Nitrogen Oxide Removal by Coal-Based Activated Carbon for a Marine Diesel Engine

Abstract

Vanadium-based catalysts are mainly used for marine diesel exhaust denitration. However, their poor catalytic ability at low temperature and poor sulfur tolerance, as well as high toxicity and cost, are big turnoffs. AC (Activated carbon) exhibits good adsorption capacity and catalytic ability in denitration because of its high specific surface area and chemical activity. In this paper, coal-based AC was used for simulating diesel exhaust denitration in different conditions. The results show that the NO removal ability of AC is poor in an NO/N₂ system. The NO₂ removal ability is excellent in an NO₂/N₂ system, where NO is desorbed. The NOx removal efficiency is 95% when the temperature is higher than 200 °C in an NO₂/NH₃/N₂ system. When the temperature is lower than 100 °C, AC can catalytically oxidize NO to NO₂ in an NO₂/O₂/N₂ system. The near-stable catalytic efficiencies of AC for a slow SCR (Selective Catalytic Reduction) reaction, a standard SCR reaction, and a fast SCR reaction at 300 °C are 12.1%, 31.6%, and 70.8%, respectively. When ships use a high-sulfur fuel, AC can be used after wet scrubber desulfurization to catalytically oxidize NO to NO₂ at a low temperature. When ships use a low-sulfur fuel, AC can be used as a denitration catalyst at high temperatures.

1. Introduction

At present, diesel engines are widely used in ships as the main power unit and generation unit. Marine diesel engines generally use high-sulfur, heavy fuel oil. In addition to CO₂ contributing to the greenhouse effect, the exhaust gas also contains lots of SOx, NOx, particulate matter (PM), and other pollutants. The International Maritime Organization (IMO) has issued MARPOL 73/78 Annex VI [1] to control the emissions of SOx and NOx from marine diesel engine exhaust. The current means to meet the Convention’s SOx emission requirements mainly include low-sulfur fuel oil and wet scrubber desulfurization technology. The alkaline liquid used in a wet scrubber includes NaOH [2], Mg(OH)₂ [3,4], seawater [5,6], and so on. The means to meet the Convention’s Tier III NOx emission requirements are mainly exhaust gas recirculation (EGR) [7,8] and selective catalytic reduction (SCR) [9]. EGR technology is generally only adopted by diesel engine manufacturers because of its high technical barriers and changes in the diesel engine body. SCR is currently the most widely used exhaust gas denitration technology, and often uses vanadium-based catalysts. The operating temperature of vanadium-based catalysts is 250–400 °C, and its denitration efficiency is generally up to 90% [10,11,12]. From the above, there are three possible technical routes that can finally achieve the desired SOx and NOx removal:

(1) Low-sulfur fuel oil → vanadium-based SCR denitration. This route is simple and effective. However, the fuel cost is expected to rise because of the high price of low-sulfur fuel oil. The fuel supply system and lubrication system of the diesel engine also need to be modified. In addition, the vanadium-based catalyst is expensive and highly toxic. It causes secondary pollution at disposal after the catalyst’s life has expired.

(2) High-sulfur fuel oil → vanadium-based SCR denitration → wet scrubber desulfurization. The fuel cost is low by this technical route, but the SOx in the exhaust gas may corrode the subsequent SCR denitration reactor. Secondly, the use of high-sulfur fuel may lead to an increase in PM emissions, and the PM often adheres to the catalyst surface, causing a decrease in denitration efficiency and an increase in exhaust back pressure. What is more, sulfur poisoning of the vanadium-based catalyst is a known issue [13].

(3) High-sulfur fuel oil → wet scrubber desulfurization → vanadium-based SCR denitration. This route can avoid the poisoning effect of SOx on the denitration catalyst. However, the temperature of the exhaust gas after wet scrubber desulfurization is generally below 100 °C, even as low as 50 °C [14]. The denitration efficiency of vanadium-based catalyst at low temperatures is poor. It needs a heat exchanger to reheat the exhaust gas before the exhaust gas enters the SCR reactor, which makes the system more complicated.

The fuel price is the most important factor in the choice of desulfurization technology. However, SCR technology seems indispensable for ship denitration. There are mainly three reactions in SCR denitration, shown as Equations (1)–(3) [11] below. Equation (1) has the slowest reaction rate, also known as the slow SCR reaction. NOx in diesel exhaust is mainly NO and NO₂, of which NO accounts for more than 90%. The reaction activation energy of Equation (2) is lower than that of Equation (3), so the reaction rate of Equation (2) is higher. Equation (2) is also called the fast SCR reaction. O₂ is much more prevalent than NO₂ in exhaust gas. So Equation (3) is dominant in the SCR reaction, also known as the standard SCR reaction. [10]. When NO/NO₂ is equal to 1, the reaction rate is the fastest. Increasing the NO₂/NOx ratio appropriately helps to increase the SCR reaction rate [15].

4NH₃ + 6NO → 5N₂ + 6H₂O

(1)

2NH₃ + NO + NO₂ → 2N₂ + 3H₂O

(2)

4NH₃ + 4NO + O₂ → 4N₂ + 6H₂O

(3)

In summary, it is important to look for a denitration catalyst that is inexpensive, has high denitration efficiency in a wide temperature range and causes no secondary pollution. Activated carbon is not only cheap and has a variety of sources, but also has good adsorption capacity and catalytic ability due to the high specific surface area and chemical activity. Some metal oxides can be impregnated onto the AC surface to further increase the denitration efficiency at high temperatures [16]; therefore, it has great application prospects in the future. There are many factors affecting the denitration efficiency of AC, including the AC type, specific surface area (mainly related to physical adsorption) and surface functional groups (mainly related to chemical adsorption and catalysis), NOx concentration, O₂ concentration, exhaust gas temperature, adding NH₃ or not, and so on. At present, there are three main types of commercial ACs, i.e., coal-based, coconut shell, and wood-based. The wood-based AC is mostly used for water treatment, and is not considered environmentally friendly because it needs to consume wood. The price of coconut shell AC is roughly twice that of coal-based AC [17]. Therefore, this paper chooses coal-based AC as the research object. Since the marine diesel engines could use different sulfur content fuels, the desulfurization means are also different, which leads to different temperatures of the exhaust gas during denitration. This paper mainly studies the performance of AC to catalyze the oxidation of NO to NO₂ at low temperatures and as the SCR catalyst at high temperatures, and explores the application prospects of AC in the field of ship denitration.

2. Experimental System and Methods

2.1. Experimental System

In order to study the effects of different gas compositions, concentrations, and temperatures on the denitration ability of the coal-based AC, a simulating gas supply system is used to simulate real diesel exhaust gas in this paper. The experimental system is shown in Figure 1. It mainly includes a gas supply unit, quartz reactor, temperature control unit, flue gas analyzer (Testo 350, Freiburg, Germany), and exhaust gas absorption device. The gas supply unit mainly includes gas cylinders, pressure reducing valves, mass flow controllers (Seven Star CS200AD, Beijing, China), mixing chamber, etc. The temperature control unit includes a tubular heating furnace (Ruipu Electric Equipment Factory, 220V/3kW, Yangzhou, China) and temperature controller. N₂ and O₂ are high-purity standard gases. NO is a 10% standard gas with N₂ as the carrier gas, and so are NO₂ and NH₃. The concentrations of each gas component in the mixed gas are controlled by the mass flow controllers. The quartz reactor, a hollow cylinder of 26 mm inner diameter, 2 mm wall thickness, and 300 mm length, is placed in the tubular heating furnace. The experimental temperature is controlled by a temperature controller with ±1 °C accuracy. The flue gas analyzer can continuously monitor the temperature and the concentrations of NO, NO₂, and CO of the mixed gas with a sampling period of 1 s by an electrochemical method. In order to prevent the exhaust gas from polluting the air, the gas passing through the flue gas analyzer is sent to an exhaust gas absorption device for treatment.

2.2. Materials and Methods

The coal-based columnar AC used in this paper was purchased from Henan Huanyu Carbon Co., Ltd., Xuchang, China. Its diameter, length, and specific surface area are 1.5 mm, 2–4 mm, and 326 m²/g, respectively. The AC was washed with deionized water before the experiments to remove impurities on the surface and then dried in a drying oven at 110 °C for 12 h. The types and contents of oxygen-containing functional groups on the AC surface were detected by the Boehm titration method. The total gas volume was 2 L/min with N₂ as the carrier gas and 30 g of AC was used in each group of experiments. (The corresponding volume of gas per volume of catalyst and per hour, i.e., VVH, was 2500 h⁻¹.) The exhaust gas temperature of large low-speed two-stroke marine diesel engines is generally lower than 300 °C [4]. Therefore, the temperature range studied in this paper was from room temperature (15 °C) to 300 °C.

