Search Results (9)

Bioceramic materials for endodontic treatments have gradually transformed over the years into materials with enhanced biocompatibility and chemical and mechanical properties compared to earlier generations. In endodontics procedures, these materials are used as restorative material in applications such as root-end fillings, pulp capping, perforations repair, and apexification repair procedures. However, they have far from ideal mechanical and handling properties, biocompatibility issues, aesthetic concerns due to tooth discolouration, limited antibacterial activity, and affordability, which are amongst several key limitations. Notably, bioceramic materials are popular due to their biocompatibility, sealing ability, and durability, consequently surpassing traditional materials such as gutta-percha and zinc oxide–eugenol sealers. A lack of recent advancements in the field, combined with nanomaterials, has improved the formulations of these materials to overcome these limitations. The existing literature emphasises the benefits of bioceramics while underreporting their poor mechanical properties, handling difficulties, cost, and various other drawbacks. The key gaps identified in the literature are the insufficient coverage of emerging materials, narrow scope, limited insights into future developments, and underreporting of failures and complications of the existing materials. Consequently, this review aims to highlight the key limitations of various endodontic materials, primarily focusing on calcium silicate, calcium phosphate, and bioactive glass-based materials, which are the most abundantly used materials in dentistry. Based on the literature, bioceramic materials in endodontics have significantly improved over recent years, with different combinations of materials and technology compared to earlier generations while preserving many of their original properties, with some having affordable costs. This review also identified key innovations that could shape the future of endodontic materials, highlighting the ongoing evolution and advancements in endodontic treatments. Full article

A prospective observational case series included six patients who presented with discoloured upper and lower teeth extending from the right second premolar to the left second premolar. The photoactivation dosimetry and treatment protocol were as follows: λ 450 nm, 1 W, CW; flattop beam profile; 1 cm²; 15 J/spot; 10 irradiated spots; an irradiation time of 15 s/spot; three whitening cycles in a single session. Blanc One ULTRA⁺ was the bleaching agent. A visual analogue scale (VAS) was utilised to evaluate the pain intensity and dental hypersensitivity during treatment immediately after complete treatment (T1), 24 h (T2), and 8 h (T3) postoperatively, and at an 8-month follow-up timepoint (T4), whereas the dental colour shade change was assessed using the VITA colour shade guide pre-treatment (T0), T1, and T4. The Gingival index and modified Wong Baker faces scale were utilised to evaluate gingival inflammation and patients’ treatment satisfaction, respectively. Our findings revealed a reduction in the dental colour shade of the six cases between 2 and 10- fold (average of 3.5-fold) at T1 and maintained at T4, indicating significant improvement in the colour shade change with optimal outcomes. The percentage of this improvement for all the patients was ranged between 16.6% and 33.3%. At all timepoints, a “0” score was provided for pain intensity, dental hypersensitivity, and gingival inflammation. Our study demonstrates the feasibility and safety of a λ 450 nm laser delivered with a flattop handpiece to achieve optimal whitening outcomes without adverse effects. This offers a useful guide for dental clinicians for vital in-office tooth whitening. Extensive clinical studies with large data are warranted to validate our study protocol. Full article

Topical cariostatic agents have become a reasonable alternative for managing dental caries in young children. Silver diamine fluoride (SDF) is a practical topical approach to arrest caries and avoid extensive and risky dental treatment. However, the literature demonstrates a parental hesitation towards accepting SDF because of black unaesthetic tooth discolouration following application. The rapid oxidation of ionic silver darkens demineralised tooth structure permanently. In this regard, nano-metallic antimicrobials could augment or substitute for silver, and thereby enhance SDF aesthetic performance. Recently, biomedical research has drawn attention to selenium nanoparticles (SeNPs) due to their antimicrobial, antioxidant, and antiviral potencies. Various in vitro studies have examined the effect of SeNPs on the virulence of bacteria. This narrative review explores practical issues when using SDF and suggests future directions to develop it, focusing on antimicrobial metals. Several methods are described that could be followed to reduce the discolouration concern, including the use of nanoparticles of silver, of silver fluoride, or of selenium or other metals with antimicrobial actions. There could also be value in using remineralising agents other than fluoride, such as NPs of hydroxyapatite. There could be variations made to formulations in order to lower the levels of silver and fluoride in the SDF or even to replace one or both of the silver and fluoride components completely. Moreover, since oxidation processes appear central to the chemistry of the staining, adding SeNPs which have antioxidant actions could have an anti-staining benefit; SeNPs could be used for their antimicrobial actions as well. Future research should address the topic of selenium chemistry to optimise how SeNPs would be used with or in place of ionic silver. Incorporating other antimicrobial metals as nanoparticles should also be explored, taking into account the optimal physicochemical parameters for each of these. Full article

To quantify the discolouration of the temporary acetal resins in vivo, based on the weeks of follow-up and the salivary pH in the three thirds of the tooth. To find out if the final CIELAB coordinates can be predicted from the initial colour coordinates, the salivary pH, the situation (in thirds) and the weeks of follow-up. Colour coordinates (L, C, and h) were recorded by spectrophotometry in 13 participants fitted with hybrid provisional complete dentures made of acetal resin. Colour recordings were made on the day of placement and after several weeks of follow-up (6 to 31 weeks). Salivary pH was also measured as a predictor variable for colour change. The ANOVA statistical test and regression models have been used. The highest colour difference according to ∆Eab* was 27.46 units after 15 weeks of follow-up and the lowest was 7.34 units after 17 weeks of follow-up. Neither in the cervical nor in the middle third any regressor variable (initial L*, initial C*, initial h*, salivary pH and weeks of follow-up) was able to significantly predict any of the final colour coordinates (p > 0.05). The colour change of the temporary acetal resins used exceeds the threshold of clinical acceptability, and it is not acceptable to maintain satisfactory aesthetics. The weeks of follow-up and the salivary pH are not capable of satisfactorily predicting the final color coordinates of the acetal resins. Full article

Discolouration resulting from regenerative endodontic procedures may have a negative impact on the quality of life of treated patients; therefore, it is recommended to minimize this risk by selecting appropriate scaffolds and barrier materials, and if discolouration occurs, the use of a simple, cost-effective and minimally invasive technique, such as whitening, should be considered. This in vitro study aimed to evaluate tooth discolouration after two- and single-visit regenerative endodontic procedures and the effectiveness of subsequent whitening procedures with carbamide peroxide. Two hundred bovine incisors were included in this study and divided into twenty groups based on the tested material combinations. Two groups were control groups, one with saline and the other group with blood. In the 12 groups, the experiment was designed to be consistent with the two-visit regenerative endodontic procedures. Triple antibiotic paste or calcium hydroxide were placed in the root canal, and then scaffolds (e.g., blood or platelet-rich fibrin) and barrier materials (Biodentine, OrthoMTA or MTA Repair HP) were applied after rinsing the disinfectant pastes. In the six groups that corresponded to the single-visit regenerative endodontic procedure, the use of a disinfectant paste was omitted. Subsequently, the specimens were bleached twice with carbamide peroxide at a 7-day interval. Colour change measurements were performed using a spectrophotometer (VITA Easyshade Compact 5.0, VITA Zahnfabrik, Bad Säckingen, Germany). Statistical analysis was performed with the Kruskal–Wallis H test, the independent t-test and t-test for related samples. Tooth discolouration was noticed after two- and single-visit regenerative endodontic procedures, except for the platelet-rich fibrin+MTA Repair HP group. After the first and second whitening procedures, all of the tested two- and single-visit regenerative endodontic procedures groups showed a change in the colour of the crown, which was noticeable to the naked eye (∆E > 3.3). When analysing the ∆E value between the first and second bleaching procedures, no changes in the colour of teeth were visually noticed in the calcium hydroxide and platelet-rich fibrin +MTA Repair HP groups (∆E < 3.3). Single-visit regenerative endodontic procedures are suggested if possible; however, if two-visit regenerative endodontic procedures are performed, it is recommended to use calcium hydroxide as the disinfectant paste because of the lower staining potential. In the context of discolouration, platelet-rich fibrin is advisable for use as a scaffold. The whitening procedure is worth considering, but does not guarantee a return to the original tooth colour, especially when triple antibiotic paste is used. Full article

Orthodontic appliances discolour over treatment time, and a yellowish plaque builds up on the contact area of the brackets, adhesive and teeth. Brilliant Blue-based plaque-staining agents (BBPSAs), which increase tooth brushing efficiency, have the potential to support the maintenance of proper oral hygiene during orthodontic treatment. However, they exhibit strong colouring properties, and their impact on the aesthetics of braces remains unclear. Therefore, the aim of this study was to investigate the influence of commercially available BBPSAs on the colour of aesthetic orthodontic materials. A light-cured, colour-changing orthodontic adhesive and new-generation, monocrystalline, sapphire brackets were chosen for the experiments. The effect of the staining agent on the tested materials was investigated in terms of the reaction temperature and time, as well as the presence of black tea-induced impurities on the materials. The CIELAB (Commission Internationale de L’éclairage L* a* b*) colour system parameters were measured, and the colour differences (ΔE*ab and ΔE₀₀—the Commission Internationale de L’éclairage 2000 colour-difference) were determined for the materials under several experimental conditions. The braces’ green-red colour expression was positively affected by the BBPSA. Under in vitro conditions, the regular use of the BBPSA for 90 days visibly improved the unfavourable colour change caused by the black tea. Full article

Calcium silicate-based cements are biocompatible materials for vital pulp therapy. However, they discolour the tooth tissue, which is important for the aesthetics of the anterior teeth. The aim of this study was to investigate the effect of calcium silicate-based cements on tooth discolouration. The study included 70 extracted bovine incisors. The crown of the tooth was cut off from the root, 2 mm below the cement-enamel junction. The pulp tissue was removed via a cervical cut with a barbed broach. The teeth were randomly divided into five experimental, one positive, and one negative control groups. The evaluated materials included Biodentine, Ortho MTA, Retro MTA, MTA Plus, MTA Repair HP, and in the positive group, ProRoot MTA. A VITA Easyshade Compact 5.0 spectrophotometer was used before the application, after 1 week, 1 month, 3 months, and 6 months. The significance levels were set at p < 0.05. All materials significantly changed the teeth colour (p < 0.05). However, Ortho MTA, ProRoot MTA, MTA Plus, and Biodentine (ΔE > 6) caused maximum colour change after 6 months. While the ProRoot MTA, Ortho MTA, and MTA Plus caused grey discolouration, Biodentine darkened the shade of the base colour. Thus, Retro MTA and MTA Repair HP can be safely used in the aesthetic dentition zone. According to these clinical results, the possibility of using Biodentine, due to its lack of gray discoloration, can be considered. Full article

Tooth bleaching is a common treatment for the amelioration of the aesthetic of discoloured teeth. In this context, there are two common approaches that employ concentrated solutions (30–40 wt.%) of either hydrogen peroxide or carbamide peroxide as bleaching agents. However, there is an ongoing debate on the possible adverse effects of these different treatments on tooth health, such as variation of the enamel structure, surface morphology, and chemistry, which also affect tooth sensitivity. In the present work, a study on the effect of the two bleaching agents, a 35 wt.% solution of hydrogen peroxide and a 30 wt.% solution of carbamide peroxide, on the permeability and surface morphology of enamel is reported. The investigation was carried out on replicas of incisors obtained after different treatment times and for several patients, employing scanning electron microscopy to study the morphological features of the treated teeth. The significance of the analytical study was corroborated by a statistical analysis of the results. The collected data suggest that hydrogen peroxide treatment increases the enamel permeability, and this could be related with tooth sensitivity, whereas the carbamide peroxide solution increases the formation of precipitates on the tooth enamel. Full article

This study investigated the effect of silver diamine fluoride (SDF) and potassium iodide (KI) treatment on secondary caries prevention and tooth discolouration in glass ionomer cement (GIC) restoration. Cervical GIC restorations were done on 30 premolars with: Group 1, SDF + KI; Group 2, SDF (positive control); Group 3, no treatment (negative control). After cariogenic biofilm challenge, the demineralisation of dentine adjacent to the restoration was evaluated using micro-computed tomography (micro-CT) and Fourier transform infrared (FTIR) spectroscopy. The colour of dentine adjacent to the restoration was assessed using CIELAB system at different time points. Total colour change (∆E) was calculated and was visible if ∆E > 3.7. Micro-CT showed the outer lesion depths for Groups 1, 2 and 3 were 91 ± 7 µm, 80 ± 7 µm and 119 ± 8 µm, respectively (p < 0.001; Group 2 < Group 1 < Group 3). FTIR found that there was a significant difference in amide I-to-hydrogen phosphate ratio among the three groups (p < 0.001; Group 2 < Group 1 < Group 3). ∆E of Groups 1, 2 and 3 after biofilm challenge were 22.5 ± 4.9, 70.2 ± 8.3 and 2.9 ± 0.9, respectively (p < 0.001; Group 3 < Group 1 < Group 2). SDF + KI treatment reduced secondary caries formation on GIC restoration, but it was not as effective as SDF treatment alone. Moreover, a perceptible staining on the restoration margin was observed, but the intensity of discolouration was less than that with solely SDF treatment. Full article