Next Article in Journal
Fibrin Hydrogel Based Bone Substitute Tethered with BMP-2 and BMP-2/7 Heterodimers
Next Article in Special Issue
Precursor-Less Coating of Nanoparticles in the Gas Phase
Previous Article in Journal
Fe-Doping Effect on Thermoelectric Properties of p-Type Bi0.48Sb1.52Te3
Previous Article in Special Issue
Kinetic Study on the Formation of Bimetallic Core-Shell Nanoparticles via Microemulsions
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 8
Issue 3
10.3390/ma8030966
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Film Growth Rates and Activation Energies for Core-Shell Nanoparticles Derived from a CVD Based Aerosol Process

by
Frederik Weis
1,*,
Martin Seipenbusch
2 and
Gerhard Kasper
1
1
Institute for Mechanical Process Engineering and Applied Mechanics, Karlsruhe Institute of Technology (KIT), Strasse am Forum 8, 76131 Karlsruhe, Germany
2
Institute of Chemical Process Engineering, University of Stuttgart, Böblinger Strasse 78, 70199 Stuttgart, Germany
*
Author to whom correspondence should be addressed.
Materials 2015, 8(3), 966-976; https://doi.org/10.3390/ma8030966
Submission received: 1 December 2014 / Revised: 17 February 2015 / Accepted: 26 February 2015 / Published: 6 March 2015
(This article belongs to the Special Issue Inorganic Core-Shell Structures)
Browse Figures
Versions Notes

Abstract

:
Silica core-shell nanoparticles of about 60–120 nm with a closed outer layer of bismuth or molybdenum oxide of 1–10 nm were synthesized by an integrated chemical vapor synthesis/chemical vapor deposition process at atmospheric pressure. Film growth rates and activation energies were derived from transmission electron microscopy (TEM) images for a deposition process based on molybdenum hexacarbonyl and triphenyl bismuth as respective coating precursors. Respective activation energies of 123 ± 10 and 155 ± 10 kJ/mol are in good agreement with the literature and support a deposition mechanism based on surface-induced removal of the precursor ligands. Clean substrate surfaces are thus prerequisite for conformal coatings. Integrated aerosol processes are solvent-free and intrinsically clean. In contrast, commercial silica substrate particles were found to suffer from organic residues which hinder shell formation, and require an additional calcination step to clean the surface prior to coating. Dual layer core-shell structures with molybdenum oxide on bismuth oxide were synthesized with two coating reactors in series and showed similar film growth rates.

Graphical Abstract

1. Introduction

Nanoparticles with core-shell structures have wide applications ranging from catalysis to medical applications and optoelectronic devices. As an alternative to conventional multistep liquid phase synthesis routes, several gas phase processes have been developed and proven to offer continuous, solvent-free and scalable synthesis methods [1,2,3]. Such an integrated chemical vapor synthesis (CVS)/chemical vapor deposition (CVD) process was used to produce well defined core-shell structures with a silica core and an oxide outer layer. A key feature of this approach is that spherical core particles are prepared continuously by decomposition of tetra-ethyl-ortho-silicate (TEOS), and then transferred immediately to a CVD coating step with molybdenum and/or bismuth oxide. These coating materials were selected, since they have potential as supported thin film catalysts for the selective oxidation of hydrocarbons [4,5,6,7]. MoO3 and Bi2O3 were furthermore investigated as electrochromic materials in “smart” windows and display devices [8], as an ion conducting electrolyte material in solid oxide fuel cells, as gas sensors [9] and nanostructured photocatalysts for the degradation of organic compounds [10]. Prerequisite for a workable coating process via CVS/CVD is the availability of suitable precursors with good thermal stability combined with clean evaporation or sublimation. Commercially available molybdenum hexacarbonyl and triphenyl bismuth were found to meet these requirements, are stable upon storage and handling and were therefore selected. CVD of MoO3 and Bi2O3 on planar substrates with these precursors has been reported [11,12,13,14,15,16]. However, little can be found with regard to the coating of micron sized or even submicron particles with such materials. To the best of our knowledge, only fluidized bed techniques have been used to date for the coating of micronsized particles with molybdenum oxide [17,18,19] or bismuth oxide [20] with focus on the subsequent catalytic application, not on the coating process itself.
The aim of this work was thus to identify the optimal process parameters for the synthesis of such core-shell structures in an aerosol process, and to derive the deposition kinetics for Mo and Bi required for future optimization and scale-up. Furthermore, comparisons of coating results were made with coatings on commercial carrier particle materials.

