Search Results (7)

Carbon is predominantly used in zinc-ion hybrid capacitors (ZIHCs) as an electrode material. Nitrogen doping and strategic design can enhance its electrochemical properties. Melamine formaldehyde resin, serving as a hard carbon precursor, synthesizes nitrogen-doped porous carbon after annealing. Incorporating transition metal catalysts like Ni, Co, and Fe alters the morphology, pore structure, graphitization degree, and nitrogen doping types/proportions. Electrochemical tests reveal a superior capacitance of 159.5 F g⁻¹ at a scan rate of 1 mV s⁻¹ and rate performance in Fe-catalyzed N-doped porous carbon (Fe-NDPC). Advanced analysis shows Fe-NDPC’s high graphitic nitrogen content and graphitization degree, boosting its electric double-layer capacitance (EDLC) and pseudocapacitance. Its abundant micro- and mesopores increase the surface area fourfold compared to non-catalyzed samples, favoring EDLC and fast electrolyte transport. This study guides catalyst application in carbon materials for supercapacitors, illuminating how catalysts influence nitrogen-doped porous carbon structure and performance. Full article

Aqueous zinc-ion hybrid capacitors (ZIHCs) have emerged as a promising technology, showing superior energy and power densities, as well as enhanced safety, inexpensive and eco-friendly features. Although ZIHCs possess the advantages of both batteries and supercapacitors, their energy density is still unsatisfactory. Therefore, it is extremely crucial to develop reasonably matched electrode materials. Based on this challenge, a surge of studies has been conducted on the modification of carbon-based electrode materials. Herein, we first summarize the progress of the related research and elucidate the energy storage mechanism associated with carbon-based electrodes for ZIHCs. Then, we investigate the influence of the synthesis routes and modification strategies of the electrode materials on electrochemical stability. Finally, we summarize the current research challenges facing ZIHCs and predict potential future research pathways. In addition, we suggest key scientific questions to focus on and potential directions for further exploration. Full article

Zinc-ion hybrid capacitors (ZICs) can achieve high energy and power density, ultralong cycle life, and a wide operating voltage window, and they are widely used in wearable devices, portable electronics devices, and other energy storage fields. The design of advanced ZICs with high specific capacity and energy density remains a challenge. In this work, a novel kind of V, N dual-doped Ti₃C₂ film with a three-dimensional (3D) porous structure (3D V-, N-Ti₃C₂) based on Zn-ion pre-intercalation can be fabricated via a simple synthetic process. The stable 3D structure and heteroatom doping provide abundant ion transport channels and numerous surface active sites. The prepared 3D V-, N-Ti₃C₂ film can deliver unexpectedly high specific capacitance of 855 F g⁻¹ (309 mAh g⁻¹) and demonstrates 95.26% capacitance retention after 5000 charge/discharge cycles. In addition, the energy storage mechanism of 3D V-, N-Ti₃C₂ electrodes is the chemical adsorption of H⁺/Zn²⁺, which is confirmed by ex situ XRD and ex situ XPS. ZIC full cells with a competitive energy density (103 Wh kg⁻¹) consist of a 3D V-, N-Ti₃C₂ cathode and a zinc foil anode. The impressive results provide a feasible strategy for developing high-performance MXene-based energy storage devices in various energy-related fields. Full article

Manganese-based materials have received more attention as cathodes for aqueous zinc ion hybrid capacitors (AZIHCs) due to their advantages such as abundant reserves, low cost, and large theoretical capacity. However, manganese-based materials have the disadvantage of poor electrical conductivity. Herein, a solid-phase method was used to synthesize a hierarchical carbon-coated calcium manganate (CaMn₂O₄/C) network framework as the cathode for AZIHCs. Thanks to the unique structural/componential merits including conductive carbon coating and hierarchical porous architecture, the achieved CaMn₂O₄/C cathode shows an exceptionally long life of close to 5000 cycles at 2.0 A g⁻¹, with a reversible specific capacity of 195.6 mAh g⁻¹. The assembled CaMn₂O₄/C-based AZIHCs also display excellent cycling stability with a capacity retention rate of 84.9% after 8000 cycles at 1.0 A g⁻¹, and an energy density of 21.3 Wh kg⁻¹ at an output power density of 180.0 W kg⁻¹. Full article

With the merits of having excellent safety, being low cost and being environmentally friendly, zinc-ion hybrid supercapacitors (ZHSCs) are expected to be widely used in large-scale energy storage and flexible wearable devices. However, limited by their sluggish kinetic process, ZHSCs suffer from low-specific capacity and poor cycling stability at high cathode mass loading. Herein, a novel designed oxygen-rich hierarchical porous carbon (HPOC) is obtained by a one-step strategy of synchronous activation and templated for high-performance ZHSCs. The fabricated ZHSCs with HPOCs show significant improvement in Zn-ion storage capability, with a capacity of 209.4 mAh g⁻¹ at 0.1 A g⁻¹ and 108.3 mAh g⁻¹ at 10 A g⁻¹. Additionally, the cycling stability is excellent, with 92.3% retention after 4000 cycles. Furthermore, an impressive areal capacity of 1.7 mAh cm⁻² is achieved, even with a high mass loading of 12.5 mg cm⁻². More importantly, the flexible quasi-solid state ZHSCs also show a considerable capability (183.5 mAh g⁻¹ at 0.1 A g⁻¹) and a high energy density of 178.0 Wh kg⁻¹. This promising result suggests a valuable route to produce functional nanocarbon materials for zinc storage applications. Full article

The great interest in developing emerging zinc-ion capacitors (ZIC) for energy storage applications is due to their inexpensiveness and the future necessity for hybrid electrical energy storage devices. The Zn-ion hybrid capacitor device was assembled using boron (B)-doped reduced graphene oxide (B-RGO) material, which acts as the cathode, and pure zinc metal as an anode. This research work aims to study the influence of B-doped reduced graphene oxide (B-RGO) with Aloe vera gel as an electrolyte. The reduced graphene oxide (RGO) and B-RGO electrode active materials were confirmed through X-ray diffraction (XRD), RAMAN, Fourier transformation infrared spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS), field emission scanning electron microscopy (FE-SEM) and field emission-transmission electron microscopy (FE-TEM) analysis. The surface morphological images reveal that a few-layered nanostructure B-RGO was used in the Zn-ion hybrid capacitor device. The electrochemical performance of the Zn-ion hybrid capacitor was evaluated through cyclic voltammetry (CV) and galvanostatic charge–discharge (GCD) measurements, with a wide active potential range of 0–2 V versus Zn/Zn⁺. The mixture composition of Aloe vera extract and 1M ZnSO₄ electrolyte generated a stable voltage and exhibited good capacitive behavior. The fabricated ZIC coin cell device with the Aloe vera gel semi-gel electrolyte containing ZnSO₄ demonstrated improved Zn⁺ ionic exchange and storage efficiency. Moreover, the B-RGO electrode active material exhibited excellent cycle stability. The simple one-step electrochemical technique is the most suitable process for boron doping into graphene nanosheets for future energy storage applications. Full article

The hybrid ion capacitor (HIC) is a hybrid electrochemical energy storage device that combines the intercalation mechanism of a lithium-ion battery anode with the double-layer mechanism of the cathode. Thus, an HIC combines the high energy density of batteries and the high power density of supercapacitors, thus bridging the gap between batteries and supercapacitors. Two-dimensional (2D) carbon materials (graphite, graphene, carbon nanosheets) are promising candidates for hybrid capacitors owing to their unique physical and chemical properties, including their enormous specific surface areas, abundance of active sites (surface and functional groups), and large interlayer spacing. So far, there has been no review focusing on the 2D carbon-based materials for the emerging post-lithium hybrid capacitors. This concept review considers the role of 2D carbon in hybrid capacitors and the recent progress in the application of 2D carbon materials for post-Li (Na⁺, K⁺, Zn²⁺) hybrid capacitors. Moreover, their challenges and trends in their future development are discussed. Full article