1. Introduction
Concrete is the world’s most prevalently utilized construction material due to unparallel compressive strength (CS), affordability, cost-effectiveness, abundance of raw materials, and durability. However, gradual degradation of concrete-based infrastructures is detrimental unless inhibited. The structural integrity and efficacy of concrete degrades due to water penetration into it. The ingress of water, undesired acidic gases, and fluids containing dissolved aggressive chemicals enable the formation of cracks in concrete at the macro- and micro-scale [
1]. Consequently, the aggressive substances and agents pass through these permeable sites, causing rapid deterioration of concrete. Hence, the durability of concrete and its steel reinforcement are negatively impacted, indicating that the concrete performance in the long-term is decided by the environment wherein concrete structures are placed [
2]. Reinforcing steel bars can be oxidized and weakened by the permeation of water, oxygen, carbon dioxide and chloride ions. Consequently, the durability of the exposed concrete infrastructure becomes limited [
3,
4]. Sometimes, the accessibility and repair of certain cracks in concrete is impossible, as they cannot be seen or associated/exist with unfavorable conditions to repair. The number of cracks and their sizes multiply as the materials undergo permeation, contraction, and expansion [
5,
6]. Consequently, an onus is increasingly placed upon the maintenance and inspection processes for prematurely ageing large portfolio of civil infrastructures. The costs associated with the maintenance are exorbitant, particularly for the large-scale infrastructures, challenging the frequent inspection and maintenance methods. Maintenance and repair can also be tricky due to the difficulty in accessing the damaged site of the infrastructures [
7,
8]. Consequently, academics in the field have increasingly focused upon the marginal capital and labor needs associated with self-healing concrete that can autonomously repair the hazardous cracks. Thus, numerous approaches have been developed to produce novel self-healing concrete, making it capable and prospective for civil engineering constructions.
Total or partial recovery and healing of the materials functionality following the degradation makes up the definition of self-healing materials [
9]. Similarly, autonomous repair and identification of the impairment of concrete cracks is another definition of self-healing materials [
10]. Thus, manual intervention can be avoided or minimized within the reparation process [
11]. The self-healing concrete is the name given for concrete that contains autonomous healing substances which can enter within the existing cracks and heal them without any human manual intervention. Autonomous healing is most frequently achieved by mixing concrete with fibers, crystalline admixtures, bacteria, polymers, and other smart materials. Normally, the chemical reactions and presence of water constitute the autonomous healing procedure that assesses the natural healing mechanisms. Therefore, the strength of the concrete is enhanced subsequent to the diminished width of the cracks via the autonomous healing procedure.
Figure 1 portrays the autonomous procedures involved in the artificial autonomous healing. The efficacy of the self-healing mechanism is enhanced via the immobilization, vascular, or encapsulation techniques that incorporate healing agents into the concrete.
The self-repairing of damaged concrete surfaces using the bacteria-mediated biological processes has recently been proposed [
12,
13,
14,
15,
16]. In the mid-1990s, Gollapudi [
17] proposed a sustainable technique to heal concrete cracks wherein ureolytic bacteria was added in the concrete to accelerate the calcium carbonate (CaCO
3) precipitation within the existing micro-cracked regions. The bacteria strains in the concrete [
18,
19,
20,
21] were utilized to produce the urease enzyme for catalyzing urea (CO(NH
2)
2) into ammonium ions (NH
4+) and carbonate (CO
32−) radicals. The overall chemical reactions followed various pathways. Using the reaction Path I, urea of 1 mol was first subjected to the intracellular hydrolyses of carbonate (1 mol) and ammonia (1 mol). Next, following the reaction Path II, spontaneous hydrolysis of carbamate occurred to generate extra 1 mole of ammonia and carbonic acid. Later, these compounds produced bi-carbonate (HCO
3−) of 1 mol and ammonium (NH
4+) and hydroxide (OH
−) each of 2 moles following the reaction Path III and IV. Following reaction Path IV and V, the mixture pH was enhanced, which could drift the equilibrium of bicarbonate, forming carbonate ions as described below.
CO(NH2)2 + H2O → NH2COOH + NH3 | Path I |
NH2COOH + H2O → NH3 + H2CO3 | Path II |
H2CO3 + H2O → HCO3− + H+ | Path III |
2NH3 + 2H2O → 2NH4+ + 2OH− | Path IV |
HCO3− + H++ 2NH4+ + 2OH− → CO32− + 2NH4+ + 2H2O | Path V |
The bacteria cell wall surface first attracted the cations from the neighboring environment due to the presence of negative charges in the cell walls, thus decomposing Ca
2+ on the cell walls surface. Then, on the bacteria cell walls surface, CaCO
3 was precipitated due to the chemicals’ reactions amid Ca
2+ and CO
32− that offered the active sites for further nucleation and growth [
18].
Figure 2 illustrates the self-repair mechanism of the cracks on the concrete surface due to the precipitation of CaCO
3 via the immobilized bacteria.
Ca2+ + Cell → Cell-Ca2+ | Path VI |
Cell-Ca2+ + CO32− → Cell-CaCO3 | Path VII |
Considering the practical benefits and demands of the smart bio-agents-activated sustainable self-healing cementitious materials in the construction engineering sectors worldwide, this paper critically reviewed diverse approaches developed for producing functional self-healing smart materials. The advantages and limitations of various self-healing techniques, mechanisms, design strategies, and measurement methods are extensively overviewed, compared, analyzed, and discussed. In addition, the effectiveness of the self-healing properties is determined by noting whether the cement-based material reflects its original form and functionality following the autonomous repair of the formed cracks. Finally, the economic and environmental benefits of the smart agents-based self-healing concretes and their prospects towards sustainable construction industry are emphasized.
3. Sustainability and Self-Healing Process of Cementitious Materials
Concrete remains one of the most widely used construction materials due to its excellent strength performance and ease of use. However, generation of cracks in different types of concretes is unavoidable due to its weakness in the tension. As a result, the lifespan of concrete structures is often compromised because of the development of cracks and ingress of harmful substances through these cracks. Crack repair is generally laborious, time consuming and costly [
19]. Conversely, the creation of self-healing concrete is an engineered approach that leads to an autonomous healing of the cracks when applied. Bacteria with calcium nutrient source are incorporated in the concrete to achieve autonomous healing of the cracks, wherein the calcium carbonate precipitates upon the formation of a crack, thus, filling the crack volume. It is known that the traditional concrete has less strength and durability than bacterial concrete. In this view, calcite precipitation into the formed cracks within concrete may be a basis of the biotechnological approach to enhance the durability and strength of the concrete structures [
20,
21].
