Next Article in Journal
Shape-Controlled Crystal Growth of Y3Al5O12:Ce Single Crystals with Application of Micro-Pulling-Down Method and Mo Crucibles, and Their Scintillation Properties
Previous Article in Journal
Comparison of Brillouin Light Scattering and Density of States in a Supported Layer: Analytical and Experimental Study
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Crystals
Volume 12
Issue 9
10.3390/cryst12091213
crystals-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Review

Plasmon Inspired 2D Carbon Nitrides: Structural, Optical and Surface Characteristics for Improved Biomedical Applications

by
Amel Gacem
1,
Suriyaprabha Rajendran
2,*,
Mohd Abul Hasan
3,
Shakti Devi Kakodiya
4,
Shreya Modi
5,
Krishna Kumar Yadav
6,
Nasser S Awwad
7,
Saiful Islam
3,
Sungmin Park
8 and
Byong-Hun Jeon
9,*
1
Department of Physics, Faculty of Sciences, University 20 Août 1955, Skikda 21000, Algeria
2
School of Nanosciences, Central University of Gujarat, Gandhinagar 382030, India
3
Civil Engineering Department, College of Engineering, King Khalid University, Abha 61421, Saudi Arabia
4
School of Bioscience, Rani Durgavati Vishwavidyalaya, Jabalpur 482001, India
5
Department of Microbiology, Shri Sarvajanik Science College, Mehsana 384001, India
6
Faculty of Science and Technology, Madhyanchal Professional University, Ratibad 462044, India
7
Department of Chemistry, King Khalid University, P.O. Box 9004, Abha 61413, Saudi Arabia
8
Department of Civil and Environmental Engineering, Hanyang University, 222-Wangsimni-ro, Seongdong-gu, Seoul 04763, Korea
9
Department of Earth Resources & Environmental Engineering, Hanyang University, 222-Wangsimni-ro, Seongdong-gu, Seoul 04763, Korea
*
Authors to whom correspondence should be addressed.
Crystals 2022, 12(9), 1213; https://doi.org/10.3390/cryst12091213
Submission received: 14 July 2022 / Revised: 17 August 2022 / Accepted: 22 August 2022 / Published: 28 August 2022
Browse Figures
Versions Notes

Abstract

:
In the past few years, noble metal-based 2D nanomaterials particularly Ag and Au enriched carbon nitrides have seen advanced catalytic actions and reactivity. These composite nanostructures’ chemical and physical characteristics have been applied to improve the targeted functionalities in healthcare and medical sciences. Many scientists and experts were inspired to study their foundational technologies in the medicinal industries via architectural and surface modifications by doping of noble nanoparticles. Here, we have provided fundamental ideas for structuring Ag and Au decorated CNs (carbon nitrides) by studying their morphological and modified surface properties for biomedical applications. There is a vast spectrum of publications that discusses the peculiarities of CNs and noble metal’s key discoveries. The impact of surface plasmons resonance (SPR) is an essential factor for noble metals and that is why it is focused extensively for better performance in biomedical sectors. The elemental combinations on the CNs surfaces and their morphological status were found to be much more efficient which is broadly discussed. The fabrication techniques, structural characterizations, and SPR role of Ag and Au are addressed including fundamental concepts followed by many suitable examples under this review.

1. Introduction

Unique electromagnetic and physicochemical functionalities of conductive nanostructures along with suitable polymeric frameworks have been employed as a multifunctional tool in the field of nanoscience and technologies range for a variety of applications, including photovoltaic, therapeutic, and photocatalyst. [1,2,3]. Noble metals in the class of metallic nanostructures were used as individual and also as co-doped ions to enhance the work quality and efficiency. Several inorganic nanoparticles (NPs) such as Pt, Pd, Ag, and Au have been appreciated due to their surface plasmon properties in materials research and nanoelectronics. The most studied metals are Ag and Au nanostructures which have distinctive photonic excitation regions in the electromagnetic spectrum due to their specific conduction bands electrons and nano range sizes. These optical and electronic characteristics provide an outstanding catalytic action against targeted applications. [4,5]. The associated electronic configurations of both the Ag and Au NPs found much better as bimetallic nanocatalysts due to their intra-bands structure and combined surface plasmon resonance (SPR, produced by the combined fluctuation of the valance band electrons after irradiated by electromagnetic wave) and that is why both candidates are mainly focused for biomedical uses as compared to other noble metals. When the particular incident light interacts with Ag and Au particles, the conduction bands electron promotes to the valance bands and combined fluctuates with the similar frequencies of incident wavelength of light. This phenomenon is called SPR which is studied in noble metal surfaces [5,6,7]. Variety morphologies offer fascinating chances for biomolecules or microbes to disperse and come into interaction with one another at the surface, enabling individuals to properly manage their specific functions. Plasmon metal nanoparticles exhibit an optical absorption band having a maximum plasmon resonance frequency which is known as localized surface plasmon resonance (LSPR). This LSPR value is found to be 520 nm for a spherical Au NPs with a confined 10 nm size. These metal nanoparticles also enhance the electromagnetic field close to their surfaces. The LSPR of the colloidal suspension is significantly influenced by the noble Ag and Au NPs width (confined sizes) and geometry, altering the optical bands at visible and near infrared range means at confined wavelength. Such type of spectral shifting might be caused by the simple clustering or random distribution of spherical particles. Nanomaterials might infiltrate organelles owing to a property exploited in biosystems assurance their widths are contained within the nanometer scale. Likewise, molecules with larger sizes as compared to nanometer NPs have several advantages as compared to other preventative medicines when used as reducing treatments and Ag and Au can moderate structurally for the efficient performances [8,9]. The addition of both AgAu NPs felicitates an advanced antibacterial impact with minimum side effects inside the living cells. However, the narrow sizes and engineered surfaces of the noble nanostructures have been targeted to use as bio markers due to their easy processing and less toxic nature, resulting an improved biomedical aspect in the medical and health environments. [10,11,12].
Gold nanoparticles are coveted for their wide range of uses in medical chemistry, pharmacology, and diagnostics, as opposed to some other nanomaterials. In vivo experiments have focused more on Au metal nanoparticles (Au NPs) over the past few years. The detrimental effects of gold chloride and photosynthesized nanomaterials utilizing Cassia roxburghii leaf extract on the African green monkey normal kidney Vero cell line and three cancer cell lines, including MCF7, HepG2, and HeLa, were studied by Pannerselvam Balashanmugam and coworkers [13]. Silver is generally a long-lasting product with antimicrobial qualities and historical qualities. Due to its dispersion nature, silver nanoparticles have a wide range of industrial applications. They are heavily utilized by the aquaculture industry. In order to lessen or completely eliminate the dangers associated with managing chemical reduction agents, production rates, and cytotoxicity, better environmentally friendly methods for creating metallic NPs were chosen [14,15]. In the past, they have been employed for a wide range of therapeutic diagnoses associated with anti-inflammatory and antioxidant actions [16,17].