The NOx concentration in the exhaust gas of marine diesel engine is generally about 1000 μL/L, and NO accounts for the main part. When the NO/NO₂ molar ratio is 1, the fast SCR reaction Equation (2) takes place, and the reaction rate is the fastest. So, the concentrations of NO and NO₂ were both 500 μL/L in the fast SCR reaction. The total concentration of NO and NO₂ remained 1000 μL/L. When NH₃ was needed, NH₃ was added at an ammonia-nitrogen ratio of 1 depending on the initial NOx. The O₂ concentration was 5% when needed. We do not pay special attention to the physical adsorption time of AC in this paper. The discussion of the denitration efficiency of AC in the following refers to the removal efficiency when the outlet NOx concentration is in a near-stable condition. The near-stable denitration efficiency is then defined as follows:

$$\eta =\frac{C_{\mathrm{in}}-C_{\mathrm{out}}}{C_{\mathrm{in}}}\times 100\%$$

(4)

Here η is the NOx removal efficiency of AC, %; C_in is the inlet NOx concentration, μL/L; C_out is the outlet NOx concentration, μL/L.

3. Results and Discussion

3.1. Effect of AC on Single-Component NO

The NO adsorption on the surface of AC is the premise of AC denitration. The temperature has a great influence on the AC denitration ability. Therefore, this paper first studied the removal ability of AC on single component NO in the range of 15–300 °C. As shown in Figure 2, there are four stages according to the temperature, which are 15 °C, 15–100 °C, 100–200 °C, and 200–300 °C, and the inlet gas is 1000 μL/L NO/N₂. The outlet NO reaches 970 μL/L within 10 min at 15 °C. Modified activated carbon fiber (ACF) was used to investigate ACF’s denitration ability at 40 °C. When the inlet gas is 900 μL/L NO/N₂, the outlet NO reaches 800 μL/L within 5 min and then increases slowly [17]. Our results are similar to his. We know that low temperature contributes to the physical adsorption of AC, and generally ACF has a larger specific surface area than AC. So ACF’s physical adsorption ability is stronger than AC’s. However, the NO adsorption amounts of both ACF and AC are still limited at low temperatures. With the increase in temperature, the physical adsorption ability of AC gradually deteriorates, and the chemisorption ability and catalytic ability gradually improve. Therefore, in order to improve the denitration ability of AC, it is also necessary to optimize its catalytic ability.

During the heating process, the outlet NO will increase slightly due to the partial desorption of the adsorbed NO. However, as the temperature increases, the chemisorption ability of AC increases, and more NO is absorbed by chemisorption. Therefore, the outlet NO is decreased. When the temperature is kept constant, the adsorption-activated sites on the surface of the AC gradually decrease over time, leading to an increasing concentration of NO at the outlet. However, as the temperature gradually increases from 15 °C to 300 °C, the catalytic ability of AC increases, and so does the denitration efficiency. It can be seen from Figure 2 that the near-stable denitration efficiencies of AC at 100 °C, 200 °C, and 300 °C are 2%, 3.6%, and 5.8%, respectively.

The chemisorption and catalytic abilities of AC are closely related to the oxygen-containing functional groups on the surface of AC [18]. The contents of oxygen-containing functional groups on the surface of AC were measured by the Boehm titration method [19,20,21] in this paper, and the results are shown in

Table 1. Surface chemical characteristics of activated carbon (Unit: mmol/g).

Species	Carboxyl	Lactone	Phenolic Hydroxyl	Acidic Groups	Basic Groups	Total Contents
Value	0.150	0.045	0.233	0.428	0.278	0.705

