Search Results (3)

To address anisotropy challenges in electric arc-based additive manufacturing of Inconel 718 alloy, this study develops a novel wire feeding oscillated double-pulsed gas tungsten arc welding additive manufacturing method (DP-GTA-AM) enabling precise thermal-mass transfer control. Series of crack-free thin-walled Inconel 718 alloy parts were successfully obtained by this proposed approach, and the microstructure and mechanical properties of the parts were thoroughly studied. The results indicate that the microstructure changes from dendrites and cellular crystals in the bottom to equiaxed grains in the midsection and entirely equiaxed crystals in the top, resulting in notable grain refinement. With an average grain size of 61.76 μm and an average length of 83.31 μm of large angle grain boundaries, the density of the <001> direction reaches 19.45. The difference in tensile strength and ductility between the horizontal and the vertical directions decreases to 6.3 MPa and 0.38%, which significantly diminishes anisotropy. Fractographic analysis confirms quasi-cleavage failure with homogeneous dimple distribution, demonstrating effective anisotropy mitigation through controlled solidification dynamics. Full article

Vertical oscillation arc welding for narrow gap gas metal arc welding (NG-GMAW) has a relatively simple structure, and it is widely used in all-position pipeline field welding. However, it has some shortcomings, such as incomplete fusion defects on the sidewall and interlayer. Aiming at resolving these shortcomings, a mathematical model is proposed to obtain appropriate welding parameters in different positions. In this model, the response surface methodology (RSM) based on the central composite design (CCD) was developed to study the interactions between welding parameters and the weld bead geometry. Then the analysis of variance (ANOVA) was used to evaluate the accuracy and significance of the proposed model. Finally, experiments were carried out in flat, vertical, and overhead positions to obtain the optimal parameters. The macroscopic metallography of the transversal section of the weld bead under the optimizing welding parameters showed that the weld beads were free of defects in the sidewall and interlayers. Full article

In fields, such as oil and gas pipelines and nuclear power, narrow-gap welding has often been used for the connection of thick and medium-thick plates. During the welding process, a lack of fusion was prone to occur due to groove size limitations, seriously affecting the service safety of large structures. The vertical oscillation arc pulsed gas metal arc welding (P-GMAW) method was adopted for narrow-gap welding in this study. The influence of the oscillation width on arc morphology, droplet transfer behavior and weld formation during narrow-gap welding was studied. Oscillation widths from 0 to 4 mm were used to weld narrow-gap grooves with a bottom width of 6 mm. The results show that, in non-oscillation arc welding, the arc always presented a bell cover shape, and the droplet transfer was in the form of one droplet per pulse, while the sidewall penetration of the weld was relatively small, making it prone to a lack of fusion. With an increase in the oscillation width, the arc gradually shifted to the sidewall. The droplet transfer mode was a mixed transfer of large and small droplets, and the sidewall penetration continued to increase, which was conducive to the fusion of the sidewall. However, when the oscillation width was wider than 3 mm, it led to the phenomenon of the arc climbing to the sidewall, and the weld was prone to porosity, undercutting and other welding defects. The oscillation width has a major impact on the stability of the welding process in vertical oscillation arc narrow-gap welding. Full article