Next Article in Journal
Combination of Multiple Operando and In-Situ Characterization Techniques in a Single Cluster System for Atomic Layer Deposition: Unraveling the Early Stages of Growth of Ultrathin Al2O3 Films on Metallic Ti Substrates
Previous Article in Journal
The Cryptic Nature of Fe-S Clusters: A Case Study of the Hepatitis B HBx Oncoprotein
Previous Article in Special Issue
Electrolytes in Multiple-Phase Hydrogen Storage Reactions
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Editorial

State-of-the-Art and Progress in Metal-Hydrogen Systems

by
Terry D. Humphries
1,*,
Craig E. Buckley
1,
Mark Paskevicius
1 and
Torben R. Jensen
2
1
Physics and Astronomy, Curtin University, GPO Box U1987, Perth, WA 6845, Australia
2
Interdisciplinary Nanoscience Center and Department of Chemistry, Aarhus University, DK-8000 Aarhus C, Denmark
*
Author to whom correspondence should be addressed.
Inorganics 2023, 11(12), 476; https://doi.org/10.3390/inorganics11120476
Submission received: 14 November 2023 / Accepted: 4 December 2023 / Published: 11 December 2023
(This article belongs to the Special Issue State-of-the-Art and Progress in Metal-Hydrogen Systems)

1. Introduction

Hydrogen is heralded as a future global energy carrier [1,2,3,4,5,6,7,8,9]. The development of hydrogen as a clean energy solution is gaining unprecedented global attention, as many countries are now recognising its potential in various applications and including hydrogen in its energy portfolio. This includes stationary, portable, and transport use today, including hydrogen fuel cell vehicles, trains, and ferries. However, hydrogen storage remains a critical challenge in expanding infrastructure for hydrogen-based transportation and industrial utilisation.
Metal hydrides have received much interest over the past several decades, which is evident from a previous related Special Issue published in Inorganics: “Functional Materials Based on Metal Hydrides” [10]. Reversible solid-state hydrogen storage at ambient conditions with moderate energy exchanges with the surroundings is the ultimate challenge to realise a hydrogen-based society. Varieties of novel hydrogen-rich materials have been investigated in the past decades, which has provided many novel compositions, fascinating structures, and functionalities [8,11,12,13,14]. Today, metal hydrides are explored for a range of applications, including hydrogen exports, remote area power systems, solid-state batteries, thermochemical energy storage, and hydrogen diffusion [15,16,17,18,19,20,21,22,23]. Indeed, the International Energy Agency (IEA) is involved in the development of hydrogen and hydrogen storage materials, where Task 40 “Energy Storage and conversion based on hydrogen” has recently released a number of review articles on the research being conducted in this area [24,25,26,27,28,29,30].
The aim of this Special Issue of Inorganics, entitled “State-of-the-Art and Progress in Metal-Hydrogen Systems”, is to inspire continued research within this important class of materials, in particular for energy-related applications. This Special Issue also serves as a collection of contributions presented at the International Symposium on Metal-Hydrogen Systems, held in Perth, Western Australia, 30 October–3 November 2022 [31]. This meeting, MH2022, is the 17th meeting in a distinguished series of conferences dating back to 1968. This conference was due to be held in 2020; however, COVID forced it to be postponed to 2022. The conference Chair was Prof. Craig Buckley, and the Vice-Chair was Assoc. Prof. Mark Paskevicius, both from Curtin University, Australia. MH2022 had a total of 159 participants from 22 countries. Five plenary talks were presented by Prof. Ping Chen (Dalian Institute of Chemical Physics, Chinese Academy of Sciences), Prof. Petra E de Jongh (Utrecht University, The Netherlands), Prof. Evan Gray (Griffith University, Australia), Dr Patrick Hartley (CSIRO, Australia), and Dr Michael Hirscher (Max Planck Institute for Intelligent Systems, Germany). There were 40 invited and 87 contributed talks and 30 posters on the topic of the fundamentals and applications of metal–hydrogen systems. The contributions covered a wide range of materials topics, including complex hydrides, metal hydrides, and chemical, organic, and nanoporous materials.
The Guest Editors would like to sincerely thank the Scientific Program Committee members for MH2022, the Local Organizing Committee, and the MH series International Steering Committee for their help in planning and successfully organizing the symposium. We gratefully acknowledge the sponsors and supporting partners of MH2022: Curtin University, The Australian Renewable Energy Agency (ARENA), Toyota, and the exhibitors Anton Paar, Hidden Analytical, Hidden Isochema, John Morris Group, and Suzuki Shokan. Furthermore, the Guest Editors would like to thank all the reviewers who spent their valuable time thoroughly reviewing and improving the articles published in this Special Edition.

2. An Overview of Published Articles

As expressed above, the field of metal hydrides is diverse, and this is exemplified by the varied topics covered in the 14 articles published in this Special Edition. This section provides a brief overview of the included manuscripts, of which they are divided into discreet, albeit cross-cutting, subsections that include: Hydrogen Release and Uptake, Electrolytes, Physical Properties, and Metallic Alloys.

