Zinc Kiln Slag Recycling Based on Hydrochloric Acid Oxidative Leaching and Subsequent Metal Recovery

The limited availability of high-quality ore deposits and the environmental hazards of metallurgical wastes highlight the importance of developing resource-efficient metal recovery technologies. Zinc kiln slag (ZKS), also known as Waelz slag, a by-product material enriched in non-ferrous metals, was processed through oxidative HCl leaching with H₂O₂ as an oxidant. Thermodynamic simulation and laboratory experiments were applied to determine optimal leaching conditions to dissolve copper, zinc, and iron. Optimal leaching efficiency was achieved with consumptions of 0.8 g HCl and 0.1 g H₂O₂ per gram of ZKS, a liquid-to-solid (L/S) ratio of 5 mL/g, a temperature of 70 °C, and a duration of 180 min, which resulted in recoveries of 96.3% Cu, 93.6% Fe, and 76.8% Zn. The solid residue with 43.5 wt.% C is promising for reuse as a reductant material in pyrometallurgical processes. Copper and arsenic were separated from the leachate via cementation with iron powder, achieving recovery rates of 98.9% and 91.2%, respectively. A subsequent two-step iron precipitation produced ferric hydroxide with 52.2 wt.% Fe and low levels of impurities. As a result, the developed novel hydrochloric acid oxidative leaching and metal precipitation route for ZKS recycling provides an efficient and sustainable alternative to conventional treatment methods.