2. Characteristics and Importance of SPR and 2D CNs

Since complete miscibility of Au and Ag can be obtained at any composition in both bulk materials and NPs, combinations of Au and Ag are notably crucial to study about their coupled elemental-sensitive optical characteristics. Au NPs have an intense SPR band at the visible spectrum at a certain wavelength that is distinct from the pure Ag NPs. The LSPR (localized surface plasmon resonance) spectra of Au/Ag composite NPs showed increasing blue- or red-shifting when the Ag or Au proportion changed, according to Mallin et al. [18]. When Au core-Ag shell nanoparticles are created through the process of gastric ripening followed by annealing, they become Au-Ag hybrid nanoparticles. Figure 1 illustrates the clear SPR shift that R. Kuladeep et al. [19] suggested for Au and Ag NPs at various concentrations. Ag, Au, and mixed alloy AgAu NPs, which had spherical shapes with diameters of less than 20 nm, respectively, showed LSPR bands located at about 410, 526, and 459 nm.
The geometries of the Au and Ag have been altered by the lab conditions and the selection of primary compounds taken for the synthesis reactions, which also affects the SPR bands. Therefore, these mixed plasmon nanostructures’ morphology, dimensions, and stoichiometry are investigated both as pure Ag and Au NPs along with the mixed composite materials.
Utilizing nanocrystals of various sizes and forms, including nanocrystals, thin films, and spherical arrays, the electrochemical performance of hybrid CNs could be altered especially by modifying the surface properties [20,21]. The g-C3N4-based (graphitic carbon nitrides) catalysts device applications to its pp-stacked heterocyclic thicker systems of heptazine (tri-s-triazine) or triazine heterocycles produce better results thanks to the core covered component of g-C3N4 [22]. Using proper techniques, major advances in the physicochemical features of composites such as carbon nanotubes, graphite, and other 2D (two-dimensional) configurations are produced in the form of one- and two carbon nitride sheets. To separate two metal-based semiconductors with acceptable topologies, nanostructures, g-C3N4, and nano ranged thick polyheptazine films were typically employed. There is a significant demand for exfoliated g-C3N4 and its analogs to form quickly in extended surfaces, such as 2D g-C3N4 (two-dimensional graphitic-carbon nitrides) and 3D g-C3N4 sheets [23]. Since doped concepts could be utilized to change the structural and electrical framework of these nanomaterials, a considerable of studies have been carried out in this area [24,25]. In the realm of mixed nanocomposites, however, defined in various conducting polymers have developed and changed substantially. Multiple combination types of 2D structures, such as nanocrystals, metals doped graphene, r-GO (graphene-oxides), CNT, and carbon nitrides (C3N4), were discovered and utilized in biomedical, energy conservation, and environmental sensors [26]. Here we explained a fundamental and descriptive overview of 2D carbon allotrope known as CNs including structural, surface associated with based on Ag and Au NPs and its use in healthcare areas.

2.1. SPR Properties of Ag and Au Nanostructures

When electromagnetic radiation interacts with plasmonic metals such as Pt, Cu, Ag, and Au NPs, the surface plasmons response (collective motions of the valance bands free electrons) changes which influences the optical absorption band intensities of the particles. However, the Ag and Au plasmonic quality are considered valuable for potential prospective in therapeutic diagnosis, and drug delivery. Whereas an Au displays red and an Ag exhibits greyish, depending on their size and form, Au and Ag nanoparticles can display any color in the spectrum, from red to green to violet. Due to the localized surface plasmon resonance (LSPR) particles on the surfaces of Ag and Au nanoparticles, they have a wide variety of colors [27,28]. In essence, elements are composed of positively charged that is encircled by an electron-free conduction band. An additional electric field is created on particle surfaces as a result of the migration of metallic electrons during illumination, which results in the production of an electric dipole [29,30,31]. The electric field created by SPR on the metal atom’s surfaces and the electric field created by the applied electromagnetic field combine to form the overall electric field. Although higher-level plasmon phases could also be produced in anisotropic nanostructures, dipole plasmons are primarily synthesized in narrow-sized nanospheres. Therefore, the distinctive bands of the ultraviolet absorption spectrum of Ag nanoprisms produced by plasmon-driven change were 340 nm (out of plane quadrupole resonance), 470 nm (in-plane quadrupole resonance), and 640 nm (in-plane dipole resonance) [32,33]. It is crucial to highlight that changing the absorption bands in spherical Ag and Au nanostructures is incredibly difficult based on experimental considerations. For instance, the size of Ag NPs is likewise influenced by pH levels, and this affects how they respond to SPR (Figure 2a) [34,35].

2.2. Surface Modification and Determinations of Carbon Nitrides

Due to bare g-CNs specific surfaces and fast photoexcited coupling, a strong note can alter its architecture and banding sites. These g-CNs’ particular geometric configurations may be used to accelerate charge recombination, increasing kinetic and chemical efficiency [36,37,38]. Researchers are very interested in graphitic carbon nitride (g-C3N4), a pretty modern type of carbonaceous material including a band-gap of about 2.7 eV, owing to its excellent intrinsic optoelectronic characteristics, including high surface and photo-responsiveness, semiconductive nature, and chemical and thermal resistance. They have improved optical absorption, photocatalyst, and storage capabilities due to optimum band gap values. Using Ag or Au nanocrystals of different sizes and forms, such as wires, cylinder configurations, and nanotubes, the catalytic activity of hybridized g-CNs is altered. Due to the core enclosed element, g-CN-based photocatalytic device applications to its pp-stacked heterocyclic bulkier systems of heptazine (tri-s-triazine) or triazine heterocycles produce better results. Runxue Liu used a straightforward one-step calcination process in his research to examine the effects of calcination time on the morphology, surface composition, and catalytic performances of Ag loaded g-C3N4 (Ag/CN-x) composites [39]. The Ag and Au loaded hybridized g-CNs were studied by Marta Jiménez-Salcedo [40] using TEM and XPS techniques. (Figure 3 and Figure 4). The almost spherical nanoparticles of the Ag were dispersed into the CNs surfaces using one-pot self-reduction of organometallic compounds, which were having a maximum 9.8 nm sizes. Figure 4 show a XPS spectra for the Ag and Au dispersed CNs hybrid materials where the full survey scan is showed in Figure 4a with all expected elements such as C, N, O and Ag.
The C1s peak observed around 284 eV, N 1s at around 285 eV, and the O 1s found near to 530 eV. Here, the C and N peaks confirmed the CNs atomic presence along with atmospheric N. The high resolution of the Au 4f and Ag 3d spectra were also confirmed around 84 and 87.7 eV for the Au 4f7/2 and Au 4f5/2 binding energy states, while the Ag 3d5/2 and 3d3/2 levels were observed at around 368 and 374 eV.
An AFM, TEM, or SEM technique is usually used to explore the structural account of the CN, which has previously been used to illustrate the typical membranous nanosheets with multiple mesoporous structures. Under particular environmental conditions, urea polycondensation is frequently used to create an atomic structure that is graphitic. While hybrid graphitic carbon composite materials can have a variety of topologies depending on the production, pure graphitic carbon frequently has nanosheets-like architectures. [41]. Numerous procedures were suggested to look into the characteristics of CN and nanomaterials, including FTIR, XRD, Raman, XPS, and many more. Theoretical approaches could be used to investigate the electrical characteristics, ionic conductivity, and surface composition of such conducting polymers. [42,43].