2.1. Hydrogen Release and Uptake

Varieties of novel hydrogen containing compounds with fascinating compositions and structures are continually discovered [1,13,32,33,34,35,36,37], well-illustrated by the Na[BH3(CH3NH)BH2(CH3NH)BH3] material presented by Zhang et al. (in contribution 1). This compound releases 4.6 wt.% of pure hydrogen below 150 °C contrary to the parent counterpart Na[BH3NH2BH2NH2BH3]. This work illustrates a new route to suppress the release of unwanted gaseous by-products by the introduction of organic methyl groups bonded to nitrogen.
Lithium and sodium borohydride, LiBH4 and NaBH4, are known to possess high gravimetric and volumetric hydrogen densities of 18.5 and 10.6 wt.% and 121 and 113 kg·m−3, respectively [37,38,39,40,41,42,43]. However, their high thermal stabilities hamper utilisation as hydrogen storage materials for practical applications. Interestingly, F. Peru et al. investigated the composite 0.71LiBH4–0.29NaBH4 with a eutectic melting point of 219 °C, which allows convenient melt infiltration into a nanoporous carbon material (CMK-3) with a pore size of ~5 nm (contribution 2) [44]. This material reveals an uptake of ~3.5 wt.% H2 after five hydrogenation/dehydrogenation cycles facilitated by carbon–hydride surface interactions and possibly enhanced heat transfer.
Magnesium hydride, MgH2, has attracted much attention during the last few decades owing to a high hydrogen content of 7.6 wt.% and possesses good reversibility [23,24,45,46,47,48]. However, hydrogen release and uptake occur at temperatures higher than 300 °C and with slow kinetics. The third and fourth paper contributed to this collection reveals new strategies for improving both kinetic and thermodynamic properties of magnesium hydride. Huang et al. (contribution 3) demonstrated that the operating temperature for pristine MgH2 can be decreased from 322 to 214 °C through the employment of Ti3CN. Furthermore, the hydrogen-release kinetics of MgH2 are also improved, as observed by a decrease in activation energy from 121 to 80 kJmol−1 for the release of hydrogen. Another strategy, developed by Qin et al. (contribution 4), is to use hydrogen-containing additives such as lithium borohydride in magnesium hydride. A new composite of MgH2-LiBH4 (5 wt%) released ~7.1 wt.% H2 within 40 min at 300 °C, where a reference sample of MgH2 only released <0.7 wt.% H2. Importantly, the kinetics of hydrogen release are improved by a factor of ten (×10) compared to that of the pure MgH2 material. This effect is suggested to be due to the creation of ion transfer channels, which can inhibit the agglomeration of MgH2 particles.
TiFe is a well-established hydrogen storage material due to its low cost, elemental abundance, and near-ambient temperature and mild pressure for hydrogen absorption [15,49]. This makes it perfect for stationary applications [50]. The main hindrance is the difficulty to activate the material for the absorption of hydrogen in the first cycle, where high pressures of ~50 bar and high temperatures of ~400 °C are often required. Contribution five by Sartori, Amati, and Gregoratti et al. studied the influence of adding 4 wt.% Zr to the material and found that the kinetics of the first hydrogenation are greatly improved. The authors employed scanning photoemission microscopy to investigate the composition and chemical state of the various phases present in this alloy and how they change upon hydrogenation/dehydrogenation and found the presence of different oxide phases that were not seen by conventional SEM investigation.

2.2. Electrolytes

Recently, a variety of new complex hydride-based electrolytes were discovered [51,52,53,54,55,56]. They deviate from classical ionic compounds by offering high cationic conductivity at moderate temperatures, also with divalent cations. The high cationic conductivity is often assigned to weak interactions, such as dihydrogen bonds, providing structural flexibility [26,57]. A new example is magnesium borohydride, templated by isopropylamine, Mg(BH4)2∙(CH3)2CHNH2, which also has hydrophobic domains, presented by Kristensen et al. (contribution 6). Aluminium oxide nanoparticles and heat treatment produce a highly conductive composite, σ(Mg2+) = 2.86 × 10−7 and 2.85 × 10−5 S cm−1 at −10 and 40 °C, respectively, with a low activation energy, Ea = 0.65 eV. Nanoparticles stabilise the partially eutectic molten state and prevent recrystallisation even at low temperatures and provide a high mechanical stability of the composite.
Electrochemical reactions taking place in a solid-state battery cell can be considered multi-phase reactions taking place at interfaces, involving cationic diffusion in the solid state [26,58]. Hydrogen storage systems based on complex hydrides, such as metal borohydrides or metal alanates, reveal similarities. In both cases, multiple solid phases nucleate and grow or are consumed as hydrogen is released or stored or electrochemical reactions take place in a battery. These reactions are limited by the kinetics of atoms or ion diffusion at grain boundaries in the solid state and also by solid state transformations. Thus, Vajo and co-workers (contribution 7) proposed to explore these challenges by investigating combined electrolytes and hydrogen storage systems. This includes the use of eutectic molten composites. An increase in reaction rates was observed in several cases, but the kinetics may become more complex. A reduction in reaction temperature may be observed, but the results also suggest that electrolytes improve intraparticle transport phenomena.

