Next Article in Journal
Aluminium Matrix Composites Reinforced with AlCrFeMnNi HEA Particulates: Microstructure, Mechanical and Corrosion Properties
Next Article in Special Issue
Fabrication and Oxidation Resistance of a Novel MoSi2-ZrB2-Based Coating on Mo-Based Alloy
Previous Article in Journal
Early-Age Cracking Behavior of Concrete Slabs with GFRP Reinforcement
Previous Article in Special Issue
Application of Constitutive Models and Machine Learning Models to Predict the Elevated Temperature Flow Behavior of TiAl Alloy
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 16
Issue 15
10.3390/ma16155490
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

The Effects of MgO and Al2O3 Content in Sinter on the Softening–Melting Properties of Mixed Ferrous Burden

by
Zhexi Li
,
Tingle Li
*,
Changyu Sun
,
Songtao Yang
and
Qi Wang
*
School of Materials and Metallurgy, University of Science and Technology, Anshan 114051, China
*
Authors to whom correspondence should be addressed.
Materials 2023, 16(15), 5490; https://doi.org/10.3390/ma16155490
Submission received: 30 June 2023 / Revised: 31 July 2023 / Accepted: 4 August 2023 / Published: 6 August 2023
(This article belongs to the Special Issue Phase and Structure Analysis of Alloys and Metal Matrix Composites)
Browse Figures
Versions Notes

Abstract

:
The softening–melting properties of mixed ferrous burden made from high-basicity sinter with increased MgO and Al2O3 content and acid pellets was investigated for optimization. The influences of MgO and Al2O3 are discussed with the aid of phase analysis. The results showed that, with decreasing MgO mass%/Al2O3 mass% in mixed burden, all the softening–melting characteristic temperatures decreased, which can be attributed to the low melting temperature and viscosity of the slag caused by MgO and Al2O3. The permeability of the melting zone deteriorated again when MgO mass%/Al2O3 mass% decreased to a certain content. The softening interval widened slightly at first and then narrowed, while the melting interval first increased slightly and then increased greatly later. It can be deduced that the softening properties were improved, but the melting properties were worsened. Under comprehensive consideration of its softening–melting properties, permeability, iron ore reduction and the thermal state of the blast furnace hearth, the optimal softening–melting properties of a mixed ferrous burden with MgO mass%/Al2O3 mass% of 0.82 is optimal.