3. Morphologies and Optical Functionalities of Ag and Au Doped Carbon Nitrides Nanocomposites towards Medicinal Aspects

The structure and elemental content of nanoscale materials determine their physical and chemical properties. Due to the unusual SPR, thin geometries, and electrical topologies of the composite nanomaterials and its doped counterparts, they were used for better medical applications [44]. Ag and Au NPs are primarily emphasized throughout this perspective for creating considerably more effective nanomaterials for enhanced monitoring and healing reasons.

3.1. Structural Modified Plasmon-Carbon Nitirides for Enhanced Bomedical Uses

The Ag and Au NPs’ absorption spectra and conformational changes have a significant effect on the kinetic efficiency and actions. Ag and Au doped highly conductive nanomaterials, including multilayered films, transition metals, nanostructures were exploited as a substantial catalyst, especially in clinical field [45,46].
Numerous studies have been conducted for all this particular job employing nanobiosensors and structured activities on metallic nanoparticles. The plasmon frequency for Ag and Au was examined at the nanoscale and was found to be 425 nm and 550 nm, correspondingly [47]. Yu Fan has successfully created a novel “on-off” electrochem-iluminescence (ECL) sensor for the sensitive and precise detection of concanavalin (ConA) [48]. For the purpose of immobilizing phenoxy dextran (DexP) by p-p interface and achieving the “signal-on” state with a strong positive ECL output, Ag-doped Ag-g-C3N4 was modified out onto the glassy carbon electrode (GCE). A carbohydrate-ConA interface was then used to affix the particular ConA to the DexP/Ag-g-C3N4 altered film. Polyani-line-3,4,9,10-perylenetetracarboxylic acid-DexP conjugate (abbreviated as PANI-PTCA-DexP), an ECL signal quenching probe, was repeatedly incubated onto the electrode via the carbohydrate-ConA connection to provide the “signal-off” state. With the greater dosage of PANI and DexP, PTCA was used as a host and PANI and DexP served as quenchers for the Ag-g-C3N4 system and sensing platforms for binding ConA. A satisfactory quenching ECL signal was seen with the creation of the sandwiched architecture of DexP, ConA, and PANI-PTCA-DexP using S2O82 as the co-reactant of Ag-g-C3N4. Using an “on-off” approach, ConA identification was achieved with a broad linear region of 0.001 ng/mL to 50 ng/mL and a detection limit of 0.0003 ng/mL (Figure 5). Using S2O82 as the co-reactant of Ag-g-C3N4, an acceptable quenching ECL signal was observed with the construction of the sandwiched architecture of DexP, ConA, and PANI-PTCA-DexP. ConA identification were obtained with a large linear region of 0.001 ng/mL to 50 ng/mL and a detection limit of 0.0003 ng/mL using such a “on-off” method.

3.2. Improved Biomedical Properties Using Metal and Metal-Based Nanocomposites

It has been investigated into if Ag ions may be incorporated on g-C3N4 to increase the efficiency of its photo-response. Pt, Ag, and Cu are just a few of the ionic metals that can be transported by the elastic structural framework known as the g-CNs nanomaterial. By exploiting the various properties of these free ions, it is also possible to identify certain substances in the atmosphere. A range of biomaterials that were combined with g-CNs nanomaterials are displayed in Table 1. By adding noble metals, the reaction rate of g-C3N4 for the eradication of dangerous bacteria and diseases might be increased [49,50].
To altering the excitation wavelength, the researchers used Au nanostructures (Au25) to enhance the results of photodynamic treatment (PDT). Upconversion nanoparticles (UCNPs) are coated with a mesoporous g-C3N4 coating, and then ultrasmall Au25 nanocrystals and PEG polymers are applied (UCNPs@g-C3N4-Au25-PEG), to form a novel dual-photosensitizer nanosystem [52]. In view of the excellent valence band of Au nanoclusters, the absorption zone of g-CNs is consistent with the emission band of Au nanoparticles. The therapeutic effects of g-CNs are strengthened by their surface plasma resonance (SPR) features. Both g-C3N4 and Au25 nanoparticles can be initiated by UV-Vis light and the powerful near-infrared (NIR) emission bands emitted by UCNPs to produce ROS, enabling the two types of photosensitizers for improved PDT capability when activated by conventional NIR light.

4. Antibacterial Impacts of Ag and Au Based CNs

Interest has been sparked by the basic elemental composition of g-C3N4, a metal-free conductors with a structure reminiscent of carbon allotropes [53]. To increase chemical and photonic capacities, designed and synthesized nanomaterials with essentially different components could be successfully produced. Numerous applications of the g-C3N4 have been researched, such as biological, chemical, and nano biomaterials. Numerous techniques, including the production of nanostructured materials and the modification of hybrid ions, have already been developed to improve biological responses qualities [54,55,56].
The plasmonic nature of nanoscale Ag and Au is also observed to have a significant impact on the changed structures due to its small size, dispersion, and support at hosts or substrates. Typically, the surface of nanostructures with a nano ranged metal (such Ag and Au) nitride substrate would improve microbe adsorption. Plasmon nanoparticles’ greater surface allows for the rapid spread of bacterial colonies, makes it simple to enter microscopic membranes, which rapidly kills bacteria. In a study, M. A. Wahab et al. [57] created an Ag NPs-loaded NCN material (NCN@Ag) that was employed as an antimicrobial agent against E. coli. A systematic illustration showed in Figure 6 for the Ag functionalized CNs nanomaterials for the antibacterial biosensors.

