1. Introduction
Welded metal bellows are elastic elements that are widely used in mechanical seals. Stress relaxation is the main failure mode of welded metal bellows, which often occurs after long-term use [
1,
2]. Due to stress relaxation, the failure of the elastic properties of welded metal bellows affects the normal operation of the entire system, so the study of their reliability is important for diverse engineering applications.
At present, there are few studies on the stress relaxation of welded metal bellows. Studying the stress relaxation of springs helps us to evaluate the stress relaxation of welded metal bellows. In the recent past, several studies have been reported by researchers that investigate the stress relaxation and associated failure of metal bellows. For instance, Simon P.A. et al. [
3] investigated the stress relaxation performance of the spiral springs of three different materials and evaluated that the stress relaxation of springs at 600 to 700 °C drops at a rate of 1–3 grades faster than predicted by the compression creep data under the action of an equivalent tensile load. Jia et al. [
4] studied the AISI 304 stainless steel spring stress relaxation process and the change of microstructure under different temperatures and loading conditions. The research results showed that at a low temperature and under a light load, the dismount austenite phase transformation stress relaxation is the main cause of the formation. Del [
5] designed a fatigue testing machine to study springs under different conditions and determine the S–N curves. Through the testing machine, different parameters were investigated, for example, the influence of the cyclic load on the stress elimination of compression springs, the residual stress on the internal and external coils of springs, and the effect of heat treatment on stress relaxation.
The stress relaxation test is performed with specialized equipment and under tight environmental conditions, which make this test costly. At present, the use of numerical simulation methods to explore the law of stress relaxation of materials is receiving increased attention.
Xin [
6] conducted stress relaxation tests on spiral compression springs at 90 °C, 110 °C, 130 °C, and 150 °C for 30 h. The creep constitutive relations were established and modified according to the test data. The constitutive relations and material parameters of the spiral compression springs were substituted into finite elements for the stress relaxation analysis. The results showed that the finite element model can effectively predict the whole relaxation process, and that the spring relaxation process occurs from inside to outside. Schedin [
7] used finite element methods to simulate the stress relaxation behavior of joints. The study used stress relaxation test data by applying a power-law form of creep expression and simulated stress relaxation behavior by setting up the stress fields linearly, along with sheet thickness. The simulation results agree well with the experimental results.
It is important to highlight that the reliability analysis of bellows using stress relaxation data is still deficient. The existing reliability analysis methods for non-welded metal bellows under failure conditions can provide a certain reference for stress relaxation studies. For example, Zeng [
8] used the ABAQUS finite element software to perform a numerical simulation of EPMB metal bellows. In the study, a metal corrugated pipe was studied to predict the limit bending stress distribution. In addition, the bending test of the metal corrugated pipe, repeated bending fatigue test, and the influence of the structural parameters of the waveform were verified. Cao et al. [
9] obtained the local strain amplitude value of U-shaped bellows under specified failure loads through an ANSYS finite element analysis. The study predicted the life of bellows using the relationship curve between strain and life, and the mean and standard deviations of the logarithm fatigue life of bellows were obtained by using the first-order Taylor expansion formula. Xie et al. [
10] defined the limit state function by applying the stress intensity interference theory to determine the statistical randomness that commonly exists in different parameters, such as the size, material, and load of metal bellows. The study used the PDS module in ANSYS to analyze the strength reliability of bellows through the Monte Carlo probability sampling method.
According to the above literature, most bellow reliability studies today are analyzed from the aspects of fatigue life and structural strength, and the finite element method is used unilaterally to analyze and solve the reliability. The results of such studies are not supported by test data, and the accuracy is poor. In view of the above problems, based on the literature discussed above, this paper studied the reliability of welded metal bellows by experimental testing and numerical simulation. A stress relaxation test rig for welded metal bellows was built to simulate the environment of the mechanical seal of welded metal bellows under a high-temperature medium, and the residual elastic data of the welded metal bellows under different compression amounts were obtained at 250 °C medium environments. According to the test data, the creep parameters needed for the finite element analysis of welded metal bellows were obtained. Finally, the reliability of the welded metal bellows was solved using the Six Sigma analysis module. The Six Sigma method can analyze various material parameters, structural parameters, and working conditions of welded metal bellows, and the obtained reliability is more convincing.
3. Concrete Case Calculation
The test material was S-type welded metal bellows. The initial displacement loads of 10 mm, 12 mm, 14 mm, 16 mm, and 18 mm were applied to the welded metal bellows at 250 degrees Celsius. The initial elastic force measured under five different compression loads is shown in
Figure 4, and the change of elastic force with loading time is shown in
Figure 5.
According to the stress relaxation theory, stress relaxation has two stages. In the first stage of stress relaxation, the elastic force decreases rapidly over time. In the second stage, the relaxation rate becomes slow and has a steady trend. According to
Figure 5, the elastic force of welded metal bellows decreases rapidly in the first 2 h and then slows down.
The stress relaxation curve used in this paper is similar to the generalized Aileen model [
15]. By fitting the generalized Aileen formula
with the test data, where
y0 represents the limit value of the function and
k and
t are constants, the regression equation of the stress relaxation curve under the generalized Aileen model can be obtained.
Table 1 lists the important parameters.
The load loss is the difference between the current value of the spring force and the initial spring force. From
Table 1, it can be seen that as the initial compression displacement load of welded metal bellows increases, the load variation of welded metal bellows also increases. By comparing the load loss rate with the initial load, it can be seen that as the initial load increases, the load loss rate also increases.
Figure 6 shows this relationship.
According to the earlier research studies, when the stress relaxation curve meets the generalized Eiling model,
and
exhibit linear relationships.
Figure 7,
Figure 8 and
Figure 9 show these relationships.
The solid line in
Figure 9 shows the actual value and the dotted line is a theoretical value line. From
Figure 7,
Figure 8 and
Figure 9, it can be concluded that
and
exhibit linear relationships, which are verified by experience [
16]. In this paper, the stress relaxation curves obtained from the stress relaxation test bench of the welded metal bellows are shown to be correct, and the data are available.
According to the study of creep or stress relaxation, the relation between creep strain, stress, time, and temperature can be well expressed by the creep constitutive equation composed of creep constants. The creep constants of the welded metal bellows are shown in
Table 2. These are used for stress relaxation finite element analysis based on the test data and the derivation of the elastic-loss formulas of the two kinds of welded metal bellows.
As shown in
Table 2, the values of creep constants
A,
m, and
n are different under different compression loads. The above parameters
A,
m, and
n satisfy the aging theory, and the general formula of the aging theory is:
According to the creep constant and the general formula proposed by Chen, this paper adopts time hardening [
17] in the creep analysis module to conduct the stress relaxation simulation analysis of welded metal bellows. The time hardening formula is
. The finite element simulation steps for the stress relaxation of welded metal bellows are explained below.
- (1)
Model development
The 3D Solidworks model of the welded metal bellows [
18] is shown in
Figure 10.
- (2)
Material and physical parameters
According to the creep model, the basic mechanical properties and physical parameters of 316 L steel at 250 °C are presented in
Table 3.
- (3)
Meshing and boundary condition setting
For the welded metal bellows, a sweep scanning grid division was adopted for discretization. The meshing results are shown in
Figure 11a, with a total of 20,457 nodes and 31,968 elements.
- (4)
Postprocessing
The loading conditions of bellows’ boundary conditions are shown in
Figure 11b. The solution is divided into two steps. The first step is used to define the initial conditions of stress relaxation, i.e., the application of load on the part, short time setting, and running the model without the creep effect; the second step is the stress relaxation stage, in which the creep effect is turned on and all boundary conditions are kept stable. The relaxation time is set as 16 h.
Table 4 shows the second step length settings.
According to the stress relaxation simulation process, projectile loss curves under the respective compression loads at 250 °C were obtained, which are shown in
Figure 12. This figure also gives a comparison between the simulation curve and the test curve.
Through the comparison of the elastic loss curves, it can be observed that the test load relaxation curve has a high degree of coincidence with the welding machine metal bellows simulation curve, and the error between the two is insignificant, i.e., within the allowable error range. Therefore, the stress relaxation simulation of welded metal bellows can accurately simulate the relaxation characteristics of welded metal bellows.
According to the published literature [
19], it can be concluded that the minimum elastic force of welded metal bellows is 545 N, and finite element analysis of the stress relaxation is required before using the Six Sigma analysis module. The reliability of welded metal bellows studied in this paper is the reliability of A at a compression load of 600 N considering a running time of 8000 h. A set of creep parameters A, m, and n values are selected, and the elastic change diagram is shown in
Figure 13.
In the process of manufacturing welded metal bellows, creep constant changes occurred due to error in the manufacturing process or differences in the material attributes. According to the fitting of the creep constant, the creep constant changes that are greater than the value of
A can be evaluated. Considering this, this article used the
A ×
m displacement value matrix and the compression loading as the design parameters by taking into account the normal distribution law. The 8000 h of the residual elastic force bellows is taken as the objective function. The mean and standard deviation value of the
A ×
m matrix, the compressive displacement load, and the upper and lower terms caused by them are presented in
Table 5, and their distribution is shown in
Figure 14 and
Figure 15.
According to
Table 4, the average value corresponding to the compression displacement load is converted to a pressure load of 600 N, and the upper and lower values are converted to a pressure load of 605 N and 595 N, respectively.
The probability density function and cumulative distribution of the 8000 h residual load are shown in
Figure 16 and
Figure 17.
The horizontal coordinates of the above probability density diagram and the cumulative distribution diagram are half of the total residual elasticity, and they show a negative trend due to the directivity of the software simulation. According to
Figure 15 and
Figure 16, after 8000 h of service time, the probability of residual elasticity was found to be 0.997 when the force was greater than 545 N. The obtained result is consistent with the published data of other researchers. For instance, Zhou [
20] used the Monte Carlo method to solve the reliability of each part in the mechanical seal, and the reliability of elastic elements in the mechanical seal was found to be 0.99. Thus, the results presented in this paper demonstrate the accuracy of the data. They meet the requirements of a mechanical seal system, and the reliability obtained in this paper is acceptable for general mechanical sealing systems.
The conventional method of calculating reliability usually requires several test samples. Based on the short-time test data, the reliability calculation of welded metal bellows is evaluated using simulation software. Compared with other reliability methods, this method requires less test sample data, and the variables are not limited to the working conditions of welded metal bellows. Moreover, this method can analyze all kinds of material and structural parameters of welded metal bellows, and the obtained reliability is convincing.