Chromium–aluminum nitride (CrAlN) coatings were deposited on polished H13 tool steel substrates using direct current (DC) magnetron sputtering. The Cr/Al composition in the target was varied by inserting either four or eight chromium (Cr) plugs into cavities machined into an aluminum (Al) plate target. Nitrogen was introduced as a reactive gas to facilitate the formation of the nitride phase. Coatings were deposited at substrate bias voltages of −30 V, −50 V, and −60 V to study the combined effects of composition and ion energy on coating properties. Compositional analysis of coatings deposited at a −50 V bias revealed Cr/Al ratios of approximately 0.8 and 1.7 for the 4- and 8-plug configurations, respectively. This increase in the Cr/Al ratio led to a 2.6-fold improvement in coating hardness. Coatings produced using the eight-Cr-plug target exhibited a nearly linear increase in hardness with increasing substrate bias voltage. Cross-sectional scanning electron microscopy revealed a uniform bilayer structure consisting of an approximately 0.5 µm metal interlayer beneath a 2–3 µm CrAlN coating. Surface morphology analysis indicated the presence of coarse microdroplets in coatings with the lower Cr/Al ratio. These microdroplets were significantly suppressed in coatings with higher Cr/Al content, especially at increased bias voltages. This suppression is likely due to enhanced ion bombardment associated with the increased Cr content, attributed to Cr’s relatively higher atomic mass compared to Al. Coatings with lower hardness exhibited greater scratch resistance, likely due to the influence of residual compressive stresses. The findings highlight the critical role of both Cr/Al content and substrate bias in tailoring the tribo-mechanical performance of PVD CrAlN coatings for wear-resistant applications. Full article

In recent years, significant attention has been directed toward the development of coating materials capable of tailoring surface properties for various functional applications. Transition metal nitrides, in particular, have garnered interest due to their superior physical and chemical properties, including high hardness, excellent wear resistance, and strong corrosion resistance. In this study, a fabrication process for CrN-based thin films was developed by combining reactive direct current magnetron sputtering (dcMS) with post-deposition annealing in air. CrN coatings were deposited by reactive dcMS using different argon-nitrogen (Ar:N₂) gas ratios (4:1, 3:1, 2:1, and 1:1), followed by annealing at 550 °C for 1.5 h in ambient air. XRD and EDS analysis revealed that this treatment results in the formation of a composite phase comprising CrN and Cr₂O₃. The resulting coating exhibited favorable mechanical and tribological properties, including a maximum hardness of 12 GPa, a low wear coefficient of 0.254 and a specific wear rate of 7.05 × 10⁻⁶ mm³/N·m, making it a strong candidate for advanced protective coating applications. Full article

Nanostructured multilayer anticorrosion coatings offer an effective strategy to mitigate the poor corrosion resistance of aluminum alloys and extend their service life. In this study, four types of Ti/Cr multilayer coatings with varied modulation periods along the growth direction were deposited on 7050 aluminum alloy substrates using direct current magnetron sputtering. The cross-sectional microstructure of the coatings was characterized by scanning electron microscopy (SEM), while their mechanical and corrosion properties were systematically evaluated through nanoindentation and electrochemical measurements. The influence of modulation period distribution on the corrosion resistance of Ti/Cr multilayers was thoroughly investigated. The results show that the average thickness of the Ti/Cr multilayer coatings is 680 nm, the structure is dense, and the coarse columnar crystals are not seen. All Ti/Cr multilayer coatings significantly reduced the corrosion current density of 7050 aluminum alloy by about 10 times compared with that of the substrate, showing good protective effect. Modulation period along the coating growth direction decreases the Ti/Cr multilayer coating surface heterogeneous interface density increases, inhibits the formation of corrosion channels, hindering the penetration of corrosive media, and the other three coatings and aluminum alloy compared to its corrosion surface did not see obvious pore corrosion, showing the most excellent corrosion resistance. Full article

Limited hardness and corrosion resistance restrict 7050 aluminum alloys in aggressive environments. Cr coatings, applied as single layers or over Ti, Al, or Ni buffer layers, were deposited onto 7050 aluminum alloy by direct-current magnetron sputtering; their microstructure, adhesion, mechanical properties, and corrosion behavior were examined. The results indicate that introducing a buffer layer significantly enhances the bonding strength between a Cr coating and an aluminum alloy substrate, with the Ni buffer layer exhibiting the highest bonding strength, nearly three times that of the Cr coating alone. Furthermore, the buffer layer influences the mechanical properties of the Cr coatings, with Ni/Cr and Al/Cr coatings demonstrating increased hardness and elastic modulus. The Ni/Cr coating achieved the highest values of 3.95 GPa and 62.09 GPa, respectively. Regarding corrosion performance, The Cr coatings containing buffer layers showed markedly better corrosion resistance than the bare 7050 Al alloy. A compact Cr₂O₃ passive film formed on their surfaces, cutting the corrosion current density by roughly two orders of magnitude. Among all samples, the Ti/Cr coating performed best, registering the lowest current density (1.687 × 10⁻⁶ A cm⁻²) and the highest charge-transfer resistance (6090 Ω cm²). Full article

