Search Results (2)

A sputtered FePt(BN, Re, C) film, here boron nitride (BN), was compared to a reference sample FePt(BN, Ag, C). Intrinsically, these films illustrate a high anisotropy field (H_k) and perpendicular magnetocrystalline anisotropy (K_u),although the reference sample shows a higher value (H_k = 69.5 kOe, K_u = 1.74 × 10⁷ erg/cm³) than the FePt(BN, Re, C) film (H_k = 66.9 kOe, K_u = 1.46 × 10⁷ erg/cm³). However, the small difference in the anisotropy constant (K2/K1) ratio presents a close tendency in the angular dependence of the switching field. Extrinsically, the out-of-plane coercivity for the reference sample is 32 kOe, which is also higher than the FePt(BN, Re, C) film (H_c = 27 kOe), and both films present lower remanence (Mr_(parallel)/Mr_{(perpendicular)} = 0.08~0.12), that is, the index for perpendicular magnetic anisotropy. The higher perpendicular magnetization for both films was due to highly (001) textured FePt films, which was also evidenced by the tight rocking width of 4.1°/3.0° for (001)/(002) X-ray diffraction peaks, respectively, and high-enough ordering degree. The reference sample was measured to have a higher ordering degree (S = 0.84) than FePt(BN, Re, C) (S = 0.63). As a result, the Ag segregant shows stronger ability to promote the ordering of the FePt film; however, the FePt(BN, Re, C) film still has comparable magnetic properties without Ag doping. From the surface and elemental composition analysis, the metallic Re atoms found in the FePt lattice result in a strong spin–orbital coupling between transition metal Fe (3d electron) and heavy metals (Re, Pt) (5d electron) and we conducted high magnetocrystalline anisotropy (K_u). Above is the explanation that the lower-ordered FePt(BN, Re, C) film still has high-enough Ku and out-of-plane Hc. Regarding the microstructure, both the reference sample and FePt(BN, Re, C) show granular structure and columnar grains, and the respective average grain size and distributions are 6.60 nm (12.5%) and 11.2 nm (15.9%). The average widths of the grain boundaries and the aspect ratio of the columnar grain height are 2.05 nm, 1.00 nm, 2.35 nm, and 1.70 nm, respectively. Full article

A comparative study of the magnetic properties of the arrays of Co nanowires and nanotubes with large external diameters (180 nm) has been carried out. The nanowires/nanotubes were grown by electrodeposition into the self-assembled pores of anodic alumina membranes. The experimental study of their magnetic behavior was focused on the angular dependence of hysteresis loops and their parameters. In both nanowire and nanotube arrays, from the analysis of experimental data, effective longitudinal magnetic anisotropy is concluded, which is stronger in the case of the nanotube array. In addition, the extremely small remanence observed for all loops indicates the important role played by magnetostatic interactions. Micromagnetic simulations were first performed considering intrinsic shape and magnetocrystalline anisotropy terms, together with an effective easy-plane anisotropy to account for those magnetostatic interactions. A qualitative agreement between experiments and simulations is found despite the complexity introduced by the intrinsic and extrinsic array properties (i.e., large diameters, grain structure, and array configuration). In addition, simulations were also carried out for individual nanowire/nanotube with a particular emphasis to understand their differences at the remanence, due to pure geometry contribution. Full article