2. Results and Discussion

For both material systems perfect core-shell structures could be synthesized as shown in Figure 1.
Materials 08 00966 g001 1024
Figure 1. TEM images of core-shell structures synthesized by a (CVS)/(CVD) at atmospheric pressure, comprising a silica core and outer layers of (a) bismuth oxide at 390 °C; (b) bismuth oxide at 370 °C and (c) molybdenum oxide at 130 °C.
Figure 1. TEM images of core-shell structures synthesized by a (CVS)/(CVD) at atmospheric pressure, comprising a silica core and outer layers of (a) bismuth oxide at 390 °C; (b) bismuth oxide at 370 °C and (c) molybdenum oxide at 130 °C.
Materials 08 00966 g001

2.1. Molybdenum Oxide Coatings

Growth rates for molybdenum oxide films on silica particles were derived from the analysis of a series of TEM images at a residence time of 50 s in the coating reactor. (Deriving the thickness of individual layers based on a recently described and very sensitive online-technique [21] is also possible, but requires exact density values for each layer. Unfortunately different values are reported in the literature for molybdenum oxide, either as MoO3 or MoO2, and one cannot be sure of some interdiffusion for double layers). No film growth was detected below 110 °C; above 140 °C no further increase of the film growth rate was observed due to the onset of competing homogeneous gas phase decomposition of the precursor resulting in the formation of fractal agglomerates of molybdenum oxide. An Arrhenius plot (Figure 2) with an exponential fit in the temperature range 110–140 °C gives an activation energy of 123 ± 5 kJ/mol for the film growth rate. This value matches the activation energy for the first dissociative CO loss as determined by Loh et al. [22] by temperature programmed decomposition of molybdenum hexacarbonyl on silica substrates. As expected, it is also lower than the activation energy required for autocatalytic homogeneous gas phase decomposition, which is reported in the range of 150–164 kJ/mol [23,24].
Prerequisite for a successful coating is the chemisorption and subsequent decomposition of the precursor on the silica particle surface. For the molybdenum hexacarbonyl precursor this occurs via adsorption on surface hydroxyl groups and an exchange of one CO ligand, followed by successive complete decarbonylation in a single step reaction with the activation energy of about 122 kJ/mol given by Loh et al. [22]. However, once the first monolayer coverage is reached in our process, further film growth continues via adsorption of the precursor molecules on molybdenum oxide layers and thus probably with a different activation energy. Unfortunately, there is no literature for the adsorption and decomposition of molybdenum hexacarbonyl on molybdenum oxide. Nonetheless, our data indicate that the activation energy does not change significantly with film thickness or compared to the plain silica substrate. According to Loh et al. [22] the activation energy for the decarbonylation is a function of the field strength of the substrate cation, namely the Si4+ ion in their studies, attached to the surface hydroxyl group, which has to be exchanged. The field strength is defined as the cation charge divided by the ionic radius (0.42 Angstrom for Si4+ in SiO2), yielding a field strength of 9.5 Å−1 for silica. Applying the same calculations to molybdenum-(VI)-oxide with an ionic radius of 0.62 Angstrom for Mo6+ as given by Pauling [25] results in a field strength of 9.6 Å−1, which is very close to silica and thus supports the assumption that the film growth rate is limited by the decarbonylation step with an activation energy of about 123 ± 5 kJ/mol. However, some uncertainties arise regarding the state of molybdenum ions, since for the as-deposited molybdenum oxide film no distinct crystalline peaks could be observed in the WAXS (wide angle X-ray) spectrum, most likely due to the very thin film and/or its partially amorphous state. Moreover, the Fourier transform infrared (FTIR) spectrum of the coated particles (see Figure A1) shows features of molybdenum blue oxide, which is an unordered, complex molybdenum phase and typically contains a mixture of Mo5+/Mo6+-Ions. Therefore, calculations were also done for Mo5+ with an effective ionic radius of 0.46–0.61 Angstrom as given by Shannon [26]. The range of ionic radii includes uncertainties regarding the coordination number of the Mo5+ ions, which might be less coordinated on the surface and could either be 4 or 6. Nonetheless the calculated field strength of 8.2–10.9 Å−1 results in an activation energy of 117–124 kJ/mol according to the data given by Loh et al. and is thus in good agreement with our experimental value of about 123 ± 5 kJ/mol.
Materials 08 00966 g002 1024
Figure 2. Arrhenius plot for CVD based growth rates of molybdenum oxide films on silica particles generated freshly by CVS (black dots), silica particles generated by CVS and coated with an additional layer of bismuth oxide (open square), and commercially available silica particles (open dot). The dashed line fit was used to derive the activation energy.
Figure 2. Arrhenius plot for CVD based growth rates of molybdenum oxide films on silica particles generated freshly by CVS (black dots), silica particles generated by CVS and coated with an additional layer of bismuth oxide (open square), and commercially available silica particles (open dot). The dashed line fit was used to derive the activation energy.
Materials 08 00966 g002
As stated above, surface hydroxyl groups favor the decomposition of the precursor on the particle surface (as opposed to homogeneous decomposition in the gas phase) and thus favor a good quality coating. The aerosol based integrated approach is advantageous in this regard because substrate surfaces are very clean and free of residue from solvents, and have a high density of hydroxyl groups [27]. Substrate particles can thus be coated directly in a continuous process to achieve conformal shells. By contrast, experiments in the same coating reactor with as-received commercial grade silica particles did not result in conformal coatings as shown in Figure 3a. This can be attributed to organic residue, which was found in FTIR investigations (see Figure A2) and most likely originated from the liquid based synthesis process of those particles. The residues were apparently not distributed uniformly across the particle surface, leading to variable layer morphologies ranging from completely uncoated to partially or even completely coated surfaces in the same batch (see Figure A3 for further TEM images). When removing this residue by calcination at 600 °C in air for 5 h, it was again possible to obtain conformal coatings with film growth rates similar to the CVS generated particles, as shown in Figure 2 and Figure 3b. Note that the residence times were shorter in this case due to practical limitations with the aerosolization of commercial silica powder, which was done in a fluidized bed.
Similar film growth rates were also obtained for consecutive coating steps to produce core-shell structures with an inner bismuth oxide shell and an outer molybdenum oxide shell as shown in Figure 3c. It was not possible to vary the coating temperature systematically in order to obtain a combined activation energy because of insufficient contrast between layers in the TEM images. However one may assume that the overall activation energy is similar to the values reported above, since it is mostly governed by chemisorption and decarbonylation on already formed molybdenum oxide, except for the first monolayer. Based on an ionic radius of 0.96 Angstrom for Bi3+ [26] in the bismuth oxide layer and comparable substrate field strengths given by Loh et al. [22], the activation energy for that first molybdenum monolayer on the bismuth oxide shell can be estimated to 102 kJ/mol. This remains to be verified. The film growth of bismuth oxide on silica will be discussed separately in the next paragraph.
Materials 08 00966 g003 1024
Figure 3. TEM images of (a) commercial silica particles (AngstromSphere™) used as-received and coated with molybdenum oxide, where residues on the particle surface hinder conformal coating; (b) the same commercial silica particles calcinated prior to coating to remove residues and then coated with molybdenum oxide; (c) CVS generated silica particles coated successively with bismuth oxide and molybdenum oxide.
Figure 3. TEM images of (a) commercial silica particles (AngstromSphere™) used as-received and coated with molybdenum oxide, where residues on the particle surface hinder conformal coating; (b) the same commercial silica particles calcinated prior to coating to remove residues and then coated with molybdenum oxide; (c) CVS generated silica particles coated successively with bismuth oxide and molybdenum oxide.
Materials 08 00966 g003

2.2. Bismuth Oxide Coatings

The precursor triphenyl-bismuth requires considerably higher CVD temperatures. Conformal coatings with a closed bismuth oxide shell were obtained in the range of 350–410 °C, as shown in Figure 1. Homogeneous decomposition sets in over about 410 °C. Figure 4 shows the Arrhenius plot for silica particles with a conformal bismuth oxide shell as shown in Figure 1a,b. The activation energy between 350 and 390 °C is 155 ± 10 kJ/mol. One can compare this value to data by Bedoya et al. [14], who used the same precursor in a cold wall CVD reactor to coat planar Pt and Ir substrates at reduced pressure. These authors did not take into account the homogeneous decomposition of precursor, which lowers growth rates significantly toward higher temperatures on as shown in Figure 4. While the average activation energy given by the authors was 100 ± 10 kJ/mol, the value for the temperature region of pure film growth (dashed line between 350 and 400 °C) agrees well with our result, despite significant differences in material system, measurement techniques and absolute film thickness.
Following the same line of thought as before, one may assume that precursor deposition now occurs via adsorption and interaction with surface hydroxyl groups by phenyl-ligand substitution, followed by successive complete loss of the ligands. Due to weakening of the metal-phenyl bond by attractive surface groups, the activation energy is somewhat lower than the average bond dissociation energy of 194 ± 10 kJ/mol for the Bi-Ph bond in gas phase triphenyl bismuth as reported by Steele [28].
The growth mechanism can now be described with a Langmuir-Hinshelwood model [14]. Deposition proceeds through simultaneous adsorption of precursor and oxygen molecules on adjacent surface sites, followed by their interaction. The growth rate is thus a function of precursor partial pressure pBi as given by Equation (1) for a constant oxygen partial pressure [14]:
growth rate γ = K 1 ∙ p Bi ( 1 + K 2 ∙ p Bi ) 2
with K1 = 5.51 × 10−3 nm/(Pa·s) and K2 = 9.49 × 10−3 Pa−1 obtained as fitting parameters to our data.
Figure 5 shows that the film growth rates in our aerosol process are described well by this model. They increase with increasing pBi partial pressure and gradually level off at high values due to the onset of homogeneous gas phase decomposition.
Materials 08 00966 g004 1024
Figure 4. Arrhenius plot for CVD based growth rates of bismuth oxide films on silica particles generated freshly by CVS (black dots) and growth rates derived from Bedoya et al. [14] (grey dots). The data of Bedoya et al. were fitted with separate regression lines for the temperature ranges with and without significant homogeneous precursor decomposition.
Figure 4. Arrhenius plot for CVD based growth rates of bismuth oxide films on silica particles generated freshly by CVS (black dots) and growth rates derived from Bedoya et al. [14] (grey dots). The data of Bedoya et al. were fitted with separate regression lines for the temperature ranges with and without significant homogeneous precursor decomposition.
Materials 08 00966 g004
Materials 08 00966 g005 1024
Figure 5. CVD based film growth rates vs. partial pressure of the bismuth precursor. Data for bismuth oxide on silica particles generated freshly by CVS, fit function for Langmuir-Hinshelwood growth kinetics.
Figure 5. CVD based film growth rates vs. partial pressure of the bismuth precursor. Data for bismuth oxide on silica particles generated freshly by CVS, fit function for Langmuir-Hinshelwood growth kinetics.
Materials 08 00966 g005

3. Experimental Section

Details of the synthesis process can also be found in previous publications [21,29,30]. Silica core particles were synthesized by decomposition of tetra-ethyl-ortho-silicate (TEOS) at 1000 °C in a flow reactor, transferred and sintered to spherical shape at 1500 °C in a second hot wall reactor, and then transferred directly to a coating reactor, to form shells of molybdenum or bismuth oxide films by CVD. All process steps occur in the gas phase at atmospheric pressure. In case of a dual coating, successive coating reactors at 390 °C (bismuth-CVD) and 130 °C (molybdenum-CVD) were applied. The respective precursors for molybdenum oxide and bismuth oxide were molybdenum hexacarbonyl and triphenyl bismuth. A small amount (~10%) of titanium precursor (titanium tetra-isopropoxide) was added in the CVS step to ensure complete sintering to spherical particles. For characterization and determination of the growth rates, particles were directly deposited from the gas phase onto TEM grids by impaction and analyzed without further sample treatment. A Philips CM 12 (120 keV) was used to record the TEM images. The film thickness was determined manually using the ImageJ© software (National Institute of Mental Health, Bethesda, MD, USA). Growth rates were derived based on the calculated residence time in the coating reactor.
Commercial grade 200-nm silica particles (AngstromSphere™, Fiber Optic Center Inc., New Bedford, MA, USA) were aerosolized in a fluidized bed as described by Clemente et al. [31] and then fed into the CVD coating reactor. Calcination prior to the experiments was done in air for 5 h at 600 °C. FTIR spectra of the particles were recorded using the postassium bromide disc method and a Vector 22 FTIR spectrometer (Bruker, Ettlingen, Germany).