Hydrogenated amorphous carbon (a-C:H) films are widely valued for their excellent mechanical strength and low friction, but their performance significantly degrades at elevated temperatures, limiting practical applications in aerospace environments. In this work, we aimed to enhance the high-temperature tribological behavior of a-C:H films through controlled silicon (Si) doping. A series of a-C:H:Si films with varying Si contents were fabricated via direct current magnetron sputtering, and their microstructure, mechanical properties, and friction behavior were systematically evaluated from room temperature up to 400 °C. Results show that moderate Si doping (8.3 at.%) substantially enhances hardness and wear resistance, while enabling ultralow friction (as low as 0.0034) at 400 °C. This superior performance is attributed to the synergistic effects of transfer layer formation, preferential Si oxidation, and tribo-induced graphitization. This study provides new insights into the high-temperature lubrication mechanisms of Si-doped a-C:H films and demonstrates the critical role of Si content optimization, highlighting a viable strategy for extending the thermal stability and lifespan of solid-lubricating films. Full article

Cotton, commonly used in wound care, has limitations such as quick saturation and wound adhesion, prompting surface modifications. In our studies, iron, which promotes platelet aggregation and coagulation, was deposited onto cotton via direct current (DC) magnetron sputtering. Thus, the biochemical properties of cotton fabrics were enhanced. Microscopic analyses revealed uniform iron coating on the fibers, and biochemical tests, such as activated partial thromboplastin time (aPTT) and prothrombin time (PT), showed that the modification did not affect the material’s coagulation activity. Measurements with the thiobarbituric acid (TBA) method (TBARS) showed that iron-modified cotton had antioxidant activity by lowering lipid peroxidation, which can be beneficial for better wound healing and lower infection risk. Moreover, our analysis showed the absence of cyto- and genotoxic properties against normal peripheral blood mononuclear cells (PBM cells). It was found that tested fabrics did not directly interact with DNA. Full article

Non-hydrogenated diamond-like carbon (DLC) films and molybdenum-doped diamond-like carbon (Mo-DLC) films were deposited by direct current magnetron sputtering. The formation was carried out on Si (100) wafers. The influence of molybdenum concentration and deposition temperature on the surface morphology, chemical composition, type of chemical bonds, friction force at nanoscale, and nanohardness of the DLC coatings were investigated by atomic force microscopy (AFM), energy dispersive X-ray spectroscopy (EDX), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, and nanoindenter, respectively. The concentration of molybdenum in the films varies from 1.2 at.% to 10.3 at.%. The increase in molybdenum content promotes the graphitization of DLC films, lowering the sp³ site fraction and increasing the oxygen content, which contributes to the reduction in nanohardness (by 21%) of the DLC films. The decrease in the synthesis temperature from 235 °C to 180 °C enhanced the oxygen amount up to 20.4 at.%. The sp³ site fraction and nanohardness of the Mo-DLC films were enhanced with the reduction in the deposition temperature. The film deposited at a substrate temperature of 235 °C exhibited the lowest friction coefficient (CoF) of 0.03, where its molybdenum concentration was 1.2 at.%. The decline in the synthesis temperature increased the CoF of the Mo-DLC films up to seven times. Full article

To increase the wear and corrosion resistance of (α + β) titanium-aluminium-vanadium (Ti6Al4V) alloy, ceramic tantalum oxide coatings were deposited by direct current (DC) magnetron sputtering at three different substrate temperatures—400, 450, and 500 °C. The crystallographic structure, surface morphology, chemical compositions, film adhesion, and hardness of the coatings were described using XRD, SEM, EDS, scratch tests, and microhardness measurements. The samples’ ability to withstand corrosion was assessed using electrochemical studies. Results revealed that thin films have an amorphous or crystalline structure dependent on temperature. The film’s thicknesses varied between 560 and 600 nm. With the increase in deposition temperature, the hardness of the film rose. All oxide coatings were tightly adherent to the titanium alloy substrate, and critical force increased from about 8.6 up to 20 N when the temperature rose from 400 to 500 °C. During the polarisation investigations, after 1 h of immersion, a drop in current density (j_corr) verified an improvement in the corrosion resistance of the amorphous and well-crystalline coatings. A two-layer model of the surface film accurately describes the coated systems’ electrochemical behaviour. However, according to the EIS analysis, the well-crystalline film deteriorates greatly, whereas the amorphous film prevents penetration during the 7-day immersion test in SBF. The wettability tests demonstrated the hydrophilic nature of the coatings, and after seven days, the mineralisation of calcium phosphate proves the coatings become bioactive in simulated bodily fluid (SBF). Thus, we produced films of tantalum oxide, which, with the proper deposition parameters, may prove to be appropriate surfaces for titanium-based implant bio-applications. Full article

