Influence of the Al/Ge Ratio on the Structure and Self-Organization of Anisometric Imogolite Nanotubes

Synthetic imogolite-like nanotubes (INT) with well-defined diameters represent a considerable opportunity for the development of advanced functional materials. Recent progress has made it possible to increase their aspect ratio and unique self-organization properties were evidenced. We suggest that slight modification of the synthesis conditions may drastically affect the resulting liquid-crystalline properties. In this work, we investigate how the precursor’s [Al]/[Ge] molar ratio (R’) impacts the morphology and the colloidal properties of aluminogermanate INTs by combining a multi-scale characterization. While only double-walled nanotubes are found for R’ ≥ 1.8, the presence of single-walled nanotubes occurs when the ratio is lowered. Except for the lowest R’ ratio investigated (R’ = 0.66), all synthetic products present one-dimensional shapes with a high aspect ratio. Small-angle X-ray scattering experiments allow us to comprehensively investigate the colloidal properties of the final products. Our results reveal that a liquid-crystalline hexagonal columnar phase is detected down to R’ = 1.33 and that it turns into a nematic arrested phase for R’ = 0.90. These results could be useful for the development of novel stimuli-responsive nanocomposites based-on synthetic imogolite nanotubes.