2.3. Metallic Hydrides for Hydrogen Purification and Compression

If the world is to move towards a hydrogen economy, hydrogen must be produced in high purity to avoid any poisoning of catalysts during consumption, e.g., in a fuel cell [59]. Palladium has been determined to be extremely effective towards the application of hydrogen-purification/separation membranes. In contribution 8, Endo et al. discusses the preparation of high-purity palladium (Pd) films using the electroplating method, which is considered a simple and cost-effective technique. However, electroplating can result in stress accumulation in the film, making it challenging to obtain a dense single Pd film. This study successfully addressed this issue by optimising the electroplating process, resulting in a high-purity Pd film with unique surface characteristics. Notably, the plated film exhibited superior mechanical properties compared to rolled Pd films, including twice the displacement and four times the breaking point strength. As such, this research demonstrates the practical feasibility of using electroplating to produce Pd-based membranes for hydrogen purification applications.
For practical applications of hydrogen gas, convenient compression using low amounts of energy is crucial. Metallic hydrides have proven useful for the development of metal hydride–hydrogen compressors [15,30,60]. This is successfully demonstrated by X. Zhang et al. (contribution 9) where the rare earth series AB5 and Ti/Zr-based AB2 hydrogen storage materials are investigated. A four-stage compressor is developed with output pressures of 8.90, 25.04, 42.97, and 84.73 MPa operating at 363 K. The first pressure stage was achieved by a CaCu5-type hexagonal structure, the others by TiCr2 and ZrFe2 type alloys.
There are many aspects to overcome to enable metal hydrides to be the ideal hydrogen storage medium, but several researchers are utilising a variety of methods to overcome these problems. Large volume expansions within these powders are observed upon cycling of hydrogen, and this can lead to the occurrence of stress on the walls of the container and the possibility of catastrophic failure [15,30,49]. Zheng et al. (contribution 10) used silicone oil as a glidant to promote stress-free conditions for V-based BCC metal hydrides and have reported that the addition of 5 wt.% silicone oil slightly reduced the initial hydrogen storage capacity of V40Ti26Cr26Fe8 (particle size ~325 μm) but improved the absorption reversibility, regardless of the oil viscosity. The maximum strain on the surface of the hydrogen storage container decreased by ≥22.5% after adding 5 wt.% silicone oil.
During absorption and desorption of hydrogen, metal hydrides interact with hydrogen via multiple bonding interactions, including covalent, ionic, and van der Waals forces [61]. This inherently produces heat during absorption and absorbs heat during desorption [22,27]. This heat must be dissipated if a steady reaction rate is to occur and avoid physical degradation, including agglomeration or side reactions that are more favourable at high temperatures. Liu et al. (contribution 11) submitted a review on improving heat transfer and stability for hydrogen storage and compression applications. Currently, several researchers have adopted the method of forming composites of alloy powders with high thermal conductivity materials, such as exfoliated natural graphite (ENG), but there are many options, including liquid-based methods, polymers, and metal foams. This article highlights the state of the art in this field of research.

2.4. Physical Properties

Fundamental research into the physical properties of metal hydrides is required if technological progress is to continue in the future [1,10,14,25,27]. Jacob, Babai, and Bereznitsky et al. (contribution 12) have concentrated on determining the elastic moduli of Zr(MoxFe1−x)2, x = 0, 0.5, 1, as well as hydrogen absorption in ZrMo2, in an attempt to shed light on the unusual trend in hydride stabilities in this system. In general, the stabilities of these hydrides exhibit a unique trend, with stability increasing from x = 0 to 0.5, but destabilisation is observed for the end member ZrMo2 hydride. They found that the bulk modulus (B) significantly increases from 148.2 GPa in ZrFe2 to 200.4 GPa in ZrMo2, which is in contrast to the moderate variation in the shear modulus (G). The increase in B suggests a bulk stiffening in ZrMo2.
Pan et al. (contribution 13) provided a study detailing how protons move within yttrium-doped barium zirconate, which is known to be one of the fastest solid-state proton conductors. This study used density functional theory with the Perdew–Burke–Ernzerhof functional to calculate the total electronic energy for each proton pair in an effort to catalogue and understand their motion, especially when the protons are in close proximity to one another. Overall, it was determined that protons are in close proximity to each other and the dopant in the lowest-energy configuration, significantly affecting the backbone structure. This knowledge is important for developing superior materials for proton-conduction applications.
The search for highly tuneable hydrogen storage materials is an ongoing field, especially as the addition of functional groups can produce novel materials with interesting properties such as superconductivity, photoluminescence, etc. Alkali organometallic complexes are known to have favourable thermodynamics and hydrogen capacities, but not many transition metal–organic complexes have been reported. The contribution by Wang, Pei, Yu, and Cui et al. (contribution 14) have demonstrated the formation of yttrium phenoxide and lanthanum phenoxide via metathesis of sodium phenoxide with YCl3 and LaCl3, respectively. Their properties were elucidated using theoretical calculations, quasi in situ NMR, and UV-vis spectroscopies. Although the hydrogenation of these rare-earth phenoxides was not successful, further research on these materials may lead to progress.

