Search Results (81)

Environmentally friendly biopolymer nanofibrous composite membranes with enhanced mechanical properties and thermal stability were fabricated via electrospinning with different compositions of polylactic acid (PLA) and cellulose acetate (CA). Firstly, PLA and CA composite membranes were prepared and optimized. Then, the optimized membranes were annealed at temperatures ranging from 80 °C to 140 °C, for annealing times between 30 and 90 min. The developed membranes were characterized by FE-SEM, XRD, FR-IT, TGA, DSC, tensile testing, water contact angle, and resistance to hydrostatic pressure. PLA 95-CA 5 was the optimum composite, with a tensile strength 9.3 MPa, an average fiber diameter of 432 nm, a water contact angle of 135.7°, and resistance to a hydrostatic pressure of 16.5 KPa. Annealing resulted in further improvements in different properties. The annealed membranes had thermally stable microporous structures, without shrinkage or deterioration in nanofiber structure, even at an annealing time of 90 min and an annealing temperature of 140 °C. By increasing either the annealing time or temperature, the crystallinity and rigidity of the nanofiber composite membranes were increased. The annealed membrane demonstrated a tensile strength of 12.3 MPa, a water contact angle of 139.2°, and resistance to a hydrostatic pressure of 36 KPa. Electrospinning of PLA-CA composite membranes with enhanced mechanical properties and thermal stability will pave the way for employing PLA-based membranes in various applications. Full article

In this study, polysulfone/polyvinylpyrrolidone (PSf/PVP, 20 wt%/5 wt%)-based ultrafiltration (UF) membranes reinforced with different ratios (0.5 and 1 wt%) of cellulose nanocrystals (CNCs) and cellulose nanofibres (CNFs) were prepared by the phase inversion method. The effect of CNC, CNF, and CNC-CNF reinforcement on the morphology, roughness, crystallinity, porosity, average pore size, mechanical properties, and filtration performance of PSf/PVP-based membrane was investigated. Distilled water and surface water (lake water) fluxes of the membranes were determined at 3 bar using a dead-end filtration system. The distilled water flux of the fouled–hydraulic cleaned membranes was determined, and scanning electron microscopy (SEM) images of the fouled–cleaned membranes were examined. The flux recovery ratio (FRR) and fouling parameters were calculated to examine the fouling behaviour of the membranes. The mechanical properties of the membranes were modelled by the Mori–Tanaka, finite element, Voigt–Reuss, self-consistent scheme, and Halpin–Tsai methods using Digimat and/or analytically. In addition, the von Mises equivalent stress distributions of the nanocomposites were presented. Among the investigated membranes, PSf/PVP/CNC-0.5 had the highest distilled water flux (475.5 ± 17.77 L/m².h), PSf/PVP/CNF-1 exhibited the stiffest behaviour with an elasticity modulus of 70.63 ± 3.15 MPa, and PSf/PVP/CNC-1 had the best organic matter removal efficiency. The finite element was the most successful modelling method for estimating the mechanical properties of nanocellulose-reinforced flat sheet membranes. Full article

Smart colorimetric packaging has been an important method to protect human health from external hazardous agents. However, the currently available colorimetric detectors use synthetic dye probes, which are costly, toxic, difficult to prepare, and non-biodegradable. Herein, an environmentally friendly cellulose nanocrystal (CNC)-supported polyvinyl alcohol (PVA) nanofibrous membrane was developed for the colorimetric monitoring of food spoilage. Anthocyanidin (ACY) is a naturally occurring spectroscopic probe that was isolated from pomegranate (Punica granatum L.). By encapsulating the anthocyanin probe in electrospun polyvinyl alcohol fibers in the presence of a mordant (M), M/ACY nanoparticles were generated. After exposure to rotten shrimp, an investigation on the colorimetric changes from purple to green for the smart nanofibrous fabric was conducted using the coloration parameters and absorbance spectra. In response to increasing the length of exposure to rotten shrimp, the absorption spectra of the anthocyanin-encapsulated nanofibrous membrane showed a wavelength blueshift from 580 nm to 412 nm. CNC displayed a diameter of 12–17 nm. The nanoparticle diameter of M/ACY was monitored in the range of 8–13 nm, and the nanofiber diameter was shown in the range of 70–135 nm. Slight changes in comfort properties were monitored after encapsulating M/ACY in the nanofibrous fabric. Full article

Recently, cellulose and other biomass nanofibers (NFs) have been increasingly utilized in the design of sustainable materials for environmental, biomedical, and other applications. However, the past literature lacks a comparison of the macromolecular and nanofibrous states of biopolymers in various materials, and the advantages and limitations of using nanofibers (NF) instead of conventional polymers are poorly understood. To address this question, hydrogels based on interpolyelectrolyte complexes (IPECs) between carboxymethyl cellulose nanofibers (CMCNFs) and chitosan (CS) were prepared by ele+ctrostatic cross-linking and compared with the hydrogels of carboxymethyl cellulose (CMC) and CS biopolymers. The presence of the rigid CMCNF altered the mechanism of the IPEC assembly and drastically affected the structure of IPEC hydrogels. The swelling ratios of CMCNF-CS hydrogels of ca. 40% were notably lower than the ca. 100–300% swelling of CMC-CS hydrogels. The rheological measurements revealed a higher storage modulus ($G^{\prime }$) of the CMCNF-CS hydrogel, reaching 13.3 kPa compared to only 3.5 kPa measured for the CMC-CS hydrogel. Further comparison of the adsorption characteristics of the CMCNF-CS and CMC-CS hydrogels toward Cu²⁺, Cd²⁺, and Hg²⁺ ions showed the slightly higher adsorption capacity of CMC-CS for Cu²⁺ but similar adsorption capacities for Cd²⁺ and Hg²⁺. The adsorption kinetics obeyed the pseudo-second-order adsorption model in both cases. Overall, while the replacement of CMC with CMCNF in hydrogel does not significantly affect the performance of such systems as adsorbents, CMCNF imparts IPEC hydrogel with higher stiffness and a frequency-independent loss ($G^{″}$) modulus and suppresses the hydrogel swelling, so can be beneficial in practical applications that require stable performance under various dynamic conditions. Full article

The excessive utilization of antimicrobials in humans and animals has resulted in considerable environmental contamination, necessitating the development of high-performance antibiotic adsorption media. A significant challenge is the development of composite nanofibrous materials that are both beneficial and easy to fabricate, with the aim of improving adsorption capacity. Herein, a new kind of zeolitic imidazolate framework-8 (ZIF-8)-modified regenerated cellulose nanofibrous membrane (ZIF-8@RC NFM) was designed and fabricated by combining electrospinning and in situ surface modification technologies. Benefiting from its favorable surface wettability, enhanced tensile strength, interconnected porous structure, and relatively large specific surface area, the resulting ZIF-8@RC NFMs exhibit a relatively high adsorption capacity for tetracycline hydrochloride (TCH) of 105 mg g⁻¹ within 3 h. Moreover, a Langmuir isotherm model and a pseudo-second-order model have been demonstrated to be more appropriate for the description of the TCH adsorption process of ZIF-8@RC-3 NFMs. Additionally, this composite fibrous material could keep a relatively stable adsorption capability under various ionic strengths. The successful fabrication of the novel ZIF-8@RC NFMs may shed light on the further development of wastewater adsorption treatment materials. Full article

Currently, the development of innovative materials for the treatment of various diseases is highly interesting and effective. Additionally, in recent years, environmental changes, including the search for a sustainable world, have become the main goal behind developing sustainable and suitable materials. In this context, this research produced innovative hydrogels that incorporate cellulose nanocrystals and nanofibres from underutilised fibres from a semiarid region of Brazil; the hydrogels were loaded with vitamin D to evaluate controlled drug release for the treatment of diverse diseases. Spectroscopic (FTIR, Raman, UV–VIS), X-ray diffraction, zeta potential and morphology (SEM, TEM) analyses were used to characterise these hydrogels. In addition, biocompatibility was assessed using a resazurin assay, and the in vitro kinetic accumulative release of vitamin D was measured. The results showed that nanocrystals and nanofibres changed the structure and crystallinity of the hydrogels. In addition, the chemical groups of the hydrogels were red- and blueshifted in the FTIR spectra when the nanocrystals, nanofibres and vitamin D were incorporated. Moreover, the nanocrystals and nanofibres were homogeneously spread into the hydrogel when vitamin D was loaded into the hydrogel matrix. Furthermore, the cytotoxicity was greater than 90%. Additionally, the in vitro accumulative kinetic data of vitamin D release were robust (close to 40 ng·mL⁻¹), with equilibrium being reached in the first 30 min. These results confirm the potential of using these hydrogels as therapeutic biomaterials for diverse diseases and problems in humans, mainly in women, who are the most harmed by vitamin D deficiency. Full article

Membranes are a selective barrier that allows certain species (molecules and ions) to pass through while blocking others. Some rely on size exclusion, where larger molecules get stuck while smaller ones permeate through. Others use differences in charge or polarity to attract and repel specific species. Membranes can purify air and water by allowing only air and water molecules to pass through, while preventing contaminants such as microorganisms and particles, or to separate a target gas or vapor, such as H₂ and CO₂, from other gases. The higher the flux and selectivity, the better a material is for membranes. The desirable performance can be tuned through material type (polymers, ceramics, and biobased materials), microstructure (porosity and tortuosity), and surface chemistry. Most membranes are made from plastic from petroleum-based resources, contributing to global climate change and plastic pollution. Cellulose can be an alternative sustainable resource for making renewable membranes. Cellulose exists in plant cell walls as natural fibers, which can be broken down into smaller components such as cellulose fibrils, nanofibrils, nanocrystals, and cellulose macromolecules through mechanical and chemical processing. Membranes made from reassembling these particles and molecules have variable pore architecture, porosity, and separation properties and, therefore, have a wide range of applications in nano-, micro-, and ultrafiltration and forward osmosis. Despite their advantages, cellulose membranes face some challenges. Improving the selectivity of membranes for specific molecules often comes at the expense of permeability. The stability of cellulose membranes in harsh environments or under continuous operation needs further improvement. Research is ongoing to address these challenges and develop advanced cellulose membranes with enhanced performance. This article reviews the microstructures, fabrication methods, and potential applications of cellulose membranes, providing some critical insights into processing–structure–property relationships for current state-of-the-art cellulosic membranes that could be used to improve their performance. Full article

This study addresses the structure–property relationship within the green concept of wood fibres with cellulose nanofibre functionalised composites (nW-PPr) containing recycled plastic polyolefins, in particular, polypropylene (PP-r). It focuses especially on the challenges posed by nanoscience in relation to wood fibres (WF) and explores possible changes in the thermal properties, crystallinity, morphology, and mechanical properties. In a two-step methodology, wood fibres (50% wt%) were first functionalised with nanocellulose (nC; 1–9 wt%) and then, secondly, processed into composites using an extrusion process. The surface modification of nC improves its compatibility with the polymer matrix, resulting in improved adhesion, mechanical properties, and inherent biodegradability. The effects of the functionalised WF on the recycled polymer composites were investigated systematically and included analyses of the structure, crystallisation, morphology, and surface properties, as well as thermal and mechanical properties. Using a comprehensive range of techniques, including X-ray diffraction (XRD), attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR), differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), scanning electron microscopy (SEM), zeta potential measurements, and dynamic mechanical analysis (DMA), this study aims to unravel the intricate interplay of factors affecting the performance and properties of the developed nanocellulose-functionalised wood fibre–polymer composites. The interfacial adhesion of the nW-PPr polymer composites, crystallisation process, and surface properties was improved due to the formation of an H-bond between the nW coupling agent and neat PP-r. In addition, the role of nW (1.0 wt%) as a nucleating agent resulted in increased crystallinity, or, on the other hand, promoted the interfacial interaction with the highest amount (3.0% wt%, 9.0% wt%) of nW in the PP-r preferentially between the nW and neat PP-r, and also postponed the crystallisation temperature. The changes in the isoelectric point of the nW-PPr polymer composites compared to the neat PP-r polymer indicate the acid content of the polymer composite and, consequently, the final surface morphology. Finally, the higher storage modulus of the composites compared to neat r-PP shows a dependence on improved crystallinity, morphology, and adhesion. It was clear that the results of this study contribute to a better understanding of sustainable materials and can drive the development of environmentally friendly composites applied in packaging. Full article

Cellulose nanofibrils (CNFs) are particles with a high aspect ratio. Typically, chemically pre-treated CNFs (containing anionic or cationic charged groups) consist of long fibrils (up to 2 μm) with very low thickness (less than 10 nm). Derived from their high aspect ratio, CNFs form strong hydrogels with high elasticity at low concentrations. Thus, CNF suspensions appear as an interesting rheology modifier to be applied in cosmetics, paints, foods, and as a mineral suspending agent, among other applications. The high viscosity results from the strong 3D fibril network, which is related to the good fibrillation of the material, allowing the nanofibrils to overlap. The overlap concentration (c*) was found to vary from ca. 0.13 to ca. 0.60 wt.% depending on the type and intensity of the pre-treatment applied during the preparation of the CNFs. The results confirm the higher tendency for the fibres treated with (3-chloro-2-hydroxypropyl) trimethylammonium chloride (CHPTAC) and 2,2,6,6-tetramethylpiperidine 1-oxyl (TEMPO) to form a 3D network, resulting in the lowest c*. For the TEMPO-oxidised CNF suspensions, it was also found that aggregation is improved at acidic pH conditions due to lower charge repulsion among fibrils, leading to an increase in the suspension viscosity as well as higher apparent yield stresses. TEMPO CNF suspensions with a low content of carboxylic groups tend to precipitate at moderately acidic pH values. Full article

In recent years, flexible pressure sensors have received considerable attention for their potential applications in health monitoring and human–machine interfaces. However, the development of flexible pressure sensors with excellent sensitivity performance and a variety of advantageous characteristics remains a significant challenge. In this paper, a high-performance flexible piezoresistive pressure sensor, BC/ZnO, is developed with a sensitive element consisting of bacterial cellulose (BC) nanofibrous aerogel modified by ZnO nanorods. The BC/ZnO pressure sensor exhibits excellent mechanical and hydrophobic properties, as well as a high sensitivity of −15.93 kPa⁻¹ and a wide range of detection pressure (0.3–20 kPa), fast response (300 ms), and good cyclic durability (>1000). Furthermore, the sensor exhibits excellent sensing performance in real-time monitoring of a wide range of human behaviors, including mass movements and subtle physiological signals. Full article

A functionally graded membrane (FGM) with a special spiral-structured cellulose acetate (CA) membrane was prepared by electrospinning under different collection distances. The membrane morphology was analyzed by scanning electron microscopy (SEM). FESEM images revealed that the high concentration shows the formation of fibers with an irregular diameter, with a large diameter distribution range. The fiber collected at a short distance of 10 cm experiences the strong electrostatic force, resulting in the short flight time for the polymer jet. This causes the bending instability of the polymer jet forming the comparatively thick fiber diameters, whereas the fiber collected at 15 cm shows the presence of a smooth, homogeneous diameter. Furthermore, the water flux of the membrane was determined using 50 mL of Amicon stirred cells. The fiber collected at different distances showed diameter variation, which is used to design a special spiral structure on the membrane by auto-moving the collector between the fixed distances of 10–20 cm. This technique will reveal a new approach for the fabrication of a special spiral structure on the nanofibrous membrane for different biomedical applications from different polymers. Meanwhile, the fabricated FGM with a special spiral-structure CA membrane demonstrates high water permeation flux. Full article

Due to environmental concerns regarding single-use plastic materials, major efforts are being made to develop new material concepts based on biodegradable and renewable resources, e.g., wood pulp. In this study, we assessed two types of wood pulp fibres, i.e., thermomechanical pulp (TMP) and Kraft pulp fibres, and tested the performance of the fibres in wet-moulding and thermopressing trials. Kraft pulp fibres appeared to retain more water than TMP, increasing the dewatering time during wet-moulding and apparently increasing the compression resistance of the pulp during thermoforming. Additionally, cellulose nanofibres (CNF) were added to the pulps, which improved the mechanical properties of the final thermopressed specimens. However, the addition of CNF to the pulps (from 2 to 6%) had a further decrease in the dewatering efficiency in the wet-moulding process, and this effect was more pronounced in the Kraft pulp specimens. The mechanical performance of the thermoformed specimens was in the same range as the plastic materials that are conventionally used in food packaging, i.e., modulus 0.6–1.2 GPa, strength 49 MPa and elongation 6–9%. Finally, this study demonstrates the potential of wood pulps to form three-dimensional thermoformed products. Full article

The effluents of industrial wastewater contain several toxic organic and inorganic pollutants that may contaminate clean and freshwater sources if untreated or poorly treated. These toxic pollutants include colors; hazardous compounds; surfactants; cosmetics; agrochemicals; pharmaceutical by-products; and agricultural, pharmaceutical, and medical contaminants. Treating wastewater has become a global problem. Many projects have been started in the last two decades to treat wastewater, resultant water pollution, and associated waste management problems. Adsorbants based on graphene oxide (GO) are viable wastewater treatment materials due to their adaptability, photocatalytic action, and capacity for self-assembly. Here, we report the fabrication of nanofibrous mats from polycaprolactone (PCL), carboxymethyl arabinoxylan (CMARX), and carboxyl-functionalized-graphene oxide using an electrospinning technique. The silver nanoparticles were loaded onto the mat to enhance their photocatalytic activity. These mats were characterized using different techniques, including Fourier transform infrared (FTIR), scanning electron microscope (SEM), and transmission electron microscope (TEM). The water contact angles were used to study their hydrophilic and hydrophobic behavior. The Langmuir isotherm model and adsorption kinetics were studied to evaluate their adsorption capabilities against methylene blue (MB). Sample 2 followed the Langmuir isotherm model (R² = 0.9939). Adsorption kinetics exhibited pseudo-second order behavior (R² = 0.9978) due to their maximum correlation coefficient values. MB has excellent adsorption at room temperature and the formation of the monolayer at the surface of the adsorption mat. An enhanced PO₄³⁻ and MB adsorption was observed, providing recyclability up to 4–5 times. Hence, the fabricated nanofibrous mat would be a potential candidate for more effective wastewater treatment applications. Full article

The currently reported methods for preparing cellulose acetate hydrogels use chemical reagents as cross-linking agents, and the prepared ones are non-porous structured cellulose acetate hydrogels. Nonporous cellulose acetate hydrogels limit the range of applications, such as limiting cell attachment and nutrient delivery in tissue engineering. This research creatively proposed a facile method to prepare cellulose acetate hydrogels with porous structures. Water was added to the cellulose acetate–acetone solution as an anti-solvent to induce the phase separation of the cellulose acetate–acetone solution to obtain a physical gel with a network structure, where the cellulose acetate molecules undergo re-arrangement during the replacement of acetone by water to obtain hydrogels. The SEM and BET test results showed that the hydrogels are relatively porous. The maximum pore size of the cellulose acetate hydrogel is 380 nm, and the specific surface area reaches 62 m²/g. The porosity of the hydrogel is significantly higher than that of the cellulose acetate hydrogel reported in the previous literature. The XRD results show that the nanofibrous morphology of cellulose acetate hydrogels is caused by the deacetylation reaction of cellulose acetate. Full article

Estradiol, a phenolic steroid oestrogen, is one of the endocrine-disrupting chemicals (EDCs) found in natural and tap waters. The detection and removal of EDCs is attracting attention daily as they negatively affect animals’ and humans’ endocrine functions and physiological conditions. Therefore, developing a fast and practical method for the selective removal of EDCs from waters is essential. In this study, we prepared 17β-estradiol (E2)-imprinted HEMA-based nanoparticles onto bacterial cellulose nanofibres (E2-NP/BC-NFs) to use for the removal of E2 from wastewater. FT-IR and NMR confirmed the structure of the functional monomer. The composite system was characterised by BET, SEM, µCT, contact angle, and swelling tests. Additionally, the non-imprinted bacterial cellulose nanofibres (NIP/BC-NFs) were prepared to compare the results of E2-NP/BC-NFs. Adsorption of E2 from aqueous solutions was performed in batch mode and investigated via several parameters for optimisation conditions. The effect of pH studies was examined in the 4.0–8.0 range using acetate and phosphate buffers and a concentration of E2 of 0.5 mg/mL. The maximum E2 adsorption amount was 254 µg/g phosphate buffer at 45 °C. The experimental data show that the Langmuir is a relevant isotherm model for E2 adsorption. Additionally, the relevant kinetic model was the pseudo-second-order kinetic model. It was observed that the adsorption process reached equilibrium in less than 20 min. The E2 adsorption decreased with the increase in salt at varying salt concentrations. The selectivity studies were performed using cholesterol and stigmasterol as competing steroids. The results show that E2 is 46.0 times more selective than cholesterol and 21.0 times more selective than stigmasterol. According to the results, the relative selectivity coefficients for E2/cholesterol and E2/stigmasterol were 8.38 and 86.6 times greater for E2-NP/BC-NFs than for E2-NP/BC-NFs, respectively. The synthesised composite systems were repeated ten times to assess the reusability of E2-NP/BC-NFs. Full article