Effects of Oil Concentration in Flood Cooling on Cutting Force, Tool Wear and Surface Roughness in GTD-111 Nickel-Based Superalloy Slot Milling

Cooling–lubricating processes have a big impact on cutting force, tool wear, and the quality of the machined surface, especially for hard-to-machine superalloys, so the choice of the right cooling–lubricating method is of great importance. Nickel-based superalloys are among the most difficult materials to machine due to their high hot strength, work hardening, and extremely low thermal conductivity. Previous research has shown that flood cooling results in the least tool wear and cutting force among different cooling–lubricating methods. Thus, the effects of the flood oil concentration (3%; 6%; 9%; 12%; and 15%) on the above-mentioned factors were investigated during the slot milling of the GTD-111 nickel-based superalloy. The cutting force was measured during machining with a Kistler three-component dynamometer, and then after cutting the tool wear and the surface roughness on the bottom surface of the milled slots were measured with a confocal microscope and tactile roughness tester. The results show that at a 12% oil concentration, the tool load and tool wear are the lowest; even at an oil concentration of 15%, a slight increase is observed in both factors. Essentially, a higher oil concentration reduces friction between the tool and the workpiece contact surface, resulting in reduced tool wear and cutting force. Furthermore, due to less friction, the heat generation in the cutting zone is also reduced, resulting in a lower heat load on the tool, which increases tool life. It is interesting to note that the 6% oil concentration had the highest cutting force and tool wear, and strong vibration was heard during machining, which is also reflected in the force signal. The change in oil concentration did not effect the surface roughness.