1. Introduction

The blast furnace (BF)–oxygen steelmaking route which uses iron ores as the raw ferrous materials is the primary source for worldwide steel production. The BF is the biggest counter-current reactor involving downward iron ores (sinter, pellets and lump ore) and upward gas flow for producing pig iron [1]. Normally, the ferrous burden and coke are charged into the BF separately, giving the furnace stack a layered structure. The ore layer undergoes a heating and reduction process in the BF. On reaching the lower part of the BF at much higher temperatures, they soften and melt, forming the region known as the cohesive zone. The softening and melting (SM) properties of ferrous burden have a signification effect on the shape, position and thickness of the cohesive zone [2,3], determining the gas utilization and heat transfer, which vitally influences BF operational performance and productivity [4].
A sinter with high basicity has good reduction and SM properties while its Fe content is low. A high Fe content and a low gangue content are favorable for acid pellets. However, it has inferior reduction and SM properties due to low-melting fayalitic slag [5]. The pelletizing process is much cleaner than the sintering process, while the former has low yields [6]. Sinter and pellets have become the popular ferrous materials for BF ironmaking [7]. It is a feasible direction to use mixed ferrous burden made with high-basicity sinter and acid pellets for green metallurgy due to their complementary advantages [8].
Recently, because of the increasing scarcity of good-quality iron ores, high Al2O3 iron ores of low grade and low cost have been utilized to make high-basicity sinter, pursuing economic benefit [9,10]. Increased Al2O3 content in BF ferrous burden leads to high viscosity [11,12,13,14] and bad desulfurization ability [15] of the slag and low permeability [16] in the cohesive zone. A popular countermeasure is adding MgO into sinter [17]. So, both the MgO and Al2O3 content in sinter increase and the MgO mass%/Al2O3 mass% changes, which are bound to influence the SM properties of high-basicity sinter and its mixed ferrous burden with acid pellets [18], consequently attracting our attention.
The effect of MgO or Al2O3 content on the SM properties of sinter and pellets has been reported in many studies in the literature. The works of Guo et al. [19,20] demonstrated that the softening temperatures and the maximum pressure drop increased, and the melting temperature interval became wide with the increasing MgO content in sinter, because the MgO existed as a wüstite solid solution when sinter softened, and then on melting it brought a high-melting point slag. Li et al. [21] conducted a study of the effect of MgO content on the SM performance of high-gangue sinter and partially supported Guo’s viewpoint. They believed that MgO content did not always improve the SM performance of sinter but it had a certain content limit. Wang et al. [22] proposed that high Al2O3 content sinter was associated with a thicker melting–dripping zone, leading to the deterioration of sinter bed permeability. Our previous work [17] on the effects of MgO and Al2O3 on the SM properties of high-basicity sinter found that MgO and Al2O3 led to increased and decreased SM characteristic temperatures, respectively. The influence of MgO on SM properties was insignificant compared with Al2O3, which was attributed to the fact that MgO existed in wüstite as an FeO–MgO solid solution and Al2O3 was distributed in slag. In the case of pellets, Iljana et al. [23] carried out experiments on metallurgical properties with different-sized pellets. They observed that the higher proportions of MgO in the silicate slag and in the wüstite resulted in increased softening temperatures. They also verified that increasing the MgO content can improve the softening properties of pellets via computational thermodynamics [24] and proposed the separation of Al2O3 from iron ore concentrate to avoid deteriorating the softening properties. Chen et al. [25] reviewed the effect of MgO on the metallurgical properties of pellets, and pointed out that the softening properties were improved obviously, but the melting properties were not improved with increasing MgO content.
However, research on the SM properties of mixed burden composed of sinter and pellet is relatively limited compared to single ore species [26,27], especially regarding the comprehensive effect of MgO and Al2O3 under the current conditions that both MgO and Al2O3 in high-basicity sinter are increased. There are still some difficulties in adjusting the MgO and Al2O3 content in sinter for the purpose of optimizing the SM properties of mixed ferrous burden. Therefore, the SM properties of mixed ferrous burden made from high-basicity sinter with increased MgO and Al2O3 content and acid pellets were investigated in this study. The influence mechanisms of MgO and Al2O3 were analyzed with the aid of phase analysis. We hope that the results will be useful to the establishment of a picture about the SM behavior of mixed burden, and its effect on BF operations.

2. Materials and Methods

2.1. Materials

Three kinds of high-basicity sinters and one kind of acid pellet, derived from actual ironmaking plants, were selected as experimental materials. The chemical compositions are listed in Table 1. It shows that there was only a little variation in the degree of the TFe content, FeO content and binary basicity (C/S) in the sinter samples. The changes in MgO and Al2O3 content in the sinters were more interesting. From S1 to S3, the MgO content increased from 1.70 to 3.16 mass% with increasing Al2O3 content (from 1.14 to 4.03 mass%), while the MgO mass%/Al2O3 mass% (M/A) decreased from 1.49 to 0.78.
The experimental samples were three kinds of mixed burdens. All the mixed burdens consisted of 70 mass% sinter and 30 mass% pellets, which is a general burden structure in China. The chemical compositions of mixed burdens are shown in Table 2. From S1P to S3P, MgO and Al2O3 content increased continually, from 1.33 to 2.36 mass% and from 1.23 to 3.25 mass %, respectively. The M/A kept a decreasing trend from 1.08 to 0.73.

