Microstructure and Properties of Ti-5Al-2.5Sn Alloy with Higher Carbon Content

This study investigates the characteristics of the Ti-5Al-2.5Sn-0.2C alloy, an alpha titanium alloy containing approximately 0.2 wt% carbon—a concentration significantly exceeding the standard allowable limit of 0.08 wt%. The Ti-5Al-2.5Sn-0.2C alloy was melted in a vacuum induction furnace with a cold copper crucible, processed into bar form through hot rolling, and subsequently annealed under standard conditions. The microstructure and mechanical properties of the Ti-5Al-2.5Sn-0.2C alloy were systematically compared with those of the Ti-5Al-2.5Sn alloy (Grade 6), which possesses a similar chemical composition. The results revealed that the addition of 0.2 wt% carbon significantly influences the alloy’s solidification process, phase transformation temperatures, phase composition, and phase lattice parameters. Moreover, the carbon addition enhances key mechanical properties, including tensile strength, yield strength, hardness, and wear resistance, as well as creep and oxidation resistance. While a slight reduction in plasticity and increase in impact energy were observed, the alloy remained within the permissible range defined by existing standards.