An Fundamental Assessment toward Biomedical Importance

Research is still being carried out on evenly disseminated dispersion plasmon Ag or Au NPs in nanostructured carbon nitrides (NCN), particularly from single carbon-nitrogen substrates, and their interaction with microbial cells. The precise atomic populations and morphologies of nanoscale particles have been discovered to be crucial for the development of biologically based nanosensors and tools for bioimaging, and antibacterial protection. Wei Bing [58] developed a very efficient framework to generate modified g-C3N4 substrates with included Ag NPs (Ag/g-C3N4). Ag/g-C3N4 nanohybrids significantly outperformed pure g-C3N4 nanosheets in terms of ROS production in the visible area. They also showed superior antimicrobial qualities and had the ability to disintegrate bacterial biofilms. When exposed to visible sunlight, the Ag/g-C3N4 nanohybrids have once again been shown to be powerful antibacterial inhibitors.
Figure 7 shows the development of bacterial colonies on LB agar supplemented with Ag/g-C3N4, Ag NPs/g-C3N4, and g-C3N4 over the course of 24 h. The plates containing Ag/g-C3N4 (50 g mL−1) showed a considerable improvement over the control in the visible region. Colony growth was nearly completely inhibited whenever bacteria were cultured on LB-agar stained with Ag/g-C3N4, but Ag NPs/g-C3N4 or g-C3N4 only produced high colony-forming units [58]. These results show that Ag/g-C3N4 is the most effective inhibitor of both G− and G+ bacteria.
By retaining photo-induced electrons in heterostructures, nanocrystals may be able to enhance carrier separation. UV light could also be used by Au NPs to complete the inter-band electron transfer. By ultrasonically processing g-CNQDs and HAuCl4, Bhowmik et al. [59] created Au-CNx composites without using an additional reducing agent. Au NPs could also accomplish the inter-band electron transfer using ultraviolet light. Owing to an increase in ROS production activity. Au is one of the most durable nanostructured materials, making it one of the safest for biological systems. Table 2 lists the numerous plasmon-associated nanostructures for medical uses.
The release of therapeutic drugs bound to Au NPs could be accomplished by heating the nanoparticles by employing a particular frequency of light. The heated Au nanostructures caused by the plasmons phenomenon can be used to deliver treatments to targeted biomolecule nuclei and organelles. The 5-fluorouracil (5-FU) (an anticancer) was discovered to be released from Au NPs by Agasti et al. [61] with the use of light. For improved dispersion and regulated cellular uptake, zwitterionic mediators were employed. When it is exposed to light with the 365 nm wavelength, the orthonitrobenzyl molecule cleaves and released 5-FU out from conjugate systems. Likewise, employing DNA-wrapped Au NRs infused by DOX (GNR@DOX), chemotherapy and photothermal treatment were conducted to cure metastatic melanoma. While spherical Au NPs exhibit plasmon resonance in the middle of the visible spectrum, their real positions could be shifted towards the infrared (IR) spectrum for rods and shells shaped structures. These nanostructures studied are highly effective for in vivo medication because biological tissues are more permeable to NIR wavelengths of sunlight [62]. These designed Au-based nanomaterials could be widely used as the building blocks for effective light-dependent controlled medication release reactions for the handling of several disorders. So, the nanoscience and technologies have played an advanced impacts on improving the catalytic functions towards optoelectronic, environments and biomedical uses [63,64,65,66].

5. Future Scopes and Conclusions

Noble metals such as Ag and Au NPs have received a lot of praise for their enhanced functionality in therapeutic and clinical applications due to their surface and narrow sizes. In the medicinal sector, their combination of these metal nanostructures with CNs was additionally applied to design the medical tools, sensors, and markers. Graphitic CNs have already been employed along with desired metal ions, having larger surface sites, stabled 2D orientations, and exceptional catalytic reactivity. Thus, to explain the physicochemical properties and chemical stabilities of Ag and Au doped CNs, we have highlighted the fundamentals of surface, 2D rearrangements of CNs units, and chemical bandings by reporting acceptable methodologies and techniques. Additionally, Ag, Au, and doped CNs might be integrated as effective catalysts in the healthcare industry to offer essential properties for enhanced biomedicine applications. Ag/Au-g-CN nanomaterials would be employed in physiological entities as therapeutic tools for antimicrobial and anticancer, uses. Further, various metal ions such as Pt, Cu, and Pd are also incorporated into the CN surface for enhancing the catalytic activities which is an essential task in the field of drug designing and developments in medical sciences. In addition, other concepts of these plasmonic materials such as photochemical and plasmonic near-field also explored to improve the biosensing uses in medical sciences. Experimentally, the thermo-induced alteration of the refractive index was used to evaluate the thermoplasmonic activities, which gave the optimum temperature for NA (nucleic acid) hybrid, Endo-IV breaking, and cyclical fluorescent probes. The highest absorbance of the 2D uniformly dispersed nanoabsorbers (AuNI) with a normal incidence angle was created specifically for 532 nm. The heated electron–hole combinations within the AuNI nanoabsorbers were photoexcited after exposed to the homogenized 532 nm pulse. The photoexcited plasmon moved to the metallic lattice in a matter of nanoseconds and later produced the heat energy to the surround aqueous environment via electron-phonon interactions. This suggested biosensing device could also be a promising technology for quick medical disease detection and serious ecological surveillance in the COVID-19 pandemic and post-pandemic period, supporting interventions in public health [67,68]. The combined effect of SPR and 2D surface of CNs could be regulated by the changing stoichiometric ratios of doped metal ions and their nano ranged sizes which directly affect the drug delivery in terms of the increasing rate of physicochemical kinetics. Therefore, these advanced nanomaterials could be highly appreciated for various areas such as biomedical, optoelectronics, and environmental applications due to their SPR spectral characteristics and surface qualities of the functionalized CNs.

Author Contributions

Conceptualization, S.R., K.K.Y. and S.M.; Data curation, S.M., A.G., S.D.K. and M.A.H.; methodology, S.R., S.M. and B.-H.J.; validation, S.R., N.S.A., S.I., K.K.Y. and A.G.; formal analysis, S.R., S.M. and S.P.; resources, S.P., S.I. and B.-H.J.; writing—original draft preparation, S.R., S.D.K. and K.K.Y.; writing—review and editing, S.P., A.G., S.I. and K.K.Y.; supervision, S.R. and B.-H.J.; project administration, B.-H.J. and M.A.H.; funding acquisition, K.K.Y., B.-H.J. and M.A.H.; investigation, S.R., S.P. and S.M.; software’s, S.R., M.A.H. and S.R.; visualization, N.S.A., S.I., B.-H.J. and S.R. All authors have read and agreed to the published version of the manuscript.

Funding

The Authors would like to express their gratitude to King Khalid University, Saudi Arabia, for providing administrative and technical support.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

All relevant data are included within the article.

