Currently, the method of solving the issues related to the environment has become a topic of great interest and is approached by researching several directions, such as recycling or the replacement of polluting materials [1]. Most glass fiber (GF) composite wastes are non-biodegradable and very bulky, causing serious environmental problems [2]. Given the requirements of the European Commission to reduce CO2 emissions by at least 40%, it is possible to consider reducing the weight of automotive by replacing metal parts with high-performance polymer composites with a low impact on the environment [3]. Starting from the development of a new nanocomposite material based on bio-polyamide and 2D nanostructure that has improved properties [4,5] and can be used to obtain automotive parts, the possibility of reducing the content of glass fiber with graphene nanoplatelets in composite based on PA6 and 30% GF was studied.
A full bio-based polyamide 1010 (PA1010), a polyamide 6 (PA6), a composite with PA6 and 30% glass fiber (PA6GF30) and graphene nanoplatelets (M5) with a particle diameter of 5 µm and an average thickness of approximately 6–8 nm were used in this study. Hybrid composites based on PA, GF and M5 were obtained by using the masterbatch method. M5 masterbatches at 39 wt.% were obtained based on both PA1010 (MB1010) and PA6 (MB6), which were diluted with PA6GF30 to the desired M5 concentration. Both masterbatches and hybrid composites were obtained under dynamic conditions using a double screw extruder. The resulting hybrid composites were characterized in terms of thermal properties (TGA and DSC), mechanical properties (tensile and impact test) and dynamic-mechanical analysis (DMA).
The dilution of the MB1010 masterbatch with PA6GF30 composite resulted in hybrid composites with a mixture of PA1010 and PA6 as a polymer matrix, which at 5 wt.% M5 showed an interesting property profile. In comparison with the starting PA6GF30 material, the strength and stiffness of the hybrid composite was affected by approximately 29% and 25%, respectively. Moreover, impact strength decreased with approximately 18%. By contrast, a smaller decrease was attained for the strength and stiffness by approximately 12%, respectively, and 8% while maintaining the impact strength when the masterbatch MB6 was diluted with PA6GF30 composite.
It is possible to reduce at least 16 wt.% of the GF (from the overall 100 wt.% GF found in neat PA6GF30) with M5, with good compromise in comparison with the starting PA6GF30 and still meet automotive field material properties requirements. By the dilution of PA6-based masterbatch with PA630GF composite, hybrid composites with better properties were obtained.
Funding
This work was supported by a grant of the Romanian Ministry of Research and Innovation, CCCDI-UEFISCDI, project number PN-III-P1-1.2-PCCDI-2017-0387/80PCCDI, Emerging Technologies for the industrial application of 2D structures (graphene and non-graphene), acronym EMERG2IND, within PNCDIIII.
Institutional Review Board Statement
Not applicable.
Informed Consent Statement
Not applicable.
Acknowledgments
ENGEL Austria GmbH and ENGEL Injecție Srl are kindly acknowledged for their support and enabling the development of the injection molding equipment. EVONIK Industries AG is gratefully acknowledged for the full biobased PA1010 offering. ADDINOL Lubricants Romania SRL is also acknowledged for equipment assistance.
Conflicts of Interest
The authors declare no conflict of interest.
References
- Wu, Y.; Xia, C.; Cai, L.; Garcia, A.C.; Shi, S.Q. Development of natural fiber-reinforced composite with comparable mechanical properties and reduced energy consumption and environmental impacts for replacing automotive glass-fiber sheet molding compound. J. Clean. Prod. 2018, 184, 92–100. [Google Scholar]
- López, F.A.; Martín, M.I.; García-Díaz, I.; Rodríguez, O.; Alguacil, F.J.; Romero, M. Recycling of Glass Fibers from Fiberglass Polyester Waste Composite for the Manufacture of Glass-Ceramic Materials. J. Environ. Prot. 2012, 3, 740–747. [Google Scholar]
- Official Journal of the European Union. Directive (EU) 2019/1161 of the European Parliament and of the Council of 20 June 2019 Amending Directive 2009/33/EC on the Promotion of Clean and Energy-Efficient Road Transport Vehicles; Official Journal of the European Union: Luxembourg, 2019. [Google Scholar]
- Vuluga, Z.; Corobea, M.C.; Florea, D.; Teodorescu, G.M.; Afilipoaei, A. Concentrate for Improving the Shock Resistance of “Bio Based” Polyamide, Process for Obtaining and Using It. Patent Application A100724, 11 November 2020. [Google Scholar]
- Corobea, M.C.; Vuluga, Z.; Zăvoianu, R.; Pavel, O.D.; Teodorescu, G.M.; Afilipoaei, A.; Stamate, E.; Cruceanu, A. Composition and Obtaining Process, for the Fire Resistance Improvement of a ‘Bio Based’ Polyamide. Patent Application A00077, 25 February 2021. [Google Scholar]
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations. |
© 2022 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (https://creativecommons.org/licenses/by/4.0/).