Next Article in Journal
Interaction in eXtended Reality Applications for Cultural Heritage
Next Article in Special Issue
Thermoelectric Properties of Polyaniline/Bismuth Antimony Telluride Composite Materials Prepared via Mechanical Mixing
Previous Article in Journal
From Patient to Musician: A Multi-Sensory Virtual Reality Rehabilitation Tool for Spatial Neglect
Previous Article in Special Issue
Effect of Silica Nanoparticles Silanized by Functional/Functional or Functional/Non-Functional Silanes on the Physicochemical and Mechanical Properties of Dental Nanocomposite Resins
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Applied Sciences
Volume 12
Issue 3
10.3390/app12031240
applsci-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

A Facile Method to Prepare Superhydrophobic Coatings for Various Substrates

by
Yuxuan Zhang
1,
Shuwen Zhou
1,
Zaosheng Lv
1,
Lixia Fan
2,
Yanfen Huang
1,* and
Xuegang Liu
3
1
Hubei Key Laboratory of Coal Conversion and New Carbon Material, School of Chemistry and Chemical Engineering, Wuhan University of Science and Technology, Wuhan 430081, China
2
School of Materials and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, China
3
Jingzhou Conservation Center, Jingzhou 434020, China
*
Author to whom correspondence should be addressed.
Appl. Sci. 2022, 12(3), 1240; https://doi.org/10.3390/app12031240
Submission received: 24 December 2021 / Revised: 19 January 2022 / Accepted: 22 January 2022 / Published: 25 January 2022
(This article belongs to the Special Issue Recent Advances in Technology for Polymer Composite Materials)
Browse Figures
Versions Notes

Abstract

:
In this study, the superhydrophobic composite coatings for self-cleaning were fabricated by mixing fluorine resin and two kinds of nanoparticles of carbon nanotubes (CNTs) and SiO2. When the mass ratio of CNTs to SiO2 is 2:3 and the added amount of nanoparticles is 75 wt. %, the superhydrophobic composite coatings with a water contact angle of 156.8° show the best self-cleaning property and 3.6° of contact angle hysteresis. Furthermore, the superhydrophobic composite coatings demonstrate good properties such as chemical resistance, thermal stability, and mechanical stability. The superhydrophobic composite coatings could be used for oil/water separation and could be applied to various substrate surfaces such as glass plates, cloth, board, steel plate, PVC plate, and so on. The superhydrophobic composite coatings show practical value in many fields because of their low cost and large area preparation.

1. Introduction

Due to their wide applications in self-cleaning, oil/water separation, corrosion resistance, anti-icing, anti-fogging, and anti-bacterial, superhydrophobic surfaces have attracted much attention over the last ten years [1,2,3,4]. A superhydrophobic surface is characterized by a water contact angle (WCA) over 150° and a sliding angle lower than 10° [5]. It is widely known that two key factors play important roles in preparing superhydrophobic surfaces: suitable multi-scale surface roughness and low surface free energy [6]. Many ways have been reported to fabricate superhydrophobic surfaces in recent years, such as chemical vapor deposition [7,8], plasma etching [9,10], hydrothermal synthesis [11,12], electrospinning [13,14], dip coating [15,16], sol-gel method [17,18], templating [19,20], and so on. There are many ways to prepare superhydrophobic surfaces, but most methods usually involve specialized equipment or multistep procedures, high cost, inconvenience, and the inability to fabricate a large area of superhydrophobic surfaces, which limits their practical uses. Simplifying the preparation procedure will greatly benefit the practical use of superhydrophobic surfaces. Facile, low cost, and suitable for large area preparation of superhydrophobic surfaces is the goal of scientific researchers in this field. Moreover, the very common problem of artificial superhydrophobic surfaces is poor mechanical properties. Recently, many researchers have attempted to solve the problem.
At present, although several researchers have chosen to fabricate fluorine-free superhydrophobic surfaces due to environmental problems [21], it is undeniable that the excellent performance of fluorine-containing materials [22,23,24], such as excellent weather resistance, high chemical stability, extraordinary water repellency, oil repellency, stain resistance, and so on. Jia et al. have prepared a superhydrophobic composite membrane of (polyvinylidene fluoride-co-hexafluoropropylene)/(polystyrene) via a novel hybrid electrospin-electrospray process [25]. Cui et al. prepared the superhydrophobic coatings using nanofibrous poly(vinylidene fluoride)/stearic acid [13]. Nanoparticles of SiO2, TiO2, ZnO, and carbon nanotubes (CNTs) are often applied to make surface roughness to fabricate superhydrophobic coatings [26,27,28,29]. One-dimensional CNTs with hydrophobic property and high aspect ratio are suitable to construct superhydrophobic surfaces [30]. SiO2 nanoparticles are also widely used in superhydrophobic surfaces [31,32,33].
We propose a facile way to prepare superhydrophobic composite coatings by integrating CNTs/SiO2 nano-additives on fluorine resin in this study. The two nanoparticles of hydrophobic silica and carbon nanotubes were used to prepare superhydrophobic coatings. The surface energy of SiO2 was low because their surfaces were modified by alkyl groups. The addition of hydrophobic nano-silica can reduce contact angle hysteresis and increase the self-cleaning property of the superhydrophobic composite coating. The superhydrophobic coatings exhibited good properties such as chemical, thermal, and mechanical stability. Moreover, the superhydrophobic composite coatings could be applied to oil/water separation and could be applied to various substrate surfaces. The superhydrophobic composite coatings show practical value in many fields because of their low-cost and large-scale preparation.