Transition metal dichalcogenide coatings have emerged as potential candidates for terrestrial and aerospace mobility applications. Among these, the alloyed MoSe₂ coatings have displayed promising results while sliding in diverse environments. N-alloyed Mose₂ coatings provide the additional benefit of overcoming the impact of PVD compositional variations on dry sliding, making them promising solid lubricants for mobility-sector applications. However, the impact of long-term storage has never been investigated for this rarely studied solid-lubricant system. This study investigates the tribological performance of direct current magnetron sputtered MoSeN coatings after 40 months of storage in an ambient atmosphere. Sliding tests were conducted under conditions consistent with pre-storage conditions. The results showed that coatings with 0 at. %, 22 at. %, 33 at. %, and 35 at. % N-alloying exhibited COF values nearly identical to the pre-storage results, with only a negligible increase in ~0.01. Similarly, all coatings displayed specific wear rates in the range of 10⁻⁷, aligning with earlier findings. The obtained results show that the sliding performance of MoSeN coatings does not deteriorate over time, highlighting their suitability for critical aerospace applications, where components and assembled parts may be stored for years before launching into space or in actual applications. Full article

In this study, four various titanium dioxide/cuprum oxide (TiO₂/Cu_xO) photovoltaic structures deposited on glass/indium tin oxide (ITO) substrates using the direct-current (DC) reactive magnetron sputtering technique were annealed in air. In our previous work, the deposition parameters for different buffer layer configurations were first optimized to enhance cell fabrication efficiency. In this paper, the effects of post-deposition annealing at 150 °C in air on the optical properties and I-V characteristics of the prepared structures were examined. As a result, significant changes in optical properties and a meaningful improvement in performance in comparison to unannealed cells were observed. Air annealing led to an increase in the reflection coefficient of the TiO₂ layer for three out of four structures. A similar increase in the reflection of the Cu_xO layer occurred after heating for two out of four structures. Transmission of the TiO₂/Cu_xO photovoltaic structures also increased after heating for three out of four samples. For two structures, changes in both transmission and reflection resulted in higher absorption. Moreover, annealing the as-deposited structures resulted in a maximum relative increase in open-circuit voltage (V_oc) by 294% and an increase in short-circuit current (I_sc) by 1200%. The presented article gives some in-depth analysis of these reported changes in character and origin. Full article

Protection against microbiologically influenced corrosion (MIC) is critical for materials used in aquatic environments, as MIC accelerates material degradation and leads to faster structural failure. Copper (Cu) has the potential to substantially improve the MIC resistance in alloys. In this study, high-entropy alloy (HEA) coatings containing Cu were deposited using DC (Direct Current) magnetron sputtering to enhance the corrosion resistance and mechanical properties of various substrates. Two CuCrFeMnNi HEA compositions in the form of bulk alloys and PVD (Physical Vapor Deposition) coatings, with 5% and 10% Cu, were analyzed for their microstructural, mechanical, and anticorrosive characteristics. Deposition parameters were varied to select the optimal values. Microstructural evaluations using SEM-EDS (scanning electron microscopy and energy dispersive X-ray spectroscopy), XRD (X-ray diffraction), and AFM (atomic force microscopy) revealed uniform, dense coatings with good adhesion composed of dendritic and interdendritic BCC (body-centered cubic) and FCC (face centered cubic) structures, respectively. Microhardness tests indicated improved mechanical properties for the samples coated with developed HEAs. The coatings exhibited improved corrosion resistance in NaCl solution, the 10% Cu composition displaying the highest polarization resistance and lowest corrosion rate. These findings suggest that Cu-containing HEA coatings are promising candidates for applications requiring enhanced corrosion protection. Full article

To improve the friction performance and service life of protective coatings in humidity-fluctuating environments, porous hard titanium nitride (TiN)–molybdenum disulfide (MoS₂) composite coatings were prepared by using direct current magnetron sputtering (DCMS) with the mode of oblique angle deposition (OAD) and chemical vapor deposition (CVD) technologies. The structure and chemical component were characterized by field emission scanning electron microscopy (FESEM), energy dispersive spectrometer (EDS), grazing incidence X-ray diffraction (GIXRD), atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), and Raman spectroscopy. The tribological properties of these TiN–MoS₂ composite coatings were investigated. The results indicate that the porous TiN–MoS₂ composite coating exhibited outstanding friction performance and long service life under humidity-fluctuating environments. At the initial 20% relative humidity (RH) stage, the MoS₂ on the porous TiN–MoS₂ composite coating surface worked as an effective lubricant; thus, the coating demonstrated excellent lubrication performance, and the friction coefficient (COF) was about 0.05. As the humidity was alternated to 70% RH, the lubrication effect diminished due to the production of molybdenum oxide (MoO₃), and the COF was about 0.2, which was attributed to the degradation of MoS₂ on the wear track and the release of fresh MoS₂ from the porous TiN matrix. After the environmental conditions shifted from 70% to 20% RH, the MoO₃ was removed, and the lubrication effect was restored. In summary, TiN–MoS₂ porous composite coating offers a promising approach for lubrication in humidity-fluctuating environments. Full article