. It can be seen that the coal-based AC is acidic, and the phenolic hydroxyl group has a relatively higher proportion. Several papers [22,23,24] studied the decomposition temperature of different oxygen-containing functional groups on the surface of AC. It can be seen from Figure 2 that CO is generated when the temperature is between 100 °C and 200 °C. However, when the temperature is kept at 200 °C, the CO concentration basically does not change. In the temperature range of 100–200 °C, it is mainly the carboxyl group decomposing [23]. When the temperature is between 200 °C and 300 °C, the experimental phenomenon is similar to that of the third stage, and both the CO concentration and the denitration efficiency are higher. In the temperature range of 200–300 °C, this is mainly due to the decomposition of the carboxyl group and the lactone group [23,24]. The decomposition temperature of the phenolic hydroxyl group is generally higher than 600 °C [24], so it does not decompose under the experimental conditions herein. These oxygen-containing functional groups may react with NO, such as Equation (5) generating CO and Equation (6) generating CO₂ (C_f represents the activated sites). CO also has a certain degree of reducibility, and will react with NO, i.e., Equation (7), which also lowers the concentration of NO. In general, the denitration efficiency of AC increases slightly with the temperature when the inlet is NO/N₂. However, there is still a big gap toward the actual applications of AC for exhaust gas denitration. Therefore, other methods should be considered.

2C_f + 2NO → N₂ + 2CO

(5)

C_f + 2NO → N₂ + CO₂

(6)

2CO + 2NO → N₂ + 2CO₂

(7)

3.2. Effect of AC on NO + NH₃

When the temperature is lower than 300 °C, the denitration ability of AC as the reductant was poor. To further improve the denitration ability of AC, NH₃ is generally added as the reductant [25,26]. As shown in Figure 3, the denitration ability of AC at different temperatures is investigated in this paper when the inlet gas is 1000 μL/L NO + 1000 μL/L NH₃, i.e., slow SCR reaction Equation (1). There are two explanations for the catalytic denitration mechanism of AC when NH₃ is present. One is the Eley–Rideal mechanism (E–R), in which the adsorbed NH₃ reacts with the gas phase NO [27], and the other is the Langmuir–Hinshelwood mechanism (L–H), in which the adsorbed NH₃ reacts with adsorbed NO [28]. Both mechanisms suggest that the NH₃ adsorption process on the surface of AC is the rate-limiting step of Equation (1). Therefore, more acidic oxygen-containing functional groups on the surface of AC can contribute to the adsorption of NH₃, which increases the reaction rate of denitration. Figure 4, which is supported by [28], shows the L–H mechanism of NO and NH₃ reacting on the surface of AC, and NH₃ is mainly adsorbed on the phenolic hydroxyl group. The coal-based AC used in this paper is acidic and the phenolic hydroxyl-containing functional group is relatively high, which promotes denitration. It can be seen from the comparison between Figure 2 and Figure 3 that the trend and concentration of CO after adding NH₃ are basically the same as without NH₃, indicating that NH₃ has no effect on the decomposition of the oxygen-containing functional groups. After adding NH₃, NO can be converted to N₂ by slow SCR reaction Equation (1), and the denitration rate of AC is slightly increased. The near-stable denitration efficiencies of AC at 15 °C, 100 °C, 200 °C, and 300 °C are 10.5%, 9.1%, 10%, and 12%, respectively, which are slightly higher than without NH₃. However, the catalytic effect of AC on the Equation (1) is still small.

3.3. Effect of AC on Single-Component NO₂ and NO₂ + NH₃

The exhaust gas of diesel engine contains a certain concentration of NO₂. The effects of AC on single-component NO₂ and NO₂ + NH₃ are the basis for the study of fast SCR reaction Equation (2). Therefore, this section will discuss the effects of AC on single NO₂ and NO₂ + NH₃ separately.

As shown in Figure 5, the experiment is divided into four stages, namely, 15 °C (1st stage), 15–100 °C (2nd stage), 100–200 °C (3rd stage), and 200–300 °C (4th stage). The inlet gas is 500 μL/L NO₂/N₂. NO₂ is not detected in the outlet during the experiment, which indicates that the NO₂ removal ability of AC is excellent at 15–300 °C. Interestingly, NO is detected in the outlet and the concentration of NO increases gradually with the temperature. There is a large amount of NO desorbed during the heating process. During the process of heating from 100 °C to 200 °C, the concentration of desorbed NO can reach up to 2800 μL/L. When the temperature remains stable at 200 °C and 300 °C, respectively, NO₂ is almost completely converted to NO, which is then desorbed. CO and CO₂ may be produced when the temperature is above 100 °C. Since the flue gas analyzer cannot measure CO₂, the amount of CO₂ needs further study. The likely reactions are Equations (8)–(10) [29,30].