2.2. Experimental Procedure

The experimental equipment of the SM test is shown in Figure 1. A packed bed comprising mixed burden (200 g) packed in between two coke layers (20 mm each) was heated with a load of 0.5 kg·cm−2 in a graphite crucible. The particle sizes of iron ores and cokes were 10~12.5 mm and 6~8 mm, respectively. All the materials were dried at 105 °C for 24 h before testing. The dripping holes in the bottom of the crucible allowed the gas flow to pass through the burden and the molten iron/slag to drip. The mixed burden was heated at 10 °C·min−1 below 950 °C, and kept at 950 °C for 1 h, and then heated at 5 °C·min−1 over 950 °C. The gas flow was changed from N2 (5 L·min−1) to a reducing gas composed of CO and N2 with the ratio 30/70 (12 L·min−1) until the sample temperature reached 400 °C. A more detailed description of the test procedure was given in our previous work [28].
In the SM process, the ferrous burden bed deformed (softened and melted) and then hindered the gas flow. During the whole experimental process, several important parameters such as the sample temperature, shrinkage ratio (Δh) and pressure drop (ΔP) were continuously recorded by the thermocouple, the displacement meter and the pressure gauge, respectively. When the test was finished, the dripped substance and residual materials in the graphite crucibles were collected for further analysis.

3. Results and Discussion

A typical set of SM curves of the mixed burden is shown in Figure 2, which includes the shrinkage ratio (Δh) and pressure drop (ΔP) changes against the sample temperature. To represent and compare the SM properties of these samples, some indexes were adopted. As evident from Figure 2, when Δh reached 10% and 40%, the sample temperatures T10% and T40% were defined as softening start temperature and softening end temperature, respectively. The melting start temperature Tm was the temperature that ΔP began to steeply increase; and Tf was the melting end temperature at which Δh tended to be unchanged. The softening temperature interval (T40%–T10%) represented the softening zone while the melting temperature interval (Tf–Tm) represented the melting zone. Because ΔP was at the low level in the softening range, the softening zone was expected to be wide while the melting zone should be narrow, indicating good SM properties of the burden. During the melting temperature interval, when the first dripping phenomenon was observed, the sample temperature was recorded as the dripping temperature Td. ΔPmax was the maximum value of the pressure drop curve. S was defined as the permeability index of the melting zone and supposed to be the integral value of the pressure drop function over the melting zone (from Tm to Tf), seeing the shaded area in Figure 2. The higher the value of S, the worse the permeability of the mixed burden in the melting zone.

3.1. The Effects of MgO and Al2O3 on Softening Properties

Figure 3 shows the effects of MgO and Al2O3 content in high-basicity sinter on the softening characteristic temperatures of mixed burdens. As the MgO and Al2O3 content increased and the M/A decreased, the softening start temperature T10% and the softening end temperature T40% showed decreasing trends from 1316 °C to 1238 °C and from 1453 °C to 1354 °C, respectively. The decrease extent of T10% from S1P to S2P was more significant than that observed from S2P to S3P. The softening interval (T40%–T10%) widened slightly from 137 °C to 149 °C at first, and then narrowed down to 116 °C. In terms of the position and thickness of the cohesive zone in BF, the upper edge of the cohesive zone and the corresponding T10% moved upward. The experimental softening results showed that the M/A of mixed burden had a certain content limit. The possible thinning of the thickness of the softening zone was achieved, which indicated that the softening properties of mixed ferrous burden were improved when adjusting the M/A.
The softening characteristic temperatures of mixed burdens tended towards those of its corresponding high-basicity sinter and could be explained as followed. First, according to previous research on sinter mineralogy [17,29], increasing the MgO and Al2O3 content facilitated the formation of magnesioferrite and dampened hematite obviously, whereas the amounts of calcium ferrite almost kept constant. The sinter containing higher amounts of MgO and Al2O3 had a relatively lower reducibility. This fact resulted in earlier deformation, leading the lower T10% and T40%. Second, the increase in Al2O3 content in sinter favored the formation of an Al2O3-rich primary slag phase with low melting temperature, such as the eutectic of 2CaO·SiO2-2CaO·Al2O3·SiO2-FeO [22]. It has been suggested that MgO has a positive influence on softening temperatures [30]. However, the effect of Al2O3 on softening was likely to be more dominant than MgO [17]. Thus, the softening temperatures were expected to decrease. It is indispensable to optimize the softening properties of mixed burden, but only when considering both the reduction property and gas permeability. In the softening process of the samples, its pressure drop was relatively low before intensely climbing. The wide softening zone benefited indirect reduction and decreasing coke rate. Therefore, it is believed that the softening property of S2P was the best where the certain M/A of the mixed burden was 0.82.

3.2. The Effects of MgO and Al2O3 on Melting Properties

The effects of MgO and Al2O3 content in sinter on the melting characteristic temperatures of mixed burdens are shown in Figure 4. With the increase in MgO and Al2O3 content in sinter, the melting start temperature Tm and the melting end temperature Tf decreased from 1490 °C to 1436 °C and from 1558 °C to 1531 °C, respectively. The melting interval (Tf–Tm) first increased slightly, and then increased greatly later. According to the experimental melting results, the lower edge of the cohesive zone and the corresponding Tf moved upward and the thickness of melting zone and corresponding Tf–Tm increased. It should be noted that once the M/A of the mixed burden was less than 0.82, the melting properties were worsened significantly, which was not the expectation. The dripping temperature Td of S1P, S2P and S3P was 1534 °C, 1506 °C and 1481 °C, respectively. The Td is an important factor which determines physical heat in the BF hearth. If the Td is too low, the heat carried by the molten iron cannot allow the blast furnace hearth to achieve good performance in desulfurization and slag tapping, which is detrimental to production. From the Td, it is proposed that the M/A of mixed burden cannot be less than 0.82.
Figure 5 shows the effects of MgO and Al2O3 content in sinter on the permeability of the melting zone. With the increase in MgO and Al2O3 content, ΔPmax decreased from 458 kPa to 232 kPa while the S value decreased at first and then increased, indicating that the permeability of the mixed burdens first became better and then deteriorated. From the width and permeability of the melting zone, the mixed burden with an M/A of 0.82 had the best melting property. Therefore, it is suggested that the proper M/A of the mixed burden made from high-basicity sinter and acid pellets should be about 0.82 when both the MgO and Al2O3 content are increased in sinter.
Tm and Td were related to the molten slag properties, such as liquidus temperature and viscosity. The slag was mainly derived from the gangue components in mixed burden and can be theoretically estimated with CaO–SiO2–MgO–Al2O3 system phase diagrams [31]. Figure 6 shows the phase diagrams of a CaO–SiO2–MgO–Al2O3 system, in which the fractions of Al2O3 are 5 mass%, 15 mass% and 20 mass%, respectively. From S1P to S3P, the liquidus temperature of the molten slag is obviously decreased. An aforementioned fact is that the low reducibility of sinter with high MgO and Al2O3 content can result in high FeO content remaining in the molten slag after mixed burden melting. FeO is a typical substance which can decrease the melting temperature of slag. In addition, it has been reported that blast furnace slag viscosity decreases with increasing FeO content [32]. Therefore, Tm and Td showed decreased trends.

3.3. Roles of MgO and Al2O3 during Melting

Figure 7 shows photos of the residual materials and dripped materials after the experiments. The residual materials consisted of large amounts of slag phase and a relatively smaller amount of iron. In contrast, the dripped materials were mainly composed of iron and relatively less slag.
To illustrate the roles of MgO and Al2O3 during melting, X-ray diffraction pattens of the residual slags and dripped slags are shown in Figure 8. For the residual slags and dripped slags of S1P and S2P, the main minerals were melilite (Ca2(Al,Mg)[(Si,Al)SiO7]) and merwinite (3CaO·MgO·2SiO2). In contrast, the residual slag and dripped slag of S3P contained an additional component, monticellite (CaO·MgO·SiO2). The melting point of monticellite is 1390 °C, which is lower than those of melilite and merwinite. It is suggested that a higher MgO and Al2O3 content in sinter results in the generation of relatively low-melting point components in the slag of mixed burden. It can be deduced that the mixed burden containing a high MgO and Al2O3 content with a low M/A can drip easily, resulting in the low Td and low ΔPmax. It is probable that the widest melting temperature interval of S3P where the M/A is less than 0.82 brings about the higher S value and worse permeability. Thus, under comprehensive consideration of the SM properties and the roles of MgO and Al2O3, the M/A of mixed burden made with high-basicity sinter and pellets should be about 0.82.

4. Conclusions

The softening–melting properties of mixed ferrous burden made from high-basicity sinter with increased MgO and Al2O3 content and acid pellets and the roles of MgO and Al2O3 during melting were investigated. Several conclusions were obtained.
(1)
With decreasing MgO mass%/Al2O3 mass% in mixed burden, the softening–melting characteristic temperatures of mixed burdens tended to decrease. The softening interval widened slightly at first, and then narrowed, while the melting interval first increased slightly, and then increased greatly. The permeability of the melting zone deteriorated once the MgO mass%/Al2O3 mass% was less than a certain content.
(2)
The low melting temperature and viscosity of the slag of mixed ferrous burden with a low MgO mass%/Al2O3 mass% was the main reason for the reduction in softening–melting characteristics.
(3)
On the whole, with decreasing MgO mass%/Al2O3 mass% in mixed burden, the softening properties were improved whereas the melting properties were worsened. Considering the iron ore reduction and thermal state of blast furnace hearth, mixed burden had the optimal softening–melting properties at an MgO mass%/Al2O3 mass% of 0.82.

Author Contributions

Z.L. and T.L. performed the experiments, material characterization, and paper writing; C.S. and S.Y. contributed to the data analysis and design of the experiment. Q.W. contributed to the conceptualization. All authors have read and agreed to the published version of the manuscript.

Funding

This work was financially supported by the National Natural Science Foundation of China (No. 52174319) and Department of Education of Liaoning Province (LJKQZ20222303).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The data presented in this study are available on request from the corresponding author.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Geerdes, M.; Chaigneau, R.; Kurunov, I.; Lingiardi, O.; Ricketts, J. Modern Blast Furnace Ironmaking: An Introduction; Ios Press: Amsterdam, The Netherlands, 2015. [Google Scholar]
  2. Bao, J.W.; Chu, M.S.; Liu, Z.G.; Han, D.; Guo, J.; Zhang, L.F. Influence mechanism of different reactive iron carbon agglomerates on softening–melting–dropping properties of BF mixed burdens. Ironmak. Steelmak. 2022, 50, 571–584. [Google Scholar] [CrossRef]
  3. Flores, I.V.; Matos, O.; Lima da Silva, A.; Covcevich Bagatini, M. Microstructure and porosity evolution during the reduction, softening and melting of iron-bearing materials. Metall. Mater. Trans. B 2021, 52, 1716–1738. [Google Scholar] [CrossRef]
  4. Lu, Y.N.; Wu, S.L.; Du, B.B.; Zhou, H. Increasing the softening as well as melting behaviors for iron ore materials within the blast furnace cohesive zone through the high-temperature interactivity. ISIJ Int. 2020, 60, 1461–1468. [Google Scholar] [CrossRef]
  5. Iljana, M.; Kemppainen, A.; Paananen, T.; Mattila, O.; Heikkinen, E.P.; Fabritius, T. Evaluating the reduction-softening behaviour of blast furnace burden with an advanced test. ISIJ Int. 2016, 56, 1705–1714. [Google Scholar] [CrossRef] [Green Version]
  6. Ju, J.T.; Ma, K.; Xing, X.D.; Zhao, G.Q.; Li, Q.D. Investigate the oxidation induration mechanism of manganese-bearing magnetite concentrate pellets. Ironmak. Steelmak. 2022, 49, 588–595. [Google Scholar] [CrossRef]
  7. Kamireddy, V.; Wang, D.Q.; Pan, W.; Chen, S.G.; Evans, T.; Tang, F.Q.; Zhao, B.J.; Ma, X.D. Liquid formation in sinters and its correlation with softening behaviour. Metals 2022, 12, 885. [Google Scholar] [CrossRef]
  8. Guo, H.; Jiang, X.; Shen, F.M.; Zheng, H.Y.; Gao, Q.J.; Zhang, X. Influence of SiO2 on the compressive strength and reduction-melting of pellets. Metals 2019, 9, 852. [Google Scholar] [CrossRef] [Green Version]
  9. Shin, S.G.; Kim, W.H.; Min, D.J. A Study on the effect of alumina on the morphology and reduction behavior of sinter by in situ observation. Metals 2021, 11, 740. [Google Scholar] [CrossRef]
  10. Ji, Z.Y.; Zhao, Y.J.; Gan, M.; Fan, X.H.; Chen, X.L.; Hu, L. Microstructure and minerals evolution of iron ore sinter: Influence of SiO2 and Al2O3. Minerals 2019, 9, 449. [Google Scholar] [CrossRef] [Green Version]
  11. Kim, H.; Matsuura, H.; Tsukihashi, F.; Wang, W.L.; Min, D.J.; Sohn, I. Effect of Al2O3 and CaO/SiO2 on the viscosity of calcium-silicate-based slags containing 10 Mass Pct MgO. Metall. Mater. Trans. B 2013, 44, 5–12. [Google Scholar] [CrossRef]
  12. Wang, Z.J.; Sun, Y.Q.; Sridhar, S.; Zhang, M.; Guo, M.; Zhang, Z.T. Effect of Al2O3 on the viscosity and structure of CaO-SiO2-MgO-Al2O3-FetO slags. Metall. Mater. Trans. B 2015, 46, 537–541. [Google Scholar] [CrossRef]
  13. Yao, L.; Ren, S.; Wang, X.Q.; Liu, Q.C.; Dong, L.Y.; Yang, J.F.; Liu, J.B. Effect of Al2O3, MgO, and CaO/SiO2 on viscosity of high alumina blast furnace slag. Steel Res. Int. 2016, 87, 241–249. [Google Scholar] [CrossRef]
  14. Sun, C.Y.; Liu, X.H.; Li, J.; Yin, X.T.; Song, S.; Wang, Q. Influence of Al2O3 and MgO on the viscosity and stability of CaO-MgO-SiO2-Al2O3 slags with CaO/SiO2 = 1.0. ISIJ Int. 2017, 57, 978–982. [Google Scholar] [CrossRef] [Green Version]
  15. Sun, C.Y.; Chen, Y.C.; Li, J.; Wang, Q.; Liu, X.H.; Sheng, X.X. Influence and dynamics analysis of MgO content on the desulfurization of blast furnace slag with high Al2O3 content. J. Chongqing Univ. 2016, 39, 82–87. (In Chinese) [Google Scholar]
  16. Wu, S.L.; Lu, Y.N.; Hong, Z.B.; Zhou, H. Improving the softening and melting properties of ferrous burden with high Al2O3 content for blast furnace by ore blending. ISIJ Int. 2020, 60, 1504–1511. [Google Scholar] [CrossRef]
  17. Li, T.L.; Sun, C.Y.; Liu, X.; Song, S.; Wang, Q. The Effects of MgO and Al2O3 behaviours on softening-melting properties of high basicity sinter. Ironmak. Steelmak. 2018, 45, 755–763. [Google Scholar] [CrossRef]
  18. Ma, L.M.; Zhang, J.L.; Wang, Y.Z.; Lu, M.; Cai, Q.Y.; Xu, C.Y.; Li, Z.; Liu, Z.J. Mixed burden softening-melting property optimization based on high-silica fluxed pellets. Powder Technol. 2022, 412, 117979. [Google Scholar] [CrossRef]
  19. Guo, H.; Shen, F.M.; Liu, M.X.; Zhang, L.; Zheng, H.Y.; Jiang, X. Effects of MgO and burden charging pattern of the sinter ore on melting and dropping. J. Mater. Metall. 2017, 16, 13–18. (In Chinese) [Google Scholar]
  20. Guo, H.; Shen, F.M.; Zhang, H.Y.; Gao, Q.J.; Jiang, X. High-temperature reduction and melting mechanism of sinter with different MgO content. Metals 2019, 9, 510. [Google Scholar] [CrossRef] [Green Version]
  21. Li, S.D.; Zhang, J.L.; Wang, Y.Z.; Lu, F.L.; Niu, L.L.; Li, Z.; Liu, Z.J. Dual effect of MgO on softing–melting performance of high gangue sinter: Changes of slag viscosity and phase composition. Ironmak. Steelmak. 2023. [Google Scholar] [CrossRef]
  22. Wang, Z.; Zhang, J.L.; Zuo, H.B.; Gao, B.; Li, F.G.; Wang, R.B. Influence of Al2O3 content on softening-melting property of high basicity sinter. Iron Steel 2015, 50, 20–25+76. (In Chinese) [Google Scholar]
  23. Iljana, M.; Paananen, T.; Mattila, O.; Kondrakov, M.; Fabritius, T. Effect of iron ore pellet size on metallurgical properties. Metals 2022, 12, 302. [Google Scholar] [CrossRef]
  24. Iljana, M.; Heikkinen, E.P.; Fabritius, T. Estimation of iron ore pellet softening in a blast furnace with computational thermodynamics. Metals 2021, 11, 1515. [Google Scholar] [CrossRef]
  25. Chen, B.J.; Jiang, T.; Wen, J.; Li, L.; Hu, P. Review of pellets and blast furnace slag research progress: The effects of MgO on metallurgical properties. Ironmak. Steelmak. 2023. [Google Scholar] [CrossRef]
  26. Liu, Z.G.; Chu, M.S.; Wang, H.T.; Zhao, W.; Xue, X.X. Effect of MgO content in sinter on the softening-melting behavior of mixed burden made from chromium-bearing vanadium-titanium magnetite. Int. J. Miner. Metall. Mater. 2016, 23, 25–32. [Google Scholar] [CrossRef]
  27. Bai, K.K.; Pan, Y.Z.; Wang, J.S.; Zuo, H.B.; Xue, Q.G. Optimizing MgO distribution between sinter and pellet based on melting behavior and interaction. Metall. Res. Technol. 2021, 118, 318. [Google Scholar] [CrossRef]
  28. Li, T.L.; Sun, C.Y.; Lan, D.; Song, J.; Song, S.; Wang, Q. Effect of mineral elements migration on softening–melting properties of ti–bearing high basicity sinter. ISIJ Int. 2019, 59, 245–252. [Google Scholar] [CrossRef]
  29. Tsutsumi, T.; Wang, Z.; Sasaki, Y.; Kashiwaya, Y.; Ishii, K.; Konno, N. Heating-Up reduction and high temperature properties of high alumina sintered ores. Tetsu-to-Hagane 1998, 84, 477–483. [Google Scholar] [CrossRef] [PubMed]
  30. Nandy, B.; Chandra, S.; Bhattacharjee, D.; Ghosh, D. Assessment of blast furnace behaviour through softening-melting test. Ironmak. Steelmak. 2006, 33, 111–119. [Google Scholar] [CrossRef]
  31. Eisenhüttenleute, V.D. Slag Atlas; Verlag Stahleisen Press: Dusseldorf, Germany, 1995. [Google Scholar]
  32. Lee, Y.S.; Min, D.J.; Jung, S.M.; Yi, S.H. Influence of basicity and FeO content on viscosity of blast furnace type slags containing FeO. ISIJ Int. 2004, 44, 1283–1290. [Google Scholar] [CrossRef] [Green Version]
Materials 16 05490 g001
Figure 1. The experimental equipment of SM test.
Figure 1. The experimental equipment of SM test.
Materials 16 05490 g001
Materials 16 05490 g002
Figure 2. A typical set of SM curves of the mixed burden.
Figure 2. A typical set of SM curves of the mixed burden.
Materials 16 05490 g002
Materials 16 05490 g003
Figure 3. Effects of MgO and Al2O3 content in sinter on softening properties of mixed burdens.
Figure 3. Effects of MgO and Al2O3 content in sinter on softening properties of mixed burdens.
Materials 16 05490 g003
Materials 16 05490 g004
Figure 4. Effects of MgO and Al2O3 content in sinter on melting properties of mixed burdens.
Figure 4. Effects of MgO and Al2O3 content in sinter on melting properties of mixed burdens.
Materials 16 05490 g004
Materials 16 05490 g005
Figure 5. Effects of MgO and Al2O3 content in sinter on the permeability of melting zone.
Figure 5. Effects of MgO and Al2O3 content in sinter on the permeability of melting zone.
Materials 16 05490 g005
Materials 16 05490 g006
Figure 6. The phase diagrams of CaO–SiO2–MgO–Al2O3 system.
Figure 6. The phase diagrams of CaO–SiO2–MgO–Al2O3 system.
Materials 16 05490 g006
Materials 16 05490 g007
Figure 7. The photos of dripped materials and residual materials.
Figure 7. The photos of dripped materials and residual materials.
Materials 16 05490 g007
Materials 16 05490 g008
Figure 8. The X-ray diffraction analysis of the residual slags and dripped slags.
Figure 8. The X-ray diffraction analysis of the residual slags and dripped slags.
Materials 16 05490 g008
Table 1. The chemical compositions of high-basicity sinters and pellets (mass%).
Table 1. The chemical compositions of high-basicity sinters and pellets (mass%).
MaterialsTFe 1FeOSiO2CaOMgOAl2O3M/A 2C/S 3
S154.399.546.6313.151.701.141.491.98
S254.709.405.5310.262.843.080.921.86
S352.309.006.1611.313.164.030.781.84
P63.800.183.380.340.481.430.690.10
1 TFe means the total Fe content in mass%; 2,3 M/A and C/S mean CaO mass%/SiO2 mass% and MgO mass%/Al2O3 mass%, respectively.
Table 2. The chemical compositions of mixed burdens (mass%).
Table 2. The chemical compositions of mixed burdens (mass%).
Mixed BurdensTFe 1FeOSiO2CaOMgOAl2O3M/A 2
S1P57.216.735.669.311.331.231.08
S2P57.436.634.897.282.132.590.82
S3P55.756.355.338.022.363.250.73
1 TFe means the total Fe content in mass%; 2 M/A means MgO mass%/Al2O3 mass%.
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Li, Z.; Li, T.; Sun, C.; Yang, S.; Wang, Q. The Effects of MgO and Al2O3 Content in Sinter on the Softening–Melting Properties of Mixed Ferrous Burden. Materials 2023, 16, 5490. https://doi.org/10.3390/ma16155490

AMA Style

Li Z, Li T, Sun C, Yang S, Wang Q. The Effects of MgO and Al2O3 Content in Sinter on the Softening–Melting Properties of Mixed Ferrous Burden. Materials. 2023; 16(15):5490. https://doi.org/10.3390/ma16155490

Chicago/Turabian Style

Li, Zhexi, Tingle Li, Changyu Sun, Songtao Yang, and Qi Wang. 2023. "The Effects of MgO and Al2O3 Content in Sinter on the Softening–Melting Properties of Mixed Ferrous Burden" Materials 16, no. 15: 5490. https://doi.org/10.3390/ma16155490

APA Style

Li, Z., Li, T., Sun, C., Yang, S., & Wang, Q. (2023). The Effects of MgO and Al2O3 Content in Sinter on the Softening–Melting Properties of Mixed Ferrous Burden. Materials, 16(15), 5490. https://doi.org/10.3390/ma16155490

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop