Search Results (6)

This review article delves into the intriguing phenomenon of low-temperature thermochromism, whereby materials change color in response to temperature variations, with a particular focus on its applications in temperature-sensitive fields like medical storage. By closely examining thermochromic materials, this article highlights their potential to offer innovative solutions for monitoring and preserving thermolabile products that require strict temperature control. This leads to a special emphasis on polydiacetylenes (PDAs), a class of conjugated polymers with unique low-temperature thermochromic properties, positioning them as promising candidates for reliable temperature indicators. This article then explores the underlying mechanisms for fine-tuning the thermochromic behavior of PDAs, particularly discussing recent advancements in PDA design, such as structural alterations of monomers to achieve low-temperature thermochromism. These modifications, influenced by factors like side-chain length, hydrogen-bonding interactions, and the use of copolymers, are intended to result in irreversible color transitions at specific low temperatures, which is crucial to maintaining the integrity of thermally sensitive products. Finally, this article discusses the potential applications of PDAs as thermochromic sensors in tissue biobanking, where their ability to provide visual indications of temperature fluctuations could significantly enhance the monitoring and management of biological samples. Full article

In this study, we demonstrate six novel xanthene derivatives and their spectroscopic and chemical properties. The presented synthesis examination allowed us to obtain two different compounds during one step, with open and closed lactone rings substituted with different length alkyl chains. Increasing the reaction efficiency to 77% was obtained using the microwave-assisted method. Moreover, the modification of O-alkylation synthesis in an ecofriendly way using a ball mill led to achieving exclusively one opened ring product. All of the synthesized compounds showed different spectroscopic behaviors in comparison with the different organic dyes; the typical concentration quenching of luminescence was not observed. The relationship between the length of the alkyl chain and the time of luminescence decay is presented. Synthetized closed forms of dyes turned out to be promising leuco dyes. For the first time, an ionic liquid was used as a developer of synthesized xanthene derivatives (as leuco dyes), which led to obtaining an irreversible thermochromic marker. Full article

This study examines the implementation of an MnNH₄P₂O₇ (ammonium manganese III pyrophosphate)-based coating on structural elements to obtain temperature information with color changes. Based on the MnNH₄P₂O₇ material, a coating was prepared and deposited on cement mortar surfaces. Heat experiments were then conducted to evaluate the thermochromism on the fabricated samples. The coated samples exhibited a superior irreversible thermochromic property at 400 °C with a color change from dark violet to light grayish blue at the heated surface. The color changes were retrieved at each temperature using a digital camera, and the change in color properties was evaluated in the RGB and L*a*b* color spaces using image processing techniques. With increasing temperature from room temperature, the RGB values were almost constant until 200 °C. At higher temperatures, the color changes started to accelerate until 400 °C. The values showed a 167%, 567%, and 49% increase in R, G, and B values, respectively, at 400 °C. In the L*a*b* color space, when the temperature was increased from room temperature to 400 °C, the L*a*b* values showed an increase of 211%, a decrease of 94%, and an increase of 78%, respectively. Full article

In recent years, advanced materials have attracted considerable interest in the field of temperature detection and sensing. This study examined the thermochromic properties of inorganic manganese violet (MV) with increasing temperature. According to the thermochromic test, the material was found to have reversible and irreversible color change properties. The MV pigment was then applied to cementitious material at ratios of 1%, 3%, and 5%. The mixed cement samples with MV pigment were heated in a furnace, and digital images were captured at each temperature interval to evaluate the changes in the color information on the surface of the specimen. The mixed samples exhibited an irreversible thermochromic change from dark violet to grayish green above 400 °C. At the critical temperature of 440 °C, the RGB values increased by approximately 22%–55%, 28%–68%, and 7%–25%, depending on the content of MV pigment. In Lab space, the L value increased by approximately 23%–60% at 440 °C. The a value completely changed from positive to negative, and the b value changed from negative to positive. All the values differed according to the content of MV pigment at room temperature but approached similar ranges at the critical temperature, irrespective of the amount of MV pigment. To assess the changes in their microstructure and composition, scanning electron microscopy and energy dispersive X-ray spectroscopy were performed on the samples exposed to temperatures ranging from room temperature to 450 °C. Full article

An irreversible thermochromic material based on manganese violet (MnNH₄P₂O₇) is synthesized. The crystal phase, chemical composition, and morphology of the synthesized material are analyzed using X-ray diffraction, scanning electron microscopy coupled with energy-dispersive X-ray spectrometry, and Fourier-transform infrared spectroscopy. The absorption spectra of the synthesized material are obtained using a UV-Vis spectrometer, and the thermochromism exhibited by the powdered samples at high temperatures is also investigated. The as-synthesized manganese violet pigment consists of pure α-MnNH₄P₂O₇ phase. In addition, the synthesized pigment largely consists of hexagonal crystals with a diameter of hundreds of nanometers. On heating, the pigment simultaneously loses H₂O and NH₃ in two successive steps at approximately 330–434.4 °C and 434.4–527 °C, which correspond to the formation of an intermediate phase and of Mn₂P₄O₁₂, respectively. An overall mass loss of 14.22% is observed, which is consistent with the expected 13.79%. An irreversible color change from violet to white is observed after exposure of the synthesized manganese violet pigment at 400 °C for 30 min. This is attributed to the oxidation of ammonia to hydroxylamine, which then decomposes to nitrogen and water, or alternatively to the direct oxidation of ammonia to nitrogen. Furthermore, we demonstrate the potential application of synthesized manganese violet in the production of irreversible thermochromic paint by mixing with potassium silicate solution as a binder and deionized water as a solvent at a specific ratio. The thermochromic paint is then applied in fabrication of irreversible thermochromic sensors by coating it onto a steel plate surface. Finally, we show that manganese violet-based irreversible thermochromic sensors are able to detect temperatures around 400 °C by changing color from violet to white/milky. Full article

Surgical simulators have recently attracted attention because they enable the evaluation of the surgical skills of medical doctors and the performance of medical devices. However, thermal damage to the human body during surgery is difficult to evaluate using conventional surgical simulators. In this study, we propose a functional surgical model with a temperature-indicating function for the evaluation of thermal damage during surgery. The simulator is made of a composite material of polydimethylsiloxane and a thermochromic dye, which produces an irreversible color change as the temperature increases. Using this material, we fabricated a three-dimensional blood vessel model using the lost-wax process. We succeeded in fabricating a renal vessel model for simulation of catheter ablation. Increases in the temperature of the materials can be measured by image analysis of their color change. The maximum measurement error of the temperature was approximately −1.6 °C/+2.4 °C within the range of 60 °C to 100 °C. Full article