Acknowledgments

The authors extend their appreciation to the Deanship of Scientific Research at King Khalid University, Abha, Kingdom of Saudi Arabia for funding this work through Large Groups RGP.2/43/43. This work was supported by the Korea Environment Industry and Technology Institute (KEITI) through Subsurface Environment Management (SEM) Projects, funded by Korea Ministry of Environment (MOE) (No. 2020002480007).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Rao, Y.; Inwati, G.K.; Singh, M. Green synthesis of capped gold nanoparticles and their effect on Gram-positive and Gram-negative bacteria. Futur. Sci. OA 2017, 3, FSO239. [Google Scholar] [CrossRef] [PubMed]
  2. Inwati, G.K.; Yadav, V.K.; Ali, I.H.; Kakodiya, S.D.; Choudhary, N.; Makwana, B.A.; Lal, C.; Yadav, K.K.; Singh, B.; Islam, S.; et al. Enhanced Plasmon Based Ag and Au Nanosystems and Their Improved Biomedical Impacts. Crystals 2022, 12, 589. [Google Scholar] [CrossRef]
  3. Inwati, G.K.; Rao, Y.; Singh, M. Thermodynamically induced in Situ and Tunable Cu Plasmonic Behaviour. Sci. Rep. 2018, 8, 3006. [Google Scholar] [CrossRef] [PubMed]
  4. Palaniappan, N.; Inwati, G.; Singh, M. Biomaterial Co-Cr-Mo Alloys Nano Coating Calcium Phosphate Orthopedic Treatment. IOP Conf. Ser. Mater. Sci. Eng. 2014, 64, 012026. [Google Scholar] [CrossRef]
  5. Modi, S.; Inwati, G.K.; Gacem, A.; Abullais, S.S.; Prajapati, R.; Yadav, V.K.; Syed, R.; Alqahtani, M.S.; Yadav, K.K.; Islam, S.; et al. Nanostructured Antibiotics and Their Emerging Medicinal Applications: An Overview of Nanoantibiotics. Antibiotics 2022, 11, 708. [Google Scholar] [CrossRef] [PubMed]
  6. Inwati, G.K.; Rao, Y.; Singh, M. In Situ Growth of Low-Dimensional Silver Nanoclusters with Their Tunable Plasmonic and Thermodynamic Behavior Article. ACS Omega 2017, 2, 5748–5758. [Google Scholar] [CrossRef] [PubMed]
  7. Chen, H.; Shao, L.; Li, Q.; Wang, J. Gold nanorods and their plasmonic properties. Chem. Soc. Rev. 2013, 42, 2679–2724. [Google Scholar] [CrossRef]
  8. Kumar, A.V.N.; Prabhu, S.M.; Shin, W.S.; Yadav, K.K.; Ahn, Y.; Abdellattif, M.H.; Jeon, B.H. Prospects of non-noble metal single atoms embedded in two-dimensional (2D) carbon and non-carbon-based structures in electrocatalytic applications. Coord. Chem. Rev. 2022, 467, 214613. [Google Scholar] [CrossRef]
  9. Condorelli, M.; Scardaci, V.; D’Urso, L.; Puglisi, O.; Fazio, E.; Compagnini, G. Plasmon sensing and enhancement of laser prepared silver colloidal nanoplates. Appl. Surf. Sci. 2019, 475, 633–638. [Google Scholar] [CrossRef]
  10. Kumar, N.; Inwati, G.K.; Ahmed, E.M.; Lal, C.; Makwana, B.; Yadav, V.K.; Islam, S.; Ahn, H.-J.; Yadav, K.K.; Jeon, B.-H. Modified 7-Chloro-11H-indeno[1,2-b]quinoxaline Heterocyclic System for Biological Activities. Catalysts 2022, 12, 213. [Google Scholar] [CrossRef]
  11. Inwati, G.K.; Rao, Y.; Singh, M. In Situ Free Radical Growth Mechanism of Platinum Nanoparticles by Microwave Irradiation and Electrocatalytic Properties. Nanoscale Res. Lett. 2016, 11, 458. [Google Scholar] [CrossRef] [PubMed]
  12. Rajendran, S.; Inwati, G.K.; Yadav, V.K.; Choudhary, N.; Solanki, M.B.; Abdellattif, M.H.; Yadav, K.K.; Gupta, N.; Islam, S.; Jeon, B.-H. Enriched Catalytic Activity of TiO2 Nanoparticles Supported by Activated Carbon for Noxious Pollutant Elimination. Nanomaterials 2021, 11, 2808. [Google Scholar] [CrossRef] [PubMed]
  13. Balashanmugam, P.; Durai, P.; Balakumaran, M.D.; Kalaichelvan, P.T. Phytosynthesized gold nanoparticles from C. roxburghii DC. leaf and their toxic effects on normal and cancer cell lines. J. Photochem. Photobiol. B Biol. 2016, 165, 163–173. [Google Scholar] [CrossRef] [PubMed]
  14. Hong, A.; Tang, Q.; Khan, A.U.; Miao, M.; Xu, Z.; Dang, F.; Liu, Q.; Wang, Y.; Lin, D.; Filser, J.; et al. Identification and Speciation of Nanoscale Silver in Complex Solid Matrices by Sequential Extraction Coupled with Inductively Coupled Plasma Optical Emission Spectrometry. Anal. Chem. 2021, 93, 1962–1968. [Google Scholar] [CrossRef]
  15. Reinsch, B.C.; Levard, C.; Li, Z.; Ma, R.; Wise, A.; Gregory, K.B.; Brown, G.E., Jr.; Lowry, G.V. Sulfidation of Silver Nanoparticles DecreasesEscherichia coliGrowth Inhibition. Environ. Sci. Technol. 2012, 46, 6992–7000. [Google Scholar] [CrossRef]
  16. Nejati, K.; Dadashpour, M.; Gharibi, T.; Mellatyar, H.; Akbarzadeh, A. Biomedical Applications of Functionalized Gold Nanoparticles: A Review. J. Clust. Sci. 2022, 33, 1–16. [Google Scholar] [CrossRef]
  17. Alkorbi, A.S.; Kumar, K.Y.; Prashanth, M.K.; Parashuram, L.; Abate, A.; Alharti, F.A.; Jeon, B.H.; Raghu, M.S. Samarium vanadate affixed sulfur self doped g-C3N4 heterojunction; photocatalytic, photoelectrocatalytic hydrogen evolution and dye degradation. Int. J. Hydrog. Energy 2022, 47, 12988–13003. [Google Scholar] [CrossRef]
  18. Mallin, M.P.; Murphy, C.J. Solution-Phase Synthesis of Sub-10 nm Au-Ag Alloy Nanoparticles. Nano Lett. 2002, 2, 10–12. [Google Scholar] [CrossRef]
  19. Kuladeep, R.; Jyothi, L.; Alee, K.S.; Deepak, K.L.N.; Narayana Rao, D. Laser-assisted synthesis of Au-Ag alloy nanoparticles with tunable surface plasmon resonance frequency. Opt. Mater. Express 2012, 2, 161. [Google Scholar] [CrossRef]
  20. Kashyap, T.; Biswasi, S.; Pal, A.R.; Choudhury, B. Unraveling the Catalytic and Plasmonic Roles of g-C3N4 Supported Ag and Au Nanoparticles Under Selective Photoexcitation. ACS Sustain. Chem. Eng. 2019, 7, 19295–19302. [Google Scholar] [CrossRef]
  21. Modi, S.; Prajapati, R.; Inwati, G.K.; Deepa, N.; Tirth, V.; Yadav, V.K.; Yadav, K.K.; Islam, S.; Gupta, P.; Kim, D.-H.; et al. Recent Trends in Fascinating Applications of Nanotechnology in Allied Health Sciences. Crystals 2022, 12, 39. [Google Scholar] [CrossRef]
  22. Liu, M.; Niu, B.; Guo, H.; Ying, S.; Chen, Z. Simple preparation of g-C3N4@Ni3C nanosheets and its application in supercapacitor electrode materials, hydrogengeneration via NaBH4 hydrolysis and reduction of p–nitrophenol. Inorg. Chem. Commun. 2021, 130, 108687. [Google Scholar] [CrossRef]
  23. Kashyap, T.; Biswas, S.; Ahmed, S.; Kalita, D.; Nath, P.; Choudhury, B. Plasmon activation versus plasmon quenching on the overall photocatalytic performance of Ag/Au bimetal decorated g-C3N4 nanosheets under selective photoexcitation: A mechanistic understanding with experiment and theory. Appl. Catal. B Environ. 2021, 298, 120614. [Google Scholar] [CrossRef]
  24. Vidyasagar, D.; Bhoyar, T.; Singh, G.; Vinu, A. Recent Progress in Polymorphs of Carbon Nitride: Synthesis, Properties, and Their Applications. Macromol. Rapid Commun. 2021, 42, 2–7. [Google Scholar] [CrossRef]
  25. Li, F.; Zhou, H.; Fan, J.; Xiang, Q. Amine-functionalized graphitic carbon nitride decorated with small-sized Au nanoparticles for photocatalytic CO2 reduction. J. Colloid Interface Sci. 2020, 570, 11–19. [Google Scholar] [CrossRef]
  26. Zhao, Y.; Zhang, X.; Wang, T.; Song, T.; Yang, P. Fabrication of rGO/CdS@2H, 1T, amorphous MoS2 heterostructure for enhanced photocatalytic and electrocatalytic activity. Int. J. Hydrog. Energy 2020, 45, 21409–21421. [Google Scholar] [CrossRef]
  27. Lee, S.H.; Jun, B.-H. Silver Nanoparticles: Synthesis and Application for Nanomedicine. Int. J. Mol. Sci. 2019, 20, 865. [Google Scholar] [CrossRef]
  28. Compagnini, G.; Condorelli, M.; Fragalà, M.E.; Scardaci, V.; Tinnirello, I.; Puglisi, O.; Neri, F.; Fazio, E. Growth Kinetics and Sensing Features of Colloidal Silver Nanoplates. J. Nanomater. 2019, 2019, 7084731. [Google Scholar] [CrossRef]
  29. Qiu, G.; Ng, S.P.; Wu, C.-M.L. Bimetallic Au-Ag alloy nanoislands for highly sensitive localized surface plasmon resonance biosensing. Sens. Actuators B Chem. 2018, 265, 459–467. [Google Scholar] [CrossRef]
  30. Linl Liu, A.; Thakur, W.; Kar Li, G.; Qiu, T.; Yang, B.; He, Y.; Lee, C.M.; Wu, L. Site specific biotinylated antibody functionalized Ag@AuNIs LSPR biosensor for the ultrasensitive detection of exosomal MCT4, a glioblastoma progression biomarker. Chem. Eng. J. 2022, 446, 137383. [Google Scholar] [CrossRef]
  31. Amendola, V.; Scaramuzza, S.; Agnoli, S.; Granozzi, G.; Meneghetti, M.; Campo, G.; Bonanni, V.; Pineider, F.; Sangregorio, C.; Ghigna, P.; et al. Laser generation of iron-doped silver nanotruffles with magnetic and plasmonic properties. Nano Res. 2015, 8, 4007–4023. [Google Scholar] [CrossRef]
  32. Mie, R.; Samsudin, M.W.; Din, L.B.; Ahmad, A.; Ibrahim, N.; Adnan, S.N.A. Synthesis of silver nanoparticles with antibacterial activity using the lichen Parmotrema praesorediosum. Int. J. Nanomed. 2013, 9, 121–127. [Google Scholar] [CrossRef] [PubMed]
  33. Yaqoob, S.B.; Adnan, R.; Rameez Khan, R.M.; Rashid, M. Gold, Silver, and Palladium Nanoparticles: A Chemical Tool for Biomedical Applications. Front. Chem. 2020, 8, 376. [Google Scholar] [CrossRef] [PubMed]
  34. Huang, X.; El-Sayed, M.A. Gold nanoparticles: Optical properties and implementations in cancer diagnosis and photothermal therapy. J. Adv. Res. 2010, 1, 13–28. [Google Scholar] [CrossRef]
  35. Riaz, M.; Mutreja, V.; Sareen, S.; Ahmad, B.; Faheem, M.; Zahid, N.; Jabbour, G.; Park, J. Exceptional antibacterial and cytotoxic potency of monodisperse greener AgNPs prepared under optimized pH and temperature. Sci. Rep. 2021, 11, 2866. [Google Scholar] [CrossRef] [PubMed]
  36. Darkwah, W.K.; Ao, Y. Mini Review on the Structure and Properties (Photocatalysis), and Preparation Techniques of Graphitic Carbon Nitride Nano-Based Particle, and Its Applications. Nanoscale Res. Lett. 2018, 13, 388. [Google Scholar] [CrossRef]
  37. Gu, Q.; Liao, Y.; Yin, L.; Long, J.; Wang, X.; Xue, C. Template-free synthesis of porous graphitic carbon nitride microspheres for enhanced photocatalytic hydrogen generation with high stability. Appl. Catal. B Environ. 2015, 165, 503–510. [Google Scholar] [CrossRef]
  38. Ghaemmaghami, M. Sustainable Energy & Fuels Carbon nitride as a new way to facilitate the next generation of carbon-based supercapacitors. Sustain. Energy Fuels 2019, 3, 2176–2204. [Google Scholar] [CrossRef]
  39. Liu, R.; Yang, W.; He, G.; Zheng, W.; Li, M.; Tao, W.; Tian, M. Ag-Modified g-C3N4 Prepared by a One-Step Calcination Method for Enhanced Catalytic Efficiency and Stability. ACS Omega 2020, 5, 19615–19624. [Google Scholar] [CrossRef]
  40. Jiménez-Salcedo, M.; Monge, M.; Tena, M.T. Combination of Au-Ag Plasmonic Nanoparticles of Varied Compositions with Carbon Nitride for Enhanced Photocatalytic Degradation of Ibuprofen under Visible Light. Materials 2021, 14, 3912. [Google Scholar] [CrossRef]
  41. Ensa, A.A.; Abarghoui, B.M.; Rezaei, B. Graphitic carbon nitride nanosheets coated with Ni2CoS4 nanoparticles as a high-rate electrode material for supercapacitor application. Ceram. Int. 2019, 45, 8518–8524. [Google Scholar] [CrossRef]
  42. Inwati, G.K.; Yadav, V.K.; Ali, I.H.; Vuggili, S.B.; Kakodiya, S.D.; Solanki, M.K.; Yadav, K.K.; Ahn, Y.; Yadav, S.; Islam, S.; et al. 2D Personality of Multifunctional Carbon Nitrides towards Enhanced Catalytic Performance in Energy Storage and Remediation. Appl. Sci. 2022, 12, 3753. [Google Scholar] [CrossRef]
  43. Yadav, V.K.; Suriyaprabha, R.; Inwati, G.K.; Gupta, N.; Singh, B.; Lal, C.; Kumar, P.; Godha, M.; Kalasariya, H. A Noble and Economical Method for the Synthesis of Low Cost Zeolites from Coal Fly Ash Waste. Adv. Mater. Process. Technol. 2021, 1–19. [Google Scholar] [CrossRef]
  44. Phys, J.A. Photoluminescence via plasmon resonance energy transfer in silver nanocomposite glasses. J. Appl. Phys. 2008, 104, 054313. [Google Scholar] [CrossRef]
  45. Su, C.; Huang, K.; Li, H.-H.; Lu, Y.-G.; Zheng, D.-L. Antibacterial Properties of Functionalized Gold Nanoparticles and Their Application in Oral Biology. J. Nanomater. 2020, 2020, 5616379. [Google Scholar] [CrossRef]
  46. Yuan, X.; Setyawati, M.I.; Tan, A.S.; Ong, C.N.; Leong, D.; Xie, J. Highly luminescent silver nanoclusters with tunable emissions: Cyclic reduction–decomposition synthesis and antimicrobial properties. NPG Asia Mater. 2013, 5, e39. [Google Scholar] [CrossRef]
  47. Saha, B.; Bhattacharya, J.; Mukherjee, A.; Ghosh, A.; Santra, C.; Dasgupta, A.K.; Karmakar, P. In Vitro Structural and Functional Evaluation of Gold Nanoparticles Conjugated Antibiotics. Nanoscale Res. Lett. 2007, 2, 614–622. [Google Scholar] [CrossRef]
  48. Fan, Y.; Tan, X.; Ou, X.; Lu, Q.; Chen, S.; Wei, S. A novel “on-off” electrochemiluminescence sensor for the detection of concanavalin A based on Ag-doped g-C 3 N 4. Electrochim. Acta 2016, 202, 90–99. [Google Scholar] [CrossRef]
  49. Khan, M.E.; Han, T.H.; Khan, M.M.; Karim, M.R.; Cho, M.H. Environmentally Sustainable Fabrication of Ag@g-C3N4 Nanostructures and Their Multifunctional Efficacy as Antibacterial Agents and Photocatalysts. ACS Appl. Nano Mater. 2018, 1, 2912–2922. [Google Scholar] [CrossRef]
  50. Li, X.; Zhu, L.; Zhou, Y.; Yin, H.; Ai, S. Enhanced Photoelectrochemical Method for Sensitive Detection of Protein Kinase A Activity Using TiO2/g-C3N4, PAMAM Dendrimer, and Alkaline Phosphatase. Anal. Chem. 2017, 89, 2369–2376. [Google Scholar] [CrossRef]
  51. Chan, M.-H.; Liu, R.-S.; Hsiao, M. Graphitic carbon nitride-based nanocomposites and their biological applications: A review. Nanoscale 2019, 11, 14993–15003. [Google Scholar] [CrossRef] [PubMed]
  52. Feng, L.; He, F.; Dai, Y.; Liu, B.; Yang, G.; Gai, S.; Niu, N.; Lv, R.; Li, C.; Yang, P. A Versatile Near Infrared Light Triggered Dual-Photosensitizer for Synchronous Bioimaging and Photodynamic Therapy. ACS Appl. Mater. Interfaces 2017, 9, 12993–13008. [Google Scholar] [CrossRef] [PubMed]
  53. Sun, Y.-P.; Ha, W.; Chen, J.; Qi, H.-Y.; Shi, Y.-P. Advances and applications of graphitic carbon nitride as sorbent in analytical chemistry for sample pretreatment: A review. TrAC Trends Anal. Chem. 2016, 84, 12–21. [Google Scholar] [CrossRef]
  54. Guo, H.; Su, Y.; Shen, Y.; Long, Y.; Li, W. In situ decoration of Au nanoparticles on carbon nitride using a single-source precursor and its application for the detection of tetracycline. J. Colloid Interface Sci. 2019, 536, 646–654. [Google Scholar] [CrossRef] [PubMed]
  55. You, C.; Han, C.; Wang, X.; Zheng, Y.; Li, Q.; Hu, X.; Sun, H. The progress of silver nanoparticles in the antibacterial mechanism, clinical application and cytotoxicity. Mol. Biol. Rep. 2012, 39, 9193–9201. [Google Scholar] [CrossRef]
  56. Mane, G.P.; Dhawale, D.S.; Anand, C.; Ariga, K.; Ji, Q.; Wahab, M.A.; Mori, T.; Vinu, A. Selective sensing performance of mesoporous carbon nitride with a highly ordered porous structure prepared from 3-amino-1,2,4-triazine. J. Mater. Chem. A 2013, 1, 2913–2920. [Google Scholar] [CrossRef]
  57. Wahab, A.; Hasan, C.M.; Alothman, Z.A.; Hossain, S.A. In-situ incorporation of highly dispersed silver nanoparticles in nanoporous carbon nitride for the enhancement of antibacterial activities. J. Hazard. Mater. 2021, 408, 124919. [Google Scholar] [CrossRef]
  58. Bing, W.; Chen, Z.; Sun, H.; Shi, P.; Gao, N.; Ren, J.; Qu, X. Visible-light-driven enhanced antibacterial and biofilm elimination activity of graphitic carbon nitride by embedded Ag nanoparticles. Nano Res. 2015, 8, 1648–1658. [Google Scholar] [CrossRef]
  59. Bhowmik, T.; Kundu, M.K.; Barman, S. Ultra small gold nanoparticles–graphitic carbon nitride composite: An efficient catalyst for ultrafast reduction of 4-nitrophenol and removal of organic dyes from water. RSC Adv. 2015, 5, 38760–38773. [Google Scholar] [CrossRef]
  60. Lou-Franco, J.; Das, B.; Elliott, C.; Cao, C. Gold Nanozymes: From Concept to Biomedical Applications; Springer: Singapore, 2021. [Google Scholar] [CrossRef]
  61. Agasti, S.S.; Chompoosor, A.; You, C.-C.; Ghosh, P.; Kim, C.K.; Rotello, V.M. Photoregulated Release of Caged Anticancer Drugs from Gold Nanoparticles. J. Am. Chem. Soc. 2009, 131, 5728–5729. [Google Scholar] [CrossRef]
  62. Faisal, M.; Jalalah, M.; Harraz, F.A.; El-Toni, A.M.; Al-Assiri, A.K.M.S. Au nanoparticles-doped g-C3N4 nanocomposites for enhanced photocatalytic performance under visible light illumination. Ceram. Int. 2020, 46, 22090–22101. [Google Scholar] [CrossRef]
  63. Yadav, V.K.; Yadav, K.K.; Gacem, A.; Gnanamoorthy, G.; Ali, I.H.; Khan, S.H.; Jeon, B.-H.; Kamyab, H.; Inwati, G.K.; Islaml, S.; et al. A novel approach for the synthesis of vaterite and calcite from incense sticks ash waste and their potential for remediation of dyes from aqueous solution. Sustain. Chem. Pharm. 2022, 29, 100756. [Google Scholar] [CrossRef]
  64. Inwati, G.; Rao, Y.; Singh, M. Single step aqueous synthesis of unsupported PtNi nanoalloys using flower extract as reducing agent and their compositional role to enhance electrocatalytic activity. AIP Conf. Proc. 2017, 1837, 040048. [Google Scholar] [CrossRef]
  65. Yadav, V.K.; Choudhary, N.; Ali, D.; Gnanamoorthy, G.; Inwati, G.K.; Almarzoug, M.H.; Kumar, G.; Khan, S.H.; Solanki, M.B. Experimental and Computational Approaches for the Structural Study of Novel Ca-Rich Zeolites from Incense Stick Ash and Their Application for Wastewater Treatment. Adsorpt. Sci. Technol. 2021, 2021, 6066906. [Google Scholar] [CrossRef]
  66. Yadav, V.K.; Gnanamoorthy, G.; Cabral-Pinto, M.M.S.; Alam, J.; Ahamed, M.; Gupta, N.; Singh, B.; Choudhary, N.; Inwati, G.K.; Yadav, K.K. Variations and similarities in structural, chemical, and elemental properties on the ashes derived from the coal due to their combustion in open and controlled manner. Environ. Sci. Pollut. Res. 2021, 28, 32609–32625. [Google Scholar] [CrossRef]
  67. Qiu, G.; Gai, Z.; Lanja, S.; Jiukai, T.; Ting, G.; Kullak-Ublick, G.A.; Wang, J. Thermo-plasmonic-Assisted Cyclic Cleavage Amplification for Self-Validating Plasmonic Detection of SARS-CoV-2. ACS Nano 2021, 15, 7536–7546. [Google Scholar] [CrossRef]
  68. Qiu, G.; Gai, Z.; Tao, Y.; Schmitt, J.; Kullak-Ublick, G.A.; Wang, J. Dual-Functional Plasmonic Photothermal Biosensors for Highly Accurate Severe Acute Respiratory Syndrome Coronavirus 2 Detection. ACS Nano 2020, 14, 5268–5277. [Google Scholar] [CrossRef] [Green Version]
Crystals 12 01213 g001 550
Figure 1. UV-Vis absorption spectra (SPR) of AgAu (0.5:0.5) concentration.
Figure 1. UV-Vis absorption spectra (SPR) of AgAu (0.5:0.5) concentration.
Crystals 12 01213 g001
Crystals 12 01213 g002 550
Figure 2. LSPR bands of the Au NPs with different sizes (a) SPR of Ag NPs, (b) SPR bands for Au NPs [34,35].
Figure 2. LSPR bands of the Au NPs with different sizes (a) SPR of Ag NPs, (b) SPR bands for Au NPs [34,35].
Crystals 12 01213 g002
Crystals 12 01213 g003 550
Figure 3. TEM images of Au and Ag loaded g-C3N4 nanomaterials (A,B) [40].
Figure 3. TEM images of Au and Ag loaded g-C3N4 nanomaterials (A,B) [40].
Crystals 12 01213 g003
Crystals 12 01213 g004 550
Figure 4. XPS analysis of AuAg loaded g-C3N4 nanomaterials (a). XPS Full survey, high-resolution of C 1s (b), N 1s (c), O 1s (d), Au 4f (e) and Ag 3d (f) [40].
Figure 4. XPS analysis of AuAg loaded g-C3N4 nanomaterials (a). XPS Full survey, high-resolution of C 1s (b), N 1s (c), O 1s (d), Au 4f (e) and Ag 3d (f) [40].
Crystals 12 01213 g004
Crystals 12 01213 g005 550
Figure 5. The functionalized Ag-g-C3N4 and PANI-PTCA-DexP-GOD for the ECL biosensor [48].
Figure 5. The functionalized Ag-g-C3N4 and PANI-PTCA-DexP-GOD for the ECL biosensor [48].
Crystals 12 01213 g005
Crystals 12 01213 g006 550
Figure 6. Ag NPs doped CN, (a) SBA15 silica substrate; (b) Ag and C-N with SBA15 silica; (c) Ag doped C-N; (d) Ag doped porous CN; and (e) Inhibitory action against MDR E. coli. [57].
Figure 6. Ag NPs doped CN, (a) SBA15 silica substrate; (b) Ag and C-N with SBA15 silica; (c) Ag doped C-N; (d) Ag doped porous CN; and (e) Inhibitory action against MDR E. coli. [57].
Crystals 12 01213 g006
Crystals 12 01213 g007 550
Figure 7. Antibacterial studies of g-C3N4, Ag NPs: g-C3N4 or Ag/g-C3N4 against (a) E. coli and (b) S. aureus.
Figure 7. Antibacterial studies of g-C3N4, Ag NPs: g-C3N4 or Ag/g-C3N4 against (a) E. coli and (b) S. aureus.
Crystals 12 01213 g007
Table
Table 1. Metal based CNs biomaterials for medical uses [51].
Table 1. Metal based CNs biomaterials for medical uses [51].
Metal IonsTargeted BiomoleculesDetection ProceduresYears
Au/CuSudan Ilectrochemiluminescence2018
Au NPsDNAElectro-chemiluminescence2018
ZnOe (SMZ)Electrochemiluminescence2018
Au/GoxGlucoseElectro-chemiluminescence2017
Cu NPsDNAElectrochemiluminescent2017
Palladium (Pd)OPs and HupAElectrochemiluminescence2016
Au NPsLactateElectro-chemiluminescence2014
Ag NPsGlutathione Persistent-luminescence2013
Table
Table 2. Metal-based biosensors for biomedical applications [60].
Table 2. Metal-based biosensors for biomedical applications [60].
TargetsNanomaterialActivitiesOutputsSamples
SARS-CoV-2Au NPsN geneElectrochemicalCoronaviruses infectious Human
Cu2+ and histidineAu nanoclustersPeroxidaseColourimetricHuman serum blood
Placental cellderived exosomesAu doped Fe2O3 nanocubesPeroxidaseColourimetric, electrochemicalCell culture media 8
SpermineAg–Au NP Oxidase, PeroxidaseFluorescenceUrine
DopamineAu nanoclustersPeroxidaseFluorescence, colourimetricPC12 cells
Pseudomonas aeruginosaAu NPsPeroxidaseElectrochemicalDrinking water
Heparine and heparinaseAu nanoclustersPeroxidaseColourimetricDiluted serum
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Gacem, A.; Rajendran, S.; Hasan, M.A.; Kakodiya, S.D.; Modi, S.; Yadav, K.K.; Awwad, N.S.; Islam, S.; Park, S.; Jeon, B.-H. Plasmon Inspired 2D Carbon Nitrides: Structural, Optical and Surface Characteristics for Improved Biomedical Applications. Crystals 2022, 12, 1213. https://doi.org/10.3390/cryst12091213

AMA Style

Gacem A, Rajendran S, Hasan MA, Kakodiya SD, Modi S, Yadav KK, Awwad NS, Islam S, Park S, Jeon B-H. Plasmon Inspired 2D Carbon Nitrides: Structural, Optical and Surface Characteristics for Improved Biomedical Applications. Crystals. 2022; 12(9):1213. https://doi.org/10.3390/cryst12091213

Chicago/Turabian Style

Gacem, Amel, Suriyaprabha Rajendran, Mohd Abul Hasan, Shakti Devi Kakodiya, Shreya Modi, Krishna Kumar Yadav, Nasser S Awwad, Saiful Islam, Sungmin Park, and Byong-Hun Jeon. 2022. "Plasmon Inspired 2D Carbon Nitrides: Structural, Optical and Surface Characteristics for Improved Biomedical Applications" Crystals 12, no. 9: 1213. https://doi.org/10.3390/cryst12091213

APA Style

Gacem, A., Rajendran, S., Hasan, M. A., Kakodiya, S. D., Modi, S., Yadav, K. K., Awwad, N. S., Islam, S., Park, S., & Jeon, B.-H. (2022). Plasmon Inspired 2D Carbon Nitrides: Structural, Optical and Surface Characteristics for Improved Biomedical Applications. Crystals, 12(9), 1213. https://doi.org/10.3390/cryst12091213

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.