Mold–Slug Interfacial Heat Transfer Characteristics of Different Coating Thicknesses: Effects on Slug Temperature and Microstructure in Swirled Enthalpy Equilibration Device Process
Previous Article in Journal
Quality Index Charts of Al-Si-Mg Semi Solid Alloys Subjected to Multiple Temperatures Aging Treatments and Different Quenching Media
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 12
Issue 11
10.3390/ma12111835
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Core-Shell and Hollow Particles of Carbon and SiC Prepared from Hydrochar

by
Wenming Hao
1,2,
Yongsheng Liu
2,
Alexandra Neagu
2,
Zoltan Bacsik
2,
Cheuk-Wai Tai
2,
Zhijian Shen
2,* and
Niklas Hedin
2,*
1
College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024, Shanxi, China
2
Department of Materials and Environmental Chemistry, Arrhenius Laboratory, Stockholm University, SE-106 91 Stockholm, Sweden
*
Authors to whom correspondence should be addressed.
Materials 2019, 12(11), 1835; https://doi.org/10.3390/ma12111835
Submission received: 11 April 2019 / Revised: 31 May 2019 / Accepted: 3 June 2019 / Published: 6 June 2019
(This article belongs to the Section Materials Chemistry)
Browse Figures
Versions Notes

Abstract

:
The applications of silicon carbide (SiC) include lightweight materials with thermal shock resistance. In this study, core-shell C-SiC particles were synthesized by compacting and rapidly heating a hydrochar from glucose by using strong pulsed currents and infiltration of silicon vapor. Hollow particles of SiC formed on removing the carbon template. In contrast to related studies, we detected not only the pure 3C polytype (β-SiC) but also significant amounts of the 2H or the 6H polytypes (α-SiC) in the SiC.

Graphical Abstract

1. Introduction

Hydrothermal carbonization is an old approach to treat biomass [1,2] that has gotten new attention. In that process, the components of biomass, especially sugars [3] and polysaccharides, are dehydrated into hydrochars [4,5]. The process has a good carbon economy [6], tunable chemistry, and the hydrochars are non-aromatic when the carbonization temperature is relatively low. The hydrochars have been refined into activated carbons [7,8,9,10], supercapacitor electrodes [11], pyrolyzed carbons [12], used to prepare hollow particles of metal oxides at low temperatures [13], and studied for energy applications [14].
Not only are hollow metal oxides interesting for applications, but also hollow SiC is a relevant lightweight material [15], which could provide thermal-shock resistance [16]. Hollow particles of SiC have been synthesized by different protocols [17,18,19,20,21,22,23,24], which include the use of carbon templates and vapor infiltration of silicon or SiO [18,19,20,21,22]. Carbon black is commonly used as carbon template, which reacts with vaporized silicon or SiO, forming SiC on the shell. Hollow SiC particle is obtained when the carbon core is oxidatively removed [18,21]. Silicon carbide (SiC) is mass-produced and has a high temperature stability [25,26,27,28,29,30,31]. With its outstanding thermal, optical, and electrical properties, SiC is a good candidate material for preparing high-frequency transistors, high-temperature sensors, and high-power devices [32,33]. Nanocrystalline powders could, in general, allow for doping and stabilization of unusual structures [34], and rapid sintering of small SiC particles seems to reduce grain-boundary migration. [35] Motivated by research showing that hydrochars from sugars are often observed in the form of spherical and carbon-rich particles [36], and that hollow particles of SiC have been shown to be possible to synthesize from carbon-rich spherical particles, we here used a sustainable hydrochar precursor to synthesize hollow particles of SiC.

2. Experimental Section

2.1. Precursors

Glucose (CAS no. 50-99-7; 99.5% purity, Sigma, Saint Louis, MO, USA) and silicon powder (CAS no. 7440-21-3; 99% purity, 325 mesh, Aldrich, Saint Louis, MO, USA) were used without any further purification.

2.2. Experimental Procedure

2.2.1. Hydrothermal Carbonization

Sixty grams of glucose was dissolved in 100 mL of distilled water and then transferred to a 200 mL autoclave. The solution was heated to 200 °C under autogenous pressure for 24 h. The black hydrochar powder was filtered off and washed five times with distilled water, before it was dried at 100 °C overnight.

2.2.2. Pulse Current Treatment

The hydrochar powder was consolidated into a disc using a Dr Sinter 2050 spark plasma sintering facility (Sumitomo Coal Mining Co., Ltd., Tokyo, Japan). The powder was loaded into a graphite die with an inner diameter of 12 mm and then subjected to a uniaxial pressure of 50 MPa. Strong pulsed currents (up to 1000 A) heated up the entire setup rapidly. The temperature of the assembly was increased to 100 °C from room temperature with a rate of 50 °C/min and held there for three minutes and then cooled down.

2.2.3. Infiltration of Vaporized Silicon

Four grams of a silicon powder was put above and under the hydrochar (0.5 g) disc and separated by a graphite felt in a graphite crucible. It was heated by pulsed currents from room temperature to 600 °C within three minutes under dynamic vacuum at a pressure <10 Pa. Thereafter, the temperature was rapidly increased to 1400 °C with a rate of 200 °C/min and held for five minutes. Subsequently, the temperature was increased to 1600 °C with a rate of 50 °C/min and held there for five minutes. After this treatment, the system was cooled down by natural convection.

2.2.4. Fabrication of Hollow Particles of SiC by Template Removal

Hollow particles of SiC were fabricated by removing the unreacted carbon from the silicon-infiltrated hydrochar in a muffle furnace at 700 °C in a flow of air for 16 h.

2.3. Characterization

2.3.1. Elemental Analyses

Carbon, hydrogen, and nitrogen elements (CHN) analyses were conducted by using combustion analysis. The Si content was analyzed by a Varian Vista MPX (Palo Alto, CA, USA) inductively coupled plasma optical emission spectrometry system, and the oxygen content was calculated as the difference.

2.3.2. Thermogravimetric Analyses (TGA)

The mass losses of the hydrochar and core-shell C-SiC composites were studied with a Perkin Elmer TAG7 instrument (Waltham, MA, USA) at 20–900 °C in dry air with a heating rate of 10 °C/min. A platinum cup was used.

2.3.3. N2 Adsorption and Textual Analyses

Analyses were performed at −196 °C with a Micromeritics ASAP 2020 device (Norcross, GA, USA). Samples were degassed at 300 °C for five hours. Specific surface areas were determined from the N2 adsorption data at relative pressures of 0.05–0.25 using the Brunauer, Emmett and Teller (BET) model.

2.3.4. Argon Ion-Beam Cross-Section Polishing

Argon ion-beam cross-section polishing was performed on the core-shell C-SiC composite using an SM-09010 Cross-Section Polisher (JEOL, Tokyo, Japan) with an accelerating voltage of 5 kV with beam currents of 70–90 μA for 15 h. The disc of the core-shell C-SiC composite was fixed on the sample holder of the cross-section polishing apparatus using a carbon paint (Conductive Carbon Cement, Plano, Wetzlar, Germany) during the polishing.

2.3.5. Scanning Electron Microscopy

A JEOL JSM-7000F microscope was used to record scanning electron microscopy (SEM in the SE mode) images with a working distance of 10 mm and an accelerating voltage of 5 kV. The sample discs were crushed, and cross sections were imaged by fixing the discs onto Oxford aluminum stubs that were coated subsequently by a thin layer of dried colloidal carbon.

2.3.6. Transmission Electron Microscopy

The transmission electron microscopy (TEM) experiments were performed at room temperature using a JEOL JEM-2100F microscope (Cs = 0.5 mm) with a Schottky-type field emission gun operated at 200 kV. Samples for TEM observations were crushed and dispersed in absolute ethanol, followed by ultrasonification for 1 min. A droplet of the suspension was transferred onto a copper grid coated with holey carbon film and dried in air.

2.3.7. Infrared Spectroscopy

Infrared (IR) spectra were collected on a Varian 670-IR IR spectrometer using a Golden Gate attenuated total reflectance (ATR) accessory and a room-temperature detector. Spectra (400–4000 cm−1) were recorded with a resolution of 4 cm−1.

2.3.8. Raman Spectroscopy

Raman spectra were recorded on a LabRAM HR 800 Raman spectrometer (Paris, France) with a resolution of 0.5 cm−1 using an air-cooled double-frequency Nd:YAG laser (50 mW, 532 nm). The frequency was calibrated to the band frequency of 520.7 cm−1 of a silicon wafer.

2.3.9. X-ray Diffraction

X-ray diffraction (XRD) data were collected using an X’PERT-PRO PANalyical powder diffractometer (Phillips Company, Amsterdam, The Netherlands) with an X’Celerator detector (CuKa1 radiation, k = 1.5418 Å) between 2θ = 20.0–80.0° in its reflection mode.

3. Results and Discussion

A hydrochar disc was prepared from a hydrochar powder, using a protocol developed by us [37], which was subsequently used as a precursor for the synthesis of core-shell particles of C-SiC and hollow particles of SiC. The hydrochar powder had a typical composition with significant amounts of C and O (see Table 1) [38]. Such hydrochars consist mainly of solid furan-rich polymers [39] and an acetone-soluble liquid fraction [37,40]. The diameters of the hydrochar particles were 5–10 µm (see Figure 1a), and the comparably polydispersed nature related to the comparably long reaction time (24 h) and high concentration of gluc4ose used for the synthesis.
The hydrochar powder was not very porous with a BET surface area of 8 m2/g. The water content was ~4 wt % as estimated from the mass loss observed at a temperature of 110 °C, as presented in Figure 2a. A dramatic mass loss was observed at temperatures >200 °C and related to evaporation of volatiles and decomposition of the condensed structure of the hydrochar [41,42].
The hydrochar disc was carbonized and used as both the sacrificial template and source of carbon for core-shell C-SiC particles subsequently transformed into hollow particles of SiC. Compared with other carbon sources, hydrochar can be prepared from biomass as a renewable source via a sustainable approach. Silicon vapor was infiltrated into the hydrochar discs, and a shell of SiC formed on the hydrochar. The hydrochar and the core-shell C-SiC particles had similar morphologies, as can be observed from Figure 1a,b. Similar and related transfer of morphological features have been observed for pyrolyzed lignocellulosic structures transformed into C-SiC particles on silicon vapor infiltration [43].
The core-shell C-SiC particles had small crystals (20–200 nm) of SiC on their surfaces assembled into thin shells with thicknesses of 300–500 nm, as shown in Figure 1c–e. The SiC particles seemed to consist of β-SiC from the XRD pattern in Figure 3b. The XRD pattern had narrow and broad peaks of amorphous carbon, some graphite, and narrow peaks from β-SiC. The broad X-ray peaks at 24° and 44° were typical for partially graphitized amorphous carbon [44,45]. The hydrochar powder was, on the other hand, X-ray amorphous (Figure 3a).
The core-shell particles of C-SiC contained 3 wt % of SiC (Table 1) and had a BET-specific surface area of 10 m2/g. The TGA trace was typical of a comparably stable structure, as can be seen from the trace in Figure 2b. No mass loss was observed at temperatures <600 °C, which indicated that the carbon core was stable at these temperatures. The sharp decrease in weight observed at temperatures of 650–700 °C was attributed to an oxidative removal of the carbon core. The weight of the sample stabilized at temperatures >800 °C with a residue attributed to SiC.
The carbon cores of the core-shell particles were removed at a temperature of 700 °C in a flow of air using a protocol similar to those of Ye et al. and Zhang et al. [18,19]. A longer oxidation time was used as compared with the study of Zhang et al. [19], as the underlying particles were larger in our case. After oxidation, the sample contained hollow and interconnected particles of SiC, as can be seen in Figure 1f (SEM) and Figure 4a (TEM). The TG curve in Figure 2c showed that the hollow SiC particle had 16 wt % of weight loss at 900 °C, which could probably be attributed to adsorbed moisture and some remaining carbon content.
Representative low-magnification TEM images illustrating the general morphology of the hollow particles of SiC are shown in Figure 4a,b. The strong contrast between the dark edge and the light area in the center further confirmed the hollow nature after the oxidation of the carbon core. We observed a relatively broad size distribution of the hollow spheres with the diameter ranging from 2.5–6 µm, which was consistent with the particle distribution of the hydrochar template. Small amounts of impurities were found, indicative of traces of amorphous SiO2. The polycrystalline nature of the SiC in the shells was studied by selected-area electron diffraction (SAED). Typical TEM images of the polycrystalline SiC grains in the shells and the corresponding SAED pattern are shown in Figure 4c,d. The grains had a broad size distribution, and the SAED pattern indicated a high density of defects, such as twinning and stacking faults, as indicated by streaking. The SAED pattern had diffraction rings characteristic of a polycrystalline phase indexed as the cubic 3C-SiC structure (F-43m), as is illustrated in Figure 4d. However, because of the high density of defects, the presence of other polytypes of SiC (like 6H-SiC) could not be excluded [46]. High-resolution TEM (HRTEM) images were recorded to further investigate the crystallinity and the type of defects in the grains. The shells consisted of highly-defective crystalline grains, as can be observed in a typical HRTEM image (Figure 4e) and a corresponding fast Fourier transform (Figure 4f). A large density of stacking faults was observed. Most of the grains were defective, and the TEM study could not give a full answer about the corresponding polymorphism.
The Raman spectrum of the hydrochar (in Figure 5a) is very similar to those in literature [5,47]. The band at 1367 cm−1 was assigned to either the ring-breathing vibration in aromatic structures or vibrations relating to sp3-hybridized carbons. The band at about 1590 cm−1 (the G-band) was assigned to the C-C stretching vibrations of sp2-hybridized carbon atoms. However, it was not judged relevant to characterize the hydrochars with the G/D-ratio. The band in the D-band regime of the hydrochars was not the defect-derived band of aromatics, as would be typically observed for amorphous carbons or graphite prepared at much higher temperatures than the hydrochars. The Raman spectrum of the core-shell C-SiC composite particles in Figure 5b, on the other hand, had the typical D (with a band at about 1347 cm−1) and G-bands (1596 cm−1), with ratios being typical for amorphous carbon materials [48], and a band at 790 cm−1 from the Si-C stretching. The Raman spectrum in Figure 5c of the hollow particles of SiC was typical for SiC [49,50]. The bands were broad and typical for disordered crystals [49]. To determine the polytype of the SiC, investigating the bands at low wavenumbers (so-called FTA modes) would have been most useful. However, only a weak band at 262 cm−1 was detected (not shown in the figure). Considering the position of the bands detected (FTO modes) at 964, 789, 764, and 262 cm−1, an attempt was made to determine the polytype of the SiC. According to these band positions, a pure 3C polytype (β-SiC) nature was clearly excluded [49]. The spectrum was most similar to the 2H polytype. Other polytypes, especially the 6H polytype with similar band intensities at around 790/760 cm−1 and with the most intense FTA mode at around 266 cm−1, could not be fully excluded because of the broad bands. The spectra were reproducible when being recorded at different spots of the sample. The very broad underlying band with maximum around 920 cm−1 was likely related to the impurity component of SiO2. However, assignments to SiC polytypes were not fully excluded as the frequency was slightly lower than commonly observed for SiO2. In contrast to other studies of hollow particles of SiC [17,18,20,22,23,24], we did not detect the pure 3C polytype (β-SiC). Instead, the spectra were consistent with highly defective and polycrystalline SiC of the 2H or possibly the 6H (α-SiC) polytype. Raman spectroscopy is, in our view, needed to be used when investigating the polymorphisms in SiC samples, such as in this study. Note that Liu et al. have shown that β-SiC can form together with an amorphous layer [21]. SiC with different polytypes can give different properties. It was reported that β-SiC and α-SiC have different behavior at high temperature [30,31].
The functional groups of the hydrochar, core-shell C-SiC, and hollow particles of SiC were studied by IR spectroscopy. The IR spectrum of the hydrochar is presented in Figure 6a. The broad band at 3600–3000 cm−1 were attributed to the O-H stretching vibrations of water, alcohols, or phenols groups; the band at 2910 cm−1 was assigned to the C-H stretching vibrations of aliphatic alkyl chains [51]; and the bands centered at 1693 and 1600 cm−1 were associated to the C=O stretching vibration of the carbonyl and carboxylic groups. The latter one could also be assigned to C=C stretching [52]. The bands in the 1300–1000 cm−1 region were assigned to mainly C-O stretching vibrations in alcohols, phenols and carboxyl groups, and the band centered at 790 cm−1 was related to the out-of-plane bending vibration of aromatic C-H groups [53] and was indicative of some aromatization of the hydrochar. The IR spectrum of the core-shell C-SiC composite basically lacked band features (Figure 6b) after the high-temperature treatment and vapor infiltration of silicon. Pure carbons do not have bands in the IR spectra, and the shape of the baseline in Figure 6b is typical for scattering of IR radiation by carbons. The two derivative-like spectral features of this spectrum likely related to bands of SiC. The derivative-like shape of these bands was a consequence of the various interactions between the IR radiation and the core-shell C-SiC material. This assignation of the derivative-like features was consistent with the features of the IR spectrum of the hollow SiC spheres in Figure 6c. The spectrum in Figure 6c agreed well with those previously being reported for SiC [54]. The IR band shapes and, to a certain extent, band positions have been shown to depend on the size of the particles but cannot provide information about the polytype of the SiC [54]. The band at 780 cm−1 corresponded to the Si-C stretching vibrations, and the bands at 1074 and 451 cm−1 were firmly assigned to the Si-O stretching and bending vibrations for the SiO2 impurities also being observed by features in certain TEM images.

4. Conclusions

Hollow and spherical particles of SiC were prepared using a precursor powder of hydrothermally carbonized glucose. The hydrochar was subjected to infiltration of silicon vapor and a subsequent oxidative removal of unreacted carbon. The spherical morphology of the hydrochar particles was transferred to the spherical shells of SiC. Analyses of the TEM and X-ray diffraction data indicated that the SiC was of the 3C polytype (β-SiC), but the features in the Raman spectrum distinctively excluded a pure β-SiC composition of the defective nanocrystals in the thin SiC shells. The Raman spectrum was consistent with significant fractions of the 2H or 6H polytypes of SiC (α-SiC).
In future work, the thickness of the SiC shell could be controlled by the time of silicon vapor infiltration or by using chemical vapor infiltration. The size of the hollow SiC particles could likely be controlled by varying the size of the hydrochar particles. In addition to such variations, it could be relevant to also test the mechanical and thermal properties of macroscopic samples of the intergrown and hollow particles of SiC.

Author Contributions

Conceptualization, N.H. and Z.S.; methodology, W.H. and Y.L.; investigation, Z.B., A.N. and C.-W.T.; writing—original draft preparation, W.H.; writing—review and editing, N.H.

Funding

The Knut and Alice Wallenberg (KAW) Foundation is acknowledged for funding the electron microscopy facilities at Stockholm University and financial support for A.N. and C.-W.T. under the project 3DEM-NATUR. N.H. acknowledges support from the Swedish Energy Agency.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Funke, A.; Ziegler, F. Hydrothermal carbonization of biomass: A summary and discussion of chemical mechanisms for process engineering. Biofuels Bioprod. Biorefining 2010, 4, 160–177. [Google Scholar] [CrossRef]
  2. Hoekman, S.K.; Broch, A.; Robbins, C. Hydrothermal Carbonization (HTC) of Lignocellulosic Biomass. Energy Fuels 2011, 25, 1802–1810. [Google Scholar] [CrossRef]
  3. Yao, C.; Shin, Y.; Wang, L.-Q.; Windisch, C.F., Jr.; Samuels, W.D.; Arey, B.W.; Wang, C.; Risen, W.M., Jr.; Exarhos, G.J. Hydrothermal dehydration of aqueous fructose solutions in a closed system. J. Phys. Chem. C 2007, 111, 15141–15145. [Google Scholar] [CrossRef]
  4. He, C.; Giannis, A.; Wang, J.-Y. Conversion of sewage sludge to clean solid fuel using hydrothermal carbonization: Hydrochar fuel characteristics and combustion behavior. Appl. Energy 2013, 111, 257–266. [Google Scholar] [CrossRef]
  5. Sevilla, M.; Fuertes, A.B.; Solis, M.S. Chemical and Structural Properties of Carbonaceous Products Obtained by Hydrothermal Carbonization of Saccharides. Chem. A Eur. J. 2009, 15, 4195–4203. [Google Scholar] [CrossRef] [PubMed]
  6. Titirici, M.-M.; Thomas, A.; Antonietti, M. Back in the black: Hydrothermal carbonization of plant material as an efficient chemical process to treat the CO2 problem? New J. Chem. 2007, 31, 787. [Google Scholar] [CrossRef]
  7. Roman, S.; Nabais, J.V.; Ledesma, B.; González, J.F.G.; Laginhas, C.; Titirici, M.; Titirici, M. Production of low-cost adsorbents with tunable surface chemistry by conjunction of hydrothermal carbonization and activation processes. Microporous Mesoporous Mater. 2013, 165, 127–133. [Google Scholar] [CrossRef]
  8. Sevilla, M.; Fuertes, A.B.; Mokaya, R. High density hydrogen storage in superactivated carbons from hydrothermally carbonized renewable organic materials. Energy Environ. Sci. 2011, 4, 1400. [Google Scholar] [CrossRef]
  9. Hao, W.; Björkman, E.; Lilliestråle, M.; Hedin, N. Activated carbons prepared from hydrothermally carbonized waste biomass used as adsorbents for CO2. Appl. Energy 2013, 112, 526–532. [Google Scholar] [CrossRef]
  10. Hao, W.; Björkman, E.; Lilliestråle, M.; Hedin, N. Activated Carbons for Water Treatment Prepared by Phosphoric Acid Activation of Hydrothermally Treated Beer Waste. Ind. Eng. Chem. Res. 2014, 53, 15389–15397. [Google Scholar] [CrossRef]
  11. Zhao, L.; Fan, L.-Z.; Zhou, M.-Q.; Guan, H.; Qiao, S.; Antonietti, M.; Titirici, M.-M. Nitrogen-Containing Hydrothermal Carbons with Superior Performance in Supercapacitors. Adv. Mater. 2010, 22, 5202–5206. [Google Scholar] [CrossRef] [PubMed]
  12. Manyà, J.J. Pyrolysis for biochar purposes: A review to establish current knowledge gaps and research needs. Environ. Sci. Tech. 2012, 46, 7939–7954. [Google Scholar] [CrossRef] [PubMed]
  13. Titirici, M.-M.; Antonietti, M.; Thomas, A. A Generalized Synthesis of Metal Oxide Hollow Spheres Using a Hydrothermal Approach. Chem. Mater. 2006, 18, 3808–3812. [Google Scholar] [CrossRef]
  14. Lai, X.; Halpert, J.E.; Wang, D. Recent advances in micro-/nano-structured hollow spheres for energy applications: From simple to complex systems. Energy Environ. Sci. 2012, 5, 5604–5618. [Google Scholar] [CrossRef]
  15. Wu, R.; Zhou, K.; Yue, C.Y.; Wei, J.; Pan, Y. Recent progress in synthesis, properties and potential applications of SiC nanomaterials. Prog. Mater. Sci. 2015, 72, 1–60. [Google Scholar] [CrossRef]
  16. Niimi, I.; Yasuhisa, K.; Noda, F.; Tsuzuki, Y. Process for Preparing Hollow Balls of Silicon Carbide and Product Formed Therby. U.S. Patent US3927181A, 16 December 1975. [Google Scholar]
  17. Shen, G.; Chen, D.; Tang, K.; Qian, Y.; Zhang, S. Silicon carbide hollow nanospheres, nanowires and coaxial nanowires. Chem. Phys. Lett. 2003, 375, 177–184. [Google Scholar] [CrossRef]
  18. Ye, J.; Zhang, S.; Lee, W.E. Novel low temperature synthesis and characterisation of hollow silicon carbide spheres. Microporous Mesoporous Mater. 2012, 152, 25–30. [Google Scholar] [CrossRef]
  19. Zhang, Y.; Shi, E.-W.; Chen, Z.-Z.; Li, X.-B.; Xiao, B. Large-scale fabrication of silicon carbide hollow spheres. J. Mater. Chem. 2006, 16, 4141. [Google Scholar] [CrossRef]
  20. Li, P.; Xu, L.; Qian, Y. Selective Synthesis of 3C-SiC Hollow Nanospheres and Nanowires. Cryst. Growth Des. 2008, 8, 2431–2436. [Google Scholar] [CrossRef]
  21. Liu, Z.; Ci, L.; Jin-Phillipp, N.Y.; Rühle, M. Vapor−Solid Reaction for Silicon Carbide Hollow Spherical Nanocrystals. J. Phys. Chem. C 2007, 111, 12517–12521. [Google Scholar] [CrossRef]
  22. Ye, J.; Zhang, S.; Lee, W.E. Molten salt synthesis and characterization of SiC coated carbon black particles for refractory castable applications. J. Eur. Ceram. Soc. 2013, 33, 2023–2029. [Google Scholar] [CrossRef]
  23. Nersisyan, H.; Won, H.; Won, C.; Lee, J. Synthesis of hollow SiC microglobules by a combustion method. Microporous Mesoporous Mater. 2009, 117, 368–371. [Google Scholar] [CrossRef]
  24. Wang, Y.; Zhang, L.; Zhang, X.; Zhang, Z.; Tong, Y.; Li, F.; Wu, J.C.-S.; Wang, X. Openmouthed β-SiC hollow-sphere with highly photocatalytic activity for reduction of CO2 with H2O. Appl. Catal. B Environ. 2017, 206, 158–167. [Google Scholar] [CrossRef]
  25. Cromarty, R.; Van Rooyen, G.; De Villiers, J.; Cromarty, R. Crush strength of silicon carbide coated TRISO particles: Influence of test method and process variables. J. Nucl. Mater. 2014, 445, 30–36. [Google Scholar] [CrossRef]
  26. Chen, F.; Yang, Y.; Shen, Q.; Zhang, L. Macro/micro structure dependence of mechanical strength of low temperature sintered silicon carbide ceramic foams. Ceram. Int. 2012, 38, 5223–5229. [Google Scholar] [CrossRef]
  27. Lim, K.-Y.; Kim, Y.-W.; Kim, K.J. Mechanical properties of electrically conductive silicon carbide ceramics. Ceram. Int. 2014, 40, 10577–10582. [Google Scholar] [CrossRef]
  28. Chen, W.; Miyamoto, Y. Fabrication of porous silicon carbide ceramics with high porosity and high strength. J. Eur. Ceram. Soc. 2014, 34, 837–840. [Google Scholar] [CrossRef]
  29. Winé, G.; Matta, J.; Tessonnier, J.-P.; Pham-Huu, C.; LeDoux, M.-J. Beta zeolite supported on silicon carbide for Friedel-Crafts fixed-bed reactions. Chem. Commun. 2003, 9, 530–531. [Google Scholar] [CrossRef]
  30. Gentile, M.; Xiao, P.; Abram, T. Palladium interaction with silicon carbide. J. Nucl. Mater. 2015, 462, 100–107. [Google Scholar] [CrossRef]
  31. Gentile, M.; Xiao, P.; Abram, T. XRD and TG-DSC Analysis of the Silicon Carbide-Palladium Reaction. In Proceedings of the 37th International Conference and Expo on Advanced Ceramics and Composites, Daytona Beach, FL, USA, 27 January–1 February 2013. [Google Scholar]
  32. Pan, Z.; Lai, H.-L.; Au, F.C.K.; Duan, X.; Zhou, W.; Shi, W.; Wang, N.; Lee, C.-S.; Wong, N.-B.; Lee, S.-T.; et al. Oriented Silicon Carbide Nanowires: Synthesis and Field Emission Properties. Adv. Mater. 2000, 12, 1186–1190. [Google Scholar] [CrossRef]
  33. Li, Z.J.; Gao, W.D.; Meng, A.; Geng, Z.D.; Gao, L. Large-Scale Synthesis and Raman and Photoluminescence Properties of Single Crystalline β-SiC Nanowires Periodically Wrapped by Amorphous SiO2 Nanospheres. J. Phys. Chem. C 2008, 113, 91–96. [Google Scholar] [CrossRef]
  34. Maglia, F.; Tredici, I.G.; Anselmi-Tamburini, U. Densification and properties of bulk nanocrystalline functional ceramics with grain size below 50nm. J. Eur. Ceram. Soc. 2013, 33, 1045–1066. [Google Scholar] [CrossRef]
  35. Peng, H.; Salamon, D.; Bill, J.; Rixecker, G.; Burghard, Z.; Aldinger, F.; Shen, Z. Consolidating and Deforming SiC Nanoceramics Via Dynamic Grain Sliding. Adv. Eng. Mater. 2007, 9, 303–306. [Google Scholar] [CrossRef]
  36. Li, M.; Li, W.; Liu, S. Hydrothermal synthesis, characterization, and KOH activation of carbon spheres from glucose. Carbohydr. Res. 2011, 346, 999–1004. [Google Scholar] [CrossRef] [PubMed]
  37. Hao, W.; Keshavarzi, N.; Branger, A.; Bergström, L.; Hedin, N. Strong discs of activated carbons from hydrothermally carbonized beer waste. Carbon 2014, 78, 521–531. [Google Scholar] [CrossRef]
  38. Titirici, M.-M.; Antonietti, M.; Baccile, N. Hydrothermal carbon from biomass: A comparison of the local structure from poly- to monosaccharides and pentoses/hexoses. Green Chem. 2008, 10, 1204. [Google Scholar] [CrossRef]
  39. Baccile, N.; Laurent, G.; Babonneau, F.; Fayon, F.; Titirici, M.-M.; Antonietti, M. Structural Characterization of Hydrothermal Carbon Spheres by Advanced Solid-State MAS 13C NMR Investigations. J. Phys. Chem. C 2009, 113, 9644–9654. [Google Scholar] [CrossRef]
  40. Hao, W.; Björkman, E.; Yun, Y.; Lilliestråle, M.; Hedin, N. Iron Oxide Nanoparticles Embedded in Activated Carbons Prepared from Hydrothermally Treated Waste Biomass. ChemSusChem 2014, 7, 875–882. [Google Scholar] [CrossRef]
  41. Liu, Z.; Quek, A.; Hoekman, S.K.; Srinivasan, M.; Balasubramanian, R.; Mp, S. Thermogravimetric investigation of hydrochar-lignite co-combustion. Bioresour. Technol. 2012, 123, 646–652. [Google Scholar] [CrossRef]
  42. Liu, Z.; Quek, A.; Kent Hoekman, S.; Srinivasan, M.P.; Balasubramanian, R. Erratum to “Thermogravimetric investigation of hydrochar-lignite co-combustion” [Bioresour Technol 123 (2012) 646-652]. Bioresour. Technol. 2013, 133, 639–640. [Google Scholar] [CrossRef]
  43. Vogli, E.; Sieber, H.; Greil, P. Biomorphic SiC-ceramic prepared by Si-vapor phase infiltration of wood. J. Eur. Ceram. Soc. 2002, 22, 2663–2668. [Google Scholar] [CrossRef]
  44. Carrott, P.; Nabais, J.; Carrott, M.R.; Pajares, J.; Nabais, J.M.V. Preparation of activated carbon fibres from acrylic textile fibres. Carbon 2001, 39, 1543–1555. [Google Scholar] [CrossRef]
  45. Misnon, I.I.; Zain, N.K.M.; Aziz, R.A.; Vidyadharan, B.; Jose, R. Electrochemical properties of carbon from oil palm kernel shell for high performance supercapacitors. Electrochim. Acta 2015, 174, 78–86. [Google Scholar] [CrossRef] [Green Version]
  46. Tempesta, G.; Capitani, G.C.; Di Pierro, S. The 6H-SiC structure model: Further refinement from SCXRD data from a terrestrial moissanite. Am. Miner. 2007, 92, 403–407. [Google Scholar]
  47. Titirici, M.M.; Thomas, A.; Yu, S.-H.; Müller, J.-O.; Antonietti, M.; Titirici, M. A Direct Synthesis of Mesoporous Carbons with Bicontinuous Pore Morphology from Crude Plant Material by Hydrothermal Carbonization. Chem. Mater. 2007, 19, 4205–4212. [Google Scholar] [CrossRef]
  48. Ferrari, A.C.; Robertson, J. Interpretation of Raman spectra of disordered and amorphous carbon. Phys. Rev. B 2000, 61, 14095–14107. [Google Scholar] [CrossRef] [Green Version]
  49. Nakashima, S.; Harima, H. Raman Investigation of SiC Polytypes. Phys. Status Solidi 1997, 162, 39–64. [Google Scholar] [CrossRef]
  50. Harima, H. Raman scattering characterization on SiC. Microelectron. Eng. 2006, 83, 126–129. [Google Scholar] [CrossRef]
  51. Jamari, S.S.; Howse, J.R. The effect of the hydrothermal carbonization process on palm oil empty fruit bunch. Biomass Bioenergy 2012, 47, 82–90. [Google Scholar] [CrossRef]
  52. Falco, C.; Baccile, N.; Titirici, M.-M. Morphological and structural differences between glucose, cellulose and lignocellulosic biomass derived hydrothermal carbons. Green Chem. 2011, 13, 3273. [Google Scholar] [CrossRef]
  53. Yu, L.; Falco, C.; Howe, J.Y.; Titirici, M.-M.; Weber, J.; White, R.J. Carbohydrate-Derived Hydrothermal Carbons: A Thorough Characterization Study. Langmuir 2012, 28, 12373–12383. [Google Scholar] [CrossRef] [PubMed]
  54. Mutschke, H.; Andersen, A.C.; Clement, D.; Henning, T.; Peiter, G. Infrared properties of SiC particles. Astron. Astrophys. 1999, 345, 187–202. [Google Scholar]
Materials 12 01835 g001 550
Figure 1. SEM images of (a) hydrochar of glucose, (b) core-shell C-SiC particles, (c) the surface of a core-shell particle, (d,e) cross-sections of core-shell particles, (f) hollow particles of SiC.
Figure 1. SEM images of (a) hydrochar of glucose, (b) core-shell C-SiC particles, (c) the surface of a core-shell particle, (d,e) cross-sections of core-shell particles, (f) hollow particles of SiC.
Materials 12 01835 g001
Materials 12 01835 g002 550
Figure 2. Thermogravimetric curves of hydrochar of glucose (a), core-shell C-SiC particles (b), hollow SiC particles (c) recorded in dry air.
Figure 2. Thermogravimetric curves of hydrochar of glucose (a), core-shell C-SiC particles (b), hollow SiC particles (c) recorded in dry air.
Materials 12 01835 g002
Materials 12 01835 g003 550
Figure 3. X-ray diffractograms of hydrochar from glucose (a) and a core-shell C-SiC composite (b). The broad peaks at about 24° and 44° are typical for amorphous carbon.
Figure 3. X-ray diffractograms of hydrochar from glucose (a) and a core-shell C-SiC composite (b). The broad peaks at about 24° and 44° are typical for amorphous carbon.
Materials 12 01835 g003
Materials 12 01835 g004 550
Figure 4. TEM images of hollow spheres of SiC: (a) and (b) Bright-field TEM image showing an overview of the hollow spheres’ morphology; (c) TEM image of polycrystalline grains from which the hollow shell is formed; (d) the corresponding selected-area electron diffraction (SAED) pattern; (e) HRTEM image of a single grain showing a high density of stacking faults; (f) the corresponding fast Fourier transform.
Figure 4. TEM images of hollow spheres of SiC: (a) and (b) Bright-field TEM image showing an overview of the hollow spheres’ morphology; (c) TEM image of polycrystalline grains from which the hollow shell is formed; (d) the corresponding selected-area electron diffraction (SAED) pattern; (e) HRTEM image of a single grain showing a high density of stacking faults; (f) the corresponding fast Fourier transform.
Materials 12 01835 g004
Materials 12 01835 g005 550
Figure 5. Raman spectra of (a) hydrochar of glucose, (b) the core-shell C-SiC composite and (c) the hollow and spherical SiC particles.
Figure 5. Raman spectra of (a) hydrochar of glucose, (b) the core-shell C-SiC composite and (c) the hollow and spherical SiC particles.
Materials 12 01835 g005
Materials 12 01835 g006 550
Figure 6. IR spectra of (a) hydrochar prepared from glucose, (b) a core-shell C-SiC composite, and (c) hollow and spherical SiC particles.
Figure 6. IR spectra of (a) hydrochar prepared from glucose, (b) a core-shell C-SiC composite, and (c) hollow and spherical SiC particles.
Materials 12 01835 g006
Table
Table 1. Brunauer, Emmett and Teller (BET) surface area, bulk element composition of the hydrochar prepared from glucose (HTC), and the core-shell C-SiC composite.
Table 1. Brunauer, Emmett and Teller (BET) surface area, bulk element composition of the hydrochar prepared from glucose (HTC), and the core-shell C-SiC composite.
SampleSBET (m2/g)Ultimate (wt %)
CHNO aSi
HTC866.24.3<0.1029.5--
Core-shell-C-SiC1098.2<0.10<0.101.470.13 b 1.40 c
a calculated by difference; b estimated by elemental analysis; c estimated by TGA.

Share and Cite

MDPI and ACS Style

Hao, W.; Liu, Y.; Neagu, A.; Bacsik, Z.; Tai, C.-W.; Shen, Z.; Hedin, N. Core-Shell and Hollow Particles of Carbon and SiC Prepared from Hydrochar. Materials 2019, 12, 1835. https://doi.org/10.3390/ma12111835

AMA Style

Hao W, Liu Y, Neagu A, Bacsik Z, Tai C-W, Shen Z, Hedin N. Core-Shell and Hollow Particles of Carbon and SiC Prepared from Hydrochar. Materials. 2019; 12(11):1835. https://doi.org/10.3390/ma12111835

Chicago/Turabian Style

Hao, Wenming, Yongsheng Liu, Alexandra Neagu, Zoltan Bacsik, Cheuk-Wai Tai, Zhijian Shen, and Niklas Hedin. 2019. "Core-Shell and Hollow Particles of Carbon and SiC Prepared from Hydrochar" Materials 12, no. 11: 1835. https://doi.org/10.3390/ma12111835

APA Style

Hao, W., Liu, Y., Neagu, A., Bacsik, Z., Tai, C.-W., Shen, Z., & Hedin, N. (2019). Core-Shell and Hollow Particles of Carbon and SiC Prepared from Hydrochar. Materials, 12(11), 1835. https://doi.org/10.3390/ma12111835

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop