Search Results (3)

The heterogeneous and recalcitrant structure of lignin hinders its practical application. Here, we describe how new approaches to lignin characterization can reveal structural details that could ultimately lead to its more efficient utilization. A suite of methods, which enabled mass balance closure, the evaluation of structural features, and an accurate molecular weight (MW) determination, were employed and revealed unexpected structural features of the five alkali lignin fractions obtained with preparative size-exclusion chromatography (SEC). A thermal carbon analysis (TCA) provided quantitative temperature profiles based on sequential carbon evolution, including the final oxidation of char. The TCA results, supported with thermal desorption/pyrolysis gas chromatography–mass spectrometry (TD-Py-GC-MS) and ³¹P NMR spectroscopy, revealed the unfolding of the lignin structure as a result of the SEC fractionation, due to the disruption of the interactions between the high- and low-MW components. The “unraveled” lignin revealed poorly accessible hydroxyl groups and showed an altered thermal behavior. The fractionated lignin produced significantly less char upon pyrolysis, 2 vs. 47%. It also featured a higher occurrence of low-MW thermal evolution products, particularly guaiacol carbonyls, and more than double the number of OH groups accessible for phosphitylation. These observations indicate pronounced alterations in the lignin intermolecular association following size-exclusion fractionation, which may be used for more efficient lignin processing in biorefineries. Full article

Lignin is a raw material that can potentially be converted into valuable compounds through depolymerization reactions in addition to its use as a polymer or material. However, the chemical recalcitrance and the heterogeneous composition and structure of lignin make it challenging to establish processes that add value to this complex aromatic biopolymer. In this work, solvent fractionation was applied to obtain lignin fractions with a narrowed molecular weight and specific structural characteristics, improving its homogeneity and purity. A kraft lignin was submitted to fractionation using different ratios of acetone, ranging from 60 to 15% v/v, in aqueous mixtures. The composition, structure, and molecular weight of each fraction were studied and their potential applications were evaluated. The most water-soluble fraction has more phenolic OH, less aliphatic OH groups, and shows the lowest content of aryl-ether linkages, which is in accordance with its highest degree of condensation. On the other hand, the insoluble fraction from the mixture with 60% of acetone has the lowest molecular weight and the highest content of inorganic material. Radar plots were applied for lignin fractions evaluation and the fraction with the highest potential (IF 30:70) was submitted to alkaline oxidation with O₂. The results were compared with the products yielded from kraft lignin. An increase of about 13 and 19% was found for vanillin and syringaldehyde, respectively, when the fraction IF 30:70 was submitted to oxidation. In conclusion, the proposed fractionation process showed to be an effective method to obtain lignin fractions with specific composition and structural characteristics that could improve its potential as a source of high added-value monomeric phenolic compounds. Full article

The extraction and characterization of defined and carboxyl-rich oligomeric lignin fragments with narrow molecular weight distribution is presented herein. With regard to the well-known pulp bleaching process, oxidative lignin depolymerization was investigated using hydrogen peroxide in an aqueous alkaline solution (i.e., at T = 318 K, t = 1 h) and subsequent selective fractionation with a 10/90 (v/v) acetone/water mixture. While the weight average molecular weight (M_W) of lignin in comparison to the starting material was reduced by 82% after oxidation (T = 318 K, t = 1 h, c_lignin = 40 g L⁻¹, c_H2O2 = 80 g L⁻¹, c_NaOH = 2 mol L⁻¹) and subsequent solvent fractionation (T = 298 K, t = 18 h, c_{cleavage product} = 20 g L⁻¹), the carboxyl group (–COOH) content increased from 1.29 mmol g⁻¹ up to 2.66 mmol g⁻¹. Finally, the successful scale-up of this whole process to 3 L scale led to gram amounts (14% yield) of oligomeric lignin fragments with a M_W of 1607 g mol⁻¹, a number average molecular weight (M_N) of 646 g mol⁻¹, a narrow polydispersity index of 3.0, and a high –COOH content of 2.96 mmol g⁻¹. Application of these oligomeric lignin fragments in epoxy resins or as adsorbents is conceivable without further functionalization. Full article