Rebar corrosion, drying shrinkage, external loading, plastic shrinkage, thermal stress, or a combination of these factors can lead to the formation of cracks. For instance, shrinkage can cause micro-crack formations and the presence of an external mechanical load enables the cracks proliferation into a network at lower stress level. Chemical degradation of the concrete structures can occur when chemicals and moisture ingress into the concrete through such network of cracks. In addition, high levels of precipitation and moisture can aggravate such issues. Substantial costs, complicated accessibility, and the production of pollution are among the issues linked with manual interventions to repair the cracks in concrete. Currently, a range of cement-based and chemical repair materials are utilized to solve the cracks-related degradation of concrete structures. Environmental and health risks, as well as the material unsuitability, are associated with the use of chemical healing agents. Presently, about 7% of the anthropogenic CO
2 emission worldwide is due to cement production [
22,
23,
24]. Significant structural or durability problems frequently arise as micro-cracks go undetected when they form at the initial or later stages of construction. It has been realized that recurrent maintenance of the concrete structures can prevent this loss, yet it comes with a significant financial toll. Thus, making manual intervention obsolete via a sustainable cost-efficient method of repairing the formed cracks in the concrete structures became necessary.
Over the last decade, the utilization of the autonomous healing techniques in the building structures has drawn much acclaim owing to their capacity in repairing the deterioration within materials of high caliber. Additional economic and environmental benefits can occur when self-healing techniques are implemented to relieve the need for human-assisted maintenance operations. Thus, researchers have focused on the precipitation mechanism of calcium carbonate stimulated by the microbes as a sustainable scheme to stop the crack formations. Bacillus Subtilis is one such bacteria and an autonomously healing microbe that directly acts upon a calcium compound such as calcium lactate to facilitate the cracks filling in concrete via the precipitation of calcium carbonate [
22]. Such precipitation also occurs through a ureolytic bacteria such as Bacillus Sphaericus, causing the decomposition of urea [
25,
26]. The setting of concrete occurs in an environmentally sustainable manner during the process of microbe-induced calcium carbonate precipitation in the cracked concrete structure [
27]. Moreover, there is no health risk associated with the bacteria Bacillus Sphaericus [
28]. The likelihood of reinforcement corrosion is further decreased as oxygen is consumed in the mentioned procedure. The bacteria species type Bacillus is discerned to be an optimal autonomous healing agent with the ability to form spores while being resistant to highly moist and alkaline environments. Thus, the most common bio-agent for the calcite precipitation in concrete is the Bacillus [
29,
30].
5. Self-Healing Mechanisms and Design Strategies
It is well-known that human skin and tissues can repair themselves through the replacement of the damaged areas based on the nutrient uptake. Similarly, the essential products serve as nutrients in the cement-based materials with a self-repair capability, enabling these materials in repairing the damage or deterioration (
Figure 3). Many studies have been performed in recent years to discover new methods for achieving an effective self-repair material alongside the durability of the cement-based materials.
Figure 4 illustrates an overview of such methods.
It is customary to discuss the self-healing mechanisms shown by varieties of materials, including plastics, polymers, paints, coatings, metals, alloys, ceramics, and concretes. These materials possessing their own self-healing traits are useful for the design strategies of the concrete mixes. The primary self-healing processes are the: (i) release of healing agent; (ii) reversibility of the cross-links; and (iii) miscellaneous technologies. Liquid-active self-healing agents, such as monomers, dyes, catalysts and hardeners enclosing the micro-capsules, hollow fibers, or channels, are usually added into the polymer system as reservoirs during their production. In the presence of cracks, these reservoirs are broken, thereby pouring the reactive agents into the cracks via the capillary forces; thereupon, they solidify due to the existence of pre-disposed catalysts, effectively healing the cracks. The cracks propagation is considered the main driving stimuli in the healing mechanism. Conversely, the stress needed from the cracks for relieving remains the main limitation of this automatic mechanism, which happens in the absence of any physical or exterior intervention. Various concepts, such as the embedment of (i) microcapsules, (ii) hollow fibers, and (iii) micro-vascular systems involved in designing the self-healing materials are explained hereunder.
Microencapsulation is a process of attaching micron-sized particles of solids, droplets of liquids, or gases in an inert shell, which in turn isolates and protects them from the external environments [
72,
73]. The end product of the microencapsulation process is termed as microcapsules. Generally, these microcapsules are spherical or irregular in shape with varying sizes in the range of few nanometers to micrometers. Various self-healing polymeric composites have been designed by incorporating different healing agents or catalysts enclosing microcapsules. It has been suggested [
74] that the implementation of microcapsules-embedded healing agents in the polyester network matrix could yield excellent self-healing efficiency, however, not successful enough to produce self-healing components useful for practical purposes. White et al. [
75] first demonstrated the possibility of getting practical self-repairing material, wherein the self-healing capabilities were achieved by embedding encapsulated healing agents into the polymer matrix containing dispersed catalysts.
Figure 5 depicts the self-healing strategy via the microcapsules embedment.
There are many advantages to the microcapsule-based self-healing approach, but the uncertainty about how to achieve a complete and/or multiple healing agent limits their applications [
77]. Multiple healing is only feasible when excess healing agent is available in the matrix after the first healing occurs. Thus, to achieve multiple healing in the composite materials, another type of reservoir that might be able to deliver larger amount of liquid healing agent was developed. However, such an approach has not received wide popularity due to limited success. Various composite systems formulated using the filled glass fibers have limitations. In fact, they could not set free the resin into the cracks because of high viscosity of epoxy resins and inadequate time of curing (
Figure 6).
Therriault et al. [
78] utilized other approaches comparable to the biological vascular systems (such as plants and animals) to surmount the problems related to inadequate delivery of the healing agents into the microcapsules-based components. They relied on central micro-vascular networks for the healing agents’ dispersion into the polymer matrix via the continuous pathways. The synthesis procedure was complicated and extremely complex to accomplish the synthetic agents compatible to these networks for realistic applications. In this approach, organic ink was deposited using three-dimensional (3D) arrays and the interstitial porous spaces among the printed linings were infiltrated by the epoxy resin. Upon curing the polymers, the fugitive ink was eliminated, leaving behind a 3D micro-vascular channel with precise connectivity. Polymer-based materials with micro-vascular networks were made by adding chemical catalysts into the polymers, which were then infiltrated into the organic ink scaffolds. The healing agents were entered within the micro-vascular channels followed by the polymers curing and scaffolds removal. Several studies were carried out to fabricate such polymer-based self-healing materials and to evaluate their self-healing abilities [
79].