This study investigates the chemical and structural modifications of vertically aligned tungsten disulfide–tungsten trioxide (WS₂-WO₃) nanosheets decorated with silver nanoparticles (Ag(NPs)) under nitrogen plasma conditions. The synthesized vertically aligned WS₂-WO₃ nanosheets were functionalized through direct-current (DC) magnetron sputtering, forming silver-decorated samples. Structural changes, as well as the size and distribution of Ag(NPs), were characterized using scanning electron microscopy (SEM). Chemical state analysis was conducted via X-ray photoelectron spectroscopy (XPS), while Raman spectroscopy was employed to investigate vibrational modes. The findings confirmed the successful decoration of Ag(NPs) and identified unexpected compound transformations that were dependent on the duration of functionalization. The synthesized and functionalized samples were evaluated for their sensing capabilities towards Rhodamine B (RhB) through surface-enhanced resonance Raman scattering (SERRS). This study discusses the impact of substrate morphology and the shape and size of nanoparticles on the enhancement of SERRS mechanisms, achieving an enhancement factor (EF) of approximately 1.6 × 10⁶ and a limit of detection (LOD) of 10⁻⁹ M. Full article

Graphene/CNT layers were deposited onto platinum electrodes of an interdigitated sensor using radio-frequency magnetron sputtering. The graphene/CNTs were synthesized in an Argon atmosphere at a pressure of (2 × 10⁻²–5 × 10⁻³) mbar, with the substrate maintained at 300 °C either through continuous heating with an electronically controlled heater or by applying a −200 V bias using a direct current power supply throughout the deposition process. The study compares the surface morphology, carbon atom arrangement within the layer volumes, and electrical properties of the films as influenced by the different methods of substrate heating. X-ray diffraction and Raman spectroscopy confirmed the formation of CNTs within the graphene matrix. Additionally, scanning electron microscopy revealed that the carbon nanotubes are aligned and organized into cluster-like structure. The graphene/CNT layers produced at higher pressures present exponential I–V characteristics that ascertain the semiconducting character of the layers and their suitability for applications in gas sensing. Full article

Molybdenum disulfide is a 2D material with excellent lubricant properties, resulting from weak van der Waals forces between lattice layers and shear-induced crystal orientation. The low forces needed to shear the MoS₂ crystal layers grant the tribological system low coefficients of friction (COF). However, film oxidation harms its efficacy in humid atmospheres, leading to an increased COF and poor surface adhesion, making its use preferable in dry or vacuum conditions. To overcome these challenges, doping MoS₂ with elements such as Nb, Ti, C, and N emerges as a promising solution. Nevertheless, the adhesion of these coatings to a steel substrate presents challenges and strategies involving the reduction in residual stresses and increased chemical affinity to the substrate by using niobium-based materials as interlayers. In this study, Nb-doped MoS₂ films were deposited on H13 steel and silicon wafers using the pulsed direct current balanced magnetron sputtering technique. Different niobium-based interlayers (pure Nb and NbN) were deposited to evaluate the adhesion properties of Nb-doped MoS₂ coatings. Unlubricated scratch tests, conducted at room temperature and relative humidity under a progressive load, were performed to analyze the COF and adhesion of the coating. Instrumented indentation tests were conducted to assess the hardness and elastic modulus of the coatings. The microstructure of the coatings was obtained by Scanning Electron Microscopy (SEM), Scanning Transmission Electron Microscopy (STEM), and Transmission Electron Microscopy (TEM), with Energy-Dispersive X-Ray Spectroscopy (EDS). Results indicated that niobium doping on MoS₂ coatings changes the structure from crystalline to amorphous. Additionally, the Nb concentration of the Nb:MoS₂ coating changed the mechanical properties, leading to different cohesive failures by different loads during the scratch tests. Results have also indicated that an NbN interlayer optimally promoted the adhesion of the film. This result is justified by the increase in hardness led by higher Nb concentrations, enhancing the load-bearing capacity of the coating. It is concluded that niobium-based materials can be used to enhance the adhesion properties of Nb-doped MoS₂ films and improve their tribological performance. Full article