Search Results (5)

Passive NOx adsorber (PNA) is one of the important means to effectively reduce NOx emission control in the cold start of a diesel engine. A series of Pd/SSZ-13 catalysts with different SiO₂/Al₂O₃ ratios (11, 17, and 25) were prepared using the impregnation method. Furthermore, the effect of the SiO₂/Al₂O₃ ratio on the adsorption performance of Pd/SSZ-13 at low-temperature NOx under realistic exhaust conditions was studied. The results show that the Pd/SSZ-13 catalyst with a low SiO₂/Al₂O₃ ratio after loading Pd has a higher specific surface area and palladium ion content. There is a negative correlation between NOx adsorption performance and the SiO₂/Al₂O₃ ratio. After high-temperature heat treatment, the acid sites closely related to palladium species increase and palladium species will redisperse, producing more palladium ions. The palladium ions coexist in Pd/SSZ-13 in the form of Pd²⁺ and Pd⁺, among which Pd²⁺ is divided into two types: Z⁻Pd²⁺Z⁻ and Z⁻[Pd(II)OH]⁺. The NOx adsorption performance of the Pd/SSZ-13 catalyst was significantly improved, and the higher the SiO₂/Al₂O₃ ratio, the more obviously the advantage of NOx adsorption performance increased after heat treatment. The NOx adsorption kinetic model of the Pd/SSZ-13 catalyst under realistic exhaust conditions was most suitably described by the pseudo-first-order model. Full article

At present, passive NO_x adsorbers (PNAs) represent one of the most effective technologies for addressing NO_x emissions from diesel engines during cold-start periods. Conventional PNAs, which primarily consist of noble metals (such as Pt, Pd, and Ag) loaded on metal oxides or zeolites, share the common drawback of high production costs. Consequently, developing low-cost PNAs with outstanding NO_x storage performance remains a significant challenge. In this study, a series of CuxBa5Ce adsorbents were synthesized using the impregnation method, and a monolithic adsorbent was employed to evaluate NO_x storage and release performance. Techniques such as XRD, UV-Vis DRs, H₂-TPR, XPS, and in situ DRIFTs confirmed the crucial roles of Cu and Ba in NO_x storage and release. Specifically, the incorporation of Cu into CeO₂ enhanced NO_x storage performance. Moreover, in the Cu3Ba5Ce adsorbent, the addition of Ba not only introduced new storage sites and altered the stability of NO_x adsorption species but also helped prevent the aggregation of CuO, thereby prolonging the complete NO_x storage duration and satisfying desorption temperature requirements. The Cu3Ba5Ce adsorbent exhibited the most favorable NO_x storage performance, including a complete NO_x storage time of 135 s and a NO_x storage efficiency exceeding 50% at 80 °C over a 10 min period. While PNAs loaded with noble metals, such as Pd/CeO₂ and Pt/CeO₂, exhibited NO_x storage efficiencies below 50% after adsorbing for 5 min at 80 °C. Therefore, this research offered a crucial strategy for developing non-noble-metal-loaded, Ce-based PNAs. Full article

In the current article, the effect of Si/Al ratio on the NO_x adsorption and storage capacity over Pd/Beta with 1 wt% Pd loading was investigated. The XRD, ²⁷Al NMR and ²⁹Si NMR measurements were used to determine the structure of Pd/Beta zeolites. XAFS, XPS, CO-DRIFT, TEM and H₂-TPR were used to identify the Pd species. The results showed that the NO_x adsorption and storage capacity on Pd/Beta zeolites gradually decreased with the increase of Si/Al ratio. Pd/Beta-Si (Si-rich, Si/Al~260) rarely has NO_x adsorption and storage capacity, while Pd/Beta-Al (Al-rich, Si/Al~6) and Pd/Beta-C (Common, Si/Al~25) exhibit excellent NO_x adsorption and storage capacity and suitable desorption temperature. Pd/Beta-C has slightly lower desorption temperature compared to Pd/Beta-Al. The NO_x adsorption and storage capacity increased for Pd/Beta-Al and Pd/Beta-C by hydrothermal aging treatment, while the NO_x adsorption and storage capacity on Pd/Beta-Si had no change. Full article

The passive NO_x adsorber (PNA) material has been considered an effective candidate for the control of NO_x from diesel exhaust during the engine cold start stage, and Pd/SSZ-13 attracts peoples’ attention mainly due to its superior hydrothermal stability and sulfur resistance. However, chemical poisoning tolerance of Pd/SSZ-13 is another key parameter to its practical application and future development. Herein, we prepared potassium-loaded Pd/SSZ-13 and evaluated the influence on NO_x adsorption ability. The characterization results revealed that the loading of potassium could not destruct the structure of SSZ-13 but impaired the BET surface area and pore structure through the sintering of Pd species to PdO. Meanwhile, the grown PdO phase restrained the NO_x adsorption ability and promoted the generation of NO₂ at high temperatures. Moreover, the presence of H₂O could also impair the NO_x adsorption ability due to the competitive adsorption between H₂O and NO_x. This work verifies that the design of Pd/SSZ-13 sample with stable Pd species and excellent hydrophobicity is significant for its further application under harsh conditions. Full article

An industry-defined evaluation protocol was used to evaluate the hydrocarbon trapping (HCT) and passive NOx adsorption (PNA) potential for BEA, ZSM-5, and SSZ-13 zeolites with ion-exchanged Pd or Ag. All materials underwent 700 °C degreening prior to exposure to an industry-derived protocol gas stream, which included NOx, ethylene, toluene, and decane as measured trapping species as well as common exhaust gasses CO, H₂O, O₂, CO₂, and H₂. Evaluation showed that BEA and ZSM-5 zeolites were effective at trapping hydrocarbons (HCs), as saturation was not achieved after 30 min of exposure. SSZ-13 also stored HCs but was only able to adsorb 20–25% compared to BEA and ZSM-5. The presence of Ag or Pd did not impact the overall HC uptake, particularly in the first three minutes. Pd/zeolites had significantly lower THC release temperature, and it aided in the conversion of the released HCs; Ag only had a moderate effect in both areas. With respect to NOx adsorption, the level of uptake was much lower than HCs on all samples, and Ag or Pd was necessary with Pd being notably more effective. Additionally, only Pd/ZSM-5 and Pd/SSZ-13 continue to store a portion of the NOx above 200 °C, which is critical for downstream selective catalytic NOx reduction (SCR). Hydrothermal aging (800 °C for 50 h) of a subset of the samples were performed: BEA, Pd/BEA, ZSM-5, Pd/ZSM-5, and Pd/SSZ-13. There was a minimal effect on the HC storage, ~10% reduction in capacity with no effect on release temperature; however, only Pd/SSZ-13 showed significant NOx storage after aging. Full article