Being an irreversible process, the cross-linked polymer-based materials are designed to attain better mechanical performance, including large elastic modulus, high resistance against various solvents, and high fracture strengths. Conversely, the cross-linking in the polymeric system negatively impacts their reproduction capacity. On top, materials with a large number of cross-links are disadvantageous due to their brittleness and tendency to develop micro-cracks. To overcome this limitation, reversible cross-linking in polymer-based materials was introduced, leading to excellent processing capability. Reversible cross-linked polymeric materials show good self-healing traits together with re-fabrication and recyclable characteristics. Nevertheless, such materials are unable to reveal self-healing capacity independently. Some externally applied stimuli, such as chemical, thermal and optical excitations, are required to obtain the reversible effects of the self-repairing capability. In short, such materials display non-autonomic repairing behavior. Various techniques for evaluating the reversible cross-linking in polymeric system are described hereunder [
79].
9. Effect of Parameters on Performance of Cementitious Self-Healing Agents
Autonomously healing concrete can be achieved via the crystalline admixtures. The hydrophilic properties of crystalline admixtures cause the water permeability of the concrete to decrease, while enhancing the mechanical properties. The corrosion of steel is overcome by the alkalinity and the stiffness of the concrete is enhanced due to the incorporation of the crystalline admixtures [
96]. The permeability of the concrete is diminished due to the needle-shaped structures that arise from the crystalline admixture when it reacts with water, acting as a waterproofing layer that fills in the formed cracks. Thus, the capacity to turn concrete into a water barrier makes its use effective in water tanks, dams, and other hydraulic structures. Subsequent sections highlight various studies that combined concrete with crystalline admixtures to achieve improved traits effective for functional applications.
The influence of crystalline admixtures on the autonomously healed concrete has been reported [
97], wherein the concrete specimen was subjected to various exposures and loading-induced pre-cracks. The propagation of the crack was halted through the use of steel fibers. The compressive and splitting tensile strengths were assessed. Standard concrete showed about 14% less CS than concrete with crystalline admixes. The values of CS and TS of the specimens were improved by 13.98% and 35%, respectively, by incorporating calcium sulphate-hydrate and calcite (
Table 5).
The compatibility of crystalline admixtures as a healing agent in the autonomously healing concrete was examined [
98], in which distinct environmental conditions were used for the crystalline admixtures and fiber-reinforced concrete mixes. The healing performance was measured via the optical microscopy and permeability assessment. The crack width was remarkably reduced due to the immersion in water. The self-healing efficacy of the concrete mixed with crystalline admixtures was also examined [
99]. The efficacy of the autonomous healing property was evaluated via the crack closing and permeability assessments, wherein two mixes were prepared one with 275 kg/m
3 of cement and water-to-cement ratio (w/c) of 0.60 and another with 350 kg/m
3 cement and w/c ratio of 0.45. The CS of standard concrete was found to be 15% lower than precast concrete that contained crystalline admixtures. Improved healing was demonstrated at 30 °C when the samples were immersed in water followed by the incorporation of crystalline admixtures.
The cracks formation in the autonomously healing mortar surface via the expansive crystalline additives (CEA) in the concrete were investigated [
100]. The healing process was enhanced by placing the pre-cracked samples in water for 28 days where the surface cracks widths were approximately 100–400 mm. The surface cracks were found to fill due to the incorporation of CEA. The crystalline admixture and calcium sulfo-aluminate content was 1.5% and 10% of the cement weight, respectively. The large surface crack of 400 mm was healed in its entirety by such autonomous healing substances. Moreover, in 28 days, an absolute drop in the healing occurred because of water penetration. It was concluded that a substantial enhancement in crack closing capability can be triggered by the incorporation of calcium sulfo-aluminate and crystalline admixtures. The calcium carbonate precipitation was crucial and was positively affected by the quantity of calcium precipitated from the concrete mix. In addition, conventional concrete was observed to release significantly fewer calcium ions than concrete incorporated with CEA. The autonomous healing performance of concrete mixed with crystalline additives was examined [
96,
101] to determine the nature of the healing rate and its impact under accelerated and natural curing conditions. The natural environment conditions were created by immersing the samples in water and air. Furthermore, the air chambers were among the accelerated environment conditions applied on the undamaged and pre-cracked beams for the flexural strength assessment. The widths of the formed pre-cracks in the samples were 270 mm and 130 mm, which were created both with and without additives.
Generally, the binding of monomers via long chains leads to the formation of the polymers. A polymer net layer that heals the cracks is made after the polymer binds with cement particles once they are incorporated into the concrete. The higher viscosity of the polymers enables them to fill the cracks efficiently. The effects of polymers as the autonomous healing agents in concrete have been intensively studied. For example, pellets filled with healing gel and made with polymers were incorporated into concrete to test their healing efficacy [
102]. The encapsulation method was used to incorporate the polyurethane capsules into the cracks to fill them using the healing agent. The mechanical properties of the concrete sample were assessed via split tensile and three-point bending tests. An increase in the spit tensile and FS were observed in the samples after curing for a week. The super-absorbent polymers and polyurethane were combined and used as healing agents [
54]. The concrete containing acrylate and acrylamide superabsorbent polymer (SAP) was mixed with polyurethane fibers. The CS of the standard concrete was found to be 18% higher than that those made using super-absorbents, thereby demonstrating that the observed improved strength was not an outcome of the polyurethane mixing. When subjected to flexural testing, the crack width in the concrete became 250 mm. The hydration process triggered the generation of calcium carbonate, wherein the swelling of the super-absorbent polymers was catalyzed via the released water inside the formed cracks. Thus, the calcium carbonate healed the cracks by filling them.
A study was conducted to determine the influence of acrylate-end capped polymer precursors for healing the cracks in concrete [
103]. This was induced via the entry of capsules into the concrete containing epoxy acrylate and polyester acrylate-like chemicals. Elongation caused the damage in the polymer walls when subjected to a load, which was due to the mixing of the concrete specimens with the polyester-based substances and propylene glycol. When the specimen was placed in an alkaline environment, such polymers still do not deteriorate because of their strong self-recovery capacity. The polyester-based healing agent strain limit was below 50% and the width of the formed crack was increased above 50%. The restriction of cement particles and PPG binding was observed via the visual test. In short, the potential of acrylate polymers as healing agents is significant and the type of acrylate-capped precursors determines the self-recovery procedure.
Various healing adhesives contained within the microcapsules and mixed with cementitious materials is an upcoming research area [
86]. The autonomous healing ability can be generated by combining the cement paste with the polystyrene-divinylbenzene (stn-DVB), diglycidyl ether of biphenyl and epoxy resin (E), and other similar types of adhesive materials. Parameters involving strength can substantially be enhanced via this mix.
