3.1. Effect of Treatment
Figure 1 shows the typical storage modulus (E’) trends of flax fiber-reinforced composites as a function of their exposition time to salt-fog environment (i.e., 0 days or unaged, 30 days and 60 days).
As is widely known [
40,
50], the storage modulus is typically associated with the material stiffness: it measures the material’s capability to store the energy applied. Two different regions of the storage modulus curve of fiber-reinforced polymers by varying temperature were evidenced, i.e., the first one below glass transition temperature (Tg) of the polymeric matrix and the second one above Tg, named glassy region and rubbery region, respectively. In the glassy region, the storage modulus of fiber-reinforced composite materials was high because the components (i.e., matrix and reinforcement) were extremely immobilized, allowing a stiff behavior. Vice versa, FRP components acquired mobility, losing their close packing arrangement in the rubbery region, thus leading to decrease of the storage modulus with temperature [
40].
By comparing
Figure 1a,b, it was noted that, in the unaged condition, sodium bicarbonate treatment allowed the composite stiffness to increase in the glassy region. In particular, the storage modulus E’ at 25 °C of Flax-T laminates (i.e., 5.0 ± 0.1 GPa) was about 47% higher than that of Flax-AR laminates (i.e., 3.4 ± 0.2 GPa). This result confirms that the adhesion between flax fibers and epoxy matrix becomes strongest due to the fiber treatment, as already stated in our previous papers [
46,
48].
It is worth noting that, during the exposition to the salt-fog environment, Flax-AR composites experienced noticeable decrements of E’ in the glassy region. In particular, laminates aged for 1 month and 2 months showed storage modulus values 32% and 49% lower than the reference (i.e., unaged laminates), respectively. Vice versa, a stable dynamic behavior during the exposition to the aggressive environment was evidenced by Flax-T composites. Indeed, the soaking of flax fabrics in NaHCO
3 solution allowed to obtain a composite laminate able to better retain its storage dynamic modulus below glass transition temperature, i.e., in comparison to unaged samples the measured decrements of E’ at 25 °C were equal to just 3% and 8% after 1 month and 2 months of aging, respectively. This suggests that, in addition to the quasi-static mechanical stability [
32], fiber treatment allows flax-reinforced epoxy composites also to better retain their dynamic behavior under salt-fog exposition.
Loss modulus E’’ represents the viscous response of the material (i.e., the material tendency to dissipate applied energy), whereas tan δ, also named damping or loss factor, is defined as the loss modulus to storage modulus ratio (E’’/E’). A high tan δ value is indicative of materials having a great non-elastic strain component while a low value indicates high elasticity. This means that, for fiber-reinforced composites, an increase of the fiber/matrix adhesion results in the reduction of tan δ due to the mobility decrement of the molecular chains surrounding the fiber/matrix interface [
51,
52]. As a consequence, the lower the energy loss of a composite system compared to its storage capacity, the greater the tan δ value [
42].
Figure 2 shows the typical tan δ versus temperature trends of flax fiber-reinforced epoxy composites for each aging condition investigated. First of all, it is worth noting that two different tan δ peaks were evidenced for all samples (i.e., regardless the fiber treatment and aging exposition time). Several authors [
38,
53,
54] stated that the first peak at lower temperatures is attributed to the glass transition temperature of the thermoset matrix, whereas the second one at higher temperatures is related to the micro-mechanical transition phenomena of the immobilized polymer layer between fiber and matrix, i.e., fiber–matrix interphase.
The comparison of
Figure 2a,b evidenced that, regardless the aging condition, Flax-AR laminates showed higher tan δ than those of Flax-T, thus confirming the beneficial effect of the sodium bicarbonate treatment on the fiber/matrix adhesion, even when flax fiber-reinforced composites were exposed to aggressive media such as salt-fog spray.
Furthermore,
Figure 2a shows that, after salt-fog aging, the tan δ peaks of Flax-AR laminates (i.e., 1-month and 2-month aged samples) shifted to lower temperatures and became wider than the unaged sample. This experimental evidence is mainly explained by coupling the softening of matrix, due to the composites’ exposition to the humid environment, and the low arrangement of the flax microfibrils network, as shown in
Figure 3. FRP constituents gained local mobility, losing their packing arrangement in the rubbery region, thus favoring the shift toward lower temperature of tan δ [
40].
From a morphological point of view, the Flax-AR laminate was characterized by low interfacial fiber–matrix adhesion, as can be seen from high tan δ peaks already shown in unaged conditions. This implies that preferential pathways for water diffusion can be identified in the interface between fibers and matrix, thus stimulating the triggering of premature water-induced degradation phenomena in the natural reinforced composite laminate. In particular, water weakens the physical bonds (i.e., van der Waals interaction) within the flax/matrix interface, as well as causing the hydrolysis of chemical bonds at the interface, thus leading to the occurrence of interfacial debonding phenomena [
40]. As evidenced in
Table 2, the temperature of both tan δ peaks decreased about 10 °C after 60 days of salt-fog exposition (i.e., from 75.4 °C to 65.5 °C, and from 105.6 °C to 95.2 °C, for the first and the second peak, respectively). As concerns the evolution of the peaks’ height, the first one varied from 0.57 to 1.15, whereas the second one varied from 0.32 to 1.13.
Vice versa, no noticeable variation was evidenced on the tan δ trends of Flax-T composites when varying the aging exposition time (
Figure 2b). Both peaks remained slightly unchanged when varying the aging condition. In particular, after 60 days of salt-fog exposition, the temperature decrements were just equal to 0.7 °C (i.e., from 77.2 °C to 76.5 °C) and 2.4 °C (from 104.7 °C to 102.3 °C) for the first and the second peak, respectively (
Table 2). At the same time, the height of the first peak varied from 0.37 to 0.38, whereas the second one varied from 0.28 to 0.37. These results are in good agreement with those achieved from the quasi-static flexural characterization [
32], confirming the improved mechanical stability shown by Flax-T laminates in comparison to Flax-AR ones.
It is noteworthy that the second peak showed a greater sensitivity to aging in the salt-fog environment than the first one. This indicates that the water diffusion phenomena, which are considered responsible for the aging activation phenomena [
55], are activated initially at the interface between the fiber and the matrix and then evolve towards the bulk of the matrix, thus causing its softening. The Flax-T laminate, being characterized by an improved interfacial adhesion, strongly limited the water absorption by inhibiting or extending over time the subsequent aging effect on the epoxy matrix.
Figure 4 shows the typical storage modulus versus temperature trends of jute laminates for each aging condition investigated. Regarding unaged samples, it is worth noting that, unlike flax laminates, fiber treatment did not increase the composite stiffness in the glassy region. In particular, epoxy laminates reinforced with untreated or raw jute fabrics (i.e., Jute-AR) showed E’ at room temperature (i.e., 4.3 ± 0.1 GPa) about 47% higher than Jute-T laminates (i.e., 2.9 ± 0.3 GPa). This experimental result confirms that the adverse effect of the sodium bicarbonate treatment on the adhesion between jute fibers and epoxy resin leads to decreasing the dynamic modulus of the resulting composites [
48].
As a consequence, Jute-T laminates experienced greater decrements of storage modulus in the glassy region due to the salt-fog exposition in comparison to their counterparts (i.e., Jute-AR laminates). In more detail, the storage modulus values at room temperature of Jute-AR-1m and Jute-AR-2m laminates were 10% and 18% lower than that of the unaged laminates, respectively. On the contrary, Jute-T composites evidenced decrements in the storage modulus at room temperature equal to 25% and 40%, after 1 month and 2 months of aging exposition, respectively.
By observing the typical tan δ versus temperature trends of jute composites at varying aging conditions (
Figure 5), it is evidenced that, regardless of fiber treatment, both tan δ peaks became higher, also shifting to lower temperatures, when increasing the salt-fog exposition time. Since the damping behavior of fiber-reinforced composites is greatly influenced by the shear stress concentrations at the fiber–matrix interfaces, as well as by the viscoelastic energy dissipation within the polymeric matrix [
51], these results are attributed both to the matrix softening and to the fiber–matrix interface degradation phenomena, due to the composites’ exposition to salt-fog. As already stated, no beneficial effect on fiber–matrix compatibility was achieved after jute fiber treatment. Consequently,
Figure 5 clearly shows that, regardless the aging time exposition, tan δ values of Jute-AR laminates were lower than those of Jute-T in the whole temperature range because they were characterized by higher mobility of the molecular chains both in the matrix bulk and surrounding the fiber/matrix interface.
This result indicates that composites reinforced with untreated Jute fibers (i.e., Jute-AR) are characterized by better fiber–matrix interfacial adhesion than surface treated ones (i.e., Jute-T) [
47]. Due to the soaking of jute fibers in the NaHCO
3 solution, a reduction of lignin and hemicellulose components from the fiber bulk occurred [
44], thus favoring the triggering of damage phenomena at the interface. Indeed, Jute-T laminates showed a larger decrement in their dynamic mechanical performances than Jute-AR laminates during the aging exposition, due to their higher sensitivity to a water-based environment.
In detail, it was found that Jute-T laminates showed greater variations of both tan δ peaks with increasing exposition time to salt-fog environment. In particular, after 60 days in the climatic chamber, the temperature of the first peak decreased from 82.0 °C to 76.3 °C (i.e., ΔT = 5.8 °C) and from 81.5 °C to 72.0 °C (i.e., ΔT = 9.5 °C) for Jute-AR and Jute-T laminates, respectively (
Table 3). With regard to the second tan δ peak, its temperature decrements were found equal to 3.3 °C (i.e., from 108.3 °C to 105.0 °C) and 4.1 °C (i.e., from 109.0 °C to 104.9 °C) for Jute-AR and Jute-T laminates, respectively. At the same time, Jute-T laminates showed increments from 0.33 to 0.62 and from 0.23 to 0.51 in the heights of the first and second tan δ peaks, respectively. Vice versa, epoxy laminates reinforced with jute untreated fibers (i.e., Jute-AR) showed lower height increments of both peaks (i.e., from 0.22 to 0.31 for the first peak and from 0.16 to 0.24 for the second one). These results are ascribed to the weaker fiber–matrix interfacial adhesion evidenced by Jute-T laminates in comparison to Jute-AR ones [
32,
33], which triggers water diffusion and, consequently, the composite aging after a short time of exposition to salt-fog environment.
3.2. Effect of Stacking Sequence
The typical trends of the damping properties (i.e., storage modulus E’ and tan δ) versus temperature of F Hybrid laminates are shown in
Figure 6 for each aging condition. By observing this figure, it can be noted that, even for hybrid stacking sequence, NaHCO
3 treatment allowed to modify the dynamic properties of the resulting composites. As shown in
Figure 6a,b, F Hybrid-T laminates evidenced higher stiffness in the glassy region than their counterparts (i.e., F Hybrid-AR), regardless the aging time exposition. In particular, the average storage moduli E’ measured at 25 °C of laminates reinforced with treated fibers (i.e., F Hybrid-T) were about 22%, 44% and 64% higher than those of F Hybrid-AR, after 0, 30 and 60 days in salt-fog environment, respectively.
Accordingly, the comparison of
Figure 6c,d evidenced that F Hybrid-AR unaged laminates showed higher tan δ values than Flax-T unaged ones, in the whole temperature range. In addition, the exposition to salt-fog clearly modified the tan δ curves of F Hybrid-AR laminates, since both tan δ peaks became higher and shifted to lower temperatures when increasing the exposition time. After 60 days of salt-fog exposition, the tan δ peak temperatures decreased about 8 °C (i.e., from 75.7 °C to 68.0 °C) and 5 °C (i.e., from 107.0 °C to 101.9 °C), for the first and the second one, respectively. As regards the peaks’ heights, the first peak grew from 0.48 to 0.69, whereas the second one grew from 0.42 to 0.87 (
Table 4).
Vice versa, the typical tan δ trends of F Hybrid-T composites remained almost unchanged when varying the exposition time to salt-fog environment, as shown in
Figure 6d, i.e., no noticeable variation was observed by comparing tan δ peaks of unaged and salt-fog aged F Hybrid-T laminates.
Both peaks remained unchanged when varying the aging condition. In particular, after 60 days of salt-fog exposition, the temperature decrements for both peaks were just equal to 1.8 °C (i.e., from 79.4 °C to 77.6 °C and from 104.3 °C to 102.5 °C for the first and the second one, respectively). At the same time, the height of the first peak varied from 0.24 to 0.28, whereas the second one varied from 0.20 to 0.28.
All these results can be ascribed to the different interactions of the two natural fibers with the sodium bicarbonate treatment. If, on one hand, the bicarbonate treatment was widely proven beneficial to the adhesion between flax fibers and epoxy matrix, on the other hand, it was equally evident that the same treatment weakened the jute fiber–epoxy matrix interface. Consequently, it is reasonable to consider that F Hybrid-T laminates showed better damping properties in comparison to their untreated counterparts (i.e., F Hybrid-AR) because the stacking sequence of F Hybrid laminates is characterized by more flax-reinforced laminae than jute ones (i.e., three versus two). Moreover, these hybrid laminates present flax-reinforced laminae as external layers. The bending performances of the composite laminates are heavily influenced by these external laminae that suffer the higher longitudinal stresses, unlike the central laminae where the neutral axis is located. Furthermore, it can be evidenced that F Hybrid-T laminates showed better damping properties in comparison to their untreated counterparts (i.e., F Hybrid-AR) because the stacking sequence of F Hybrid laminates is characterized by a larger amount of flax-reinforced laminae than jute ones (i.e., three reinforced laminae versus two).
On the contrary, J Hybrid laminates have three epoxy-based laminae reinforced with jute fibers versus two reinforced with flax ones in their stacking sequence. In addition, the external laminae supporting the highest longitudinal stresses are reinforced with jute fibers. Consequently, the detrimental effect of the treatment on jute fiber–epoxy matrix adhesion, in addition to worsening the damping properties of J Hybrid-T laminates in comparison to the laminates reinforced with as received fabrics (i.e., J Hybrid-AR) in the unaged condition [
32], reduced their service life when exposed to salt-fog.
Indeed, J Hybrid-T laminates showed the greater decrement of the storage modulus E’ in the glassy region with the exposition time to salt-fog in comparison to J Hybrid-AR laminates, as evidenced by comparing
Figure 7a,b. In particular, it was found that E’ measured at room temperature of J Hybrid-T laminates after 1 month and 2 months under salt-fog environment was 23% and 37% lower than unaged laminates, respectively. On the other hand, J Hybrid-AR composites better retained their dynamic stiffness, showing a reduction of the storage modulus at room temperature equal to 12% and 24% after 1 month and 2 months of aging exposition, respectively.
Concerning the effect of salt-fog exposition on tan δ trends,
Figure 7c,d evidences that both tan δ peaks became higher and shifted to lower temperatures when increasing the salt-fog exposition time, for laminates reinforced with treated or as received fabrics. However, it is worth noting that tan δ values of J Hybrid-AR laminates were lower than those of J Hybrid-T in the whole temperature range, regardless the aging exposition time. In accordance with the evolution of the storage modulus, hybrid laminates reinforced with treated fabrics (i.e., J Hybrid-T) showed greater variations of both tan δ peaks with salt-fog exposition time in comparison to J Hybrid-AR laminates.
Table 5 evidences that the temperature of the first peak slightly decreased 5.4 °C (i.e., from 79.9 °C to 74.5 °C) and 10.1 °C (i.e., from 81.9 °C to 71.8 °C) for J Hybrid-T and J Hybrid-AR laminates after 60 days under salt-fog, respectively. The second tan δ peak decreased from 109.6 °C to 99.9 °C (i.e., ΔT = 9.7 °C) and 106.8 °C to 103.6 °C (i.e., ΔT = 3.2 °C) for J Hybrid-T laminates and J Hybrid-AR, respectively.
At the same time, J Hybrid-T laminates increased the heights of first and second tan δ peaks from 0.43 to 0.63 and from 0.38 to 0.86 after 60 aging days, respectively. Vice versa, hybrid laminates reinforced with untreated fabrics (i.e., J Hybrid-AR) showed reduced height increments of both peaks (i.e., from 0.33 to 0.46 for the first peak and from 0.18 to 0.33 for the second one). This phenomenon can be related to the effect induced by the sodium bicarbonate treatment that, as reported in [
48], leads to a significant enhancement of the quasi-static performances of flax-reinforced composites and, conversely, a reduction in strength and stiffness of jute-based composites.
3.3. Damping Properties Versus Moisture Content
Useful information can be extrapolated by analyzing the correlation between the damping properties variation and the progressive water absorption evidenced by the NFRPs during their exposition to the salt-fog condition. This approach allows to discriminate how mechanical parameters are more affected by degradative phenomena. In such a context,
Table 6 reports the water uptake values evidenced by all the compared laminates after 30 days and 60 days under salt-fog condition, respectively.
It is worth noting that all samples evidenced a relevant hydrophilic behavior, showing weight gain values in the range 10–13% after 30 days of salt-fog exposition. Moreover, it was found that Flax-AR and Jute-T laminates were the most sensitive laminates to wet environments. This indicates that the water uptake is not related to the water sorption capability of natural fibers or epoxy matrix, but it is mainly related to competing fiber–matrix phenomena that synergistically play an important role in the degradative process of these NFRP materials.
In order to relate the dynamic mechanical performance modification with environmental aging in wet conditions, the relationships between the variation of damping properties of all the resulting laminates and their moisture content are shown in
Figure 8,
Figure 9 and
Figure 10. In particular, the variation of each damping property was calculated as follows:
where
Pt is the value of the damping property of the laminate under salt-fog condition for a specific time
t (i.e., 1 or 2 months) and
P0 is the value of the same property at the beginning of the aging campaign (i.e., for the unaged condition).
In particular,
Figure 8 shows that moisture had a significant influence on the storage modulus E’ measured at 25 °C of NFRP laminates. It was clearly found a linear relationship between the storage modulus variation (indicated as SMV index) and the water uptake. Similar to what was observed by Wang and Petru [
40], a clear decrease of the dynamic stiffness was found with increasing the composites’ moisture content. Due to the polysaccharide content of natural fibers and the voids and cracks in the epoxy matrix bulk, flax and jute fibers tended to absorb a great amount of water when composites were exposed to humid environments such as a marine one [
10,
23]. Hence, the penetration of water molecules and ions (i.e., Na
+ and Cl
−) within the composite structure led to softening both matrix and natural reinforcing fibers, as well as chemically and physically degrading the inherently weak fiber/matrix interface.
Furthermore, it is worth noting that composites having the strongest fiber–matrix adhesion (i.e., Flax-T and F Hybrid-T laminates) [
48] were characterized by lower moisture absorptions and, consequently, more contained stiffness reductions (as visible by the positioning of purple dots in the graph of
Figure 8). On the contrary, the highest values of moisture absorption and storage modulus reductions were shown by composites with weak fiber–matrix adhesion (i.e., Flax-AR, Jute-T, J Hybrid-T, F Hybrid-AR). These results can be explained, taking into account the different interactions of the investigated natural fibers (i.e., flax and jute) with the sodium bicarbonate treatment. As shown in our previous paper [
48], bicarbonate treatment softens jute fibers, due to their higher amount of lignin (i.e., up to 25–27%) in comparison to flax fibers (i.e., up to 5%) [
1,
56,
57]. Conversely, this mildly alkaline treatment is able to remove the impurities from the surface of flax fibers without any chemical interaction with the fiber bulk because of the lower lignin content and the more compact structure, compared to jute fibers [
58]. These different interactions allow composites reinforced with treated flax fibers to have a stronger fiber–matrix adhesion in comparison to those reinforced with raw fibers. Conversely, a slight worsening of adhesion between jute fibers and epoxy resin is achieved after sodium bicarbonate treatment.
In accordance with the trend of the dynamic storage modulus, the height of loss factor (i.e., tan δ) peaks increased with the moisture content, as shown in
Figure 9 and
Figure 10.
It is well known that the loss factor versus temperature trend of FRP materials is influenced by the incorporation of fibers in the polymeric matrix, due to the energy dissipation in the matrix bulk and to the shear stress concentrations at the fiber–matrix interfaces [
51]. In particular, composites with a weak fiber–matrix interface show high and large loss factor peaks because they tend to dissipate more energy in comparison to FRPs having the strongest fiber–matrix adhesion [
54,
59]. Moreover, when composites are exposed to a humid environment, the value of loss factor peaks increases with the exposition time to humid environments and, consequently, moisture content [
40]. This detrimental effect is more pronounced for composites characterized by a weak fiber–matrix interface because they dramatically suffer mechanical performance degradation when exposed to humid environments during their service life [
12,
13].
By observing the trend of LFV
1 (i.e., loss factor variation for the first peak) index as a function of the moisture content, it was possible to identify two different stages of the degradative process (
Figure 9). The first one (i.e., Stage 1) occurring at low water uptake values, was characterized by limited variation of the loss factor for the first peak. This could be ascribed to a water uptake not relevant enough to modify the mobility of the polymer chains in the matrix bulk. On the other hand, when the water absorption phenomenon became significant, a relevant enhancement of LFV
1 index was highlighted, as evidenced by the increased slope of the curve trend (i.e., Stage 2). Water molecules are able to diffuse inside the laminate structure, thus triggering softening phenomena of the matrix with, as a consequence, greater LFV
1 index values occurring. Indeed, samples evidencing the highest water absorption showed LFV
1 index values higher than 1.5.
As evidenced in
Figure 9, the water uptake level equal to 12% can be considered as a threshold transition value between the two abovementioned stages for these natural composite laminates.
Similar considerations were drawn by observing the LFV
2 (i.e., loss factor variation for the second peak) index versus water uptake trend shown in
Figure 10. It was of upmost importance to evidence that the second peak variation was more affected by water uptake in comparison to the first peak. Even in this case, two different degradative stages were identified at low and high water uptake values, respectively. Noticeable variations of the second peak height were evidenced already in the first stage, i.e., LFV
2 values equal to about 1.4 for water uptake lower than 12%. These experimental results confirmed that the fiber–matrix adhesion weakening was strongly correlated with the water absorption experienced by the laminate in the beginning phase of the salt-fog exposition.
Therefore, this stage can be considered a discriminating factor concerning the micro-mechanical transition phenomena of the immobilized polymer layer between fiber and matrix (i.e., fiber–matrix interphase).
On this basis, it is reasonable to consider that the water diffusion inside the composite structure mainly depended on a weak fiber–matrix adhesion that, in turn, represented the main factor activating degradative phenomena. The transition between the two degradative stages was identified, also in this case, at water uptake values equal to 12%. Beyond this threshold limit, the LFV2 index became higher than 2 (i.e., up to 3.5 for Flax-AR samples, for instance), thus indicating a serious loss of the adhesion between the main components of the composite (i.e., fiber and matrix).
Due to the above reasons, composites having the weakest fiber–matrix adhesion, such as Flax-AR and Jute-T, evidenced the highest increments in loss factor peaks as well as the greatest moisture absorption during their exposition to the salt-fog environment. On the contrary, the beneficial effect of the NaHCO3 treatment on the adhesion between flax fibers and epoxy resin allowed composites such as Flax-T and F-Hybrid T to reduce their moisture absorption and, as a consequence, to better retain their damping peaks. Similarly, composites with inherently good fiber–matrix adhesion, such as Jute-AR and J Hybrid-AR, showed low moisture adsorption and slight variations in both loss factor peaks, also after long exposition time in the salt-fog environment.
With the aim to better correlate the degradative phenomena evolution, a comparison of LFV
1 and LFV
2 versus water uptake trends is schemed in
Figure 11. Concerning Stage 1, LFV
2 was equal to about 1.4, thus indicating peak variation of about 40%, twice the variation of the first peak. In addition, the slope of the LFV
2 trend was noticeably higher than that evidenced for LFV
1. These experimental results further confirmed that the main limiting factor in the application of NFRPs in humid or wet conditions is represented by the worsening effect on the fiber–matrix adhesion of these environments. This degradation phenomenon is much more sensitive than other ones such as matrix softening, which, although giving an appreciable contribution on aging degradation, can be considered, in this case, a sub-degradation step of the global degradation mechanisms.
Further studies will be aimed to better discriminate among the different damage evolution stages occurring in critical environmental conditions, such as salt-fog spray. This will provide added value in the identification of synergistic actions between various degradative mechanisms that contribute to the degradation of the laminate. However, the achieved results are promising and potentially suitable to integrate the design knowledge of natural composite laminates and their durability performance under specific environmental conditions during the design phase.