2. Materials and Methods

2.1. Materials

Fluorine resin (CF-803) and curing agent were purchased from Shanghai De Yude Trading Co., Ltd. (Shanghai, China). CF-803 is a solvent-based two-component fluorocarbon resin that is a product of the copolymerization of chlorotrifluoroethylene with vinyl ester and other functional monomers. Silica sol (xylene) with a particle size of approximately 20 nm (30 wt. %) was supplied by Wuhan Green Chemical Technology Co., Ltd. (Wuhan, China). CNTs were purchased from Qingdao Haoxin New Energy Technology Co., Ltd. (Qingdao, China). Butyl acetate was purchased from Sinopharm Chemical Reagent Co., Ltd. (Shanghai, China). Cloths, boards, steel plates, and PVC (polyvinyl chloride) plates were purchased through Taobao online shopping. Glass plates (7.5 cm × 2.5 cm) were purchased from CITOTEST® Scientific.

2.2. Preparation of the Coatings

A dispersion containing fluorine resin, curing agent, and butyl acetate was prepared by 30 min of magnetic stirring. Then, a mixed solution was obtained by mixing a certain ratio of silica sol (xylene), CNTs, and the as-prepared fluorine resin solution by 10 min of ultrasonic dispersion and 30 min of magnetic stirring. The total solid content of the mixed solution was regulated to 2 wt. %. All substrates (cloths, boards, steel plates, PVC, and glass plates) were ultrasonically cleaned in the detergent solution, rinsed with deionized water, and dried in air dry oven at 40 °C as the preparative. About 1.5 mL of the mixed solution was dripped onto the glass plate through a pipette. The coatings were dried for 12 h at room temperature.
Below was an optimal formula (1.5:1 of the mass ratio of silica sol to CNTs nanoparticles, 75 wt. % of total nanoparticles): fluorine resin (0.180 g) and curing agent (0.018 g) were homogeneously mixed with butyl acetate (14.32 g) by 30 min of magnetic stirring. Then, the above solution was mixed with silica sol (1.20 g) and CNTs (0.24 g), then there was 10 min of ultrasonic dispersion and 30 min of magnetic stirring. The mixed solution was dripped onto every substrate through a pipette. The composite coatings were dried for 12 h at room temperature. Note here that the silica sol used in this study was a solution of 30 % solid content.

2.3. Characterization

KRÜSS DSA 100 (Hamburg, Germany) was used to test water contact angle (WCA). WCA was measured at room temperature through 5 µL water drop and the result was an average of 6 fresh points. Advancing and receding contact angles were measured through the growth and shrinkage of a drop, respectively. Cloths, boards, steel plates, and PVC plates were used as substrates to investigate the superhydrophobic coatings on different substrates. The chemical resistance of the superhydrophobic composite coating was tested by dipping the coating into HCl (pH = 2), NaOH (pH = 12), and 3.5 wt. % NaCl solution, respectively. Field emission scanning electron microscopy (FESEM, Nova NanoSEM400) was used to characterize the surface topography of the coatings. Thermal gravimetric analysis (TGA) was performed on NETZSCH F1 Libra® (TGA209F1D-0315-L) under air atmosphere from room temperature to 600 °C with 10 °C/min of a constant heating rate. The superhydrophobic composite coatings were placed in an electricity heat drum wind drying oven at 200 °C for 3 days to further test the thermal stability of the superhydrophobic composite coatings. Mechanical stability was measured by sandpaper-abrasion and the experimental steps were as follows: (1) the sample was placed face-down to sandpaper (standard sandpaper, grit no. 1000); (2) moved for 15 cm along the ruler under a weight of 100 g; (3) the sample was rotated by 90° (face to the sandpaper) and moved for 15 cm; and (4) the operation was repeated 3 times. The method of the self-cleaning test of the superhydrophobic composite coatings was as follows: (1) river sand as the model contamination was placed to the surfaces of the superhydrophobic composite coatings; (2) the water droplets were dripped; and (3) the river sand was removed with water drops rolling off the surfaces of the superhydrophobic composite coatings. A camera was used to record the self-cleaning behavior of the superhydrophobic composite coatings.

3. Results

3.1. Preparation and Characterization of the Superhydrophobic Coatings

The wettability of the composite coatings influenced with the SiO2 content was shown in Figure 1. The mass fraction of CNTs in each of these coatings was fixed at 30%. With increasing SiO2 nanoparticles content, the WCA of the composite coating improved gradually. At the same time, the contact angle hysteresis of the composite coating decreased gradually. When the total mass of the nanoparticles accounted for 75% of the coatings and the mass ratio of CNTs to SiO2 was 2:3, the superhydrophobic composite coatings with a WCA of 156.8° and contact angle hysteresis of 3.6° were fabricated through mixing fluorine resin and two kinds of nanoparticles of CNTs and SiO2. In fact, the hydrophobic property of the composite coating could be improved slightly by further improving the amount of SiO2 nanoparticles used. However, it was not suitable to further increase the SiO2 nanoparticles content considering the surface state and mechanical strength of the composite coatings. In this study, the optimal formula is that the mass ratio of CNTs to SiO2 is 2:3, and the loading of nanoparticles is 75 wt. %. Unless otherwise stated, the following superhydrophobic composite coating refers to the coating in this formulation. Many methods for preparing superhydrophobic surfaces are based on specific substrates. The dependence on substrates is due to the need for substrates to provide all or part of the roughness. For example, the superhydrophobicity of metal surfaces can be achieved by chemical etching and post-hydrophobic molecular modification [34]. If the superhydrophobicity of a surface does not depend on the substrate, then the superhydrophobic coatings can be used more widely. In this study, the superhydrophobic coatings can be used for various substrates. The superhydrophobic composite coatings coated on cloth, board, steel plate, and PVC plate are shown in Figure 2. In Figure 2, the superhydrophobic composite coating is suitable for a variety of substrates. The superhydrophobic composite coatings were dipped into three aqueous solutions for three days to investigate their chemical stability. The photographs of the experiment are displayed in Figure 3. The superhydrophobic composite coating could still maintain its hydrophobicity after being soaked in HCl (pH = 2), NaOH (pH = 12) and 3.5 wt. % NaCl solution for three days. This result shows that the superhydrophobic composite coating has good chemical stability. The surface topography of the composite coatings are displayed in Figure 4. The CNTs are clearly visible in Figure 4a–c. In Figure 4d, to the composite of silica nanoparticles and fluorine resin, a lesser degree of surface roughness of the composite coating can be observed. The mass fraction of silica nanoparticles is 75%. The surface roughness of the composite coating was significantly improved with an increase in the use of CNTs. Compared to adding CNTs alone, the composite application of silica nanoparticles and CNTs can further improve the hydrophobicity of the coating and reduce the contact angle hysteresis. The difference between the three images (Figure 4a–c) is not obvious because the silica nanoparticles have little change on the surface morphology of the composite coatings. This may be because silica nanoparticles have good compatibility with fluorine resin due to the large number of alkyl groups on its surface. Therefore, the silica nanoparticles have little change on the surface morphology of the composite coatings.

3.2. Thermal Stability Properties of the Superhydrophobic Coatings

High thermal stability is very important for superhydrophobic coatings to their practical application. In this study, two methods were applied to test the thermal stability of the superhydrophobic composite coating. The results of the TGA test in air atmosphere are displayed in Figure 5. As shown in Figure 5, CNTs showed the highest thermal stability. Fluorine resins were almost completely weightless at 600 °C (Figure 5a). The addition of nano-additives slightly increases the thermal stability of the composite coatings. These composite coatings have almost no weight loss up to 250 °C. As Figure 5c shows, the superhydrophobic composite coatings lost about 5 wt. % at around 310 °C. The superhydrophobic composite coatings were processed by 3 days of heat treatment at 200 °C to further test their heat resistance. The photos of the superhydrophobic composite coatings before and after heat treatment are exhibited in Figure 6. From Figure 6d, the composite coatings are still very hydrophobic with WCA of 154.5°. These two kinds of test results show that the superhydrophobic composite coatings have good thermal stability.

3.3. Mechanical Property of the Superhydrophobic Composite Coatings

The mechanical robustness of the superhydrophobic composite coating was examined by an abrasion test. As can be seen in Figure 7, the superhydrophobic composite coating had partially peeled off after the abrasion test. The test had little effect on the hydrophobicity of the composite coatings. This result of the surface robustness test of the superhydrophobic composite coatings reflects the good mechanical stability of them.

3.4. The Self-Cleaning Property of the Superhydrophobic Composite Coatings

The self-cleaning property plays an important function to the superhydrophobic composite coatings in the practical application. As illustrated in Figure 8, the self-cleaning test of the superhydrophobic composite coatings was measured by contaminating with river sands. The river sands were taken away by water drops rolling. The surface of the superhydrophobic composite coatings became clean after a short time, which suggested that they could be applied for self-cleaning. The superhydrophobic composite coatings could also be applied to oil/water separation and the oil/water separation results are shown in Figure S1.

4. Conclusions

In conclusion, we successfully prepared superhydrophobic composite coatings by mixing CNTs/SiO2 nanoparticles and fluorine resin. The superhydrophobic composite coatings with WCA of 156.8° and contact angle hysteresis of 3.6° show the best self-cleaning property. Moreover, the superhydrophobic composite coatings exhibited good properties such as chemical stability, thermal stability, and mechanical stability. Moreover, the superhydrophobic composite coatings could be applied to various substrate surfaces such as glass plates, cloth, board, steel plate, PVC plate, and so on. Therefore, the superhydrophobic composite coatings have great potential for practical applications.

Supplementary Materials

The following are available online at https://www.mdpi.com/article/10.3390/app12031240/s1, Figure S1: The images illustrate oil/water separation of the superhydrophobic coatings. Water droplets were dyed blue by methylene blue. DCM was dyed red by oil red O.

Author Contributions

Y.Z. and S.Z. conducted research and reporting, Z.L. Supervisor, L.F. Tester, Y.H. supervisor and research director, X.L. Supervisor. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by Key Laboratory of Hubei Province for Coal Conversion and New Carbon Materials (Wuhan University of Science and Technology) (No. WKDM202105).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Conflicts of Interest

No potential conflict of interest was reported by the authors.

References

  1. Chen, H.; Wang, F.; Fan, H.; Hong, R.; Li, W. Construction of MOF-based superhydrophobic composite coating with excellent abrasion resistance and durability for self-cleaning, corrosion resistance, anti-icing, and loading-increasing research. Chem. Eng. J. 2021, 408, 127343. [Google Scholar] [CrossRef]
  2. Liu, Z.; Zhang, C.; Zhang, X.; Wang, C.; Liu, F.; Yuan, R.; Wang, H. Durable superhydrophobic PVDF/FEVE/GO@TiO2 composite coating with excellent anti-scaling and UV resistance properties. Chem. Eng. J. 2021, 411, 128632. [Google Scholar] [CrossRef]
  3. Xiao, X.; Xie, W.; Ye, Z. Preparation of corrosion-resisting superhydrophobic surface on aluminium substrate. Surf. Eng. 2019, 35, 411–417. [Google Scholar] [CrossRef]
  4. Jagdheesh, R.; Kopecek, J.; Brajer, J.; Mocek, T. Superhydrophobic microspiked surface structures by ultrashort laser patterning. Surf. Eng. 2021, 37, 1–11. [Google Scholar] [CrossRef]
  5. Zong, L.; Wu, Y.; Li, X.; Jiang, B. The preparation of superhydrophobic photocatalytic fluorosilicone/SiO2-TiO2 coating and its self-cleaning performance. J. Coat. Technol. Res. 2021, 18, 1245–1259. [Google Scholar] [CrossRef]
  6. Jafari, R.; Momen, G.; Eslami, E. Fabrication of icephobic aluminium surfaces by atmospheric plasma jet polymerisation. Surf. Eng. 2019, 35, 450–455. [Google Scholar] [CrossRef]
  7. Sun, Y.; Huang, J.; Guo, Z. A CVD-Assisted Modification Approach for Preparing a Dual Superlyophobic Fabric with In-Air Superhydrophobicity and Underwater Superoleophobicity. Langmuir 2020, 36, 5802–5808. [Google Scholar] [CrossRef]
  8. Guo, X.-J.; Xue, C.-H.; Sathasivam, S.; Page, K.; He, G.; Guo, J.; Promdet, P.; Heale, F.L.; Carmalt, C.J.; Parkin, I.P. Fabrication of robust superhydrophobic surfaces via aerosol-assisted CVD and thermo-triggered healing of superhydrophobicity by recovery of roughness structures. J. Mater. Chem. A 2019, 7, 17604–17612. [Google Scholar] [CrossRef]
  9. Yang, J.; Pu, Y.; He, H.; Cao, R.; Miao, D.; Ning, X. Superhydrophobic cotton nonwoven fabrics through atmospheric plasma treatment for applications in self-cleaning and oil-water separation. Cellulose 2019, 26, 7507–7522. [Google Scholar] [CrossRef]
  10. Vazirinasab, E.; Jafari, R.; Momen, G. Evaluation of atmospheric-pressure plasma parameters to achieve superhydrophobic and self-cleaning HTV silicone rubber surfaces via a single-step, eco-friendly approach. Surf. Coat. Technol. 2019, 375, 100–111. [Google Scholar] [CrossRef]
  11. Chu, J.H.; Sun, G.X.; Tong, L.B.; Jiang, Z.H. Facile one-step hydrothermal fabrication of Allium giganteum-like superhydrophobic coating on Mg alloy with self-cleaning and anti-corrosion properties. Colloids Surf. A 2021, 617, 126370. [Google Scholar] [CrossRef]
  12. Wang, M.; Peng, M.; Weng, Y.-X.; Li, Y.-D.; Zeng, J.-B. Toward durable and robust superhydrophobic cotton fabric through hydrothermal growth of ZnO for oil/water separation. Cellulose 2019, 26, 8121–8133. [Google Scholar] [CrossRef]
  13. Cui, M.; Xu, C.; Shen, Y.; Tian, H.; Feng, H.; Li, J. Electrospinning superhydrophobic nanofibrous poly(vinylidene fluoride)/stearic acid coatings with excellent corrosion resistance. Thin Solid Films 2018, 657, 88–94. [Google Scholar] [CrossRef]
  14. Attia, H.; Johnson, D.J.; Wright, C.J.; Hilal, N. Robust superhydrophobic electrospun membrane fabricated by combination of electrospinning and electrospraying techniques for air gap membrane distillation. Desalination 2018, 446, 70–82. [Google Scholar] [CrossRef] [Green Version]
  15. Zhu, Y.; Pei, L.; Ambreen, J.; He, C.; Ngai, T. Facile Preparation of a Fluorine-Free, Robust, Superhydrophobic Coating through Dip Coating Combined with Non-Solvent Induced Phase Separation (Dip-Coating-NIPS) Method. Macromol. Chem. Phys. 2020, 221, 2070017. [Google Scholar] [CrossRef]
  16. Nguyen-Tri, P.; Altiparmak, F.; Nguyen, N.; Tuduri, L.; Ouellet-Plamondon, C.M.; Prud’homme, R.E. Robust Superhydrophobic Cotton Fibers Prepared by Simple Dip-Coating Approach Using Chemical and Plasma-Etching Pretreatments. ACS Omega 2019, 4, 7829–7837. [Google Scholar] [CrossRef] [Green Version]
  17. Xie, A.; Cui, J.; Chen, Y.; Lang, J.; Li, C.; Yan, Y.; Dai, J. One-step facile fabrication of sustainable cellulose membrane with superhydrophobicity via a sol-gel strategy for efficient oil/water separation. Surf. Coat. Technol. 2019, 361, 19–26. [Google Scholar] [CrossRef]
  18. Liu, S.; Liu, X.; Latthe, S.S.; Gao, L.; An, S.; Yoon, S.S.; Liu, B.; Xing, R. Self-cleaning transparent superhydrophobic coatings through simple sol-gel processing of fluoroalkylsilane. Appl. Surf. Sci. 2015, 351, 897–903. [Google Scholar] [CrossRef]
  19. Zhang, N.; Zhou, Y.; Zhang, Y.; Jiang, W.; Wang, T.; Fu, J. Dual-templating synthesis of compressible and superhydrophobic spongy polystyrene for oil capture. Chem. Eng. J. 2018, 354, 245–253. [Google Scholar] [CrossRef]
  20. Tao, C.; Yan, H.; Yuan, X.; Yao, C.; Yin, Q.; Zhu, J.; Ni, W.; Yan, L.; Zhang, L. Synthesis of shape-controlled hollow silica nanostructures with a simple soft-templating method and their application as superhydrophobic antireflective coatings with ultralow refractive indices. Colloids Surf. A 2016, 501, 17–23. [Google Scholar] [CrossRef]
  21. Celik, N.; Altindal, S.; Gozutok, Z.; Ruzi, M.; Onses, M.S. Effect of fabric texture on the durability of fluorine-free superhydrophobic coatings. J. Coat. Technol. Res. 2020, 17, 785–796. [Google Scholar] [CrossRef]
  22. Hu, J.; Fang, Z.; Huang, Y.; Lu, J. Fabrication of superhydrophobic surfaces based on fluorosilane and TiO2/SiO2 nanocomposites. Surf. Eng. 2021, 37, 271–277. [Google Scholar] [CrossRef]
  23. Ma, L.; Wang, J.; Zhang, Z.; Kang, Y.; Sun, M.; Ma, L. Preparation of a superhydrophobic TiN/PTFE composite film toward self-cleaning and corrosion protection applications. J. Mater. Sci. 2021, 56, 1413–1425. [Google Scholar] [CrossRef]
  24. Hamzah, N.; Leo, C.P.; Ooi, B.S. Superhydrophobic PVDF/TiO2-SiO2 Membrane with Hierarchical Roughness in Membrane Distillation for Water Recovery from Phenolic Rich Solution Containing Surfactant. Chin. J. Polym. Sci. 2019, 37, 609–616. [Google Scholar] [CrossRef]
  25. Jia, W.; Kharraz, J.A.; Guo, J.; An, A.K. Superhydrophobic (polyvinylidene fluoride-co-hexafluoropropylene)/(polystyrene) composite membrane via a novel hybrid electrospin-electrospray process. J. Membr. Sci. 2020, 611, 118360. [Google Scholar] [CrossRef]
  26. Shen, Y.; Li, K.; Chen, H.; Wu, Z.; Wang, Z. Superhydrophobic F-SiO2@PDMS composite coatings prepared by a two-step spraying method for the interface erosion mechanism and anti-corrosive applications. Chem. Eng. J. 2021, 413, 127455. [Google Scholar] [CrossRef]
  27. Zeng, C.; Wang, Y.; Gao, C.; Liu, Y. Hierarchical Cu2O/CuO/TiO2 composite films with high superhydrophobicity and strong adhesion. Surf. Eng. 2021, 37, 1–8. [Google Scholar] [CrossRef]
  28. Zhou, H.; Chen, R.; Liu, Q.; Liu, J.; Yu, J.; Wang, C.; Zhang, M.; Liu, P.; Wang, J. Fabrication of ZnO/epoxy resin superhydrophobic coating on AZ31 magnesium alloy. Chem. Eng. J. 2019, 368, 261–272. [Google Scholar] [CrossRef]
  29. Wang, Q.; Chen, A.; Gu, H.; Qin, G.; Zhang, J.; Xu, J.; Jiang, G.; Liu, W.; Zhang, Z.; Huang, H. Highly interconnected porous PDMS/CNTs sandwich sponges with anti-icing/deicing microstructured surfaces. J. Mater. Sci. 2021, 56, 11723–11735. [Google Scholar] [CrossRef]
  30. Ding, Y.-R.; Xue, C.-H.; Guo, X.-J.; Wang, X.; Jia, S.-T.; An, Q.-F. Fabrication of TPE/CNTs film at air/water interface for flexible and superhydrophobic wearable sensors. Chem. Eng. J. 2021, 409, 128199. [Google Scholar] [CrossRef]
  31. Wang, X.; Ding, H.; Sun, S.; Zhang, H.; Zhou, R.; Li, Y.; Liang, Y.; Wang, J. Preparation of a temperature-sensitive superhydrophobic self-cleaning SiO2-TiO2@PDMS coating with photocatalytic activity. Surf. Coat. Technol. 2021, 408, 126853. [Google Scholar] [CrossRef]
  32. Zhang, J.; Liu, S.; Huang, Y.; Lv, Y.; Kong, M.; Li, G. Durable fluorinated-SiO2/epoxy superhydrophobic coatings on polycarbonate with strong interfacial adhesion enhanced by solvent-induced crystallization. Prog. Org. Coat. 2021, 150, 106002. [Google Scholar] [CrossRef]
  33. Liang, Z.; Geng, M.; Dong, B.; Zhao, L.; Wang, S. Transparent and robust SiO2/PDMS composite coatings with self-cleaning. Surf. Eng. 2020, 36, 643–650. [Google Scholar] [CrossRef]
  34. Huang, Y.; Sarkar, D.K.; Grant Chen, X. Superhydrophobic aluminum alloy surfaces prepared by chemical etching process and their corrosion resistance properties. Appl. Surf. Sci. 2015, 356, 1012–1024. [Google Scholar] [CrossRef] [Green Version]
Applsci 12 01240 g001 550
Figure 1. Relation between weight ratio of SiO2, water contact angles, and contact angle hysteresis. The mass fraction of CNTs in each of these coatings was 30%. The inserts were 5 µL water drop profiles on the surface of the composite coatings.
Figure 1. Relation between weight ratio of SiO2, water contact angles, and contact angle hysteresis. The mass fraction of CNTs in each of these coatings was 30%. The inserts were 5 µL water drop profiles on the surface of the composite coatings.
Applsci 12 01240 g001
Applsci 12 01240 g002 550
Figure 2. The superhydrophobic composite coatings coated on cloth (a), board (b), steel plate (c), and PVC plate (d). Water drops were dyed blue by methylene blue, dyed orange by coffee, and dyed red by methyl orange in acids.
Figure 2. The superhydrophobic composite coatings coated on cloth (a), board (b), steel plate (c), and PVC plate (d). Water drops were dyed blue by methylene blue, dyed orange by coffee, and dyed red by methyl orange in acids.
Applsci 12 01240 g002
Applsci 12 01240 g003 550
Figure 3. The superhydrophobic composite coatings against water droplets after dipping into (a1–a3) HCl (pH = 2), (b1–b3) NaOH (pH = 12), and (c1–c3) 3.5 wt. % NaCl aqueous solution for three days.
Figure 3. The superhydrophobic composite coatings against water droplets after dipping into (a1–a3) HCl (pH = 2), (b1–b3) NaOH (pH = 12), and (c1–c3) 3.5 wt. % NaCl aqueous solution for three days.
Applsci 12 01240 g003
Applsci 12 01240 g004 550
Figure 4. Surface topography of the coatings with same CNTs of 30 wt. % and different SiO2 nanoparticles contents: (a) 0 wt. %, (b) 15 wt. %, (c) 45 wt. %; (d) surface topography of the coatings with SiO2 nanoparticles of 75 wt. %.
Figure 4. Surface topography of the coatings with same CNTs of 30 wt. % and different SiO2 nanoparticles contents: (a) 0 wt. %, (b) 15 wt. %, (c) 45 wt. %; (d) surface topography of the coatings with SiO2 nanoparticles of 75 wt. %.
Applsci 12 01240 g004
Applsci 12 01240 g005 550
Figure 5. The TGA curves: (a) fluorine resin; the coatings with same CNTs of 30 wt. % and different SiO2 nanoparticles contents: (b) 0 wt. %; (c)15 wt. %; (d) 45 wt. %; (e) the coatings with SiO2 nanoparticles of 75 wt. %.
Figure 5. The TGA curves: (a) fluorine resin; the coatings with same CNTs of 30 wt. % and different SiO2 nanoparticles contents: (b) 0 wt. %; (c)15 wt. %; (d) 45 wt. %; (e) the coatings with SiO2 nanoparticles of 75 wt. %.
Applsci 12 01240 g005
Applsci 12 01240 g006 550
Figure 6. (a) The picture of the superhydrophobic composite coatings; (c) the picture of the superhydrophobic composite coatings after 3 days of heat treatment at 200 °C; (b,d) the picture of water drops on the composite coatings of (a,c), respectively. Water drops were dyed blue by methylene blue, dyed orange by coffee, and dyed red by methyl orange in acids.
Figure 6. (a) The picture of the superhydrophobic composite coatings; (c) the picture of the superhydrophobic composite coatings after 3 days of heat treatment at 200 °C; (b,d) the picture of water drops on the composite coatings of (a,c), respectively. Water drops were dyed blue by methylene blue, dyed orange by coffee, and dyed red by methyl orange in acids.
Applsci 12 01240 g006
Applsci 12 01240 g007 550
Figure 7. The experimental pictures of sandpaper-abrasion, the superhydrophobic composite coating: (a) test preparation; (b) under a weight at 100 g was placed face-down to sandpaper; (c) after the test; (d) the pictures of water drops sitting on the tested composite coatings. Blue water drops were dyed by methylene blue.
Figure 7. The experimental pictures of sandpaper-abrasion, the superhydrophobic composite coating: (a) test preparation; (b) under a weight at 100 g was placed face-down to sandpaper; (c) after the test; (d) the pictures of water drops sitting on the tested composite coatings. Blue water drops were dyed by methylene blue.
Applsci 12 01240 g007
Applsci 12 01240 g008 550
Figure 8. Pictures of self-cleaning test: (a) the superhydrophobic composite coating with river sands to be tested; (b,c) pictures in the test.
Figure 8. Pictures of self-cleaning test: (a) the superhydrophobic composite coating with river sands to be tested; (b,c) pictures in the test.
Applsci 12 01240 g008
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Zhang, Y.; Zhou, S.; Lv, Z.; Fan, L.; Huang, Y.; Liu, X. A Facile Method to Prepare Superhydrophobic Coatings for Various Substrates. Appl. Sci. 2022, 12, 1240. https://doi.org/10.3390/app12031240

AMA Style

Zhang Y, Zhou S, Lv Z, Fan L, Huang Y, Liu X. A Facile Method to Prepare Superhydrophobic Coatings for Various Substrates. Applied Sciences. 2022; 12(3):1240. https://doi.org/10.3390/app12031240

Chicago/Turabian Style

Zhang, Yuxuan, Shuwen Zhou, Zaosheng Lv, Lixia Fan, Yanfen Huang, and Xuegang Liu. 2022. "A Facile Method to Prepare Superhydrophobic Coatings for Various Substrates" Applied Sciences 12, no. 3: 1240. https://doi.org/10.3390/app12031240

APA Style

Zhang, Y., Zhou, S., Lv, Z., Fan, L., Huang, Y., & Liu, X. (2022). A Facile Method to Prepare Superhydrophobic Coatings for Various Substrates. Applied Sciences, 12(3), 1240. https://doi.org/10.3390/app12031240

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop