Research on the Performance of Steel Strand-Reinforced Reactive Powder Concrete with Mixed Steel Fibers and Basalt Fibers under the Salt Dry–Wet Erosion

In this study, the properties of steel strand-reinforced reactive powder concrete (RPC) with mixed steel fibers and basalt fibers were investigated. The volume ratios of steel fibers and basalt fibers ranged from 0% to 2%. The reinforcement ratio of steel strands was 1%. The flexural strength and toughness were measured. Moreover, the impact toughness was determined. The studies were carried out under an erosion environment with chlorides and sulfates. The electrical resistance and the ultrasonic velocity were obtained to assess the salt corrosion resistance performance of steel strand-reinforced RPC. The results show that the addition of basalt fibers and steel fibers can improve the mechanical strength, ultrasonic velocity, flexural toughness, and impact toughness and decrease the performance degradation of the steel strand-reinforced RPC under the conditions of dry–wet alternations of NaCl and Na₂SO₄ solutions. Basalt fibers and steel fibers can improve the steel strand-reinforced RPC’s flexural strength by rates of up to 13.1% and 28.7%, respectively. Moreover, the corresponding compressive strength increases by 10.3% and 18.3%. The flexural strength decreases by 11.2%~33.6% and 7.3%~22.7% after exposure to the NaCl and Na₂SO₄ dry–wet alternations. Meanwhile, the corresponding compressive strength decreases by 22.1%~38.9% and 14.6%~41.3%. The electrical resistance increases with the addition of basalt fibers and decreases with the increasing dosages of steel fibers. The steel strand-reinforced RPC with the assembly units of 1% steel fibers and 1% basalt fibers shows the optimal mechanical properties and salt resistance considering its wet–dry alternation performance. The properties of steel strand-reinforced RPC decrease more rapidly after undergoing NaCl erosion than Na₂SO₄ erosion.