Next Article in Journal
Composites Based on Nanoparticle and Pan Electrospun Nanofiber Membranes for Air Filtration and Bacterial Removal
Next Article in Special Issue
Yb:MoO3/Ag/MoO3 Multilayer Transparent Top Cathode for Top-Emitting Green Quantum Dot Light-Emitting Diodes
Previous Article in Journal
CO2 Hydrogenation over Nanoceria-Supported Transition Metal Catalysts: Role of Ceria Morphology (Nanorods versus Nanocubes) and Active Phase Nature (Co versus Cu)
Previous Article in Special Issue
Influence of Annealing Temperature on Weak-Cavity Top-Emission Red Quantum Dot Light Emitting Diode
Open AccessArticle

Spray Coated Colloidal Quantum Dot Films for Broadband Photodetectors

Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China
Department of Chemical Physics and NanoLund, Lund University, Box 124, 22100 Lund, Sweden
Author to whom correspondence should be addressed.
Nanomaterials 2019, 9(12), 1738;
Received: 30 October 2019 / Revised: 23 November 2019 / Accepted: 4 December 2019 / Published: 6 December 2019
(This article belongs to the Special Issue Quantum Dots and Micro-LED Display)
A technique for scalable spray coating of colloidal CdSeTe quantum dots (QDs) for photovoltaics and photodetector applications is presented. A mixture solvent with water and ethanol was introduced to enhance the adhesive force between QDs and the substrate interface. The performance of the detector reached the highest values with 40 spray coating cycles of QD deposition. The photodetectors without bias voltage showed broadband response in the wavelength range of 300–800 nm, and high responsivity of 15 mA/W, detectivity of more than 1011 Jones and rise time of 0.04 s. A large size QD-logo pattern film (10 × 10 cm2) prepared by the spray coating process displayed excellent uniformity of thickness and absorbance. The large area detectors (the active area 1 cm2) showed almost the same performance as the typical laboratory-size ones (the active area 0.1 cm2). Our study demonstrates that the spray coating is a very promising film fabrication technology for the industrial-scale production of optoelectronic devices. View Full-Text
Keywords: quantum dots; spray coating; photodetector quantum dots; spray coating; photodetector
Show Figures

Graphical abstract

MDPI and ACS Style

Song, K.; Yuan, J.; Shen, T.; Du, J.; Guo, R.; Pullerits, T.; Tian, J. Spray Coated Colloidal Quantum Dot Films for Broadband Photodetectors. Nanomaterials 2019, 9, 1738.

AMA Style

Song K, Yuan J, Shen T, Du J, Guo R, Pullerits T, Tian J. Spray Coated Colloidal Quantum Dot Films for Broadband Photodetectors. Nanomaterials. 2019; 9(12):1738.

Chicago/Turabian Style

Song, Kaixuan; Yuan, Jifeng; Shen, Ting; Du, Jiuyao; Guo, Ruiqi; Pullerits, Tönu; Tian, Jianjun. 2019. "Spray Coated Colloidal Quantum Dot Films for Broadband Photodetectors" Nanomaterials 9, no. 12: 1738.

Find Other Styles
Note that from the first issue of 2016, MDPI journals use article numbers instead of page numbers. See further details here.

Article Access Map by Country/Region

Search more from Scilit
Back to TopTop