Then we carried out the experiment with NO₂ + NH₃. As shown in Figure 6, the experiment is divided into five stages, namely, 15 °C without AC (1st stage), 15 °C with AC (2nd stage), 15–100 °C with AC (3rd stage), 100–200 °C with AC (4th stage), and 200–300 °C with AC (5th stage). The inlet gas is 500 μL/L NO₂ + 500 μL/L NH₃/N₂. NH₃ can react with NO₂ at room temperature [31]. It can be seen from Figure 6 that NO₂ gradually decreases without AC in the first stage, that is, the reaction takes place between NO₂ and NH₃, and the products include N₂ and NO. When the gas is passed into the AC reactor (2nd–5th stages), NO₂ almost completely disappears. During the heating process, NO desorbs, resulting in an increase in the concentration of NO at the outlet. When the temperature is stable, the temperature is higher and the lower the outlet NO is acquired. When the temperature is higher than 200 °C, the removal efficiency of NOx by AC is more than 95% in the presence of NH₃.

In summary, this study suggests that when there is no NH₃, AC converts NO₂ into NO, and the concentration of NO in the outlet increases with temperature. When NH₃ is added, AC catalyzes NO₂ and NH₃ to generate N₂, i.e., Equation (11). The catalytic activity of AC increases gradually with the temperature. In addition, the desorbed NO participates in the rapid SCR reaction Equation (2), thereby further improving the denitration ability of AC.

C_f + NO₂ → NO + C_f-O

(8)

C_f + 2NO₂ → 2NO + CO₂

(9)

Cf + NO₂ → NO + CO

(10)

8NH₃ + 6NO₂ → 7N₂ + 12H₂O

(11)

3.4. Effect of AC on NO + NO₂ + NH₃

When the NO/NO₂ molar ratio is 1, SCR denitration mainly takes place according to the fast SCR reaction Equation (2). At present, the catalytic effect of AC on Equation (2) at different temperatures is not clear. Therefore, this section mainly studies the catalysis of AC for Equation (2) at 15–300 °C.

The inlet gas is 500 μL/L NO + 500 μL/L NO₂ + 1000 μL/L NH₃. As shown in Figure 7, the experiment is divided into six stages, namely, 15 °C without AC (1st stage), 15 °C with AC (2nd stage), 15–100 °C with AC (3rd stage), 100–200 °C with AC (4th stage), 200–300 °C with AC (5th stage), and 300 °C with AC and without NH₃ (6th stage). It can be seen from Figure 7 that NO₂ can react with NH₃ to generate NO and N₂ at room temperature without AC in the 1st stage. In the 2nd stage, there is almost no NO₂ at the outlet when the gas is introduced into the activated carbon reactor. The concentration of the outlet NO is also reduced to some extent. The denitration efficiency is about 59.5% at 15 °C. In the 3rd stage, when the temperature is raised from 15 °C to 100 °C, the chemical denitration of AC is not significantly improved, but its physical adsorption ability is greatly reduced, resulting in an increase in outlet NO, and the denitration efficiency is about 53%. In the 4th stage, when the temperature is raised from 100 °C to 200 °C, the chemical denitration of AC is greatly enhanced, around 69.2%, and the outlet NO is greatly reduced. In the 5th stage, when the temperature is further increased from 200 °C to 300 °C, the denitration ability of AC does not change significantly, and the near-stable denitration efficiency reaches 70.8%. In the 6th stage, when NH₃ is turned off, most NO₂ is converted to NO and then desorbed, resulting in a rapid NO concentration increase at the outlet, eventually reaching 920 μL/L. This indicates that NH₃ plays an important role in the denitration ability of AC at high temperatures. It is found that NH₃ increases the denitration efficiency of AC from 8% to 70.8% at 300 °C.

3.5. Effect of AC on NO + O₂ and NO + O₂ + NH₃

The diesel engine exhaust gas contains a large amount of O₂. O₂ can not only oxidize NO to NO₂, but also is the reactant of standard SCR reaction Equation (3). Therefore, O₂ will have a great influence on the denitration ability of AC. When the inlet gas is 1000 μL/L NO + 5% O₂, the denitration ability of AC at different temperatures is shown in Figure 8, which shows that it takes 660 min for outlet NOx to reach 900 μL/L at 15 °C and 500 min at 50 °C. Compared with the experiment without O₂ at 15 °C (Figure 2), the adsorption saturation time of AC is greatly prolonged, indicating that O₂ can greatly promote the chemical adsorption of NO on the surface of AC. In addition, NO₂ starts to appear at the outlet after 300 min at 15 °C. Then NO₂ gradually increases and finally stabilizes, while NO basically maintains about 300 μL/L. When the temperature is 50 °C, NO₂ starts to appear at the outlet after 200 min and since then NO maintains about 480 μL/L. The trends of NO and NO₂ are similar to that at 15 °C. The above experimental phenomenon is mainly due to the different adsorption sites (C_f-A and C_f-B) on the surface of AC for NO and NO₂. C_f-A can adsorb NO and NO₂, but it is easier to adsorb NO, while C_f-B can adsorb NO₂ only [27]. At the beginning of the experiment, gaseous NO can be directly adsorbed on the oxygen-containing functional groups and then converted into C_f-A-NO₂, or it can be adsorbed on the activated sites to form C_f-A-NO, and then oxidized to C_f-A-NO₂ by O₂. Due to the combination force of NO₂ on C_f-A-NO₂ being relatively small, NO₂ is easy to desorb or directly transfer to the adjacent C_f-B to form C_f-B-NO₂. When C_f-B is saturated, the desorbed NO₂ will be out of the reactor. Finally, the adsorption and oxidation of NO balance the adsorption and desorption of NO₂ dynamically. The outlet concentrations of NO and NO2 remain roughly stable. As can be seen from Figure 8, the conversion rates of AC to catalyze the oxidation of NO to NO₂ at 15 °C and 50 °C are 62.3% and 43.8%, respectively.

When ships use low-sulfur fuel oil, the wet scrubber desulfurization will no longer be needed and the temperature of the exhaust gas entering the SCR reactor is higher than that coming out of the scrubber in a high-sulfur case. Therefore, it is necessary to study the denitration ability of AC at higher temperatures. As shown in Figure 9, the denitration ability of AC are simulated with or without NH₃ at 100 °C, 200 °C, and 300 °C, respectively. Each experiment is divided into three stages: the first stage is the heating process (from room temperature to the set temperature), and the second and third stages are maintained at the set temperature. In the first stage and the third stage, the inlet gas is 1000 μL/L NO + 5% O₂, and in the second stage, 1000 μL/L NH₃ is added. It can be seen from Figure 9 that in the first 60 min, the NO concentration in the outlet rises rapidly during the heating process. The faster the heating rate, the higher the NO concentration in the outlet. When the temperature is stable, the outlet NO gradually decreases and eventually stabilizes. Compared with Figure 8, the adsorption saturated time of AC is shorter when the temperature is higher than 100 °C. After the adsorption is saturated, NO will not be oxidized to NO₂, indicating that the catalytic oxidation of NO by AC is poor when the temperature is higher than 100 °C. At this time, the stable denitration efficiencies of AC at three temperatures are 12.6%, −0.5%, and 2.5%, respectively. Illán-Gómez [32] carried out temperature-programmed reduction (TPR) experiments using coal-based activated carbon with 0.5% NO + 5% O₂/He from room temperature to 500 °C. The results show that the denitration rate of AC decreases and then increases with the temperature. The denitration rate is basically negative between 150 and 300 °C, about −20% at 220 °C. Shu [33] used sawdust, rice husk, and corncob-activated carbon to carry out TPR experiments with 0.1% NO + 5% O₂/N₂ from room temperature to 600 °C. The results show that the trend of denitration efficiency is basically the same as that of Illán-Gómez, and the denitration efficiency is negative at 150–350 °C. The experimental results obtained in this paper are basically the same as those Illán-Gómez and Shu obtained via the TPR method. The experimental phenomenon is mainly caused by the dynamic balance between the better adsorption ability of AC at low temperature and the better reduction and catalytic ability at high temperature. When the temperature is lower than 200 °C, the adsorption ability is dominant. When the temperature is higher than 200 °C, the reduction and catalytic ability are dominant. However, since the diesel engine exhaust gas temperature is generally lower than 300 °C, the denitration ability of AC is not ideal when no reductant is added. At the 60th minute, NH₃ is added to simulate standard SCR reaction Equation (3). The NO concentrations of the outlet at three temperatures decrease rapidly. When the NH₃ is stopped, the NO concentration of the outlet increases rapidly. When the temperatures are 100 °C, 200 °C, and 300 °C, the corresponding near-stable denitration efficiencies are 34.6%, 16%, and 31.6%, respectively. Experimental results show that NH₃ can greatly improve the denitration ability of AC in the range of 100–300 °C.

3.6. The Application Prospect of AC in Ship Exhaust Gas Denitration

When ships use low-sulfur fuel oil, the temperature of the exhaust gas entering the SCR denitration reactor is generally 200–300 °C. From the above experimental results, we know that the near-stable denitration efficiencies of the slow SCR reaction Equation (1), the fast SCR reaction Equation (2), and the standard SCR reaction Equation (3) under the action of activated carbon are 12.1%, 70.8%, and 31.6%, respectively. Increasing the proportion of NO₂ in the exhaust gas can increase the denitration efficiency of AC. In addition, the AC may be modified or loaded with other metal oxides to further increase the denitration efficiency. When ships use high-sulfur fuel, we know from the above experimental results that the exhaust gas cooled to about 50 °C after wet scrubber desulfurization can be passed into the activated carbon oxidizer to oxidize the NO to NO₂. As NO₂ is easily soluble in water, the gas can be introduced into the washing tower again for denitration treatment. Therefore, it does not need the heat exchanger to reheat the exhaust gas. What is more, ammonia- and vanadium-based catalysts are no longer needed. The activated carbon is cheaper and has a wide range of sources. In the future, based on changes in oil prices, whether using low-sulfur fuel oil or high-sulfur fuel oil with wet scrubber to meet ships’ sulfur emission requirements, SCR will be an effective method of ship denitration. Activated carbon can be used as an oxidation catalyst in low-temperature exhaust gas and as an SCR denitration catalyst in high-temperature exhaust gas. It will have good application prospects in the field of ship exhaust gas denitration in the future.

4. Conclusions

Based on the above experiments on the denitration ability of coal-based activated carbon under different conditions, the paper mainly draws the following conclusions:

(1) In the range of 15–300 °C, when the inlet gas is NO/N₂, the removal of NO by coal-based activated carbon mainly depends on the adsorption, and the near-stable denitration efficiency is low. When the inlet gas is NO₂/N₂, NO₂ is finally converted to NO and desorbs from the surface of activated carbon. However, when NH₃ is added and the temperature is higher than 200 °C, the NOx removal efficiency is up to 95% in the NO₂/N₂ system.

(2) When the inlet gas is 1000 μL/L NO + 5% O₂, the saturated adsorption time of NO for AC at 10 °C and 50 °C is 660 min and 500 min, respectively. However, the adsorption saturation time drops sharply with an increase in temperature. When the temperature is above 200 °C, the adsorption saturation time is less than 10 min. When the temperature is lower than 100 °C, activated carbon can catalyze the oxidation of NO to NO₂. The conversion efficiency of NO to NO₂ at 15 °C and 50 °C is 62.3% and 43.8%, respectively. When the temperature is higher than 100 °C, the ability of AC for catalytic oxidation of NO is minimal.

(3) The stable denitration efficiencies of activated carbon with different inlet gas are investigated at 100 °C, 200 °C, and 300 °C. When the inlet gas is NO/NH₃/N₂, simulating slow SCR reaction Equation (1), the NOx removal rates corresponding to the three temperatures are 9.1%, 10%, and 12%. When the inlet gas is NO/NO₂/NH₃/N₂, simulating the fast SCR reaction Equation (2), the NOx removal efficiencies corresponding to the three temperatures are 53%, 69.2%, and 70.8%, respectively. When the inlet gas is NO/NH₃/O₂/N₂, simulating the standard SCR reaction Equation (3), the NOx removal efficiencies corresponding to the three temperatures are 34.6%, 16%, and 31.6%, respectively.

(4) There are two main methods for the application of activated carbon in the exhaust gas denitration of marine diesel engines. When ships use high-sulfur fuel oil, the exhaust gas cooled after the wet scrubber desulfurization can be passed into the activated carbon to oxidize NO to NO₂, which is more soluble in water. Then the gas can be passed to a wet scrubber for denitration. When ships use low-sulfur fuel oil, the high-temperature exhaust gas can be passed into the activated carbon catalytic reactor. Then NH3 can be injected into the reactor for SCR denitration treatment.