Table 6 shows that the FS and CS of normal concrete were 1.3 times and 1.9 times weaker, respectively, than that of the autonomously healing concrete. The efficacy of the superabsorbent polymers as self-recovery agents was examined [
104] and ascertained via a water flow test. When exposed to water, the superabsorbent polymer showed an expansive trait and functioned as a cross-linked polymer. The widths of large cracks were significantly reduced through the self-healing procedure. The FS of the control concrete was 8% weaker compared to the self-healing concrete (
Table 6). In addition, the autonomous healing capabilities of the cementitious composite materials were investigated [
105], wherein the reaction rate was found to improve via the accelerator microencapsulating triethyl borane and methyl methacrylate monomers. A comprehensive mixing of the solution containing the microcapsules and methyl methacrylate occurred within the concrete. Three kinds of carbon microfiber-reinforced mortars were designed, and their mechanical performance was assessed. The first served as the control sample, the second was the sulfonated polystyrene modified mortars, and the third one was the autonomously healing mortar. The polymers-based self-healing cementitious materials designed using the encapsulation method showed significant improvement (
Table 6) in their strength properties (CS, FS and TS). The strength of the healed crack in the concrete was examined after incorporating the flexible polymers as healing agents [
106], wherein the encapsulation method enabled the incorporation of polymers into the concrete (
Table 6). The TS of the autonomously healing concrete was evaluated using the split tensile tests, wherein the specimen was cured for 3 days at 20 °C. The FS of the concrete was found to improve by 35% after the healing of the crack by the flexible polymers.
In a study, the concrete specimens were pre-cracked with the cracks’ widths in the range of 100 to 400 μm with the incorporation of SAP to determine the healing efficiency [
107]. Specimens made with SAP showed 85% lower water flow than the normal concrete. In addition, a substantial reduction in the water flow was experienced by other mortars compared to the standard concrete. With regard to the cracks healing performance, the SAP was better than poly-acrylate. The results in
Table 7 show more effective healing of the formed cracks in the concrete structures when the SAP particles were bigger. Various doses of the acrylic polymers and styrene-butadiene rubbers were mixed into the autonomously healing concrete [
49]. The hydration process and healing time were evaluated via the thermogravimetric and UPV measurements. After nearly 3 weeks of curing, the rate of cracks healing was reduced. This was mainly due to the presence of styrene rubber in the concrete, wherein the cement particles were bonded with the polymer, indicating that the polymer dosage determined the healing time. Furthermore, the incorporation of styrene-butadiene rubber caused a reduction in the hydration process, while the healing time was prolonged by the polymer content.
Most common kinds of fibers are the man-made and natural ones. The former is known as synthetic fibers, industrially fabricated, and include polyvinyl alcohol, polypropylene, vinyl alcohol, polyester, and polyethylene. Drying shrinkage and plastic induced cracks in concretes are regulated and prevented via the incorporation of synthetic fibers, which also enhance the toughness and TS of the concrete. Water penetration through pores is safeguarded as fibers enable to decrease the permeability of the concrete mix. Enhancements in the mechanical properties of the concrete occur because of the fiber’s incorporation. The cracks filling efficacy of various types of fibers as healing agents within concrete has widely been explored. The ability of the fiber-reinforced cementitious materials to seal the formed cracks was examined in detail [
108]. Steel fibers, wollastonite, antifoaming agents, silica fume cement, and super-plasticizer were among the materials used in this study. When immersed in water, numerous cracks formed in the close proximity within the concrete were more effectively healed by the proposed materials. Surface cracks were examined via the microscopy and air permeability measurement. The autonomous healing procedure commenced with the immersion in water of the pre-cracked specimens. A decrease in the air permeability was observed while the cracks were filled by the precipitated crystalline particles emerged from the fiber-reinforced cementitious materials. The results indicated that the un-cracked samples had reduced air permeability compared to the cracked samples.
Multiple synthetic fibers were utilized to ascertain the healing performance of the fiber-reinforced cementitious concrete (FRCC) [
109]. Several distinct fibers such as polypropylene, ethylene-vinyl alcohol, poly-vinyl alcohol, and polyacetal were used. The primary materials consisted of polycarboxylic acid (super-plasticizer), silica fume, cement, and sand. The particles’ diameters for cement-polypropylene (C-PP) and polypropylene (PP), polyvinyl alcohol (PVA)-I and II, ethylene vinyl alcohol (EVOH), and polyacetal (POM) were 18 mm, 11 mm, 37 mm, 14 mm, 15 mm, and 48 mm, respectively. The microscopic and air permeability of the samples were measured. The results revealed that the precipitates near the fibers led to a reduction in the water permeability. With PVA incorporation, a higher rate of calcium carbonate precipitation was observed in the high polarity of the fiber composites for cracks of width up to 0.3 mm. A reduction in the water permeability was found in the PVA II-included samples, while healing occurred within 72 h for the PVA-included specimen.
Under cryogenic temperatures, the autonomous healing capacity of the fiber-reinforced concrete examined [
110]. The samples were first cured in water for 28 days at 20 °C and then cured again under air exposure for 3 days at room temperature. A week was needed to seal the cracks of widths in the range of 10 and 50 μm for the pre-cracked samples cured for 28 days. The sealing of the cracks of widths up to 50 μm was achieved when the samples were subjected to 24 h of cryogenic temperatures. The FS properties of the specimen were affected by the fibers’ lengths, wherein shorter fibers showed weaker FS. Three days of air cured specimen under cryogenic temperatures showed an improved FS wherein the pre-cracked samples were made with steel fibers with an aspect ratio of 97.5. The pre-cracked samples containing steel fiber (with an aspect ratio of 100) revealed weakest energy absorption capability. Some studies were performed to determine the effects of cellulose fibers mixing into concrete on the water permeability and autonomous healing efficacy [
14]. The autonomous healing rate of the specimen was estimated via the water penetrability measurement and other tests. Concrete specimen prepared with 0.5% of cellulose fibers showed a decrease in the CS value. Contrastingly, the FS of the standard concrete was found to be 7.84% lower than that of the specimens made with fibers.
The effects of microfibers and SAP inclusion in concrete on the autonomous healing mechanisms were examined [
48], wherein the cracks’ sealing ability was improved via the incorporation of SAP. Upon exposure to a wet environment, SAP was swelled. When subjected to the wet and dry cycles, a crack of size 138 μm was healed when 1% of SAP was included in the specimen. In addition, the SAP inclusion into the concrete was responsible for the cracks’ healing and water permeability reduction. The feasibility of enhancing the autonomous healing capacity of cracks through the incorporation of diverse bacteria and fibers in the concrete were studied [
111]. A decrease in the concentration and growth of the bacteria was observed, while the cracks with a width up to 500 μm were successfully sealed. Following one week of curing, the pre-cracked control samples without bacteria or fiber demonstrated about 30% healing, which was further improved by 2% after 28 days of curing. Following 28 days of curing, the control sample demonstrated higher crack repair ratio than those designed with PP1 (polypropylene) fiber. After 28 days of curing, a crack healing ratio of 31% was achieved in the sample designed with PP2 fiber. In the first week of curing, an improvement in the crack healing ratio of 36% was observed. The incorporation of only PP1 and PP2 fibers into the mortar produced weaker effects than the mortar prepared with polyvinyl alcohol (PVA) fiber. The crack healing ratio of mortars containing PVA fibers after curing for 7 and 28 days was enhanced from 44% to 50%, respectively. Enhanced healing rates were observed when microscopic organisms such as bacteria were mixed in the mortar. Samples containing only fiber displayed lower healing rates than those made with fiber and bacteria. Concrete with these fiber and bacteria mixes showed reduced water absorption and improved FS.
Many investigations have been conducted to determine the effects of fibers, polymers, and diverse crystalline materials incorporation into concrete on the autonomously healing efficiency of cracks. The mechanical properties of autonomously healing concrete were measured using the split tensile, water tightness, flexural, permeability test, and CS tests. Elemental compositions and microstructures were analyzed using EDS and SEM measurements. Diminished water permeability was achieved via the surface layer cracks in the concrete when sealed after the reactions. Despite enough air exposure, such samples could seal the cracks by absorbing the moisture from the environment because of the hydrophilic properties of the admixtures. Furthermore, an enhanced crack sealing capacity was developed when the cracks were exposed to water [
97]. Upon water exposure, such hydrophilic products melted and re-crystallized within the formed cracks due to the presence of crystalline admixtures. The internal cracks of the sample were plugged-in as calcium carbonate was produced and the supply of Ca
2+ was facilitated by the incorporation of the expansive additives and crystalline admixtures into the concrete. Exposure to a humid environment could also enhance the precipitation of calcium because the additives mixed into the concrete had higher pH [
100]. The incorporation of multiple polymer precursors into the concrete could facilitate the sealing of the generated larger and wider cracks in the sample. The mechanical properties of the concrete were enhanced due to the superior binding of mortar and polymers facilitated by the elastic properties of polyurethane [
106].
The effects of microcapsules (containing triethylborane and methyl methacrylate monomer) insertion as healing agents into the concrete and their ability to heal cracks were studied [
20]. After 28 days of curing, the value of CS of the concrete was increased up to 45.8%. As a result of swelling, the polymer particles become larger, leading to a reduction in the micro-cracks within the concrete due the presence of SAP. A high pH environment in the concrete caused the reduced swelling of the SAP [
104]. The cellulose fibers-assisted autonomous healing mechanism on cracks in the concrete was examined [
112]. A reduction in the CS value of the concrete occurred due to the use of cellulose fibers. The mix ratio, cracked surface, roughness, and interaction of the fibers with the concrete were among the influential factors that were found to be responsible for effective healing [
109]. Autonomous healing capability of cracks were improved in the ultra-high performance hybrid fiber-reinforced (UHFR) cementitious concrete [
108]. The incorporation of bacteria and polypropylene into concrete was found to be less effective than PVA-based concrete in terms of healing efficacy [
111]. The sealing of crack width was enhanced through the incorporation of micro-fibers and SPA into the concrete [
48]. The autonomous healing capability and flexural performance of the concrete were also enhanced upon the incorporation of steel fibers into the concrete when subjected cryogenic temperatures [
110].
11. Self-Healing Cementitious Materials Obtained Using Encapsulation Technology
In optimal circumstances in a natural environment, the availability of nucleation sites, solution pH, calcium ions concentration, and dissolved inorganic carbon concentration can appreciably influence the precipitation of calcium carbonate in the concrete [
140]. The first of these aspects is delivered by the bacterial cell while the other three are linked to the concrete matrix. Hydrolysis of urea by bacterial metabolism or the conversion of calcium compounds such as Ca-lactate are the means through which bacterial precipitation can be achieved. The first method involves the hydrolysis of urea into carbonate and ammonium that triggers the calcium carbonate precipitation. The enzyme urease, which is produced by the Bacillus Sphaericus bacteria, functions as a catalyst during the hydrolysis. The generated carbonate reacts with the calcium ions extracted from the calcium nitrate or other calcium sources by the negatively charged bacterial cell, resulting in the calcium carbonate precipitation. The second method involves the production of carbon dioxide and calcium carbonate after calcium lactate reacts with the oxygen that enters into the concrete via the crack formations on the surface [
140]. The produced additional calcium carbonate can be used for autonomous healing via the reaction of carbon dioxide with any portlandite particles in the close proximity. Non-hydrated calcium hydroxide particles can still be present in the freshly prepared concrete, enabling this method is more effective in such context.
It has been established that the efficacy of autonomous healing in concrete can be achieved using various methods, wherein the long lifespan of the bacteria, the depth or widths of the cracks to be repaired, moisture content, and the age of the concrete are the main governing factors. Improvement of the autonomously healing capacity in concrete was performed through the introduction of bacteria spores of different kinds to deduce their compatibility [
141]. Bacillus pseudofirmus, Bacillus halodurans, and Bacillus cohnii were mixed in the cement stone-chips to improve its autonomous healing capacity. The tensile and CS of the cement stone-chips were assessed after they were cured in a peptone-based medium and yeast extract, wherein the bacteria-incorporated specimen revealed a significant improvement in strength properties compared to the control sample. Following 12 days of incubation, calcium carbonate crystals were precipitated as shown by the SEM image analysis. Nonetheless, the germination occurred after the specimens were cured in the medium enriched of organic carbon sources that were externally sourced.
More recently, the potential impacts of the mineral precursor compounds, peptone, and yeast extract on the autonomous healing capacity in concrete were examined [
8]. The highly alkaline environment of the concrete is the principal difficulty that the bacteria must overcome to survive and, thereby, commence autonomous healing. The direct additions of different kinds to achieve bacteria-induced carbonate precipitation in the concrete for autonomous healing of cracks demonstrated their enormous potential [
12]. Bacillus cohnii and Bacillus pseudofirmus were found to species of spores that form alkaliphilic bacteria. The mineral precursor compound was selected by assessing the calcium lactate and calcium acetate level. A marginal improvement in the strength occurred via the calcium lactate inclusion, while the calcium acetate produced high strength. Specimen cured for 28 days did not shown any precipitates on them, while the sample cured for 7 days revealed the deposition of calcium carbonate crystals in the size range of 20–80 mm. Concrete with the decreasing pore size in highly alkaline environments showed a reduction in the number of suitable bacteria spores [
85]. The deterioration of the concrete matrix was due to nitric acid generation from increased metabolic activity or reinforcement of the corrosion via the excess ammonia production that occurred in the urease-based method, demonstrating the superiority of the aforementioned technique for autonomous healing of cracks.
The direct incorporation of the substrate and alkali resistant spores in the concrete enabled the formation of bacteria which was further influenced by the cracks’ ages and widths as well as the curing conditions. Concrete containing various ages (90, 60, 28, 14, and 7 days) of cracks in the size range of 0.1 and 0.5 mm was subjected to the wet-dry cycles at 25 °C, water curing, and wet curing conditions to determine their effects on the autonomous healing process. The repair rates of such diverse cracks were assessed to ascertain the healing performance. The results revealed that roughly 85% of the generated cracks of widths 0.1–0.3 mm were filled and repaired entirely when subjected to the water curing condition. While the wet-dry cycle condition demonstrated a slower rate of healing; however, the condition of water curing was found to produce the best healing results. Older cracks were not healed as effectively as new or young cracks. The shorter transport distance of the mineral emerged from the reduction of the concrete porosity could partially explain this observation, while the lack of a protective shell for the bacteria might have caused a low survival rate [
85].
The binding of the original concrete matrix with mineral precipitates is a key area to investigate in addition to their autonomous healing efficacy. The binding of the precipitated calcium carbonate with the parent concrete network, as well the nanomechanical properties of the former, were determined using a non-indentation technique, wherein a non-ureolytic bacteria was added within the mixing water that revealed the mechanical performance of autonomously healing concrete [
94]. The creation of cracks led to the addition of air pockets for bacteria survival and a decrease in the alkalinity of the cement paste. However, the addition of air entraining agents, silica fume, and basalt fibers sustained the integrity of the specimens, thus, demonstrating an outperforming nature of this technique. Given that the durability and mechanical properties of concrete can be impacted by air voids in the tropics, this method may not be as suitable as in temperate climates where the dangers of thawing and freezing are reduced by such air voids. Nonetheless, in the case of fire, the release of vapor pressure is enabled by these voids, thereby enhancing the concrete’s resistance to fire. The mineral precursor compound was filled by calcium glutamate and calcium lactate, wherein calcium lactate produced a less substantial conversion of calcium ion to carbonate than calcium glutamate. The latter (calcium lactate) formed granular-shaped crystals, which were totally absent in the former. Nevertheless, while thicker and denser carbonate from the glutamate was found in the transition zone, the biding of the carbonates made from the lactate and glutamate were found to vary insignificantly. Calcium glutamate specimens were observed to demonstrate a greater capacity in restoring the FS. Bacterial metabolism triggered the mineral precipitation that filled a part of the cracks of width between 0.1 mm and 0.4 mm. The efficacy of the external healing was not surpassed by the samples incorporated with bacterial spores, yet the latter did exceed the healing performance of the control specimen. The limited amount of nutrients was responsible for this action, thereby impacting the performance of the bacteria, despite the voids aiding the bacteria.
The production costs of the cultures, such as the axenic spores of bacteria, are substantial, which is the major limitation of this approach, despite its promising results regarding the effective self-healing. The microbial community named cyclic enriched ureolytic powder (CERUP) was aimed to address this issue by offering a cheaper bioagent alternative [
142]. Reduced production costs were achieved by making the specimen in non-sterile conditions while using a sub-stream of a vegetable plant as the microbial source. During a period of 4 weeks, the capacity to plug-in the cracks and autonomous healing was assessed via the incorporation of non-autoclaved and autoclaved CERUP. The width of the largest crack that was repaired by the autoclaved CERUP was below 0.37 mm, while the width of the largest crack healed by the non-autoclaved CERUP was 0.45 mm. A more accurate representation of the autonomous healing capacity of the non-sterile agent is essential, wherein additional evaluations regarding the durability and strength are necessary to ascertain its proficiencies besides significantly lower costs and deficiencies.
Autonomous healing that occurs during the entire lifespan of a concrete structure indicates the substantial effectiveness of the self-healing technique in filling the cracks indefinitely. Thus, a critical aspect is the survivability of the bacteria wherein multiple obstacles hindering the survivability of bacteria can appear upon the direct addition of bio-agents to the concrete. Relatively young specimens were found to be the only kind that achieved efficient autonomous healing, as the unprotected spores had a lifespan of two months [
143]. The hydration of cement, mixing of concrete and alkalinity of the cement matrix were the main factors that contributed to the lifespan shortening. Residing in a highly alkaline environment for a prolonged period of time could significantly reduce the activity of spores. Additionally, the impact of aggregates, along with the mixing force, could lead to spores being damaged in the mixing stage. Despite the average size of bacteria cells being above 0.5 mm, a reduction in the pore size of the matrix and porosity was triggered by the hydration of cement up to 0.5 mm [
25]. It was concluded that, at an advanced stage, a concrete structure can experience a significant or even absolute decrease in the germination of cells due to the shrinkage of pores. The bacteria-induced carbonate precipitation and concrete properties were not impacted when the bacteria were encapsulated, thereby working around the mentioned limitation. The developed techniques to safeguard the bacterial strains include the hydrogels encapsulation, diatomaceous earth, melamine-based microcapsules, polyurethane and silica gel in glass tubes, and expanded clay aggregate encapsulation [
139,
144].
Bacillus Sphaericus spores were encapsulated via the melamine-based microcapsules [
25]. The nutrients, such as urea and yeast extract, were mixed along with the mineral precursor calcium nitrate in the concrete to obtain efficient autonomous healing of cracks. The ratio of the initial and healed crack area was used to evaluate the healing efficacy of the bacteria. The healing ratio could not surpass 50% in the specimens with no spores, while those with the spores’ encapsulation achieved a proportion in the range of 48 to 80%. When water functioned as a medium during the wet and dry cycle of the samples, the highest decrease in crack area occurred. It was argued that the manual intervention may be the main drawback under typical circumstances when performing the wet cycle, as the procedure takes around 16 h. A crack of maximum width of 1000 µm was repaired using this procedure. While a capsule dosage of 5% led to less deviation, the most effective dosage for the crack healing and restoration of water permeability, was 3%. A dosage of 5% was not considered superior, as a greater decrease in the concrete strength was observed for said dosage compared to the former.
Little to no manual intervention and inner moistures were required for the bacterial growth and activities when delivered in the inventive hydrogels encapsulation technique [
10]. Furthermore, the bacteria were safeguarded in the protective shell of the capsule. When the hydrogels contained both bio-reagents and encapsulated bacteria, healing efficacy in the range of 40% to 90% was attained. Additionally, the highest reduction of 68% water permeability occurred. The retention ability of hydrogels and water uptake enabled the hydrogels-encapsulated bacteria to perform the healing effectively. At 20 °C, in an air composition with 60% relative humidity (RH), pure hydrogels, after a day, and half a day, retained 30% and 70% of water, respectively [
10]. This study indicated that the bacterial activity can be encouraged in the tropical climates by the effective retention and absorption of water that hydrogels offer, given that such climates experience high levels of precipitation and humidity. However, the non-ionic or ionic nature of the hydrogels played a significant role [
10]. While retention and uptake ability of water was not impacted by the ions in the moisture for non-ionic hydrogels, for ionic hydrogels, the uptake ability was influenced by the chemicals in the air due to their sensitivity on pH. The curing condition of dry and wet cycles lasting for 8 h and 16 h, respectively was found to be the most effective regarding the healing performance upon the use of melamine-based microcapsules [
25]. A substantial decrease in the contact time with water occurred when the hydrogels were used. In short, the concrete containing hydrogels possess many benefits in terms of replacing the need to manually added water, given that moisture from the air can be absorbed by the hydrogels.
The performance of the tailored sodium alginate-based hydrogels as a bacteria spore carrier was assessed [
144]. The consumption of oxygen at a damaged site in the concrete was used to evaluate the suitable bacteria spores following hydrogels encapsulation. While the majority of spores maintained their encapsulated form, the concrete mixing stage led to a leakage of around 1% of the spores of the altered hydrogels. Due to the incorporation of 0.5% and 1% of the hydrogels, the values of CS and TS were reduced by 30% and 23.4%, respectively, without appreciably affecting the workability of the concrete. The addition of hydrogels might have led to the formation of macro-voids and, thus, negatively influenced the strength properties of the concrete. The observed lowering in the strength and creation of voids in the concrete was the outcome of SAP addition. Contrastingly, it also enabled the development of the strength and provided the moisture for internal healing. In addition, various factors, including the age of the concrete, dosage of SAP, and water to cement ratio (w/c) determined the final outcome [
145]. A decrease in the strength and lower strength development upon the incorporation of SAP were most likely due to the gel-space ratio changes when the w to c ratio in the concrete was above 0.45. It was acknowledged that the specimens added with SAP could experience a diminished strength when the w/c ratio became high, around 0.5 [
144].
In the past, the precursor compound for the mineral precipitate and calcium lactate together with the porous expanded clay aggregates was used in the concrete to immobilize the bacteria spores [
145]. Exposure to air stimulated the bacterial action, thereby inducing the calcium carbonate precipitation because of the fracturing of the soft and lightweight clay aggregates within the concrete network. A crack of maximum width 0.46 mm was filled when the specimen was immersed inside tap water for 14 days. Additionally, no signs of decreased viability of the bacteria were observed, even after 6 months. Bacterial precipitation activity was encouraged by the internal source of moisture provided by the clay aggregates that were widely used earlier in the lightweight concretes. Nonetheless, the pore structures, expanded clay aggregate spacing, and water in aggregate were the major factors that affected the autonomous crack healing efficacy of the clay aggregates [
22]. The decrease in the strength was the main drawback to using clay aggregates rather than the standard granite aggregates. The CS of concrete depended on the toughness of the aggregates, given that the vast majority of the concrete was composed of the aggregates that are used in standard concrete. These aggregates were stronger than the concrete matrix wherein cracks eventually appeared because such strong aggregates can resist the crack formations in the standard concrete. Furthermore, the aggregates might be less tough than the matrix, especially for the clay aggregates, making it highly probable that the aggregates could break via the crack formation. Thus, the cracks were attracted to the weaker plane that generated the soft aggregates. The lightweight clay aggregates incorporated concrete after 28 days of curing revealed a decrease in the strength up to 50%, making it unsuitable for structural uses [
139].
Currently, the high cost of the bio-agents is the main limitation for a broad array of applications in autonomous healing. However, increasing the lifespan and resistance of autonomous healing agents for effective performance in harsh environments such that they could endure multiple cycles of loading that frequently affect the concrete structure is one way to make such agents commercially feasible. Another strategy is to reduce the production costs of bio-agents. During the lifespan of a concrete structure, the persistent deterioration necessitates multiple maintenance operations, demanding high expenditure. To explain this aspect, a life-cycle cost model was formulated by van Breugel [
146], wherein it was shown that the cost incurred to build a structure may even be surpassed by the cost to repair it. In contrast, while the initial construction cost may increase due to the use of autonomously healing concrete, the total cost of the structure throughout its lifespan decreases considerably, as damages are autonomously managed without any extra cost.
One of the critical components of the autonomous healing is related to the capsules design. Identifying and producing the appropriate capsules that can impact the concrete properties is an active area of research. In fact, a very limited number of studies exist on the bio-based autonomous healing for the fatigue performance of a concrete structure. The capsules’ releasing behavior determines the fatigue performance of the bio-based autonomously healing concretes. The smart or controlled release from the capsules can enable the autonomous healing of cracks when subjected to multiple loading cycles. In addition, a reduced alkalinity in the concrete matrix can lead to the corrosion of the reinforcement bars. A study was conducted to heal such deterioration via the smart release of the microcapsules [
147]. Nonetheless, implementation of the smart release of capsules for the bio-based autonomous healing is a method that is essential for further replication and study to validate its potency. The incorporation of capsules provokes the formation of the weak spots in the mortar, wherein such spots can be diminished in size by the nanocapsules. Presently, in some studies, only the encapsulation of a chemical healing agent has been carried out, wherein the sonification method enabled the creation of urea formaldehyde capsules of dimension 77 nm (thick) and 220 nm (diameter) [
148]. Briefly, various biological healing agents can be effectively integrated using this approach by altering the capsule material to suit the bio-agents. Furthermore, the formations of cracks in the matrix can lead to the nanoparticle agglomeration spots, wherein the nanoparticle debris must be assessed to guarantee the absence of agglomeration.
Under appropriate curing conditions of the concrete, prolonged periods in the range of 14 and 21 days were needed for the biological agents to activate the self-healing of the generated racks. Bacteria in the alkaline concrete environment produced a lower precipitation rate, justifying the need of longer durations. Higher precipitation rates and increased bacteria lifespan was achieved via the creation of genetically modified bacteria cultures. In was concluded that prolonged periods for curing are necessary for the activation of the biological agents in the concrete, thus, achieving quicker healing of wider cracks. Through the biological action, faster and more effective autonomous healing can be attained by placing an emphasis on the vital aspects of controlling the width of the cracks [
128]. Following autonomous healing, highly effective restoration of the original properties can be obtained via the incorporation of the hybrid fibers to regulate the widths of the cracks [
149,
150]. Via the amalgamation of polymer fibers and steel, diverse healing agents and products can be placed close to the faces of the cracks in the concrete for hindering the widths of the cracks from further expansion [
149].
Further investigations in a real-life construction site are required to assess the autonomous healing performance more accurately. Careful analyses of the social and environmental benefits, costs lowering strategies, and lifespan improvement of the concrete structures should be performed in the future studies. The impact of climate change acclimatization of the bio-based autonomously healing concrete was investigated [
151]. The life cycle of the bio-based autonomous healing systems was enhanced by the implementation of the life cycle tests and other methods for sustainability evaluations [
152]. It was acknowledged that the autonomous healing composites with more sustainable traits can be generated by mixing the carbon sequestering materials with biological healing agents [
153]. It was asserted that the bio-based autonomous healing performance in actual buildings can be evaluated more accurately via the establishment of assessment standards and other stipulations. The application of the bio-based autonomous healing concrete and other such materials is a distinct possibility in the near future, as much academic attention has been placed in the field over the last decade. In essence, widespread industrial use can only occur once the present technological challenges are overcome.
12. Sustainability of Self-Healing Concrete
Certainly, concrete is the foremost material used in the construction industry worldwide. The formation of cracks in the concrete structure due to the entry of harmful substances through such cracks and subsequent decrease in the durability performance of the concrete must be inhibited to enhance the service life span. Deterioration of the concrete structures is more likely to happen with the ingress of corrosive substances through such cracks [
154,
155]. The incorporation of the autonomous healing materials into the concrete mix can counteract such issues. The widths of the cracks can be diminished and the concrete durability can be improved via the addition of smart autonomous healing materials into the concrete. The restoration of the strength of the cracked structures is a characteristic of the cementitious materials that form a part of the autonomous healing concrete [
97]. Diverse approaches, such as microencapsulation, regular encapsulation, vascular, and direct methods have been developed to incorporate various healing agents into the concrete [
98]. In addition, different artificial techniques have been adopted to enhance the efficacy of the autonomous healing in concrete. Improved outcomes were observed when water immersion conditions were combined with the incorporation of crystalline admixtures into the concrete. The FS value of the concrete was enhanced due to the incorporation of fibers and polymers with the greater proportions.
Generally, OPC-based concrete releases high amount of CO
2 during the lime de-carbonation and calcination reaction of the cement clinker. The CO
2 emission can appreciably be lowered through the use of nanomaterial-based self-repairing technologies. Presently, advancement of the world without concrete cannot be imagined [
156]. Historically, magnificent structures such as the Sydney Opera House, Chrysler Building, Taj Mahal, etc., to cite a few, were not possible to erect without concrete. In addition, the skyscrapers in the metropolis worldwide could not reach such an outstanding height without the existence of concrete. Overall, the concrete’s durability and strength performance played a significant role in the erecting of numerous signposts and historical structures over the centuries in the absence of modern engineering knowledge and technologies. Undoubtedly, concrete is now an integrated component of the modern civilization. To meet the ever-increasing demand of sustainable and environmentally friendly construction materials, the production of functional, smart, and novel concrete became a new norm in the civil engineering sector, requiring huge investments. In fact, every year, an enormous amount of raw materials are discarded as wastes because of ineffective concrete manufacturing processes. Furthermore, the worldwide manufacturing of the main concrete binder called OPC is responsible for the emission of more than 5% of the entire greenhouse gases yearly. It has become a serious concern regarding environmental pollution and global warming. Modern civilization must aim to perform future construction using green, sustainable materials together with environmentally friendly technologies [
157]. Thus, it is important to build more unconventional, efficient, clean, sustainable, safe, reliable, and strong functional construction materials as substitute to the OPC-based concrete. To mitigate the environmental problems, nanomaterials-based smart concretes and self-healing technologies became an emergent area with several implications.
An increased service life span of the concrete structures can lower the demand of new structural materials. Thus, the uses of the resource raw materials be can radically lowered and the pollution level of CO
2 emission can be diminished together with the low consumption of energy. Repeated research has revealed that a substantial cost is involved in maintaining and repairing poor construction quality as well as low durability performance of the concrete in the construction sectors. In the US, the cost for reconstructing bridges is estimated to be in the range of USD 20 to 200 billion [
158], wherein the average maintenance costs for these bridges per year is about USD 5.2 billion. Detailed analyses of the life cycle clearly indicated that the indirect expenditure due to traffic jam and related low output is 10 times higher than the direct one spent for their maintenance and repairs [
159]. The Netherlands spent about one-third of their annual budget on the inspection, monitoring, maintenance, up-gradation, and repair of the outsized civil engineering construction works. The repairing and maintenance cost of the construction in the United Kingdom is more than 45% of their annual spending [
160,
161]. The department for environment, food, and rural affairs (DEFRA) reports showed that nearly half of CO
2 emissions in the UK were due to poor-quality building structures. For instance, the manufacturing of 1 tons of OPC is responsible for the emission of 1 tons of CO
2 because of the calcination and fuel combustion process [
162,
163].
Worldwide, approximately 2.35 × 109 tons of cement is manufactured per year, which results in major emissions of CO2, nearly 5–7% of the total CO2 emissions in the world. The rapid expansion of the economy of China and India caused the largest consumption of cement, which is anticipated to amplify if the present technologies that are used to manufacture cement remains unaltered. Enhancement of the durability and reduction of the repair costs of the building infrastructures can certainly lessen the negative impact of cement and related pollution due to greenhouse gases emission, thus, improving our activities and stabilizing the biosphere. In this view, it is necessary to perform more studies and look for promising solutions for the future sustainable development. In-depth understanding of the negative impact of the construction materials on our environment is expected to benefit several stakeholders concerned with the construction industries, improving the quality of social life and service life span of the concrete structures, thereby meeting the sustainable goals. Traditionally, concrete structures have been designed to fulfill the desired specifications in the beginning of its service life. Then, the durability of such structures has been monitored via the maintenance plans. Lately, material scientists have adopted some new strategies by considering the adaptability or self-healing properties of the materials over the service life span of the construction materials. This inspiration of using new functional and smart materials in the construction industries has appeared from nature via the bio-mimicry of diverse living organisms. Motivated by the feasibility of achieving self-healing concrete structures, some of the pioneering research has focused on both natural capacity of hydrates to heal cracks over a certain period, as well as artificial ways to repair cracks using adhesive reservoirs embedment into the concrete network matrix.