Search Results (9)

Hip resurfacing is a bone-conserving alternative to total hip replacement particularly suited to younger or more active patients with good bone stock. Historical issues with metal-on-metal hip resurfacing devices have led to investigations of new materials. In this study, the wear of a BIOLOX delta ceramic-on-ceramic hip resurfacing under a range of activities of daily function was investigated in an experimental simulation model. Under a standard walking gait, increased frequency, and stop–dwell–start conditions, the wear of the ceramic head and cup was low and at the limit of the sensitivity of the measurement technique used (<0.1 mm³/million cycles). Only when tested under a jogging-like protocol with higher loading (maximum 4.5 kN) coupled with higher frequency (1.25 Hz), under both continuous running and stop–dwell–start conditions, was wear measurable but still low, with a mean <0.15 mm³/million cycles. At the conclusion of the study, no wear scar was visible on any components and no changes in the surface roughness of the implants was measured. This short-term, pre-clinical study showed low wear of BIOLOX delta ceramic-on-ceramic hip resurfacings when evaluated under a range of activities of daily living and that this material combination has potential for the next generation of large-diameter hip bearings. Full article

Ceramic-on-ceramic (CoC) bearings are widely used in total hip arthroplasty due to their extremely low wear rate, excellent chemical stability, and good biocompatibility. They are considered one of the most reliable long-term friction bearing systems. Although frictional instability, lubrication regime transitions, and microstructural damage mechanisms have been widely reported at the experimental and retrieval-analysis levels, current clinical evidence, limited by follow-up duration and event incidence, has not demonstrated a definitive negative impact on the clinical performance of fourth-generation ceramic components, including BIOLOX^® delta. Data from national arthroplasty registries consistently demonstrate excellent survivorship and low complication rates for 4th-generation ceramics in both hard-on-soft and hard-on-hard configurations. The most reported causes for revision, such as infection, dislocation, aseptic loosening, and periprosthetic fracture, are not primarily associated with ceramic-related complications, such as ceramic fracture, excessive wear, squeaking, and revision, related to bearing failure; however, these mechanisms remain highly relevant for the design and evaluation of emerging ceramic materials and next-generation implant systems, where inadequate control may potentially impact long-term clinical performance. This review summarizes recent advances in the tribological research of CoC artificial joints, focusing on clinical tribological challenges, material composition and surface characteristics, lubrication mechanisms, wear and microdamage evolution, and third-body effects. Recent progress in ceramic toughening strategies, surface engineering, biomimetic lubrication simulation, and structural optimization is also discussed. Finally, future research directions are outlined to support the performance optimization and long-term reliability assessment of CoC artificial joint systems. Full article

(1) Background: The kinematic characteristics of disc prosthesis undergoing complex motion are not well understood. Therefore, examining complex motion may provide an improved understanding of the post-operative behavior of spinal implants. (2) Methods: The aim of this study was to develop kinematic tests that simulate multiplanar motion and combined rotational–translational motion in a disc prosthesis. In this context, five generic zirconia-toughened alumina (BIOLOX^®delta, CeramTec, Germany) ball and socket samples were tested in a 6 DOF spine simulator under displacement control with an axial compressive force of 100 N in five motion modes: (1) flexion–extension (FE = ± 7.5°), (2) lateral bending (LB = ± 6°), (3) combined FE-LB (4) combined FE and anteroposterior translation (AP = 3 mm), and (5) combined LB and lateral motion (3 mm). For combined rotational–translational motion, two scenarios were analyzed: excessive translational movement after sample rotation (scenario 1) and excessive translational movement during rotation (scenario 2). (3) Results: For combined FE-LB, the resultant forces and moments were higher compared to the unidirectional motion modes. For combined rotational–translational motion (scenario 1), subluxation occurred at FE = 7.5° with an incremental increase in AP translation = 1.49 ± 0.18 mm, and LB = 6° with an incremental increase of lateral translation = 2.22 ± 0.16 mm. At the subluxation point, the incremental increase in AP force and lateral force were 30.4 ± 3.14 N and 40.8 ± 2.56 N in FE and LB, respectively, compared to the forces at the same angles during unidirectional motion. For scenario 2, subluxation occurred at FE = 4.93° with an incremental increase in AP translation = 1.75 mm, and LB = 4.52° with an incremental increase in lateral translation = 1.99 mm. At the subluxation point, the incremental increase in AP force and lateral force were 39.17 N and 38.94 N in FE and LB, respectively, compared to the forces in the same angles during the unidirectional motion. (4) Conclusions: The new test protocols improved the understanding of in vivo-like behavior from in vitro testing. Simultaneous translation–rotation motion was shown to provoke subluxation at lower motion extents. Following further validation of the proposed complex motion testing, these new methods can be applied future development and characterization of spinal motion-preserving implants. Full article

To understand the possible lubricant mechanism in ceramic-on-ceramic hip joint prostheses, biochemical reactions of the synovial fluid and the corresponding frictional coefficients were studied. The experiments were performed in a hip joint simulator using the ball-on-cup configuration with balls and cups made from two types of ceramics, BIOLOX^®forte and BIOLOX^®delta. Different lubricants, namely albumin, γ-globulin, hyaluronic acid and three model synovial fluids, were studied in the experiments and Raman spectroscopy was used to analyze the biochemical responses of these lubricants at the interface. BIOLOX^®delta surface was found less reactive to proteins and model fluid lubricants. In contrast, BIOLOX^®forte ball surface has shown chemisorption with both proteins, hyaluronic acid and model fluids imitating total joint replacement and osteoarthritic joint. There was no direct correlation between the measured frictional coefficient and the observed chemical reactions. In summary, the study reveals chemistry of lubricant film formation on ceramic hip implant surfaces with various model synovial fluids and their components. Full article

Ceramic-on-ceramic bearings for total hip replacement are considered the best choice to avoid problems such as osteolysis and wear, mainly related to soft bearings. The aim of this work was to investigate in a comparative way different kinds of ceramic femoral heads for total hip replacements from a biotribological point of view, discussing the results obtained in terms of topographies, presence of metal transfer (MT) phenomena, and wettability on their worn surfaces in a tribological framework. Different ceramic femoral heads derived from in vitro wear tests, retrieved form patients, and brand new total hip replacements were investigated. The patients group had an average age of 60 years (ranging from 27 to 83). In most cases, the cause of failure was aseptic loosening of the acetabular component. Roughness analyses were performed to measure the tribological surface evolution of the material; an SEM and EDS investigation on the explanted heads proves and quantified MT, while the wettability was measured through a novel optical laboratory set-up with the aim to furnish useful data in the framework of synovial lubrication phenomena acting in the tribosystem. For the average roughness measurements on explanted specimens were considered three parameters (Ra = the average area between the roughness profile and its mean line; Rt = the vertical distance from the deepest valley to the highest peak of the roughness profile; and Rsk = it is the skewness and it is a measure of the asymmetry of the amplitude distribution function. In other words, the skewness indicates whether a surface is dominated by peaks or by valleys) and their values were: Ra 0.22 ± 0.12 μm, Rt 34.5 ± 13.5 μm and Rsk −0.01 ± 11.3; on the new specimens we measured Ra 0.01 ± 0.001 μm, Rt 0.12 ± 0.09 μm, and Rsk = 5.67 ± 8.7; for the in vitro specimens they were Ra 0.05 ± 0.12 μm, Rt 0.71 ± 1.4 μm and Rsk 7.73 ± 20.6. The wettability angle measurements showed hydrophilic surfaces for all femoral heads considered in this study with small differences between the three investigated categories, allowing to discuss their effects on the biobearings’ lubrication phenomena. Full article

The purpose of the present study was to compare the wear behavior of ceramic-on-vitamin-E-diffused crosslinked polyethylene (Vit-E XLPE) hip bearings employing the gold standard oxide ceramic, zirconia (ZrO₂)-toughened alumina (Al₂O₃) (ZTA, BIOLOX^®delta) and a new non-oxide ceramic, silicon nitride (Si₃N₄, MC^2®). In vitro wear test was performed using a 12-station hip joint simulator. The test was carried out by applying the kinematic inputs and outputs as recommended by ISO 14242-1:2012. Vitamin-E-diffused crosslinked polyethylene (Vit-E XLPE) acetabular liners (E1^®) were coupled with Ø28-mm ZTA and Si₃N₄ femoral heads. XLPE liner weight loss over 5 million cycles (Mc) of testing was compared between the two different bearing couples. Surface topography, phase contents, and residual stresses were analyzed by contact profilometer and Raman microspectroscopy. Vit-E XLPE liners coupled with Si₃N₄ heads produced slightly lower wear rates than identical liners with ZTA heads. The mean wear rates (corrected for fluid absorption) of liners coupled with ZTA and Si₃N₄ heads were 0.53 ± 0.24 and 0.49 ± 0.23 mg/Mc after 5 Mc of simulated gait, respectively. However, after wear testing, the ZTA heads retained a smoother topography and showed fewer surface stresses than the Si₃N₄ ones. Note that no statistically significant differences were found in the above comparisons. This study suggests that the tribochemically formed soft silica layer on the Si₃N₄ heads may have reduced friction and slightly lowered the wear of the Vit-E XLPE liners. Considering also that the toughness of Si₃N₄ is superior to ZTA, the present wear data represent positive news in the future development of long-lasting hip components. Full article

Zirconia-toughened alumina (ZTA) currently represents the bioceramic gold standard for load-bearing components in artificial hip joints. ZTA is long known for its high flexural strength and fracture toughness, both properties arising from a microscopic crack-tip shielding mechanism due to the stress-induced tetragonal-to-monoclinic (t→m) polymorphic transformation of zirconia. However, there have been concerns over the years regarding the long-term structural performance of ZTA since the t→m transformation also spontaneously occurs at the material’s surface under low-temperature environmental conditions with a concomitant degradation of mechanical properties. Spontaneous surface degradation has been extensively studied in vitro, but predictive algorithms have underestimated the extent of in vivo degradation observed in retrievals. The present research focused on burst-strength assessments of Ø28 mm ZTA femoral before and after long-term in vitro hydrothermal ageing according to ISO 7206-10. An average burst strength of 52 kN was measured for pristine femoral heads. This value was ~36% lower than results obtained under the same standard conditions by other authors. A further loss of burst strength (~13% in ultimate load) was observed after hydrothermal ageing, with increased surface monoclinic content ranging from ~6% to >50%. Nevertheless, the repetitively stressed and hydrothermally treated ZTA heads exceeded the minimum burst strength stipulated by the US Food and Drug Administration (FDA) despite severe test conditions. Lastly, Raman spectroscopic assessments of phase transformation and residual stresses on the fracture surface of the femoral heads were used to clarify burst-strength fluctuations and the effect of hydrothermal ageing on the material’s overall strength degradation. Full article

Biolox^® delta has been widely used in joint replacements thanks to its high strength and wear resistance. In this study, eleven Biolox^® delta femoral head retrievals affected by metal transfer (MT) were analysed by Raman spectroscopy to estimate the tetragonal to monoclinic zirconia phase transformation, whose occurrence may compromise ceramic chemical stability and mechanical strength. The residual stress state was evaluated by both Raman and photoemission spectroscopy. V_m monoclinic zirconia contents were higher near the centre of the articulating surface and in the MT area than in the border control area of the retrievals. In only one retrieval, stress related to MT appeared a more severe condition, able to induce zirconia phase transformation; for all the others, stresses related to loading in the central region and related to MT, were conducive to a zirconia phase transformation of nearly the same extent. V_m depth profiling analyses showed that the transformation involved different thicknesses in different samples. Raman data allowed for the investigation of the mechanism of zirconia phase transformation and confirmed that the growth stage was absent and the nucleation stage was not occurring as freely as it would in unconstrained zirconia. Full article

A clear discrepancy between predicted in vitro and actual in vivo surface phase stability of BIOLOX^®delta zirconia-toughened alumina (ZTA) femoral heads has been demonstrated by several independent research groups. Data from retrievals challenge the validity of the standard method currently utilized in evaluating surface stability and raise a series of important questions: (1) Why do in vitro hydrothermal aging treatments conspicuously fail to model actual results from the in vivo environment? (2) What is the preponderant microscopic phenomenon triggering the accelerated transformation in vivo? (3) Ultimately, what revisions of the current in vitro standard are needed in order to obtain consistent predictions of ZTA transformation kinetics in vivo? Reported in this paper is a new in toto method for visualizing the surface stability of femoral heads. It is based on CAD-assisted Raman spectroscopy to quantitatively assess the phase transformation observed in ZTA retrievals. Using a series of independent analytical probes, an evaluation of the microscopic mechanisms responsible for the polymorphic transformation is also provided. An outline is given of the possible ways in which the current hydrothermal simulation standard for artificial joints can be improved in an attempt to reduce the gap between in vitro simulation and reality. Full article