPs.
Recently, single-Au-atom catalysts have attracted increasing interest in order to minimize the use of precious metals [9]. CeO2 [10], Co3O4 [11], FeOx [12], and NiO [13] are regarded as suitable supports because single Au atoms can be stabilized at their metal vacancies. However, these single-Au-atom catalysts can be only realized in extremely low loading weights, such as 0.03 wt% of Au [12], except for NiO [13]. This means that a large amount of support is required to exhibit demanding catalytic performance, despite the fact that these metal oxides are classified as rare metals except for FeOx. Therefore, there is a need to minimize the usage of both Au and these rare metal oxides for sustainable development. Although FeOx is an abundant metal oxide, the T1/2 value of Au1/FeOx, i.e., the temperature of 50% CO conversion, has been reported to be at around 40 °C [12]. Photocatalytic CO oxidation over Au/TiO2 has been also reported, but the working temperature exceeded 60 °C [14].
Despite the abundance of SiO2 on Earth, SiO2 is regarded as an unsuitable support for Au NPs because of the lack of oxygen vacancies and aggregation of Au NPs on SiO2. Conversely, irreducible metal oxides such as SiO2 and Al2O3 are tolerant of deactivation in CO oxidation under humid air conditions, while Au/TiO2 experiences a decrease in activity in high humidity [15,16,17]. Thus, there is still room for the development of CO oxidation catalysts that incorporate minimal amounts of Au and rare metals and catalysts capable of functioning at ambient temperature in humid air for applications in air purification.
Layered double hydroxides (LDHs) consist of divalent metal hydroxides with a brucite-layered structure, wherein trivalent metal ions are partially replaced with divalent ones. Many types of LDHs have been synthesized [18]. The chemical formula of LDH is [M2+1−xM3+x(OH)2][An−x/n·yH2O], where the anion (An−) and water molecules are intercalated to compensate for the positive surface charge. LDHs have interesting features such as a solid base, anion exchange ability, and transformation into mixed metal oxides (MMOs). Natural LDHs, known as hydrotalcite ([Mg0.75Al0.25(OH)2][(CO32−)0.125·0.5H2O]), have been used as supports for Au. Because the hydroxyl groups at the edge sites of LDHs are more basic, Au tends to be initially deposited at the edge sites on Mg-Al LDHs, resulting in the formation of Au clusters at low Au loadings. Subsequently, Au is deposited on the lateral face of the LDH to produce aggregated Au NPs [19]. The size of the LDH affects the generation of defects in LDHs [20], and metal- and oxygen vacancies after transformation into MMOs [21,22]. Zhang et al. transformed ultrafine Ni-Ti LDH particles (<4 nm) into defect-rich Ni-Ti MMOs with abundant Ni3+ and Ti3+ sites [21]. Thus, Ni-Ti LDH NPs with abundant edge OH groups and Ni vacancies are beneficial for stabilizing small Au particles. In addition, the rich oxygen vacancies on the TiOx domain derived from the Ni-Ti LDH NPs are expected to efficiently activate O2, leading to high catalytic activity for CO oxidation.
In this study, we attempted to form highly dispersed ultrafine Ni-Ti LDH on SiO2 and deposited Au NPs on the prepared Ni-Ti LDH/SiO2 and Ni-Ti MMO/SiO2. The Au particle size and catalytic activity for CO oxidation varied according to the preparation method and support used (LDH/SiO2 or MMO/SiO2). The deposition of Au onto LDH/SiO2 by deposition–precipitation with urea (DPU) followed by the transformation of LDH into MMO gave the most active catalyst, which was active for CO oxidation at room temperature. On the other hand, deposition–precipitation (DP) of Au onto LDH/SiO2, followed by calcination, resulted in relatively large Au NPs with much lower activity. However, DP is more suitable for the deposition of Au onto MMO/SiO2 to obtain small Au NPs. The presence of Au during calcination affected the transformation of LDHs into MMOs, and the number of Ni- and oxygen vacancies in the resultant ultrafine Ni-Ti MMO varied based on the preparation method. Au/Ni-Ti MMO/SiO2, prepared from LDH/SiO2 followed by calcination, possessed abundant oxygen vacancies in the TiOx domain, which contributed to its high activity. Consequently, we found that the oxygen vacancies could be generated easily by using ultrafine Ni-Ti LDH. Because Ni-Ti LDHs were highly dispersed on SiO2, the use of Ni could also be reduced. Furthermore, the LDH-DPU catalyst exhibited enhanced activity in CO oxidation even at 4% water concentration, which is equal to 100% relative humidity (RH) at room temperature. The results suggest that Au on ultrafine Ni-Ti MMO/SiO2 can serve as efficient air purification catalysts under high humidity conditions.

2. Results and Discussion

2.1. Characterization of Ni-Ti LDH/SiO2

Ni-Ti LDH/SiO2 (Ni/Ti = 4/1 atomic ratio) was prepared through hydrothermal synthesis using Ni(NO3)2·6H2O and TiCl4, following previously reported methods [23,24] with minor modification. Subsequently, Ni-Ti LDH/SiO2 was converted to Ni-Ti MMO/SiO2 by calcination in air at 500 °C for 2 h (Scheme 1, upper side). Additionally, bulk Ni-Ti MMO was obtained by preparing pristine Ni-Ti LDH in the absence of SiO2 in the same manner, followed by calcination at 500 °C for 2 h. The powder X-ray diffraction (XRD) patterns of bulk Ni-Ti LDH, Ni-Ti LDH/SiO2, and Ni-Ti MMO/SiO2 (Ni/Ti = 4) are shown in Figure 1a. Zhang et al. prepared Ni-Ti LDH NPs with ~20 nm using a reverse microemulsion method in an organic solvent and reported diffraction peaks at 35 and 60°, which corresponded to the (012) and (110) planes, respectively. Additionally, unassigned peaks were observed at around 25, 38, and 45° [21,24]. For the bulk Ni-Ti LDH, diffraction peaks were observed at 10, 25, 34, and 60°, which are almost in agreement with previous reports [21,24]. The peaks at 10 and 25° were probably attributed to the (003) and (006) planes, respectively, suggesting the typical layered structure of LDHs. The peak at 19° was probably ascribed to a partial formation of β-Ni(OH)2 (ICDD No. 00-014-0117) [25]. The broad peaks indicate that small Ni-Ti LDH crystallites were obtained using hydrothermal method. The XRD peaks corresponding to Ni-Ti LDH were also observed for Ni-Ti LDH/SiO2, together with the halo pattern of amorphous SiO2 at approximately 25°. The broad and weak peaks of Ni-Ti LDH suggest that very small Ni-Ti LDH crystallites were formed on SiO2 and/or that the Ni-Ti LDH on SiO2 had low crystallinity.
Thermogravimetric analysis (TGA) was performed to elucidate the transformation of LDHs into MMOs (Figure S1). In the case of bulk Ni-Ti LDH, the weight gradually decreased up to 300 °C, followed by a sharp decline from 300 to 350 °C. These steps coincide with the desorption of the intercalated H2O and CO2 and the dehydration of hydroxides, respectively [26]. The transformation of LDH to MMO was completed at 400 °C, with a weight loss of 31%, which is consistent with the previous report [21]. These desorption and dehydration steps were shifted to higher temperatures for Ni-Ti LDH/SiO2 (Figure S1), and the transformation into MMO was completed at 550 °C.

