In this work, novel conducting graft copolymers: DodecSil (Poly(dimetylesiloksane)-co-[poly(metylhydrosiloksane)-graft-2-winyl-poly(3-heksylthiophene)]-co-[poly(dimetylsiloksane)-graft-dodec-1-en]) and PEGSil (Poly(dimetylsiloksan)-co-[poli(metylohydrosiloksane)-graft-2-winyl-poly(3-heksylthiophene)]-co-[poly(dimetylsiloksane)-graft-metakrylane ethere metylene poly(etylene glicole)]) were tested as gas receptor thin films in resistance gas sensors. For both graft copolymers, two variants were tested: fractions with shorter (hexane fraction-H) and longer (chloroform fraction-CH) side-chains of P3HT. Sensors were obtained using the spin coating method on interdigital transducers (Au on Si/SiO2). Sensor responses to NO2 (1–20 ppm) were tested and compared. Experiments were carried out in the dry nitrogen atmosphere at different operating temperatures (room temperature (RT), 50 °C and 100 °C). Results showed that both copolymers with PEG side-chines had higher response to NO2 than materials with dodec-1-en side-chains. What is more, results showed that in both cases hexane fractions are more sensitive than chloroform fractions. Measured responses (Ra/Rg·100%) to 1 ppm of NO2 at RT are: 250% DodecSIL-CH, 460% DodecSIL-H, 600% PEGSil-Ch and 1330% PEGSil-H. Similarly, in other operating temperatures, PEGSil film responses were higher than DodecSil ones, and H fractions were more sensitive than CH fractions. This showed that graft copolymers of P3HT have a huge potential for low temperature NO2 sensing, and the proper choice of other side-chains can improve their sensing properties.
Conflicts of Interest
The authors declare no conflict of interest.
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations. |
© 2017 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (https://creativecommons.org/licenses/by/4.0/).