3. Conclusions

The necessity for reliable methods to store renewable energy is driving the development of hydrogen production, utilisation, distribution, and storage. The most-efficient method of storing hydrogen is by using metal hydrides, whereas, simultaneously, many of these metal hydrides are finding applications in a variety of functions, including solid-state batteries, thermal energy storage, compression, etc.
The presentations, posters, and manuscripts that have arisen from MH2022 in Australia are a testament to the world-class research being undertaken in this area. The Editors of this Special Edition “State-of-the-Art and Progress in Metal-Hydrogen Systems” welcome you to read the contributed articles in the issue.

Conflicts of Interest

The authors declare no conflict of interest.

List of Contributions

  • Zhang, T.; Steenhaut, T.; Devillers, M.; Filinchuk, Y. Release of Pure H2 from Na[BH3(CH3NH)BH2(CH3NH)BH3] by Introduction of Methyl Substituents. Inorganics 2023, 11, 202. https://10.3390/inorganics11050202.
  • Peru, F.; Payandeh, S.; Jensen, T.R.; Charalambopoulou, G.; Steriotis, T. Destabilization of the LiBH4-NaBH4 Eutectic Mixture through Pore Confinement for Hydrogen Storage. Inorganics 2023, 11, 128. https://10.3390/inorganics11030128.
  • Huang, X.T.; Lu, C.L.; Li, Y.; Tang, H.M.; Duan, X.Q.; Wang, K.K.; Liu, H.Z. Hydrogen Release and Uptake of MgH2 Modified by Ti3CN MXene. Inorganics 2023, 11, 243. https://10.3390/inorganics11060243.
  • Qin, Z.K.; He, L.Q.; Ding, X.L.; Si, T.Z.; Cui, P.; Li, H.W.; Li, Y.T. Liquid Channels Built-In Solid Magnesium Hydrides for Boosting Hydrogen Sorption. Inorganics 2023, 11, 216. https://10.3390/inorganics11050216.
  • Sartori, S.; Amati, M.; Gregoratti, L.; Jensen, E.H.; Kudriashova, N.; Huot, J. Study of Phase Composition in TiFe + 4 wt.% Zr Alloys by Scanning Photoemission Microscopy. Inorganics 2023, 11, 26.
  • Kristensen, L.G.; Amdisen, M.B.; Andersen, M.; Jensen, T.R. Synthesis, Structure and Mg2+ Ionic Conductivity of Isopropylamine Magnesium Borohydride. Inorganics 2023, 11, 17. https://10.3390/inorganics11010017.
  • Vajo, J.J.; Uddin, J.; Hwang, S.J.; Graetz, J. Electrolytes in Multiple-Phase Hydrogen Storage Reactions. Inorganics 2023, 11, 267. https://10.3390/inorganics11070267.
  • Endo, N.; Kaneko, Y.; Dezawa, N.; Komo, Y.; Higuchi, M. Collectable Single Pure-Pd Metal Membrane with High Strength and Flexibility Prepared through Electroplating for Hydrogen Purification. Inorganics 2023, 11, 111. https://10.3390/inorganics11030111.
  • Zhang, X.; Zhao, Y.Y.; Li, B.Q.; Prokhorenkov, M.; Movlaev, E.; Xu, J.; Xiong, W.; Yan, H.Z.; Mitrokhin, S. Hydrogen Compression Materials with Output Hydrogen Pressure in a Wide Range of Pressures Using a Low-Potential Heat-Transfer Agent. Inorganics 2023, 11, 180. https://10.3390/inorganics11050180.
  • Zheng, X.; Kong, H.Y.; Chu, D.S.; Hu, F.P.; Wang, Y.; Yan, Y.G.; Wu, C.L. Stress Reduction of a V-Based BCC Metal Hydride Bed Using Silicone Oil as a Glidant. Inorganics 2022, 10, 167. https://10.3390/inorganics10100167.
  • Liu, L.; Ilyushechkin, A.; Liang, D.; Cousins, A.; Tian, W.; Chen, C.; Yin, J.; Schoeman, L. Metal Hydride Composite Structures for Improved Heat Transfer and Stability for Hydrogen Storage and Compression Applications. Inorganics 2023, 11, 181. https://10.3390/inorganics11050181.
  • Jacob, I.; Babai, D.; Bereznitsky, M.; Shneck, R.Z. The Role of Bulk Stiffening in Reducing the Critical Temperature of the Metal-to-Hydride Phase Transition and the Hydride Stability: The Case of Zr(MoxFe1−x)2-H2. Inorganics 2023, 11, 228. https://10.3390/inorganics11060228.
  • Pan, Y.Q.; Hoang, M.T.; Mansoor, S.; Gomez, M.A. Exploring Proton Pair Motion Away from the Global Proton-Tuple Energy Minimum in Yttrium-Doped Barium Zirconate. Inorganics 2023, 11, 160. https://10.3390/inorganics11040160.
  • Wang, J.T.; Pei, Q.J.; Yu, Y.; Cui, J.R.; Wang, S.S.; Tan, K.C.; Guo, J.Q.; He, T.; Chen, P. Investigation on the Formation of Rare-Earth Metal Phenoxides via Metathesis. Inorganics 2023, 11, 115. https://10.3390/inorganics11030115.