2.2. Characterization of Ni-Ti MMO/SiO2

A temperature-dependence study was conducted by varying the calcination temperatures of Ni-Ti LDH/SiO2 within the range of 500 to 900 °C (Figure S2). No obvious change was observed after calcination of Ni-Ti LDH/SiO2 at 500 and 600 °C. However, above 700 °C distinct peaks corresponding to NiO peak at 43° and NiTiO3 peaks at 33 and 35.8° (ICDD No. 00-033-0960) were observed. Calcination below 600 °C produced NiO and TiO2, while Ni2TiO4 and NiTiO3 were formed above 600 °C [21]. Thus, Ni-Ti LDH/SiO2 was calcined at 500 °C to convert Ni-Ti MMO/SiO2 (Figure 1a).
The XRD pattern of the Au/bulk Ni-Ti MMO showed sharp peaks at 25, 37, 43, and 63°, which were attributed to TiO2 (anatase, ICDD No. 00-021-1272) and NiO (ICDD No. 00-044-1159) (Figure 1b). No obvious change of XRD pattern was observed for Ni-Ti MMO/SiO2, whereas the (003) diffraction at 10° disappeared. In addition, the peaks at 25 and 37° attributed to TiO2 and NiO, respectively, became slightly increased. These results suggest that LDH was converted to MMO, although LDH remaining was not fully ruled out. The broad and weak diffraction peaks suggest that the aggregation of Ni-Ti MMO crystallites could be prevented on SiO2 support during calcination. Scanning electron microscopy (SEM) revealed that Ni and Ti species were highly dispersed on SiO2 (Figure S3). The Ni and Ti loadings were calculated using inductively coupled plasma–atomic emission spectroscopy (ICP-AES) (Table 1). The Ni/Ti atomic ratio was estimated to be 4.8 by ICP-AES, which is almost consistent with the initial Ni/Ti ratio (4/1).

2.3. Characterization of Au/Ni-Ti MMO/SiO2

The deposition of Au NPs to Ni-Ti LDH/SiO2 and Ni-Ti MMO/SiO2 was performed by DP and DPU to give four types of Au catalysts, as shown in Scheme 1. First, Au was deposited on Ni-Ti LDH/SiO2 by DP and DPU, followed by calcination in air at 500 °C to transform LDH to MMO, yielding Au/Ni-Ti MMO/SiO2; the catalysts were denoted as LDH-DP and LDH-DPU, respectively. Alternatively, Au was also deposited on Ni-Ti MMO/SiO2 by DP and DPU; this was followed by the reduction of Au(III) species by air calcination at 300 °C and by reduction with NaBH4, according to the literature [27], giving Au/Ni-Ti MMO/SiO2, denoted as MMO-DP and MMO-DPU, respectively. The initial Au loading was set to 0.3 wt%, and almost 80% of Au was deposited, except for MMO-DP (Table 1). The relatively low actual Au loading for MMO-DP (Au 0.15 wt%) was ascribed to the negatively charged surface (−29 mV) at pH 7, as determined by zeta potential measurement. This surface charge led to electronic repulsion between the MMO/SiO2 and negatively charged Au precursors.
The XRD patterns of four Au/Ni-Ti MMO/SiO2 (Figure 1b) resembled that of Ni-Ti MMO/SiO2 (Figure 1a). No diffraction peaks corresponding to Au were observed owing to low Au loading (Figure 1b). The size of Au particles was estimated by high-angle annular dark-field transmission electron microscopy (HAADF-STEM), and the size distributions are summarized in Table 1 and Figure 2. In Figure 2, a needle-like structure can be observed, which would be ascribed to the layered structure of MMO derived from LDH. The Au particles were highly dispersed on the Ni-Ti MMO/SiO2 of all the catalysts. Although LDH-DP and MMO-DPU gave Au NPs with diameters of 3.5–4.0 nm, Au clusters with diameters of 2.3 and 1.7 nm could be deposited on LDH-DPU and MMO-DP. The Au particle size in the Au/bulk Ni-Ti MMO prepared by DP was estimated to be 3.2 nm (Figure S4). From these results, LDH-DPU and MMO-DP are suitable preparation methods and highly dispersed ultrafine LDH and MMO are beneficial for the deposition of Au clusters.
Because the M2+/M3+ ratio of LDHs can be varied up to 2/1, Ni-Ti LDH with a Ni/Ti ratio of 2/1 was synthesized. Subsequently, Au/Ni-Ti MMO/SiO2 with the Ni/Ti ratio of 2/1 was prepared from NiTi LDH/SiO2 by DPU, followed by calcination to form MMO. However, relatively large Au NPs (6.0 nm) were obtained (Figure S5). The Ni/Ti ratio affected the crystallite size of NiO and TiO2 domains, and a suitable Ni/Ti ratio (4/1) resulted in small Au particles.

2.4. Catalytic Activity for CO Oxidation

The catalytic activity of the Au/Ni-Ti MMO/SiO2 for CO oxidation was evaluated using a fixed-bed flow reactor, and the results are shown in Table 1 and Figure 3. The order of catalytic activity is LDH-DPU > MMO-DP > LDH-DP > MMO-DPU (entries 1–4). When compared to LDH-DP and LDH-DPU, LDH-DPU stabilized smaller Au particles with higher loading, exhibiting in higher catalytic activity. In contrast, comparing MMO-DPU and MMO-DP, MMO-DP stabilized smaller Au particles, resulting in higher activity. However, the actual Au loading of MMO-DP was lower than LDH-DPU. As a result, LDH-DPU exhibited the highest catalytic activity and recorded T1/2 of 10 °C.
In order to reveal the factors for the high activity of LDH-DPU, the transformation of LDH into MMO is discussed. Au/Ni-Ti LDH/SiO2 prepared by DPU followed by the reduction of Au(III) with NaBH4 (entry 5) showed much higher T1/2 than LDH-DPU, suggesting that the transformation of LDH into MMO is important for achieving high catalytic activity. The calcination of Au/Ni-Ti LDH/SiO2 at 300 and 400 °C denoted as LDH-DPU-300 and LDH-DPU-400, respectively, was also performed. Although LDH-DPU-400 showed similar activity to that of LDH-DPU, LDH-DPU-300 showed much lower catalytic activity than that of LDH-DPU. Thus, the incomplete transformation of LDH to MMO at 300 °C gave unsatisfactory results (entries 2, 6, and 7).
Next, the dependence of Ni/Ti ratio of Ni-Ti MMO on the catalytic activity was examined. Compared to Ni/Ti = 4/1, Au/Ni-Ti MMO/SiO2 (Ni/Ti = 2/1) showed lower activity than LDH-DPU because of its larger Au NPs (entry 8). Moreover, LDH-DPU exhibited higher activity than Au/bulk Ni-Ti MMO (entries 2 and 9). Given that bulk Ni-Ti MMO has large NiO and TiO2 crystallites, according to XRD (Figure 1), highly dispersed ultrafine NiO and TiO2 domains would work as an efficient support for CO oxidation.
The catalytic activity of the most active LDH-DPU was compared with those of commercially available Au/TiO2, Au/NiO, Au/SiO2, and Au/Fe2O3 (entries 10–13). Au/SiO2 showed very low activity because O2 could not be activated due to the lack of oxygen vacancies in SiO2 (entry 12). LDH-DPU exhibited higher catalytic activity than Au/NiO, although single Au atoms are major species in Au/NiO (entry 11). It has been reported that inverse NiO-on-Au supported on SiO2 catalysts exhibited high catalytic activity for CO oxidation at room temperature and that the reaction rate was recorded to be 1.74 molCO gAu−1 h−1 [28]. The reaction rate of LDH-DPU was calculated to be 2.32 molCO gAu−1 h−1 at 25 °C, which is superior to the previous report. Au/NiO prepared by double impregnation was also reported to show high activity, and the reaction rate was calculated to be 2.59 molCO gAu−1 h−1 [29]. Although the reaction rate of LDH-DPU was slightly lower than this value, the amount of Ni was lower than the reported Au/NiO. The T1/2 of LDH-DPU was almost the same as that of Au/TiO2 whereas the Au loading was smaller (0.3 wt%) than that of 1 wt% Au/TiO2 (entry 10). Moreover, the T1/2 of Au/Fe2O3 was 36 °C, which showed lower activity than LDH-DPU despite the small Au particle size and redox activity of Fe2O3 (entry 13). From these results, LDH-DPU exhibited the highest catalytic activity based on the amount of Au used.

2.5. Evaluation of Oxygen Vacancies on Ni-Ti MMO/SiO2

These CO oxidation results suggest that the catalytic activity significantly varies depending on not only the Au particle size but also the support (LDH or MMO) on which the Au particles are deposited and on the preparation method used. It has been reported that abundant Ni- and O vacancies are formed by the conversion of LDH to MMO, as the size of Ni-Ti LDH decreases [21]. Therefore, the Ni 2p, O 1s, and Ti 2p XPS of the four Au catalysts were measured to evaluate these vacancies, and the results are shown in Figure 4.
Ni 2p3/2 peaks of LDH-DP, LDH-DPU, MMO-DP, and MMO-DPU were observed at 857.3, 856.7, 858.4, and 857.7 eV, respectively (Figure 4A). The peaks of Ni2+, Ni3+, Ni oxyhydroxide (NiOOH), and Ni(OH)2 were observed at 854.0–854.4, 855.5–856.3, 856.8–857.7, and 855.4–856.2 eV, respectively [30,31,32,33,34,35]. When Au was deposited on LDH, the resultant MMO contained Ni2+ as the major species, while NiO domains of MMO-DP and MMO-DPU showed a higher energy shift. Although Ni(OH)2 species remaining cannot be fully ruled out, the higher binding energy shift compared to the typical Ni2+ of NiO implies the presence of Ni3+ species, i.e., rich Ni vacancies, in MMO/SiO2. However, the energy shift did not correlate with the size of the Au particles. Therefore, the size of the Au particles was affected by the preparation method. Accordingly, the smallest Au particle size of MMO-DP was probably due to the low actual Au loading, which prevented aggregation during calcination. For Ni-Ti LDH/SiO2, LDH-DP resulted in larger Au NPs than LDH-DPU, indicating that the aggregation of Au proceeded during calcination at 300 °C before converting LDH into MMO at 500 °C. Compared the samples prepared by DPU, LDH-DPU produced smaller Au particles than MMO-DPU, suggesting that the abundant edge OH groups of ultrafine Ni-Ti LDH were beneficial for stabilizing small Au particles.
The presence of oxygen vacancies was evaluated by O 1s and Ti 2p XPS. As shown in Figure 4B, the major O 1s peak was observed at 532.2–532.8 eV corresponding to the lattice oxygen of SiO2 and MMO. The peak at higher binding energy was observed in the range of 533.8–534.2 eV, which was attributed to the oxygen vacancy on the MMO surface [36,37]. Percentages of the peak area ascribed to the oxygen vacancy were calculated to be 23.7%, 14.6%, 14.2%, and 12.3% for LDH-DPU, MMO-DP, LDH-DP, and MMO-DPU, respectively. The number of the oxygen vacancies of MMO increased particularly for LDH-DPU, and the order of the number of oxygen vacancies was consistent with the catalytic activity order.
Furthermore, Ti 2p XPS was also investigated to discuss the oxygen vacancies of the TiOx domain. Ti 2p3/2 peaks of LDH-DP, MMO-DP, and MMO-DPU were observed at 459.4, 460.4, and 459.8 eV, respectively (Figure 4C), which are almost consistent with those of TiO2 [38,39]. In contrast, the Ti 2p3/2 peak of LDH-DPU shifted toward lower binding energies compared to the other three catalysts, at 458.9 eV. The lower energy shift suggests the presence of Ti3+ species, indicating an increase in the number of oxygen vacancies in the TiOx domain. Thus, LDH-DPU, which was rich in oxygen vacancies, exhibited the highest CO oxidation activity. The TGA diagram shows that the transformation of LDH to MMO shifted to a higher temperature in the presence of Au particles on the LDH. This leads to the suppression of MMO crystal growth, resulting in small MMOs with rich oxygen vacancies.
Au 4f XPS analysis was also measured. The Au 4f7/2 peaks of LDH-DP, LDH-DPU, MMO-DP, and MMO-DPU were observed at 83.4, 83.5, 83.3, and 83.8 eV, respectively. These values are consistent with those of the Au0 NPs (Figure S6).
Figure 5 depicts the relationships between the mean diameter of Au particles and the catalytic activity for CO oxidation based on the XRD, XPS, TEM, and CO oxidation reactions. To exhibit high activity, both an Au particle size smaller than about 2 nm and rich oxygen vacancies on MMOs were found to be key factors. As a result, LDH-DPU exhibited the highest activity.

2.6. Temperature-Programmed Reaction of CO

To further investigate the difference in the CO oxidation activity with respect to O2 activation, a temperature-programmed reaction of CO (CO-TPR) was performed. Figure 6 shows CO-TPR profiles after pretreatment in air at 250 °C. CO was fed into the sample cell, and the amount of CO2 generated was determined by mass spectrometry. LDH-DPU showed two CO2 desorption peaks at approximately 0 and 100 °C, whereas the other catalysts showed peaks at much higher temperatures. CO2 gradually formed at 20 °C for MMO-DP, whereas only at temperatures above 100 °C for MMO-DPU. The order of the CO2 desorption temperatures was consistent with the T1/2 values for CO oxidation.
Behm et al. proposed the Au-assisted Mars–van Krevelen mechanism for CO oxidation over Au/TiO2 [8]. In this mechanism, CO is adsorbed on Au, CO reacts with the surface lattice oxygen of TiO2, and the oxygen vacancy is formed. The lattice oxygen is replenished again by O2, and CO2 finally desorbs. This mechanism is well explained at ambient temperature or above. We reported that the Au-assisted Mars–van Krevelen mechanism for Au/ZnO-catalyzed CO oxidation changes at around −20 °C, and that the activation of weakly adsorbed O2 molecules is critically important for CO oxidation at low temperature [40]. According to these reports, it is likely that the lattice oxygen was used for CO oxidation above 30 °C, but that the CO2 desorption peak at 0 °C is related to weakly adsorbed O2 molecules at the oxygen vacancies. Thus, the CO-TPR results suggest that LDH-DPU possessed more active oxygen species on the MMO surface; O2 would be adsorbed on the abundant oxygen vacancies in the TiOx domain of MMOs; and/or the surface lattice oxygen of MMOs would be more labile owing to the disordered small crystallites.

2.7. CO Oxidation in Humid Air

We examined the dependence of water concentration on Au-catalyzed CO oxidation, because high catalytic activity in humid air at ambient temperature is crucial for catalytic application in air purification. We have reported that the catalytic activity of Au/TiO2 markedly dropped to about half of that in dry conditions, even in the presence of 1% H2O [15]. However, the catalytic activity of Au/Al2O3 and Au/SiO2 at room temperature was maintained or increased up to 4% H2O vapor (ca. 100% RH at 20 °C). As shown in Figure 7, the catalytic activity of LDH-DPU increased with increasing water concentration and was 1.5 times higher at 4 vol% H2O than that under dry conditions. Thus, LDH-DPU was found to be tolerant to high humidity and is a promising candidate for air purification catalysts.

3. Materials and Methods

3.1. Catalyst Preparation

3.1.1. Materials

Au/SiO2, Au/NiO, Au/TiO2, and Au/Fe2O3 (Au 1 wt%) were purchased from Haruta Gold Inc., Tokyo, Japan (https://www.haruta-gold.com/en/) (accessed on 20 July 2023). Aqueous solution of tetrachloroauric acid (0.497 g/L Au) was purchased from Tanaka Kikinzoku Kogyo K.K. and used as received. SiO2 (Q-10) was supplied from Fuji silysia Co., Ltd., Aichi, Japan. Nickel (II) nitrate hexahydrate (Ni(NO3)2·6H2O: 98%), super-dehydrated toluene (99.5+%), and sodium tetrahydroborate (NaBH4: >95.0%) were purchased from FUJIFILM Wako Pure Chemical Corporation. Titanium (IV) chloride (TiCl4: >99.0%) and urea (CO(NH2)2: >99.0%) were purchased from Kanto Chemical Co., Inc., Tokyo, Japan (https://www.kanto.co.jp/english/) (accessed on 20 July 2023). Other reagents were commercially available and used without further purification.

3.1.2. Ni-Ti LDH/SiO2

Ni-Ti LDH/SiO2 (Ni/Ti = 4) was prepared using hydrothermal synthesis method according to the literature [23,24] with modifications in the presence of SiO2. Ni(NO3)2 6H2O (6 mmol), TiCl4 (1.5 mmol), and urea (15 mmol) were dissolved in 30 mL of distilled water at room temperature, and the solution was stirred at room temperature for 2 h. SiO2 (1.2 g) was added to the solution, and the mixture was transferred to a 50 mL Teflon-lined autoclave and aged at 130 °C for 48 h. The resulting solid was centrifuged, washed with water three times, and dried in air at 80 °C to obtain Ni-Ti LDH/SiO2. The obtained Ni-Ti LDH/SiO2 was calcined in air at 500 °C for 2 h to obtain Ni-Ti MMO/SiO2. Bulk Ni-Ti LDH was prepared in the same manner in the absence of SiO2.

3.1.3. Au/Ni-Ti MMO/SiO2 (LDH-DP and MMO-DP)

Au/Ni-Ti MMO/SiO2 (LDH-DP and MMO-DPU) was prepared by DP. Typically, an aqueous solution of HAuCl4 (10 mM, 0.76 mL) dissolved in distilled water (6.8 mL) was heated to ca. 70 °C, and the pH of the solution was adjusted to 5 by adding 0.1 M NaOH aq. while stirring. A Ni-Ti MMO/SiO2 support was added, and the pH of the suspension was adjusted to 7 by adding 0.1 M NaOH aq. After aging at 70 °C for 1 h, the precipitate was collected by centrifugation, washed five times with water at 40 °C, and dried in air at 80 °C overnight. The resulting solid was calcined in air at 300 °C for 4 h to obtain MMO-DP. Au/Ni-Ti MMO/SiO2 (LDH-DP) was prepared in a similar manner using Ni-Ti LDH/SiO2 as a support, followed by calcination in air at 500 °C for 2 h to convert LDH into MMO, after depositing Au.

3.1.4. Au/Ni-Ti MMO/SiO2 (LDH-DPU and MMO-DPU)

Au/Ni-Ti MMO/SiO2 (LDH-DPU and MMO-DPU) was prepared by DP-Urea according to the literature [27] with minor modifications. For LDH-DPU, an aqueous solution of HAuCl4 (8.7 × 10−5 mol; 10 mM, 870 μL, Au 0.3 wt% initial loading) and 28% ammonia solution (1.2 mL) were dissolved in distilled water (200 mL), and the solution was stirred at room temperature for 4 h. Then, the Ni-Ti LDH/SiO2 support (525 mg) and urea (2.1 g, 35 mmol) were added into the solution. After stirring the suspension at 75 °C for 4 h, the suspension was left overnight at room temperature. The precipitate was collected by centrifugation, washed three times with water at room temperature, and dried in air at 80 °C overnight. The resulting solid (436 mg) was dispersed in anhydrous toluene (109 mL), and NaBH4 (54 mg) was added. The suspension was stirred at room temperature for 2 h. Then, EtOH (33 mL) was added, and the suspension was stirred at room temperature for an additional 6 h. After filtrating and washing with water and ethanol, the solid was dried in air at 80 °C overnight. Subsequently, the solid was calcined in an N2 flow (50 mL min−1) at 300, 400, and 500 °C for 2 h at a heating rate of 5 °C min−1, to convert LDH to MMO, resulting in LDH-DPU-300, LDH-DPU-400, and LDH-DPU, respectively. Au/Ni-Ti MMO/SiO2 (MMO-DPU) was also prepared by following a similar manner and using Ni-Ti MMO/SiO2 as the support but without calcination in N2 at 500 °C at the final step.

3.1.5. Au/bulk Ni-Ti MMO

Au/bulk Ni-Ti MMO was prepared by DP. The obtained bulk Ni-Ti LDH was converted to bulk Ni-Ti MMO by calcination at 500 °C for 2 h at a ramping rate of 5 °C min−1. Subsequently, Au was deposited on bulk Ni-Ti MMO by DP. An aqueous solution of HAuCl4 (25 mM, 0.30 mL) dissolved in distilled water (7.3 mL) was heated to 70 °C, and the pH of the solution was adjusted to 5 by adding 0.1 M NaOH aq. while stirring. The bulk Ni-Ti MMO was added, and the pH of the suspension was adjusted to 7 by adding 0.1 M NaOH aq. After aging at 70 °C for 1 h, the precipitate was collected by centrifugation, washed five times with water at 40 °C, and dried in air at 120 °C overnight. The resulting solid was calcined in air at 300 °C for 4 h to yield Au/bulk Ni-Ti MMO.

3.2. Characterization

XRD patterns were obtained using a Rigaku, MiniFlex with Cu Kα1 radiation (λ = 0.154 0562 nm). The scan speed and step scan were 5° min−1 at 0.02°, respectively. TGA was performed using a HITACHI STA7200. The samples were heated from room temperature to 900 °C at a ramping rate of 10 °C min−1 and maintained at 900 °C for 30 min. The actual Au loadings were estimated by ICP-AES using a SPECTRO, CIROS-120, and SHIMADZU, ICPE-9820. The size of the Au particles was estimated HAADF-STEM using a JEOL, ARM-200F NEOARM operating at 200 kV at Tokyo Metropolitan University and an FEI, Titan G2 operating at 300 kV at Hokkaido University. The Au particles were counted more than 150 particles to calculate the mean diameters except for LDH-DPU. For LDH-DPU, it was hard to observe Au particles, and 70 particles were counted. The electronic states of Au, Ni, and Ti were evaluated by XPS using a JEOL, JPS-9010MX with Mg Kα radiation. The C 1s peak at 284.6 eV was used for charge correction in the XPS spectra. The CO-TPR was performed on a MicrotracBEL, BELCAT II to investigate the oxygen activation ability of the catalysts. The catalyst sample was pretreated in a flow of 20 vol% O2 in He (30 mL min−1) at 250 °C for 1 h and cooled to −100 °C. Then, 0.5 vol% CO in He (30 mL min−1) was passed through the catalyst sample at a temperature range of −100–200 °C with a ramping rate of 10 °C min−1. The amount of CO2 generated was estimated by mass spectrometry using a MicrotracBEL, BELMASS.

3.3. CO Oxidation

The CO oxidation was performed in a continuous fixed-bed flow reactor. The catalyst sample (0.1 g) was placed in a U-shaped glass reactor and pre-treated in a flow of 20 vol% O2 in N2 (50 mL min−1) at 200 °C for 1 h. After cooling to room temperature, 1 vol% CO in air (33.3 mL min−1, SV 20,000 mL h−1 gcat−1) was passed through the catalyst bed while heating from room temperature to 300 °C. The CO conversion and CO2 yield were estimated by GC using an Agilent microGC. CO conversion was calculated using the following equation:
CO   conversion   % = CO in - CO out CO in × 100
The effect of water concentration on CO oxidation was evaluated using a MicrotracBEL, BELCAT II equipped with an Agilent microGC. The Au/Ni-Ti LDH/SiO2 catalyst (200 mg) was pre-treated in N2 (50 mL min−1) at 500 °C for 2 h. After the pretreatment, the catalyst was cooled to room temperature in a flow of N2 (50 mL min−1), and then 1 vol% CO in air containing H2O vapor (50 mL min−1) was fed into the sample cell with water vapor at 20 °C.

4. Conclusions

The ultrafine Ni-Ti LDH particles were highly dispersed on SiO2 and converted into small MMO crystallites. Au was deposited on Ni-Ti LDH/SiO2 and Ni-Ti MMO/SiO2 by DP and DPU, and LDHs were finally converted to MMOs. The Au particle size was affected by the preparation method and the support, revealing that the deposition of Au onto LDH by DPU was suitable. The abundant OH groups at the edge sites of LDHs contributed to stabilizing Au clusters. Calcination of LDH/SiO2 after depositing Au by DPU affected the transformation of LDH into MMO, resulting in rich oxygen vacancies in the TiOx domain. Thus, LDH-DPU exhibited the highest catalytic activity for CO oxidation among the Au/Ni-Ti MMO/SiO2 catalysts and commercially available Au catalysts, despite low Au loading (0.3 wt%). Furthermore, the dispersion of ultrafine Ni-Ti MMO on SiO2 reduced the amount of rare Ni species compared with conventional Au/NiO. In addition, LDH-DPU was active for CO oxidation at room temperature in humid air. These findings will pave the way for the development of highly efficient Au catalysts for air purification.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/catal13081155/s1, Figure S1: TG diagrams of bulk Ni-Ti LDH, Au/Ni-Ti LDH/SiO2, Ni-Ti LDH/SiO2, and SiO2; Figure S2: XRD patterns of Ni-Ti LDH/SiO2 calcined at different temperatures with references, NiO, TiO2, and NiTiO3; Figure S3: SEM-EDS elemental mappings of Ni-Ti LDH/SiO2. (a) SEM, (b) Si, (c) O, (d) Ni, and (e) Ti; Figure S4: TEM image and size distribution of Au particles of Au/bulk Ni-Ti MMO; Figure S5: TEM image and size distribution of Au particles of Au/Ni-Ti LDH/SiO2 (Ni/Ti = 2/1); Figure S6: Au 4f XPS spectra of Au/Ni-Ti MMO/SiO2: (a) LDH-DP, (b) LDH-DPU, (c) MMO-DP, and (d) MMO-DPU.

Author Contributions

Conceptualization, T.I.; validation, T.M. and T.I.; investigation, A.T., A.N. and N.S.; data curation, A.T. and A.N.; writing—original draft preparation, A.T. and T. I.; writing—review and editing, T.M., T.S., S.T. and T.I.; visualization, A.T.; supervision, T.I.; project administration, T.I.; funding acquisition, T.I. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by JSPS and NSFC under the Joint Research Program (JRP with NSFC, Grant Numbers JPJSJRP20191804, MEXT Grant-in-Aid for JSPS KAKENHI (Grant Numbers 19 K05152 and 23H02005), and Izumi Science and Technology Foundation. The research was supported by the Joint Usage/Research Center for Catalysis (Proposal #22DS0077 and 23DS0219) and the JST establishment of university fellowships towards the creation of science technology innovation (Grant Number JPMJFS2139).

Data Availability Statement

All relevant data presented in this paper. Catalyst samples are available or not available from the authors.

Acknowledgments

We thank Yuki Ono at Tokyo Metropolitan University and Ryo Oota at Hokkaido University for helping with TEM observations.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Haruta, M.; Kobayashi, T.; Sano, H.; Yamada, N. Novel Gold Catalysts for the Oxidation of Carbon Monoxide at a Temperature Far Below 0 °C. Chem. Lett. 1987, 16, 405–408. [Google Scholar] [CrossRef] [Green Version]
  2. Ishida, T.; Murayama, T.; Taketoshi, A.; Haruta, M. Importance of Size and Contact Structure of Gold Nanoparticles for the Genesis of Unique Catalytic Processes. Chem. Rev. 2019, 120, 464–525. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  3. Okumura, M.; Fujitani, T.; Huang, J.; Ishida, T. A Career in Catalysis: Masatake Haruta. ACS Catal. 2015, 5, 4699–4707. [Google Scholar] [CrossRef]
  4. Ishida, T.; Koga, H.; Okumura, M.; Haruta, M. Advances in Gold Catalysis and Understanding the Catalytic Mechanism. Chem. Rec. 2016, 16, 2278–2293. [Google Scholar] [CrossRef] [PubMed]
  5. Min, B.K.; Friend, C.M. Heterogeneous Gold-Based Catalysis for Green Chemistry: Low-Temperature CO Oxidation and Propene Oxidation. Chem. Rev. 2007, 107, 2709–2724. [Google Scholar] [CrossRef]
  6. Fujitani, T.; Nakamura, I. Mechanism and Active Sites of the Oxidation of CO over Au/TiO2. Angew. Chem. Int. Ed. 2011, 50, 10144–10147. [Google Scholar] [CrossRef]
  7. Widmann, D.; Behm, R.J. Activation of Molecular Oxygen and the Nature of the Active Oxygen Species for Co Oxidation on Oxide Supported Au Catalysts. Acc. Chem. Res. 2014, 47, 740–749. [Google Scholar] [CrossRef]
  8. Schlexer, P.; Widmann, D.; Behm, R.J.; Pacchioni, G. CO Oxidation on a Au/TiO2 Nanoparticle Catalyst via the Au-Assisted Mars–van Krevelen Mechanism. ACS Catal. 2018, 8, 6513–6525. [Google Scholar] [CrossRef]
  9. Qiao, B.; Liang, J.X.; Wang, A.; Liu, J.; Zhang, T. Single Atom Gold Catalysts for Low-Temperature CO Oxidation. Chin. J. Catal. 2016, 37, 1580–1586. [Google Scholar] [CrossRef]
  10. Qiao, B.; Liu, J.; Wang, Y.G.; Lin, Q.; Liu, X.; Wang, A.; Li, J.; Zhang, T.; Liu, J. Highly Efficient Catalysis of Preferential Oxidation of CO in H2-Rich Stream by Gold Single-Atom Catalysts. ACS Catal. 2015, 5, 6249–6254. [Google Scholar] [CrossRef]
  11. Qiao, B.; Lin, J.; Wang, A.; Chen, Y.; Zhang, T.; Liu, J. Highly Active Au1/Co3O4 Single-Atom Catalyst for CO Oxidation at Room Temperature. Chin. J. Catal. 2015, 36, 1505–1511. [Google Scholar] [CrossRef]
  12. Qiao, B.; Liang, J.X.; Wang, A.; Xu, C.Q.; Li, J.; Zhang, T.; Liu, J.J. Ultrastable Single-Atom Gold Catalysts with Strong Covalent Metal-Support Interaction (CMSI). Nano Res. 2015, 8, 2913–2924. [Google Scholar] [CrossRef]
  13. Mochizuki, C.; Inomata, Y.; Yasumura, S.; Lin, M.; Taketoshi, A.; Honma, T.; Sakaguchi, N.; Haruta, M.; Shimizu, K.; Ishida, T.; et al. Defective NiO as a Stabilizer for Au Single-Atom Catalysts. ACS Catal. 2022, 12, 6149–6158. [Google Scholar] [CrossRef]
  14. Pennington, A.M.; Pitman, C.L.; Desario, P.A.; Brintlinger, T.H.; Jeon, S.; Balow, R.B.; Pietron, J.J.; Stroud, R.M.; Rolison, D.R. Photocatalytic CO Oxidation over Nanoparticulate Au-Modifi Ed TiO2 Aerogels: The Importance of Size and Intimacy. ACS Catal. 2020, 10, 14834–14846. [Google Scholar] [CrossRef]
  15. Dien, L.X.; Ishida, T.; Taketoshi, A.; Truong, D.Q.; Dang Chinh, H.; Honma, T.; Murayama, T.; Haruta, M. Supported Gold Cluster Catalysts Prepared by Solid Grinding Using a Non-Volatile Organogold Complex for Low-Temperature CO Oxidation and the Effect of Potassium on Gold Particle Size. Appl. Catal. B Environ. 2019, 241, 539–547. [Google Scholar] [CrossRef]
  16. Daté, M.; Okumura, M.; Tsubota, S.; Haruta, M. Vital Role of Moisture in the Catalytic Activity of Supported Gold Nanoparticles. Angew. Chem. Int. Ed. 2004, 43, 2129–2132. [Google Scholar] [CrossRef] [PubMed]
  17. Saavedra, J.; Pursell, C.J.; Chandler, B.D. CO Oxidation Kinetics over Au/TiO2 and Au/Al2O3 Catalysts: Evidence for a Common Water-Assisted Mechanism. J. Am. Chem. Soc. 2018, 140, 3712–3723. [Google Scholar] [CrossRef]
  18. Xu, M.; Wei, M. Layered Double Hydroxide-Based Catalysts: Recent Advances in Preparation, Structure, and Applications. Adv. Funct. Mater. 2018, 28, 1802943. [Google Scholar] [CrossRef]
  19. Zhang, F.; Zhao, X.; Feng, C.; Li, B.; Chen, T.; Lu, W.; Lei, X.; Xu, S. Crystal-Face-Selective Supporting of Gold Nanoparticles on Layered Double Hydroxide as Efficient Catalyst for Epoxidation of Styrene. ACS Catal. 2011, 1, 232–237. [Google Scholar] [CrossRef]
  20. Zhao, Y.; Li, B.; Wang, Q.; Gao, W.; Wang, C.J.; Wei, M.; Evans, D.G.; Duan, X.; O’Hare, D. NiTi-Layered Double Hydroxides Nanosheets as Efficient Photocatalysts for Oxygen Evolution from Water Using Visible Light. Chem. Sci. 2014, 5, 951–958. [Google Scholar] [CrossRef]
  21. Zhao, Y.; Jia, X.; Chen, G.; Shang, L.; Waterhouse, I.N.; Wu, L.; Tung, C.; Hare, D.O.; Zhang, T. Ultrafine NiO Nanosheets Stabilized by TiO2 from Monolayer NiTi-LDH Precursors: An Active Water Oxidation Electrocatalyst. J. Am. Chem. Soc. 2016, 138, 6517–6524. [Google Scholar] [CrossRef] [PubMed]
  22. Zhao, Y.; Chen, G.; Bian, T.; Zhou, C.; Waterhouse, G.I.N.; Wu, L.; Tung, C.; Smith, L.J.; Hare, D.O.; Zhang, T. Defect-Rich Ultrathin ZnAl-Layered Double Hydroxide Nanosheets for Efficient Photoreduction of CO2 to CO with Water. Adv. Mater. 2015, 27, 7824–7831. [Google Scholar] [CrossRef] [PubMed]
  23. Ge, X.; Gu, C.; Yin, Z.; Wang, X.; Tu, J.; Li, J. Periodic Stacking of 2D Charged Sheets: Self-Assembled Superlattice of Ni–Al Layered Double Hydroxide (LDH) and Reduced Graphene Oxide. Nano Energy 2016, 20, 185–193. [Google Scholar] [CrossRef] [Green Version]
  24. Wang, H.; Fan, G.; Zheng, C.; Xiang, X.; Li, F. Facile Sodium Alginate Assisted Assembly of Ni-Al Layered Double Hydroxide Nanostructures. Ind. Eng. Chem. Res. 2010, 49, 2759–2767. [Google Scholar] [CrossRef]
  25. Cells, D.S.; Qu, Y.; Zhou, W.; Miao, X.; Li, Y.; Jiang, L.; Pan, K. A New Layered Photocathode with Porous NiO Nanosheets: An Effective Candidate for p-Type Dye-Sensitized Solar Cells. Chem. Asian J. 2013, 8, 3085–3090. [Google Scholar] [CrossRef]
  26. Rathee, G.; Kohli, S.; Panchal, S.; Singh, N.; Awasthi, A.; Singh, S.; Singh, A.; Hooda, S.; Chandra, R. Fabrication of a Gold-Supported NiAlTi-Layered Double Hydroxide Nanocatalyst for Organic Transformations. ACS Omega 2020, 5, 23967–23974. [Google Scholar] [CrossRef]
  27. Wang, L.; Zhang, J.; Zhu, Y.; Xu, S.; Wang, C.; Bian, C.; Meng, X.; Xiao, F.S. Strong Metal-Support Interactions Achieved by Hydroxide-to-Oxide Support Transformation for Preparation of Sinter-Resistant Gold Nanoparticle Catalysts. ACS Catal. 2017, 7, 7461–7465. [Google Scholar] [CrossRef]
  28. Xu, X.; Fu, Q.; Guo, X.; Bao, X. A Highly Active “NiO-on-Au” Surface Architecture for CO Oxidation. ACS Catal. 2013, 3, 1810–1818. [Google Scholar] [CrossRef]
  29. Carabineiro, S.A.C.; Bogdanchikova, N.; Avalos-borja, M.; Pestryakov, A.; Tavares, P.B.; Figueiredo, J.L. Gold Supported on Metal Oxides for Carbon Monoxide Oxidation. Nano Res. 2011, 4, 180–193. [Google Scholar] [CrossRef] [Green Version]
  30. Li, X.; Patil, K.; Agarwal, A.; Babar, P.; Jang, J.S.; Chen, X.; Yoo, Y.T.; Kim, J.H. Ni(OH)2 Coated CoMn-Layered Double Hydroxide Nanowires as Efficient Water Oxidation Electrocatalysts. New J. Chem. 2022, 46, 2044–2052. [Google Scholar] [CrossRef]
  31. Xu, J.; Tang, M.; Hu, Z.; Hu, X.; Zhou, T.; Song, K.; Wu, J.; Cheng, J. Standing and Lying Ni(OH)2 Nanosheets on Multilayer Graphene for High-Performance Supercapacitors. Nanomaterials 2021, 11, 1662. [Google Scholar] [CrossRef]
  32. Liu, G.; Ouyang, X.; Wei, X.; Bao, W.; Feng, X.; Zhang, J. Coupling Interface Construction of Ni(OH)2/MoS2 Composite Electrode for Efficient Alkaline Oxygen Evolution Reaction. Catalysts 2022, 12, 966. [Google Scholar] [CrossRef]
  33. Liu, A.; Liu, G.; Zhu, H.; Shin, B.; Fortunato, E. Hole Mobility Modulation of Solution-Processed Nickel Oxide Thin-Film Transistor Based on High-k Dielectric. Appl. Phys. Lett. 2016, 108, 233506. [Google Scholar] [CrossRef]
  34. Chen, Y.S.; Kang, J.F.; Chen, B.; Gao, B.; Liu, L.F.; Liu, X.Y.; Wang, Y.Y.; Wu, L.; Yu, H.Y.; Wang, J.Y.; et al. Microscopic Mechanism for Unipolar Resistive Switching Behaviour of Nickel Oxides. J. Phys. D Appl. Phys. 2012, 45, 065303. [Google Scholar] [CrossRef]
  35. Shih, Y.; Huang, Y.; Huang, C.P. Electrocatalytic Ammonia Oxidation over a Nickel Foam Electrode: Role of Ni(OH)2(s)-NiOOH(s) Nanocatalysts. Electrochim. Acta 2018, 263, 261–271. [Google Scholar] [CrossRef]
  36. Wang, Z.; Lin, R.; Huo, Y.; Li, H.; Wang, L. Formation, Detection, and Function of Oxygen Vacancy in Metal Oxides for Solar Energy Conversion. Adv. Funct. Mater. 2022, 32, 2109503. [Google Scholar] [CrossRef]
  37. Ali, H.; Vandevyvere, T.; Lauwaert, J.; Kumar, S.; Saravanamurugan, S.; Thybaut, J.W. Impact of Oxygen Vacancies in Ni Supported Mixed Oxide Catalysts on Anisole Hydrodeoxygenation. Catal. Commun. 2022, 164, 106436. [Google Scholar] [CrossRef]
  38. Wang, S.; Cai, J.; Mao, J.; Li, S.; Shen, J.; Gao, S. Defective Black Ti3+ Self-Doped TiO2 and Reduced Graphene Oxide Composite Nanoparticles for Boosting Visible-Light Driven Photocatalytic and Photoelectrochemical Activity. Appl. Surf. Sci. 2019, 467–468, 45–55. [Google Scholar] [CrossRef]
  39. Nawaz, R.; Kait, C.F.; Chia, H.Y.; Isa, M.H.; Huei, L.W.; Sahrin, N.T. Synthesis of Black-TiO2 and Manganese-Doped TiO2 Nanoparticles and Their Comparative Performance Evaluation for Photocatalytic Removal of Phenolic Compounds from Agro-Industrial Effluent. J. Nanopart. Res. 2021, 23, 263. [Google Scholar] [CrossRef]
  40. Fujita, T.; Ishida, T.; Shibamoto, K.; Honma, T.; Ohashi, H.; Murayama, T.; Haruta, M. CO Oxidation over Au/ZnO: Unprecedented Change of the Reaction Mechanism at Low Temperature Caused by a Different O2 Activation Process. ACS Catal. 2019, 9, 8364–8372. [Google Scholar] [CrossRef]
Figure 1. (a) XRD patterns of bulk Ni-Ti LDH, Ni-Ti LDH/SiO2, and Ni-Ti MMO/SiO2. (b) XRD patterns of Au/bulk Ni-Ti MMO and Au/Ni-Ti MMO/SiO2 (LDH-DP, LDH-DPU, MMO-DP, and MMO-DPU).
Figure 1. (a) XRD patterns of bulk Ni-Ti LDH, Ni-Ti LDH/SiO2, and Ni-Ti MMO/SiO2. (b) XRD patterns of Au/bulk Ni-Ti MMO and Au/Ni-Ti MMO/SiO2 (LDH-DP, LDH-DPU, MMO-DP, and MMO-DPU).
Catalysts 13 01155 g001
Scheme 1. Schematic representation for preparation of four kinds of Au/Ni-Ti MMO/SiO2.
Scheme 1. Schematic representation for preparation of four kinds of Au/Ni-Ti MMO/SiO2.
Catalysts 13 01155 sch001
Figure 2. TEM images and size distributions of Au/Ni-Ti MMO/SiO2. (a) LDH-DP, (b) LDH-DPU, (c) MMO-DP, and (d) MMO-DPU.
Figure 2. TEM images and size distributions of Au/Ni-Ti MMO/SiO2. (a) LDH-DP, (b) LDH-DPU, (c) MMO-DP, and (d) MMO-DPU.
Catalysts 13 01155 g002
Figure 3. Conversion curves for Au-catalyzed CO oxidation. : LDH-DP, : LDH-DPU, : MMO-DP, ●: MMO-DPU, : Au/TiO2, : Au/NiO, : Au/SiO2. Reaction conditions: 0.1 g of catalyst, 1 vol% CO in air (33.3 mL min−1), and space velocity (SV) of 20,000 mL h−1 gcat−1.
Figure 3. Conversion curves for Au-catalyzed CO oxidation. : LDH-DP, : LDH-DPU, : MMO-DP, ●: MMO-DPU, : Au/TiO2, : Au/NiO, : Au/SiO2. Reaction conditions: 0.1 g of catalyst, 1 vol% CO in air (33.3 mL min−1), and space velocity (SV) of 20,000 mL h−1 gcat−1.
Catalysts 13 01155 g003
Figure 4. (A) Ni 2p, (B) O 1s, and (C) Ti 2p XPS spectra of Au/Ni-Ti MMO/SiO2: (a) LDH-DP, (b) LDH-DPU, (c) MMO-DP, and (d) MMO-DPU.
Figure 4. (A) Ni 2p, (B) O 1s, and (C) Ti 2p XPS spectra of Au/Ni-Ti MMO/SiO2: (a) LDH-DP, (b) LDH-DPU, (c) MMO-DP, and (d) MMO-DPU.
Catalysts 13 01155 g004
Figure 5. Relationships between Au particle size of Au/Ni-Ti MMO/SiO2 and T1/2 for CO oxidation.
Figure 5. Relationships between Au particle size of Au/Ni-Ti MMO/SiO2 and T1/2 for CO oxidation.
Catalysts 13 01155 g005
Figure 6. CO-TPR profiles of Au/Ni-Ti MMO/SiO2 (LDH-DP, LDH-DPU, MMO-DP, and MMO-DPU). Pretreatment conditions: catalyst (0.1 g), 20 vol% O2 in He (30 mL/min−1), 250 °C, 1 h. Measurement conditions: 0.5 vol% CO in He (30 mL/min−1), 10 °C/min−1.
Figure 6. CO-TPR profiles of Au/Ni-Ti MMO/SiO2 (LDH-DP, LDH-DPU, MMO-DP, and MMO-DPU). Pretreatment conditions: catalyst (0.1 g), 20 vol% O2 in He (30 mL/min−1), 250 °C, 1 h. Measurement conditions: 0.5 vol% CO in He (30 mL/min−1), 10 °C/min−1.
Catalysts 13 01155 g006
Figure 7. Dependence of water concentration on CO oxidation over LDH-DPU at 20 °C. Reaction conditions: catalyst (1.0 wt% Au loading, LDH-DPU, 200 mg), 1 vol% CO in air. H2O vapor was added, and the total gas flow was set to 50 mL min−1. The LDH-DPU was pretreated in N2 (50 mL min−1) at 500 °C for 2 h, cooled to room temperature in a flow of N2 (50 mL min−1). Subsequently, 1 vol% CO in air containing water vapor (50 mL min−1) was passed through the sample cell.
Figure 7. Dependence of water concentration on CO oxidation over LDH-DPU at 20 °C. Reaction conditions: catalyst (1.0 wt% Au loading, LDH-DPU, 200 mg), 1 vol% CO in air. H2O vapor was added, and the total gas flow was set to 50 mL min−1. The LDH-DPU was pretreated in N2 (50 mL min−1) at 500 °C for 2 h, cooled to room temperature in a flow of N2 (50 mL min−1). Subsequently, 1 vol% CO in air containing water vapor (50 mL min−1) was passed through the sample cell.
Catalysts 13 01155 g007
Table 1. Physicochemical properties and catalytic activity of Au/Ni-Ti MMO/SiO2.
Table 1. Physicochemical properties and catalytic activity of Au/Ni-Ti MMO/SiO2.
EntryCatalystLoading/wt% 1Au Size 2/nmT1/23/°C
AuNiTi
1LDH-DP0.24152.04.0 ± 1.5115
2LDH-DPU0.28152.62.3 ± 2.010
3MMO-DP0.15152.91.7 ± 0.538
4MMO-DPU0.3152.03.5 ± 1.8191
5Au/Ni-Ti LDH/SiO20.28152.63.5 ± 1.2182
6LDH-DPU-3000.28152.687
7LDH-DPU-4000.28152.611
8Au/Ni-Ti MMO/SiO2 (Ni/Ti = 2/1)0.25322.06.0 ± 2.1 465
9Au/bulk Ni-Ti MMO0.233.2 ± 1.324
10Au/TiO20.964.1 ± 2.210–20
11Au/NiO0.93557
12Au/SiO21.006.6 ± 2.7>300
13Au/Fe2O30.811.8 ± 0.736
1 Estimated by ICP-AES. 2 Estimated by HAADF-STEM. 3 The temperature at 50% CO conversion. CO oxidation conditions: 0.1 g of catalyst, 1 vol% CO in air (33.3 mL min−1), and space velocity (SV) of 20,000 mL h−1 gcat−1. 4 The mean diameters of Au particles were estimated by TEM before calcination. 5 Single Au atoms were mainly deposited on NiO [13].
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Takahashi, A.; Nakayama, A.; Murayama, T.; Sakaguchi, N.; Shimada, T.; Takagi, S.; Ishida, T. Au Clusters Supported on Defect-Rich Ni-Ti Oxides Derived from Ultrafine Layered Double Hydroxides (LDHs) for CO Oxidation at Ambient Temperature. Catalysts 2023, 13, 1155. https://doi.org/10.3390/catal13081155

AMA Style

Takahashi A, Nakayama A, Murayama T, Sakaguchi N, Shimada T, Takagi S, Ishida T. Au Clusters Supported on Defect-Rich Ni-Ti Oxides Derived from Ultrafine Layered Double Hydroxides (LDHs) for CO Oxidation at Ambient Temperature. Catalysts. 2023; 13(8):1155. https://doi.org/10.3390/catal13081155

Chicago/Turabian Style

Takahashi, Ayu, Akihiro Nakayama, Toru Murayama, Norihito Sakaguchi, Tetsuya Shimada, Shinsuke Takagi, and Tamao Ishida. 2023. "Au Clusters Supported on Defect-Rich Ni-Ti Oxides Derived from Ultrafine Layered Double Hydroxides (LDHs) for CO Oxidation at Ambient Temperature" Catalysts 13, no. 8: 1155. https://doi.org/10.3390/catal13081155

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop