Search Results (3)

In the present work, the development of geopolymeric materials with Na or K based on industrial kaolin samples, with variable kaolinite content and alkaline silicates, is studied. XRF, XRD, FTIR and SEM-EDS have been used as characterization techniques. Three ceramic kaolin samples, two from Algeria and one from Charente (France), have been considered. In particular, chemical and mineralogical characterization revealed elements distinct of Si and Al, and the content of pure kaolinite and secondary minerals. Metakaolinite was obtained by grinding and sieving raw kaolin at 80 μm and then by thermal activation at 750 °C for 1 h. This metakaolinite has been used as a base raw material to obtain geopolymers, using for this purpose different formulations of alkaline silicates with NaOH or KOH and variable Si/K molar ratios. The formation of geopolymeric materials by hydroxylation and polycondensation characterized with different Si/Al molar ratios, depending on the original metakaolinite content, has been demonstrated. Sodium carbonates have been detected by XRD and FTIR, and confirmed by SEM-EDS, in two of these geopolymer materials being products of NaOH carbonation. Full article

Lime-sand bricks of different ages were investigated using IR-spectroscopy, thermogravimetry, and X-ray diffraction/scattering. After subtraction of the dominant quartz contribution (80%), the IR spectra show the absorption peaks of the hydrothermally formed binder phases. The spectra also show the alteration of the binder during ageing under atmospheric conditions by the influence of CO₂ forming carbonate and a condensed SiO₂-gel (secondary gel). The alteration could also be proven in X-ray pattern, obtaining a separation between crystalline CSH and amorphous contributions in the freshly produced lime-sand brick, too. Here, the formation of CSH_amorph could be understood as a precursor state (primary gel) to the crystallization of CSH phases. X-ray patterns of aged bodies of alkali-silicate solution activated slags (AAS), CEM-I/CEM-III pastes, and CEM-I concrete indicate that in all cases a similar amorphous CSH-type phase (CSH_amorph) was formed, which is responsible for the hardening properties as the glue. The main X-ray peak of CSH_amorph obtained using CuK_α-radiation with a usual diffractometer is observed between 24° and 35° 2 Theta with maximum at about 29° 2 Theta, whereas it appears much more broadly distributed between 15° and 35° 2 Theta with maximum between 26° and 28° 2 Theta for a geopolymer body prepared using the reaction of alkali-silicate solution and metakaolin (AAMK). This is due to the network formed by siloxo and sialate units in the case of AAMK, given that any crystallization can be ruled out. The origin of increasing mechanical strength during the ageing of AAS mortars must be due to further crosslinking of the preformed siloxo chains. Thermal treatment up to 800 °C leads to a complete loss of any mechanical strength of the CEM pastes due to the destruction of crystalline CSH-phases, whereas geopolymer bodies maintain their strength. Implications for next generation concrete include that cement clinker could be completely replaced by using a using alkali silcate solution technology for gel formation. Full article

Geopolymers are zeolites like structures based on hydrated aluminosilicates units of SiO₄ and AlO₄. These units, known as poly(sialate), poly(sialate)-siloxo or poly(sialate)-disiloxo are chemically balanced by the group I cations of K⁺, Li⁺, or Na⁺. Simultaneously, the chemical reaction of formation, known as geopolymerization, governs the orientation of the unit, generating mesoporous structures. Multiple methods can be used for pore structure and porosity characterization. Among them, nuclear magnetic resonance (NMR) relaxometry allows the detection of the porous structure in a completely nonperturbative manner. NMR relaxometry may be used to monitor the relaxation of protons belonging to the liquid molecules confined inside the porous structure and, thus, to get access to the pore size distribution. This monitoring can take place even during the polymerization process. The present study implements transverse relaxation measurements to monitor the influence introduced by the curing time on the residual liquid phase of geopolymers prepared with two different types of reinforcing particles. According to our results, the obtained geopolymers contain three types of pores formed by the arrangement of the OH⁻ and Si groups (Si-OH), Si-O-Si groups, Si-O-Al groups, and Si-O rings. After 48 days, the samples cured for 8 h show a high percentage of all three types of pores, however, by increasing the curing time and the percentage of reinforcing particle, the percent of pores decrease, especially, the gel pores. Full article