Method of Preparation for High-Purity Nanocrystalline Anhydrous Cesium Perrhenate

Institute of Non Ferrous Metals, Hydrometallurgy Department, ul. Sowińskiego 5, 44-100 Gliwice, Poland
Author to whom correspondence should be addressed.
Academic Editor: Hugo F. Lopez
Metals 2017, 7(3), 96;
Received: 23 December 2016 / Revised: 3 March 2017 / Accepted: 9 March 2017 / Published: 15 March 2017
PDF [2927 KB, uploaded 16 March 2017]


This paper is devoted to the preparation of high-purity anhydrous nanocrystalline cesium perrhenate, which is applied in catalyst preparation. It was found that anhydrous cesium perrhenate with a crystal size <45 nm can be obtained using cesium ion sorption and elution using aqueous solutions of perrhenic acid with subsequent crystallisation, purification, and drying. The following composition of the as-obtained product was reported: 34.7% Cs; 48.6% Re and <2 ppm Bi; <3 ppm Zn; <2 ppm As; <10 ppm Ni; < 3 ppm Mg; <5 ppm Cu; <5 ppm Mo; <5 ppm Pb; <10 ppm K; <2 ppm Na; <5 ppm Ca; <3 ppm Fe. View Full-Text
Keywords: cesium; caesium; rhenium; perrhenate; cation resin cesium; caesium; rhenium; perrhenate; cation resin

Figure 1

This is an open access article distributed under the Creative Commons Attribution License which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited (CC BY 4.0).

Share & Cite This Article

MDPI and ACS Style

Leszczyńska-Sejda, K.; Benke, G.; Ciszewski, M.; Malarz, J.; Drzazga, M. Method of Preparation for High-Purity Nanocrystalline Anhydrous Cesium Perrhenate. Metals 2017, 7, 96.

Show more citation formats Show less citations formats

Note that from the first issue of 2016, MDPI journals use article numbers instead of page numbers. See further details here.

Related Articles

Article Metrics

Article Access Statistics



[Return to top]
Metals EISSN 2075-4701 Published by MDPI AG, Basel, Switzerland RSS E-Mail Table of Contents Alert
Back to Top