Search Results (5)

Alkaline anion exchange membranes (AAEMs) are an enabling component for next-generation electrochemical devices, including alkaline fuel cells, water and CO₂ electrolyzers, and flow batteries. While commercial systems, notably fuel cells, have traditionally relied on proton-exchange membranes, hydroxide-ion conducting AAEMs hold promise as a method to reduce cost-per-device by enabling the use of non-platinum group electrodes and cell components. AAEMs have undergone significant material development over the past two decades; however, challenges remain in the areas of durability, water management, high temperature performance, and selectivity. In this review, we survey crosslinking as a tool capable of tuning AAEM properties. While crosslinking implementations vary, they generally result in reduced water uptake and increased transport selectivity and alkaline stability. We survey synthetic methodologies for incorporating crosslinks during AAEM fabrication and highlight necessary precautions for each approach. Full article

Membranes made up of composite materials have shown promising advantages for application in alkaline fuel cell anion exchange membranes. In this study, a general method is employed to improve the overall performance and properties of alkaline anion exchange membranes by making use of polyethersulfone quaternized with imidazolium groups and blended with imidazolium functionalized graphene oxide inorganic filler (ImGO). The inorganic filler blended with the polymer matrix yielded better ionic transport, with 73.2 mS·cm⁻¹ being the highest ion conductivity for the polymer membrane with 0.5% ImGO content, which is higher than that of the QPES parent material. The 0.5% ImGO content also showed better swelling ratio, water uptake, alkaline stability, ion exchange capacity and alkaline stability in comparison to other membranes. Furthermore, it also exhibited 130 mW·cm⁻² peak power. Full article

Polymer electrolyte fuel cells with alkaline anion exchange membranes (AAEMs) have gained increasing attention because of the faster reaction kinetics associated with the alkaline environment compared to acidic media. While the development of anion exchange polymer membranes is increasing, the catalytic layer structure and composition of electrodes is of paramount importance to maximize fuel cell performance. In this work, we examine the preparation procedures for electrodes by catalyst-coated substrate to be used with a well-known commercial AAEM, Fumasep^® FAA-3, and a commercial ionomer of the same nature (Fumion), both from Fumatech GmbH. The anion exchange procedure, the ionomer concentration in the catalytic layer and also the effect of membrane thickness, are investigated as they are very relevant parameters conditioning the cell behavior. The best power density was achieved upon ion exchange of the ionomer by submerging the electrodes in KCl (isopropyl alcohol/water solution) for at least one hour, two exchange steps, followed by treatment in KOH for 30 min. The optimum ionomer (Fumion) concentration was found to be close to 50 wt%, with a relatively narrow interval of functioning ionomer percentages. These results provide a practical guide for electrode preparation in AAEM-based fuel cell research. Full article

The physicochemical and mechanical properties of new alkaline anion-exchange membranes (AAEMs) based on chitosan (CS) and poly(vinyl alcohol) (PVA) polymers doped with unsupported copper nanoparticles (NPs) and copper exchanged over different porous materials were investigated regarding ion-exchange capacity (IEC), OH⁻ conductivity, water uptake (WU), water vapor permeability (WVP), and thermal and mechanical resistance. The influence of the type of filler included in different morphologies and filler loading has been explored using copper exchanged materials such as the layered porous titanosilicate AM-4, layered stannosilicate UZAR-S3, and zeolites Y, MOR, and BEA. Compared to commercially available anion-exchange membranes, the best performing membranes in terms of WU, IEC, OH⁻ conductivity and WVP in this study were those containing 10 wt % of Cu-AM-4 and Cu-UZAR-S3, although 10 wt % Cu-MOR provided better mechanical strength at close values of WVP and anion conductivity. It was also observed that when Cu was exchanged in a porous silicate matrix, its oxidation state was lower than when embedded as unsupported metal NPs. In addition, the statistical analysis of variance determined that the electrochemical properties of the membranes were noticeably affected by both the type and filler loading, and influenced also by the copper oxidation state and content in the membrane, but their hydrophilic properties were more affected by the polymers. The largest significant effects were noticed on the water sorption and transport properties, which gives scope for the design of AAEMs for electrochemical and water treatment applications. Full article

Mixed matrix membranes (MMM) based on chitosan (CS) and poly (vinyl) alcohol (PVA) with a 50:50 w/w ratio doped with graphene oxide (GO) are prepared by solution casting and characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), thermogravimetric analysis (TGA), water uptake, alcohol permeability, ion exchange capacity (IEC) and OH⁻ conductivity measurements. The SEM analysis revealed a dense MMM where the GO nanosheets were well dispersed over the entire polymer matrix. The incorporation of GO increased considerably the thermal stability of the CS:PVA membrane. The GO-based MMM exhibited a low conductivity of 0.19 mS·cm⁻¹ in part because the GO sheets did not change the crystallinity of the CS:PVA matrix. The reinforced structure created by the hydrogen bonds between the GO filler and the CS:PVA matrix resulted to be a good physical barrier for alcohol permeability, achieving a coefficient of diffusion of 3.38 × 10⁻⁷ and 2.43 × 10⁻⁷ cm²·s⁻¹ after 60 and 120 min, respectively, thus avoiding additional alcohol crossover. Finally, the electrochemical performance of the GO-based MMM in the electrooxidation of propargyl alcohol was investigated in a Polymer Electrolyte Membrane Electrochemical Reactor (PEMER) under alkaline conditions, through the polarization curve and the electrolysis reactions, showing a performance comparable to anion-exchange commercial membranes. Full article