4. Conclusions

An aerosol process combining chemical vapor synthesis and chemical vapor deposition at atmospheric pressure was used to synthesize spherical core-shell structures of silica of 60–120 nm covered with thin layers of molybdenum and/or bismuth oxide in the range of 1–10 nm. Dual layer structures with molybdenum oxide on bismuth oxide were synthesized by two coating reactors in series. The CVS/CVD process is continuous and solvent-free, leading to clean, hydroxylated substrate surfaces and conformal coatings. Commercial grade silica particles coated by the same method required an additional calcination to remove organic residues from the liquid-phase synthesis process which hinder the formation of conformal shells.
Activation energies for film growth from the respective precursors (molybdenum hexacarbonyl and triphenyl bismuth) were found to be 123 ± 10 and 155 ± 10 kJ/mol. These values compare well with data from the literature, provided homogeneous decomposition of the precursor at elevated process temperatures is taken into account. The deposition kinetics for bismuth oxide are described well by a Langmuir-Hinshelwood mechanism.

Acknowledgments

Funding for this work was in part provided by the Deutsche Forschungsgemeinschaft (DFG) under grant Ka-18/1373. This project is part of the JointLab IP3, a joint initiative of KIT and BASF. Financial support by the ministry of science, research and the arts of Baden-Württemberg (Az. 33-729.61-3) is gratefully acknowledged. The authors wish to thank A. Linnenbach for his help with the experiments.

Author Contributions

F.W. designed and performed the experiments. F.W., M.S. and G.K. analyzed the data and wrote the paper.

Appendix

Materials 08 00966 g006 1024
Figure A1. FTIR spectra of the silica particles before and after coating with molybdenum oxide by combined CVS/CVD. The additional peaks in the coated sample at 955, 914 and 563 cm−1 can be assigned to terminal double-bond Mo=O vibrations in surface molybdates [32], Mo–O–Si linkage vibrations [33] and single bond Mo–O vibration in octahedral MoO6 units [34], respectively. The broad band in the range of 600–900 cm−1 is due to overlapping Mo–O single bond and Mo–O–Mo vibrations of Mo–Ions in tetrahedral and octahedral coordination and typically observed in nonstoichiometric molybdenum oxides [35].
Figure A1. FTIR spectra of the silica particles before and after coating with molybdenum oxide by combined CVS/CVD. The additional peaks in the coated sample at 955, 914 and 563 cm−1 can be assigned to terminal double-bond Mo=O vibrations in surface molybdates [32], Mo–O–Si linkage vibrations [33] and single bond Mo–O vibration in octahedral MoO6 units [34], respectively. The broad band in the range of 600–900 cm−1 is due to overlapping Mo–O single bond and Mo–O–Mo vibrations of Mo–Ions in tetrahedral and octahedral coordination and typically observed in nonstoichiometric molybdenum oxides [35].
Materials 08 00966 g006
Materials 08 00966 g007 1024
Figure A2. FTIR spectra of commercial silica particles (AngstromSphere™) measured as-received and after calcination at 600 °C in air. Peak positions of organic residues are indicated. The peak around 960 is attributed to surface hydroxyl groups and –CH2 vibrations.
Figure A2. FTIR spectra of commercial silica particles (AngstromSphere™) measured as-received and after calcination at 600 °C in air. Peak positions of organic residues are indicated. The peak around 960 is attributed to surface hydroxyl groups and –CH2 vibrations.
Materials 08 00966 g007
Materials 08 00966 g008 1024
Figure A3. TEM image of commercially available silica particles used without further treatment and coated with molybdenum oxide. The picture shows different morphologies of the coating, likely due to irregular residues on the particle surface, which hinder conformal coating.
Figure A3. TEM image of commercially available silica particles used without further treatment and coated with molybdenum oxide. The picture shows different morphologies of the coating, likely due to irregular residues on the particle surface, which hinder conformal coating.
Materials 08 00966 g008

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Faust, M.; Enders, M.; Gao, K.; Reichenbach, L.; Muller, T.; Gerlinger, W.; Sachweh, B.; Kasper, G.; Bruns, M.; Bräse, S.; et al. Synthesis of Pt/SiO2 catalyst nanoparticles from a continuous aerosol process using novel cyclo-octadienylplatinum precursors. Chem. Vap. Depos. 2013, 19, 274–283. [Google Scholar] [CrossRef]
  2. Pratsinis, S.E. Aerosol-based technologies in nanoscale manufacturing: From functional materials to devices through core chemical engineering. AIChE J. 2010, 56, 3028–3035. [Google Scholar] [CrossRef]
  3. Sigmund, S.; Yu, M.; Meyer, J.; Kasper, G. An aerosol-based process for electrostatic coating of particle surfaces with nanoparticles. Aerosol Sci. Technol. 2013, 48, 142–149. [Google Scholar] [CrossRef]
  4. Bhakoo, A.; Bond, G.C.; Rees, R.D.; Sauerhammer, B.; Taylor, A.O.; York, I. Supported binary oxide monolayers as selective oxidation catalysts: Bi2Mo3O12/TiO2. Catal. Lett. 1999, 57, 55–60. [Google Scholar] [CrossRef]
  5. Debecker, D.P.; Schimmoeller, B.; Stoyanova, M.; Poleunis, C.; Bertrand, P.; Rodemerck, U.; Gaigneaux, E.M. Flame-made MoO3/SiO2-Al2O3 metathesis catalysts with highly dispersed and highly active molybdate species. J. Catal. 2011, 277, 154–163. [Google Scholar] [CrossRef]
  6. Duc, D.T.; Ha, H.N.; Fehrmann, R.; Riisager, A.; Le, M.T. Selective oxidation of propylene to acrolein by silica-supported bismuth molybdate catalysts. Res. Chem. Intermed. 2011, 37, 605–616. [Google Scholar] [CrossRef]
  7. Ohler, N.; Bell, A.T. Selective oxidation of methane over MoOx/SiO2: Isolation of the kinetics of reactions occurring in the gas phase and on the surfaces of SiO2 and MoOx. J. Catal. 2005, 231, 115–130. [Google Scholar] [CrossRef]
  8. Greiner, M.T.; Helander, M.G.; Wang, Z.B.; Tang, W.M.; Qiu, J.; Lu, Z.H. A metallic molybdenum suboxide buffer layer for organic electronic devices. Appl. Phys. Lett. 2010, 96, 213302:1–213302:3. [Google Scholar] [CrossRef]
  9. Cheng, L.; Shao, M.W.; Wang, X.H.; Hu, H.B. Single-crystalline molybdenum trioxide nanoribbons: Photocatalytic, photoconductive, and electrochemical properties. Chem. Eur. J. 2009, 15, 2310–2316. [Google Scholar] [CrossRef] [PubMed]
  10. Ho, C.-H.; Chan, C.-H.; Huang, Y.-S.; Tien, L.-C.; Chao, L.-C. The study of optical band edge property of bismuth oxide nanowires α-Bi2O3. Opt. Express 2013, 21, 11965–11972. [Google Scholar] [CrossRef] [PubMed]
  11. Abdellaoui, A.; Leveque, G.; Donnadieu, A.; Bath, A.; Bouchikhi, B. Iteratively derived optical constants of MoO3 polycrystalline thin films prepared by CVD. Thin Solid Films 1997, 304, 39–44. [Google Scholar] [CrossRef]
  12. Bandoli, G.; Barreca, D.; Brescacin, E.; Rizzi, G.A.; Tondello, E. Pure and mixed phase Bi2O3 thin films obtained by metal organic chemical vapor deposition. Chem. Vap. Depos. 1996, 2, 238–242. [Google Scholar] [CrossRef]
  13. Barreca, D.; Rizzi, G.A.; Tondello, E. A chemical vapour deposition route to MoO3-Bi2O3 thin films. Thin Solid Films 1998, 333, 35–40. [Google Scholar] [CrossRef]
  14. Bedoya, C.; Condorelli, G.G.; Anastasi, G.; Baeri, A.; Scerra, F.; Fragala, I.L.; Lisoni, J.G.; Wouters, D. Mocvd of bismuth oxides: Transport properties and deposition mechanisms of the Bi(C6H5)3 precursor. Chem. Mater. 2004, 16, 3176–3183. [Google Scholar] [CrossRef]
  15. Diskus, M.; Nilsen, O.; Fjellvag, H.; Diplas, S.; Beato, P.; Harvey, C.; van Schrojenstein Lantman, E.; Weckhuysen, B.M. Combination of characterization techniques for atomic layer deposition MoO3 coatings: From the amorphous to the orthorhombic α-MoO3 crystalline phase. J. Vac. Sci. Technol. A 2012, 30. [Google Scholar] [CrossRef]
  16. Ivanova, T.; Gesheva, K.A.; Szekeres, A. Structure and optical properties of CVD molybdenum oxide films for electrochromic application. J. Solid State Electrochem. 2002, 7, 21–24. [Google Scholar] [CrossRef]
  17. Lamouroux, E.; Corrias, M.; Ressier, L.; Kihn, Y.; Serp, P.; Kalck, P. Improving purity and size control of iron- and molybdenum-supported nanoparticles prepared by omcvd from their carbonyl precursors. Chem. Vap. Depos. 2008, 14, 275–278. [Google Scholar] [CrossRef]
  18. Shi, G.; Franzke, T.; Sánchez, M.D.; Xia, W.; Weis, F.; Seipenbusch, M.; Kasper, G.; Muhler, M. Thin-film β-MoO3 supported on α-Fe2O3 as a shell–core catalyst for the selective oxidation of methanol to formaldehyde. ChemCatChem 2012, 4, 760–765. [Google Scholar] [CrossRef]
  19. Shi, G.; Franzke, T.; Xia, W.; Sanchez, M.D.; Muhler, M. Highly dispersed MoO3/Al2O3 shell-core composites synthesized by CVD of Mo(CO)6 under atmospheric pressure. Chem. Vap. Depos. 2011, 17, 162–169. [Google Scholar] [CrossRef]
  20. Reuge, N.; Dexpert-Ghys, J.; Caussat, B. Fluidized-bed mocvd of Bi2O3 thin films from bismuth triphenyl under atmospheric pressure. Chem. Vap. Depos. 2010, 16, 123–126. [Google Scholar] [CrossRef]
  21. Weis, F.; Seipenbusch, M.; Kasper, G. Coating thickness measurements on gas-borne nanoparticles by combined mobility and aerodynamic spectrometry. J. Nanopart. Res. 2015, 17, 39. [Google Scholar] [CrossRef]
  22. Loh, W.L.; Jaenicke, S.; Chuah, G.K.; Ang, H.G. Temperature programmed decomposition (TPDE) of [Mo(CO)6] on metal oxide supports: A novel tool to elucidate surface acidity and surface-mediated reactions. Talanta 1998, 45, 739–749. [Google Scholar] [CrossRef] [PubMed]
  23. Ang, H.-G.; Chan, K.-S.; Chuah, G.-K.; Jaenicke, S.; Neo, S.-K. Thermal reactions of Mo(CO)6 on metal-oxide surfaces. J. Chem. Soc. Dalton Trans. 1995, 1995, 3753–3758. [Google Scholar] [CrossRef]
  24. Lewis, K.E.; Golden, D.M.; Smith, G.P. Organometallic bond dissociation energies: Laser pyrolysis of Fe(CO)5, Cr(CO)6, Mo(CO)6 and W(CO)6. J. Am. Chem. Soc. 1984, 106, 3905–3912. [Google Scholar] [CrossRef]
  25. Pauling, L. The Nature of the Chemical Bond, 3rd ed.; Cornell University Press: Ithaca, NY, USA, 1960. [Google Scholar]
  26. Shannon, R.D. Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides. Acta Crystallogr. Sect. A 1976, 32, 751–767. [Google Scholar] [CrossRef]
  27. Binder, A.; Heel, A.; Kasper, G. Deposition of palladium nanodots of controlled size and density onto surface-modified SiO2 particles by an atmospheric pressure CVS/MOCVD process. Chem. Vap. Depos. 2007, 13, 48–54. [Google Scholar] [CrossRef]
  28. Steele, W.V. The standard enthalpies of formation of the triphenyl compunds of the Group V elements 2. Triphenylbismuth and the Ph-Bi mean bond-dissociation energy. J. Chem. Thermodyn. 1979, 11, 187–192. [Google Scholar] [CrossRef]
  29. Weis, F.; Gao, K.; Seipenbusch, M.; Kasper, G. An aerosol-process for the synthesis of nanostructured molybdenum oxide catalysts by integrated chemical vapour synthesis/chemical vapour deposition at atmospheric pressure. J. Nanosci. Nanotechnol. 2011, 11, 8313–8317. [Google Scholar] [CrossRef] [PubMed]
  30. Weis, F.; Schneider, R.; Seipenbusch, M.; Kasper, G. Synthesis of Bi2O3/SiO2 core-shell nanoparticles by an atmospheric CVS/CVD process and their modification by hydrogen or electron-beam induced reduction. Surf. Coat. Technol. 2013, 230, 93–100. [Google Scholar] [CrossRef]
  31. Clemente, A.; Balas, F.; Lobera, M.P.; Irusta, S.; Santamaria, J. Fluidized bed generation of stable silica nanoparticle aerosols. Aerosol Sci. Technol. 2013, 47, 867–874. [Google Scholar] [CrossRef]
  32. Liu, Y.; Ma, X.; Wang, S.; Gong, J. The nature of surface acidity and reactivity of MoO3/SiO2 and MoO3/TiO2–SiO2 for transesterification of dimethyl oxalate with phenol: A comparative investigation. Appl. Catal. B Environ. 2007, 77, 125–134. [Google Scholar] [CrossRef]
  33. Said, A.E.-A.A.; El-Wahab, M.M.A. Surface properties and catalytic behavior of MoO3/SiO2 in esterification of acetic acid with ethanol. J. Chem. Technol. Biotechnol. 2006, 81, 329–335. [Google Scholar] [CrossRef]
  34. Belhekar, A.A.; Ayyappan, S.; Ramaswamy, A.V. FT-IR studies on the evolution of different phases and their interaction in ferric molybdate-molybdenum trioxide catalysts. J. Chem. Technol. Biotechnol. 1994, 59, 395–402. [Google Scholar] [CrossRef]
  35. Dhas, N.A.; Gedanken, A. Characterization of sonochemically prepared unsupported and silica-supported nanostructured pentavalent molybdenum oxide. J. Phys. Chem. B 1997, 101, 9495–9503. [Google Scholar] [CrossRef]

Share and Cite

MDPI and ACS Style

Weis, F.; Seipenbusch, M.; Kasper, G. Film Growth Rates and Activation Energies for Core-Shell Nanoparticles Derived from a CVD Based Aerosol Process. Materials 2015, 8, 966-976. https://doi.org/10.3390/ma8030966

AMA Style

Weis F, Seipenbusch M, Kasper G. Film Growth Rates and Activation Energies for Core-Shell Nanoparticles Derived from a CVD Based Aerosol Process. Materials. 2015; 8(3):966-976. https://doi.org/10.3390/ma8030966

Chicago/Turabian Style

Weis, Frederik, Martin Seipenbusch, and Gerhard Kasper. 2015. "Film Growth Rates and Activation Energies for Core-Shell Nanoparticles Derived from a CVD Based Aerosol Process" Materials 8, no. 3: 966-976. https://doi.org/10.3390/ma8030966

Article Metrics

Back to TopTop