References

  1. Hirscher, M.; Yartys, V.A.; Baricco, M.; Bellosta von Colbe, J.; Blanchard, D.; Bowman, R.C.; Broom, D.P.; Buckley, C.E.; Chang, F.; Chen, P.; et al. Materials for hydrogen-based energy storage—Past, recent progress and future outlook. J. Alloys Compd. 2020, 827, 153548. [Google Scholar] [CrossRef]
  2. Orimo, S.; Nakamori, Y.; Eliseo, J.R.; Zuttel, A.; Jensen, C.M. Complex hydrides for hydrogen storage. Chem. Rev. 2007, 107, 4111–4132. [Google Scholar] [CrossRef] [PubMed]
  3. van den Berg, A.W.C.; Arean, C.O. Materials for hydrogen storage: Current research trends and perspectives. Chem. Commun. 2008, 6, 668–681. [Google Scholar] [CrossRef] [PubMed]
  4. Felderhoff, M.; Weidenthaler, C.; von Helmolt, R.; Eberle, U. Hydrogen storage: The remaining scientific and technological challenges. Phys. Chem. Chem. Phys. 2007, 9, 2643–2653. [Google Scholar] [CrossRef] [PubMed]
  5. Hagemann, H. Boron Hydrogen Compounds: Hydrogen Storage and Battery Applications. Molecules 2021, 26, 7425. [Google Scholar] [CrossRef]
  6. Crabtree, G.W.; Dresselhaus, M.S.; Buchanan, M.V. The hydrogen economy. Phys. Today 2004, 57, 39–44. [Google Scholar] [CrossRef]
  7. Abbott, D. Hydrogen Without Tears: Addressing the Global Energy Crisis via a Solar to Hydrogen Pathway [Point of View]. Proc. IEEE 2009, 97, 1931–1934. [Google Scholar] [CrossRef]
  8. He, T.; Pachfule, P.; Wu, H.; Xu, Q.; Chen, P. Hydrogen carriers. Nat. Rev. Mater. 2016, 1, 16059. [Google Scholar] [CrossRef]
  9. Egeland-Eriksen, T.; Hajizadeh, A.; Sartori, S. Hydrogen-based systems for integration of renewable energy in power systems: Achievements and perspectives. Int. J. Hydrogen Energy 2021, 46, 31963–31983. [Google Scholar] [CrossRef]
  10. Li, H.W.; Zhu, M.; Buckley, C.; Jensen, T.R. Functional Materials Based on Metal Hydrides. Inorganics 2018, 6, 91. [Google Scholar] [CrossRef]
  11. Webb, C.J. A review of catalyst-enhanced magnesium hydride as a hydrogen storage material. J. Phys. Chem. Solids 2015, 84, 96–106. [Google Scholar] [CrossRef]
  12. Li, C.; Peng, P.; Zhou, D.W.; Wan, L. Research progress in LiBH4 for hydrogen storage: A review. Int. J. Hydrogen Energy 2011, 36, 14512–14526. [Google Scholar] [CrossRef]
  13. Dovgaliuk, I.; Filinchuk, Y. Aluminium complexes of B- and N-based hydrides: Synthesis, structures and hydrogen storage properties. Int. J. Hydrogen Energy 2016, 41, 15489–15504. [Google Scholar] [CrossRef]
  14. Callini, E.; Atakli, Z.Ö.K.; Hauback, B.C.; Orimo, S.-i.; Jensen, C.; Dornheim, M.; Grant, D.; Cho, Y.W.; Chen, P.; Hjörvarsson, B. Complex and liquid hydrides for energy storage. Appl. Phys. A 2016, 122, 353. [Google Scholar] [CrossRef]
  15. Lototskyy, M.V.; Yartys, V.A.; Pollet, B.G.; Bowman, R.C. Metal hydride hydrogen compressors: A review. Int. J. Hydrogen Energy 2014, 39, 5818–5851. [Google Scholar] [CrossRef]
  16. Pasini, J.M.; Corgnale, C.; van Hassel, B.A.; Motyka, T.; Kumar, S.; Simmons, K.L. Metal hydride material requirements for automotive hydrogen storage systems. Int. J. Hydrogen Energy 2013, 38, 9755–9765. [Google Scholar] [CrossRef]
  17. de Jongh, P.E.; Allendorf, M.; Vajo, J.J.; Zlotea, C. Nanoconfined light metal hydrides for reversible hydrogen storage. MRS Bull. 2013, 38, 488–494. [Google Scholar] [CrossRef]
  18. Song, Y. New perspectives on potential hydrogen storage materials using high pressure. Phys. Chem. Chem. Phys. 2013, 15, 14524–14547. [Google Scholar] [CrossRef]
  19. Mohtadi, R.; Orimo, S.-i. The renaissance of hydrides as energy materials. Nat. Rev. Mater. 2016, 2, 16091. [Google Scholar] [CrossRef]
  20. Yartys, V.; Noreus, D.; Latroche, M. Metal hydrides as negative electrode materials for Ni–MH batteries. Appl. Phys. A 2016, 122, 43. [Google Scholar] [CrossRef]
  21. Schouwink, P.; Didelot, E.; Lee, Y.-S.; Mazet, T.; Černý, R. Structural and magnetocaloric properties of novel gadolinium borohydrides. J. Alloys Compd. 2016, 664, 378–384. [Google Scholar] [CrossRef]
  22. Manickam, K.; Mistry, P.; Walker, G.; Grant, D.; Buckley, C.E.; Humphries, T.D.; Paskevicius, M.; Jensen, T.; Albert, R.; Peinecke, K.; et al. Future perspectives of thermal energy storage with metal hydrides. Int. J. Hydrogen Energy 2019, 44, 7738–7745. [Google Scholar] [CrossRef]
  23. Yartys, V.A.; Lototskyy, M.V.; Akiba, E.; Albert, R.; Antonov, V.E.; Ares, J.R.; Baricco, M.; Bourgeois, N.; Buckley, C.E.; Bellosta von Colbe, J.M.; et al. Magnesium based materials for hydrogen based energy storage: Past, present and future. Int. J. Hydrogen Energy 2019, 44, 7809–7859. [Google Scholar] [CrossRef]
  24. Pasquini, L.; Sakaki, K.; Akiba, E.; Allendorf, M.D.; Alvares, E.; Ares, J.R.; Babai, D.; Baricco, M.; Bellosta von Colbe, J.; Bereznitsky, M.; et al. Magnesium- and intermetallic alloys-based hydrides for energy storage: Modelling, synthesis and properties. Prog. Energy 2022, 4, 032007. [Google Scholar] [CrossRef]
  25. Dematteis, E.M.; Amdisen, M.B.; Autrey, T.; Barale, J.; Bowden, M.E.; Buckley, C.E.; Cho, Y.W.; Deledda, S.; Dornheim, M.; de Jongh, P.; et al. Hydrogen storage in complex hydrides: Past activities and new trends. Prog. Energy 2022, 4, 032009. [Google Scholar] [CrossRef]
  26. Cuevas, F.; Amdisen, M.B.; Baricco, M.; Buckley, C.E.; Cho, Y.W.; de Jongh, P.; de Kort, L.M.; Grinderslev, J.B.; Gulino, V.; Hauback, B.C.; et al. Metallic and complex hydride-based electrochemical storage of energy. Prog. Energy 2022, 4, 032001. [Google Scholar] [CrossRef]
  27. Adams, M.; Buckley, C.E.; Busch, M.; Bunzel, R.; Felderhoff, M.; Heo, T.W.; Humphries, T.D.; Jensen, T.R.; Klug, J.; Klug, K.H.; et al. Hydride-based thermal energy storage. Prog. Energy 2022, 4, 032008. [Google Scholar] [CrossRef]
  28. Ulucan, T.H.; Akhade, S.A.; Ambalakatte, A.; Autrey, T.; Cairns, A.; Chen, P.; Cho, Y.W.; Gallucci, F.; Gao, W.; Grinderslev, J.B.; et al. Hydrogen storage in liquid hydrogen carriers: Recent activities and new trends. Prog. Energy 2023, 5, 012004. [Google Scholar] [CrossRef]
  29. Zhang, L.; Allendorf, M.D.; Balderas-Xicohténcatl, R.; Broom, D.P.; Fanourgakis, G.S.; Froudakis, G.E.; Gennett, T.; Hurst, K.E.; Ling, S.; Milanese, C.; et al. Fundamentals of hydrogen storage in nanoporous materials. Prog. Energy 2022, 4, 042013. [Google Scholar] [CrossRef]
  30. Dornheim, M.; Baetcke, L.; Akiba, E.; Ares, J.-R.; Autrey, T.; Barale, J.; Baricco, M.; Brooks, K.; Chalkiadakis, N.; Charbonnier, V.; et al. Research and development of hydrogen carrier based solutions for hydrogen compression and storage. Prog. Energy 2022, 4, 042005. [Google Scholar] [CrossRef]
  31. 17th International Symposium on Metal-Hydrogen Systems. Available online: https://www.metal-hydrogen2022.com/ (accessed on 31 October 2023).
  32. Dovgaliuk, I.; Le Duff, C.S.; Robeyns, K.; Devillers, M.; Filinchuk, Y. Mild Dehydrogenation of Ammonia Borane Complexed with Aluminum Borohydride. Chem. Mater. 2015, 27, 768–777. [Google Scholar] [CrossRef]
  33. Chua, Y.S.; Chen, P.; Wu, G.; Xiong, Z. Development of amidoboranes for hydrogen storage. Chem. Commun. 2011, 47, 5116–5129. [Google Scholar] [CrossRef]
  34. Chua, Y.S.; Wu, G.T.; Xiong, Z.T.; Karkamkar, A.; Guo, J.P.; Jian, M.X.; Wong, M.W.; Autrey, T.; Chen, P. Synthesis, structure and dehydrogenation of magnesium amidoborane monoammoniate. Chem. Commun. 2010, 46, 5752–5754. [Google Scholar] [CrossRef] [PubMed]
  35. Brinks, H.W.; Hauback, B.C.; Jensen, C.M.; Zidan, R. Synthesis and crystal structure of Na2LiAlD6. J. Alloys Compd. 2005, 392, 27–30. [Google Scholar] [CrossRef]
  36. Brinks, H.W.; Istad-Lem, A.; Hauback, B.C. Mechanochemical synthesis and crystal structure of alpha ‘-AlD3 and alpha-AlD3. J. Phys. Chem. B 2006, 110, 25833–25837. [Google Scholar] [CrossRef] [PubMed]
  37. Filinchuk, Y.; Chernyshov, D.; Dmitriev, V. Light metal borohydrides: Crystal structures and beyond. Z. Kristallogr. 2008, 223, 649–659. [Google Scholar] [CrossRef]
  38. Paskevicius, M.; Jepsen, L.H.; Schouwink, P.; Cerny, R.; Ravnsbaek, D.B.; Filinchuk, Y.; Dornheim, M.; Besenbacher, F.; Jensen, T.R. Metal borohydrides and derivatives—Synthesis, structure and properties. Chem. Soc. Rev. 2017, 46, 1565–1634. [Google Scholar] [CrossRef] [PubMed]
  39. Remhof, A.; Mauron, P.; Züttel, A.; Embs, J.P.; Łodziana, Z.; Ramirez-Cuesta, A.J.; Ngene, P.; de Jongh, P. Hydrogen Dynamics in Nanoconfined Lithiumborohydride. J. Phys. Chem. C 2013, 117, 3789–3798. [Google Scholar] [CrossRef]
  40. Liu, X.; Peaslee, D.; Jost, C.Z.; Baumann, T.F.; Majzoub, E.H. Systematic Pore-Size Effects of Nanoconfinement of LiBH4: Elimination of Diborane Release and Tunable Behavior for Hydrogen Storage Applications. Chem. Mater. 2011, 23, 1331–1336. [Google Scholar] [CrossRef]
  41. Sartori, S.; Knudsen, K.D.; Hage, F.S.; Heyn, R.H.; Bardaji, E.G.; Zhao-Karger, Z.; Fichtner, M.; Hauback, B.C. Influence of nanoconfinement on morphology and dehydrogenation of the Li11BD4–Mg(11BD4)2 system. Nanotechnology 2012, 23, 255704. [Google Scholar] [CrossRef]
  42. Chen, W.; Ouyang, L.Z.; Liu, J.W.; Yao, X.D.; Wang, H.; Liu, Z.W.; Zhu, M. Hydrolysis and regeneration of sodium borohydride (NaBH4)—A combination of hydrogen production and storage. J. Power Sources 2017, 359, 400–407. [Google Scholar] [CrossRef]
  43. Demirci, U.B.; Akdim, O.; Andrieux, J.; Hannauer, J.; Chamoun, R.; Miele, P. Sodium Borohydride Hydrolysis as Hydrogen Generator: Issues, State of the Art and Applicability Upstream from a Fuel Cell. Fuel Cells 2010, 10, 335–350. [Google Scholar] [CrossRef]
  44. Schneemann, A.; White, J.L.; Kang, S.; Jeong, S.; Wan, L.F.; Cho, E.S.; Heo, T.W.; Prendergast, D.; Urban, J.J.; Wood, B.C.; et al. Nanostructured Metal Hydrides for Hydrogen Storage. Chem. Rev. 2018, 118, 10775–10839. [Google Scholar] [CrossRef] [PubMed]
  45. de Jongh, P.E.; Wagemans, R.W.P.; Eggenhuisen, T.M.; Dauvillier, B.S.; Radstake, P.B.; Meeldijk, J.D.; Geus, J.W.; de Jong, K.P. The Preparation of Carbon-Supported Magnesium Nanoparticles using Melt Infiltration. Chem. Mater. 2007, 19, 6052–6057. [Google Scholar] [CrossRef]
  46. Gross, A.F.; Ahn, C.C.; Van Atta, S.L.; Liu, P.; Vajo, J.J. Fabrication and hydrogen sorption behaviour of nanoparticulate MgH2 incorporated in a porous carbon host. Nanotechnology 2009, 20, 204005. [Google Scholar] [CrossRef]
  47. Ares, J.R.; Aguey-Zinsou, K.F.; Klassen, T.; Bormann, R. Influence of impurities on the milling process of MgH2. J. Alloys Compd. 2007, 434–435, 729–733. [Google Scholar] [CrossRef]
  48. Oelerich, W.; Klassen, T.; Bormann, R. Metal oxides as catalysts for improved hydrogen sorption in nanocrystalline Mg-based materials. J. Alloys Compd. 2001, 315, 237–242. [Google Scholar] [CrossRef]
  49. Dematteis, E.M.; Berti, N.; Cuevas, F.; Latroche, M.; Baricco, M. Substitutional effects in TiFe for hydrogen storage: A comprehensive review. Mater. Adv. 2021, 2, 2524–2560. [Google Scholar] [CrossRef]
  50. Modi, P.; Aguey-Zinsou, K.-F. Room Temperature Metal Hydrides for Stationary and Heat Storage Applications: A Review. Front. Energy Res. 2021, 9, 616115. [Google Scholar] [CrossRef]
  51. Roedern, E.; Kühnel, R.S.; Remhof, A.; Battaglia, C. Magnesium Ethylenediamine Borohydride as Solid-State Electrolyte for Magnesium Batteries. Sci. Rep. 2017, 7, 46189. [Google Scholar] [CrossRef]
  52. Choi, Y.S.; Lee, Y.-S.; Choi, D.-J.; Chae, K.H.; Oh, K.H.; Cho, Y.W. Enhanced Li Ion Conductivity in LiBH4–Al2O3 Mixture via Interface Engineering. J. Phys. Chem. C 2017, 121, 26209–26215. [Google Scholar] [CrossRef]
  53. Tang, W.S.; Matsuo, M.; Wu, H.; Stavila, V.; Unemoto, A.; Orimo, S.-i.; Udovic, T.J. Stabilizing lithium and sodium fast-ion conduction in solid polyhedral-borate salts at device-relevant temperatures. Energy Storage Mater. 2016, 4, 79–83. [Google Scholar] [CrossRef]
  54. Matsuo, M.; Orimo, S.-i. Lithium Fast-Ionic Conduction in Complex Hydrides: Review and Prospects. Adv. Energy Mater. 2011, 1, 161–172. [Google Scholar] [CrossRef]
  55. Tutusaus, O.; Mohtadi, R.; Arthur, T.S.; Mizuno, F.; Nelson, E.G.; Sevryugina, Y.V. An Efficient Halogen-Free Electrolyte for Use in Rechargeable Magnesium Batteries. Angew. Chem. Int. Ed. 2015, 54, 7900–7904. [Google Scholar] [CrossRef] [PubMed]
  56. Kisu, K.; Kim, S.; Inukai, M.; Oguchi, H.; Takagi, S.; Orimo, S.-i. Magnesium Borohydride Ammonia Borane as a Magnesium Ionic Conductor. ACS Appl. Energy Mater. 2020, 3, 3174–3179. [Google Scholar] [CrossRef]
  57. Yan, Y.; Dononelli, W.; Jørgensen, M.; Grinderslev, J.B.; Lee, Y.-S.; Cho, Y.W.; Černý, R.; Hammer, B.; Jensen, T.R. The mechanism of Mg2+ conduction in ammine magnesium borohydride promoted by a neutral molecule. Phys. Chem. Chem. Phys. 2020, 22, 9204–9209. [Google Scholar] [CrossRef] [PubMed]
  58. Hadjixenophontos, E.; Dematteis, E.M.; Berti, N.; Wołczyk, A.R.; Huen, P.; Brighi, M.; Le, T.T.; Santoru, A.; Payandeh, S.; Peru, F.; et al. A Review of the MSCA ITN ECOSTORE—Novel Complex Metal Hydrides for Efficient and Compact Storage of Renewable Energy as Hydrogen and Electricity. Inorganics 2020, 8, 17. [Google Scholar] [CrossRef]
  59. Faye, O.; Szpunar, J.; Eduok, U. A critical review on the current technologies for the generation, storage, and transportation of hydrogen. Int. J. Hydrogen Energy 2022, 47, 13771–13802. [Google Scholar] [CrossRef]
  60. Gray, E.M.; Webb, C.J. Metal-hydride hydrogen compressors for laboratory use. J. Phys. Energy 2020, 2, 034004. [Google Scholar] [CrossRef]
  61. Züttel, A.; Remhof, A.; Borgschulte, A.; Friedrichs, O. Hydrogen: The future energy carrier. Phil. Trans. R. Soc. A 2010, 368, 3329–3342. [Google Scholar] [CrossRef]
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Humphries, T.D.; Buckley, C.E.; Paskevicius, M.; Jensen, T.R. State-of-the-Art and Progress in Metal-Hydrogen Systems. Inorganics 2023, 11, 476. https://doi.org/10.3390/inorganics11120476

AMA Style

Humphries TD, Buckley CE, Paskevicius M, Jensen TR. State-of-the-Art and Progress in Metal-Hydrogen Systems. Inorganics. 2023; 11(12):476. https://doi.org/10.3390/inorganics11120476

Chicago/Turabian Style

Humphries, Terry D., Craig E. Buckley, Mark Paskevicius, and Torben R. Jensen. 2023. "State-of-the-Art and Progress in Metal-Hydrogen Systems" Inorganics 11, no. 12: 476. https://doi.org/10.3390/inorganics11120476

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.