The Corrosion Susceptibility of 304L Stainless Steel Exposed to Crevice Environments

The present study focuses on the corrosion behavior of 304L stainless steel in crevice corrosion environments. The specimen with a salt deposit of 0.1 g/m² was assembled with a crevice former made of Poly-tetra fluoroethylene (PTFE) to make a test device. The assembled test devices were kept at the ambient temperature of 45 °C in combination with a relative humidity of 45%, 55%, and 70%. After testing for 5000 h, the corroded area of the specimen exposed to 70% humidity was three times larger than that subjected to 45% humidity. For the specimen sustaining a tensile force, the crack growth rate was approximately 1.4 mm/year at the stress level of 300 MPa in a crevice corrosion environment with 0.1 g/m² of sea salt deposited on the surface. The small portion of intergranular cracking occurred at the surface due to the existed strain on the surface. As cracks propagate in a grain, the grain undergoes a greater localized deformation, and some secondary cracks would develop inside the grain; transgranular cracking was vigorous due to the path corrosion that nucleated at the slip steps.