Search Results (6)

We investigated the effects of lithium disilicate ceramic thickness and translucency on the degree of polymerization of light-cured resin cement using the measure of hardness. Lithium disilicate specimens of three translucencies (low, medium and high) were prepared to four thicknesses (0.5, 1.0, 2.0 and 3.0 mm). A light-cured resin cement was cured through each of the ceramic specimens using a handheld curing light for 50 s. A 3D printed jig was used to achieve a uniform thickness of the resin cement. Directly cured resin cement was used as the control. Hardness was measured using nano-indentation to determine the degree of polymerization of the resin cement. Two-way ANOVA and Tukey post hoc tests were used to evaluate interaction between translucency and thickness. Hardness values from control specimens were assessed using the two-tailed t-test with the Bonferroni approach. The translucency of the specimens significantly influenced the hardness (p < 0.001), where a negative linear relationship between cement hardness and ceramic thickness was present for low translucency and high translucency. However, at a 0.5 mm thickness, all specimens showed similar hardness regardless of the translucency. The translucency of ceramics affected the hardness, and hence polymerization, of light-cure resin cement. However, the effect of increased thickness was a more significant factor. Full article

Introduction: Today’s dentistry frequently employs bonded partial restorations, which are usually fabricated in ceramic materials. In the last decade, hybrid materials have emerged that attempt to combine the properties of composites and ceramics. Objectives: To evaluate in vitro, by means of a microtensile test, the bond strength between CAD-CAM restorative materials and the cement recommended by their manufacturer. Material and Method: From blocks of CAD-CAM restorative material bonded to composite blocks (Filtek 500^®), beams with a bonding area of approximately 1 mm² were made and divided into four groups: EMAX (IPS e.max CAD^® lithium disilicate), VE (VITA Enamic^® polymer-infiltrated ceramic matrix), LUA (Lava Ultimate^® nano-ceramic resin with sandblasting protocol) and LUS (Lava Ultimate^® nano-ceramic resin with silica coating protocol). In each group, perimeter (external) or central (internal) beams were differentiated according to the position in the block. The samples were tested on the LMT 100^® microtensile machine. Using optical microscopy, the fractures were categorized as adhesive or cohesive (of the restorative material or composite), and the data were analysed with parametric tests (ANOVA). Results: The LUS group had the highest results (42 ± 20 MPa), followed by the LUA group (38 ± 18 MPa). EMAX had a mean of 34 ± 16 MPa, and VE was the lowest in this study (30 ± 17 MPa). In all groups, the central beams performed better than the perimeter beams. Both EMAX and VE had the most adhesive fractures, while LUA and LUS had a predominance of cohesive fractures. Conclusions: Lava Ultimate^® nanoceramic resin with the silica coating protocol obtains the best bond strength values. Full article

The aim of this study was to compare the load-to-failure resistance and optical properties of nano-lithium disilicate (NLD) with lithium disilicate (LDS) and zirconia-reinforced lithium silicate (ZLS) in different aging processes. Thirty crowns were milled from NLD, LDS, and ZLS (n = 10). All crowns were subjected to thermomechanical aging and loaded until catastrophic failure. Ten specimens from each material were prepared in two different thicknesses (0.7 mm and 1.5 mm, n = 5), and color coordinates were measured before and after coffee thermocycling. Color differences (ΔE00) and relative translucency parameter (RTP) were calculated. Data were analyzed by using ANOVA and Bonferroni-corrected t-tests (α = 0.05). ZLS had the highest load-to-failure resistance (p ≤ 0.002), while the difference between LDS and NLD was nonsignificant (p = 0.776). The interaction between material type and thickness affected ΔE00 (p < 0.001). Among the 0.7 mm thick specimens, ZLS had the lowest ΔE00 (p < 0.001). Furthermore, 1.5 mm thick ZLS had lower ΔE00 than that of 1.5 mm thick LDS (p = 0.036). Other than ZLS (p = 0.078), 0.7 mm thick specimens had higher ΔE00 (p < 0.001). The interaction between material type, thickness, and thermocycling affected RTP (p < 0.001). Thinner specimens presented higher RTP (p < 0.001). NLD and LDS had higher RTP than ZLS (p ≤ 0.036). However, 0.7 mm thick specimens had similar RTP after coffee thermocycling (p ≥ 0.265). Coffee thermocycling reduced the RTP values of 0.7 mm thick NLD (p = 0.032) and LDS (p = 0.008). NLD may endure the occlusal forces present in the posterior region. However, long-term coffee consumption may impair the esthetics of restorations particularly when thin NLD is used. Full article

The aim of this in vitro study was to investigate the fracture resistance, fracture failure pattern, and fractography of four types of chairside computer-aided design/computer-aided manufacturing (CAD/CAM) restoration materials in teeth and titanium abutments fabricated using a standardization method. An artificial mandibular left first premolar prepared for all-ceramic crown restoration was scanned. Forty extracted mandibular molars and cylindrical titanium specimens were milled into a standardized shape. A total of eighty CAD/CAM restoration blocks were milled into a crown and twenty pieces of each lithium disilicate (LS), polymer-infiltrated-ceramic-network (PICN), resin nano ceramic (RNC), and zirconia-reinforced lithium silicate (ZLS) materials were used. Crowns were bonded to abutments, and all specimens underwent thermal cycling treatment for 10,000 cycles. Fracture resistance was measured using a universal testing machine and fracture failure patterns were analyzed using optical microscopy and scanning electron microscopy. Statistical differences were analyzed using appropriate ANOVA, Tukey HSD post hoc tests, and independent sample t-tests (α = 0.05). The results indicated that, in both teeth abutments and titanium abutments, the fracture resistances showed significantly the highest values in LS and the second highest in ZLS (p < 0.05). The fracture resistances based on teeth abutments and titanium abutments were significantly different in all the CAD/CAM restoration materials (p < 0.05). There are statistically significant correlations between the types of materials and the types of abutments (p < 0.05). Each of the different materials showed different fracture failure patterns, and there was no noticeable difference in fractographic analysis. Lithium disilicates and zirconia-reinforced lithium silicates exhibited statistically high fracture resistance, indicating their suitability as restoration materials for natural teeth or implant abutments. There were no distinct differences in the fracture pattern based on the restoration and abutment materials showed that the fracture initiated at the groove where the ball indenter was toughed and propagated toward the axial wall. Full article

The development of various dental glass-ceramic materials and the evolution of novel processing technologies lead to an essential change in the clinical and technical workflow. The long-term success of a dental restoration treatment is defined by its durability, which is directly influenced by the oral environment. This study’s purpose was to evaluate the artificial aging behavior of nanostructured, respective microstructured ceramics related to surface topography, roughness, and optical properties. Six monolithic restoration materials were selected: milled lithium disilicate glass-ceramic (LDS-M) MT (medium translucency), hot-pressed lithium disilicate glass-ceramic (LDS-P) MT and HT (high translucency), milled zirconia-reinforced lithium silicate ceramic (ZLS-M) MT and hot-pressed zirconia-reinforced lithium silicate ceramic (ZLS-P) MT and HT, resulting n = 96 surfaces. All the samples were artificially aged by thermal cycling, and all investigations were made before and after thermal cycling. In terms of optical properties, differences recorded between ZLS and LDS ceramics are not significant. Thermal cycling increases the translucency of ZLS and LDS glass-ceramic materials significantly, with the most harmful effect on the pressed and polished samples. Micro- and nano roughness are significantly influenced by in vitro aging and a negative correlation was recorded. Glazed samples are characterized by significant rougher surfaces for all types of materials. On nanolevel, ZLS materials are significantly smoothed by thermal cycling. Full article

Dental ceramic restorations are widely used in restorative dentistry. However, these restorations can be affected once cemented in the oral cavity by several factors. How can conventional surface treatments, such as glazing and mechanical polishing, diminish the effects of aging? The purpose of this in vitro study was to evaluate the effect of thermocycling and conventional surface treatments on the surface roughness and microhardness of three types of glass-ceramics by using a profilometer, scanning electron microscopy (SEM), atomic force microscopy (AFM), and a microhardness tester. Three types of ceramic systems (zirconia reinforced lithium silicate glass-ceramic, lithium disilicate glass-ceramic, and feldspathic glass-ceramic) (n = 48) were prepared. The samples were subjected to thermocycling for 10,000 cycles. Surface roughness was evaluated numerically using a profilometer and visually by using SEM and AFM. Microhardness was performed using a microhardness tester. The data were interpreted using the ANOVA test, and the results were correlated using Pearson’s correlation formula (r). Significant differences were found before and after thermocycling for the Ra (p < 0.01) and Rz (p < 0.05) parameters. As well, differences between glazed and polished surfaces were significant before and after thermocycling for surface roughness and microhardness (p < 0.05). A correlation was made between average surface roughness and microhardness (r = −460) and for the maximum surface roughness and microhardness (r = −606). Aging increases the roughness and decreases in time the microhardness. The tested ceramic systems behaved differently to the aging and surface treatments. Surface treatments had a significant impact on the microhardness and surface characteristics. The glazed groups were reported with higher surface roughness and lower microhardness when compared to the polished groups before and after thermocycling. The measuring roughness techniques determine the scale-dependent values for the Ra (Sa) and Rz (Sq) parameters. Thermocycling almost doubled the surface roughness for all the tested samples. Microhardness decreased only for the Celtra glazed samples. Nano-roughness increased the values for Vita and slightly for Emax. Thermocycling had little effect on Emax ceramic and a more significant impact on Celtra Press ceramic. Full article