Next Article in Journal
Influence of Stress on Electronic and Optical Properties of Rocksalt and Wurtzite MgO–ZnO Nanocomposites with Varying Concentrations of Magnesium and Zinc
Previous Article in Journal
Microstructure and Mechanical Properties of Unidirectional, Laminated Cf/SiC Composites with α-Al2O3 Nanoparticles as Filler
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 12
Issue 19
10.3390/nano12193409
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Roles of TOPO Coordinating Solvent on Prepared Nano-Flower/Star and Nano-Rods Nickel Sulphides for Solar Cells Applications

by
Mojeed A. Agoro
1,2,* and
Edson L. Meyer
1
1
Fort Hare Institute of Technology, University of Fort Hare, Private Bag X1314, Alice 5700, South Africa
2
Department of Chemistry, University of Fort Hare, Private Bag X1314, Alice 5700, South Africa
*
Author to whom correspondence should be addressed.
Nanomaterials 2022, 12(19), 3409; https://doi.org/10.3390/nano12193409
Submission received: 3 September 2022 / Revised: 22 September 2022 / Accepted: 27 September 2022 / Published: 28 September 2022
Browse Figures
Versions Notes

Abstract

:
The present study describes a cheap, safe, and stable chemical process for the formation of nickel sulphide (NiS) with the use of mixed and single molecular precursors. The production pathway is uncomplicated, energy-efficient, quick, and toxic-free, with large-scale commercialization potential. The obtained results show the effect of tri-N-octylphosphine oxide (TOPO) as a coordinating solvent on the reaction chemistry, size distributions, morphology, and optical properties of both precursors. Ni[N,N-benz-N-p-anisldtc] as NiSa, Ni[N,N-benzldtc] as NiSb, and Ni[N-p-anisldtc] as NiSc thermally decompose in a single step at 333–334 °C. The X-ray diffraction peaks for NiSa, NiSb, and NiSc matched well with the cubic NiS nanoparticles and corresponded to planes of (111), (220), and (311). The extrapolated linear part from the Tauc plots reveals band gap values of 3.12 eV, 2.95 eV, and 2.5 eV, which confirms the three samples as potential materials for solar cell applications. The transmission electron microscopy (TEM) technique affirmed the quantum dot size distribution at 19.69–28.19 nm for NISa, 9.08–16.63 nm for NISb, and 9.37–10.49 nm for NISc, respectively. NiSa and NiSc show a clearly distinguishable flower/star like morphology, while NiSb displays a compact nano-rod shape. To the best of the authors’ knowledge, very few studies have been reported on the flower/star like and nano-rod shapes, but none with the dithiocarbamate molecular precursor for NiS nanoparticles.

1. Introduction

The current situation between Russia and most of the developed western countries, namely their sore dependence on Russian coal, fuels, and gas products, is having a serious impact on their economies. The only possible solution to these geometrical political constraints is a change to a renewable energy that is cost-effective, easy to generate, and environmentally friendly, such as solar energy. The most promising next-generation solar cells in the last two decades have been quantum dot-sensitized solar cells (QDSCs), which have reasonable efficiency and future-enhancement prospects. These future expectations are linked to their ability to optimize quantum dots (QDs) particle sizes, their cost friendliness, easy fabrication, and different wavelength ranges that will cover the visible light spectrum. Furthermore, a single photon can greatly enhance the conversion output of QDSCs through multiple-exciton excitons, making QDs a potential candidate in applications, such as solar cells [1,2,3,4,5,6,7]. Replacing the dye molecules in the dye-sensitized solar cell structure principle with QD semiconductors will increase conversion efficiency [8,9,10].
QDs semiconductors from metal chalcogenides (selenides, sulphides, tellurides) have been employed in QDSCs as photosensitizers, displaying remarkable performance, as well as in other applications such as optical conductors, IR detectors, coatings, and many more [11,12]. Nickel sulphide (NiS) has a phase structure that is more intricate than the lanthanide sulphides [13]. NiS has distinct properties, with similarities in its two crystalline formulas and formation but differences in molecular packing [12]. At lower temperatures, rhombohedral phase (millerite) NiS was observed, while NiAs-type “symmetry” was shown at higher temperatures. The rhombohedral structure has a tetragonal pyramidal coordination of Ni atoms surrounded by five sulphur atoms, whereas NiAs displays an octahedral structure of Ni atoms coordinated with every sulphur atom. Furthermore, rhombohedral NiS exhibits temperature-independent paramagnetism-sami-metallic behaviour, whereas hexagonal NiS exhibits an antiferromagnetic semiconducting metallic phase [12]. NiS is a p-type semiconductor material with a 0.5 eV band gap and has been applied in applications such as solar cells, sensors, IR detectors, photoelectrochemical catalysts, and lithium batteries [12,13,14,15,16,17].
These attractions are sorely linked to their size, phase, surface properties, morphology, and crystal structure through the choice of preparation techniques adopted. Various approaches have been used to fabricate NiS, such as solution-processing, hydrothermal, laser ablation, and successive ionic-layer adsorption reaction methods [12,17,18,19,20]. The single-source precursors technique (SSPs) is cheap, safe, and stable with the use of one precursor. This is usually achieved through metal dithiocarbamate complexes as molecular precursors, which decompose by heating to produce QD metal sulphide materials, as reported by many research groups [21,22,23]. Changes in the dithiocarbamate organic moiety at the N-bond can give QD metal sulphide the desired morphology, size distribution, and phases [22]. Furthermore, metal dithiocarbamate complexes have better conductivity, magnetic, structural diversity, thermal, and electrochemical properties with huge potential in industrial, analytical, and biological applications [1,24,25]. The current work focuses on the optical, morphological, thermal, and structural properties of NiS prepared from N,N-dibenzyldithiocarbamate and N-p-anisidineldithiocarbamate ligands with nickel(II) complexes.

2. Experimental Section

2.1. Materials and Methods

All chemicals were of analytical grade, received from SigmaAldrich (Johannesburg, South Africa), and used without further purification. We synthesized ammonium, nickel(II) chloride hexahydrate (NiCl2*6H2O), Tri-n-octylphosphine oxide (TOPO), oleic acid, methanol, diethyl ester, carbon disulphide, N,N-dibenzyldithiocarbamate, and N-p-anisidineldithiocarbamate by slit modification of the previously published literature [23]. [N,N-dibenzldtc]. Colour: olive green; yield: 6.88 g 66%, mp 228–230 °C. 1H NMR (DMSO) δ 6.8–7.1 (m, 8H-C6H5), 3.3 (s, 2H-NH), 1.3 (t, 2H-CH2), 2.5 (s, 1H-SH). 13C NMR (DMSO) δ40 (-NH2), 51.0 (-S-C), 129 (-8H-C6H5), 207 (-CS2). Selected IR (cm−1) 1412 v(C-N), 1218 v(C-S), 3289 v(N-H). UV–Vis (CH3OH solution, nm): 315. [N-p-anisldtc]. Colour: olive green; yield: 20.20 g 93.87%, mp 228–230 °C. 1H NMR (DMSO) δ 9.42 (m, 8H-C6H5), 3.37 (s, 2H –NH), 6.89 (s, O-C6H5), 2.5 (s, 1H-SH). 13C NMR (DMSO) δ40 (-NH2), 55.8 (-S-C), 180.7 (s, O-C6H5), 124.3 (-8H-C6H5), 206 (-CS2). Selected IR (cm−1) 1412 v(C-N), 1218 v(C-S), 3391 v(N-H). UV–Vis (CH3OH solution, nm): 327.

2.2. Synthesis of Complexes

Synthesis of Bis(N,N-Benzyl-N-p-Asnisidineldithiocarbamato)Nickel(II) (Complex 1)

We dissolved 2.5 mmol of N,N-dibenzyldithiocarbamate and N-p-anisidineldithiocarbamate (0.7262 g and 0.5409 g) in 15 mL of distilled water. We mixed these solutions at a ratio of 1:1:1 with (0.5939 g, 2.5 mmol) of NiCl2*6H2O dissolved in 15 mL of distilled water and stirred for 2 h at room temperature. A solid bright green precipitate was formed, washed several times with distilled water, and air dried in a calcium vacuum to yield the following end product as seen in Scheme 1: [Ni[N,N-benz-N-p-anisldtc]. Colour: bright green; yield: 68%, mp 232–234 °C. 1H NMR (DMSO) δ 7.47–9.46 (m, 8H-C6H5), 4.04–5.05 (s, 2H-NH), 6.86 (s, O-C6H5), 2.51 (s, 1H-SH). 13C NMR (DMSO) δ40 (-NH2), 51.3–55.7 (-S-C), 181.9 (s, O-C6H5), 126.5–157 (-8H-C6H5), 210 (-CS2). Selected IR (cm−1) 1428 v(C-N), 1140 v(C-S), 3215 v(N-H), 518 v(M-S). UV–Vis (CH3OH solution, nm): 265. We followed same path for the synthesis of N,N-dibenzyldithiocarbamate with nickel(II) complex at ratio (2:1) labelled as [Ni[N,N-benzldtc] and N-p-anisidineldithiocarbamate with nickel(II) complex at ratio (2:1) labelled as [Ni[N-p-anisldtc]. [Ni[N,N-benzldtc]. Colour: bright green; yield: 74%, mp 234–236 °C. 1H NMR (DMSO) δ 7.47–9.46 (m, 8H-C6H5) 3.7 (s, 2H –NH), 1.32 (t, 3H-CH2), 3.30 (s, 1H-SH). 13C NMR (DMSO) δ 126–143 (-C6H5), 40 (-CH2), 203 (-CS2), 52 (-C–NH). Selected IR (cm−1) 1495 v(C-N), 1228 v(C-S), 3028 v(N-H), 518 v(M-S). UV–Vis (CH3OH solution, nm): 259. [Ni[N-p-anisldtc]. Colour: green; yield: 78%, mp 234–236 °C. 1H NMR (DMSO) δ 6.82–9.43 (m, 8H-C6H5), 3.6 (s, 2H –NH), 3.32 (t, 3H-CH2), 2.5 (s, 1H-SH). 13C NMR (DMSO) δ 137–146 (-C6H5)40 (-CH2), 206 (-CS2), 55.9 (-C–NH). Selected IR (cm−1) 1467 v(C-N), 1030 v(C-S), 3166 v(N-H), 520 v(M-S). UV–Vis (CH3OH solution, nm): 277.

2.3. Synthesis of Nickel Sulfide Nanoparticles

In a neck-bottom flask, we dissolved 0.2 g of bis(N,N-dibenzyl-N-p-anisidineldithiocarbamato) nickel(II) as Ni[N,N-benz-N-p-anisidineldtc] [2] in 4 mL of oleic acid mixed with 3 g of hot coordinating solvent TOPO. We observed the 20–30 °C initial heating of the TOPO in the bottom flask for about 20 min. We heated the reaction to 260 degrees Celsius and held there for one hour. We took the dark aqueous solution from the flask at a reduced temperature of around 70 °C. We added an additional 50 mL of methanol to remove the excess capping agent and toxic solvent by centrifugation at 2000 rpm for 30 min, followed by drying with an air vacuum. We labelled the prepared NiS as NiSa, while we used Ni[N,N-benzldtc] and Ni[N-p-anisldtc] to fabricate NiSb and NiSc under similar conditions and procedures.

2.4. Characterization

We elevated the optical properties, surface morphology, thermal stability, elemental compositions, and thickness of the NiS nanoparticles through the following techniques: field emission scanning electron microscope (FE-SEM, S-4200, Hitachi, Munich, Germany) coupled with energy dispersive X-ray spectroscopy (EDS) on-system, operating at a voltage of 15 kV. We identified the size distributions of the three samples using JEOL JEM 2100 (Pleasanton, CA, USA) Transmission Electron Microscope (TEM) operating at 200 kV. We established their structural patterns using X-ray diffraction (XRD) analysis by Cu Ka radiation run at 40 mA and 40 kV. We obtained surface roughness using an atomic force microscope (JPK NanoWizard II AFM, JPK Instruments, Berlin, Germany) at a scan rate of 0.8 Hz. We carried out TGA analysis at temperatures ranging from 30 to 600 degrees Celsius at a rate of 10 degrees Celsius per min−1. We achieved Fourier transform infrared spectroscopy (FTIR) analysis through the aid of Bruker Platinum ATR Model Alpha (Waltham, MA, USA). We used the PerkinElmer instrument of the model LAMBDA 365 and LS 45 fluorimeters to understand the optical properties (UV-Vis and PL analysis) of the three samples. We carried out NMR analysis using a Bruker AV-400 spectrometer (Waltham, MA, USA) working at 400.13 MHz, 300 K, and a spinning rate of 4 kHz.

3. Results and Discussion

3.1. TGA and FTIR Analysis

The thermal decomposition of Ni[N,N-benz-N-p-anisldtc], Ni[N,N-benzldtc], and Ni[N-p-anisldtc] is shown in Figure 1a–c. The onset decomposition heat for Ni[N,N-benz-N-p-anisldtc] and Ni[N-p-anisldtc] complexes is 275 °C, while the final decomposition heat is 333–334 °C, resulting in NiSa and NiSc conversion. Ni[N,N-benzldtc] has a decomposition profile onset at 270 °C and a single-step decomposition at 348 °C for the formation of NiSb. The three samples revealed a complete loss in their final mass residual. This occurrence is consistent with the reports by Ref. [26] on the thermolysis of Ni complexes. An FTIR spectra analysis was taken (see Figure 1d), which affirmed the presence of typical constituents of dithiocarbamates and Ni-S compounds. The absorption bands of N-H at 3324 cm−1 and the vibration modes of C-S and C-N bands at 972–729 cm−1 and 1479–1643 cm−1 revealed the interface between the aromatic precursors and metal ion substances. The presence of the vibration frequencies at 587 and 423 cm−1 correlates to the metal with sulphur atoms M-S coordination, which agrees with the report in Ref. [27].

3.2. XRD

Figure 2a and the inset Figure 2b show the patterns with the presence of one-phase nickel sulphide nanoparticles. The diffraction peaks for NiSa and NiSc at 19.82°, 21.68°, and 37.02° and for NiSb at 19.82°, 22.52°, and 37.02° exhibited by the three samples correspond to the (111), (220), and (311) planes of cubic NiS nanoparticles (ICDD card number 043-1469). The XRD pattern illustrates the polycrystalline nature of the samples, with some impurities from the coordinating solvent around 19° to 24° being observed. The small peak observed at 43.64° is ascribed to pure nickel, which is similar to the observation by Ref. [27] for cubic NiS nanoparticles. The results of this study on the formation of NiS with a dithiocarbamate complex via thermolysis at high temperatures are consistent with previous research [28,29].

3.3. UV-Vis

The optical spectra along with the estimated Tauc plots for the NiSa, NiSb, and NiSc nanoparticles synthesized from mixed and single molecular precursors with TOPO coordinating solvent are shown in Figure 3a,b. The optical spectra for NiSa and NiSc nanoparticles have an absorbance response in the blue-shifted regions at 482 nm and 446 nm. The obtained optical properties for both nanoparticles have better size distributions as a result of the quantum confinement effect, which is better than the previous studies using HDA capping agents [30]. The absorption properties of NiSb show a lower response wavelength at 388 nm, 629 nm, and 758 nm. The optical characteristics from this study suggest that the prepared nanoparticles have strong potential for solar cell applications due to their absorption in the blue shift regions. By extrapolating the linear part of the data in the Tauc plots, optical band gap values of 3.12 eV, 2.95 eV, and 2.5 eV were obtained for NiSa, NiSb, and NiSc, respectively.

3.4. PL Analysis

The PL spectra of NiSa, NiSb, and NiSc nanoparticles with an excitation wavelength of 350 nm are seen in Figure 4. The emission peaks at 447 nm and 488 nm for NiSa and NiSc are due to defects. The corresponding emission peaks at 625 nm and 684 nm for NiSc, and 612 nm and 662 nm for NiSb, are attributed to the red shift. These emission peaks are a strong indication of a larger size distribution or anisotropic particles. The observed emission in this study is similar to that in the literature [27,31].

3.5. TEM

The TEM technique was used to obtain a detailed analysis of the particle structure. The size distribution of the three nanoparticles was found to be between 19.69 and 28.19 nm for NISa, 9.08 and 16.63 nm for NISb, and 9.37 and 10.49 nm for NISc. The TEM image further verifies the uniformity of NiSa nanoparticles with a large number of mesopores and less aggregation, as seen in Figure 5b,d. The lattice d-spacing of 0.30 nm is in correlation with the (111) plane of cubic NiS [32], as seen in the inserted Figure 5b, which is in agreement with the report by Ref. [33]. The porous and loose structure of NiSa has been shown to improve electrocatalytic activity by increasing electrolyte contact [33]. The compact nature of NiSb agglomerates was demonstrated in Figure 5f,h. Figure 5f,h reveal the spherical structure of NiSb nanoparticles through the aid of TOPO coordinating solvent surface passivation, leading to the fabrication of nanopores. The lattice spacing of 0.25 nm corresponds to the (111) plane of NiS (as shown in the inserted Figure 5g), which is in good agreement with the literature [34]. TEM images of NISc display spherically shaped particles (see Figure 5j,l and the inset in Figure 5i,k) due to coalescence, which involves the interaction between the particle–particle with several neighbouring nanospheres. This phenomenon is associated with the reduction of surface energy in nanoparticles as a result of their small dimensions, which results in a high reactive surface energy and unstable nanoparticles [30,35,36]. The lattice d-spacing of 0.30 nm correlates to the plane (111) of cubic NiS nanoparticles, while the SAED image reveals bright spots and the crystallinity nature of NiSc nanoparticles. This study further affirmed the report by Ref. [30] on the role of long alkyl chains in changing the shape and thermal stability of nanoparticles. The summary of the three samples prepared by the SSPs method is found in Table 1.

3.6. AFM

The surface roughness of NiSa, NiSb, and NiSc nanoparticles was studied using AFM, as shown in Figure 6a,d,g. The quantitative details of the surface profile, such as average roughness (Ra), 3D dimensional simulation, and root mean square roughness (Rq), were obtained from the samples. The topographical view confirms that three metal sulphides are characterized by indentations and irregular surfaces. The Rq was found at 93.8, 75.7, and 425 nm for NiSa, NiSb, and NiSc, respectively, while the Ra for NiSa, NiSb, and NiSc was found at 46.8, 49.1, and 334 nm, respectively. The slight difference in surface roughness corresponds to the relative changes in particle size. The particle size can influence the electron transfer speed and current density [37,38]. The AFM measurements correspond with results obtained from the TEM.

3.7. FE-SEM

Figure 6b,c,e,f,h,i illustrate the morphological evolution of the as-prepared NiS for the three samples. The images in Figure 6b,c,e,f,h,i reveal a clearly distinguishable flower/star-like morphology for NiSa and NiSc with some clustered nanoparticles. The formation of an irregular flower/star finer morphology for NiSa and NiSc is linked to their larger surface area, which promotes higher reducibility, better size distribution, and superior catalytic reactions [39,40]. On the other hand, NiSb reveals compact nanorod-shaped nanoparticles, as seen in Figure 6e,f, which supports the TEM results. The predominant nanorods observed in NiSb are vital aspects of materials that can enhance electrolyte transport, photoactivity, and the optimization of light absorbance. To the best of our knowledge, very few studies on the flower/star-like and nanorod shapes have been reported, and none with dithiocarbamate as a molecular precursor for NiS nanoparticles [41,42,43].

3.8. EDS

Figure 7a–c confirm the elemental composition and purity of the synthesized NiS nanoparticles through EDS. The annealed nanoparticles reveal the presence of strong Ni and S in the three samples. The organic elements of Ni and S observed from the profiles of the three samples originated from the molecular precursors, which indicates the successful synthesis of NiS and affirms the FTIR results [44].

4. Conclusions

In conclusion, the SSP route is a risk-free, low-cost, and simple method of synthesizing quantum dot nickel sulphide using a molecular precursor. The TOPO-capped agent with the mixed and single precursor influences the novel flower/star-like and nanorod nickel sulphide NiS quantum dot nanostructures. This has a significant impact on particle sizes, surface roughness, morphologies, and optical properties. Surface roughness and size distribution can influence the electron transfer speed and the current density for solar cell applications. The emission peaks in the blue and red shift regions are strong indications that these materials can absorb the entire solar spectrum, giving rise to better efficiency in solar cell applications, such as quantum dot-sensitized solar cells. Moreover, flower/star-like and nanorod materials are vital aspects that can enhance electrolyte transport, photoactivity, and light-absorbance optimization.

Author Contributions

Conceptualization, M.A.A.; methodology, M.A.A.; validation, M.A.A.; formal analysis, M.A.A.; investigation, M.A.A.; resources, E.L.M.; data curation, M.A.A.; writing—original draft preparation, M.A.A.; writing—review and editing, M.A.A. and E.L.M.; supervision, E.L.M.; funding acquisition, E.L.M. All authors have read and agreed to the published version of the manuscript.

Funding

The authors gratefully acknowledge the PV Spoke National Energy Research Programme of the Department of Science (GUN: 137944) and Innovation and National Research Foundation (GUN: 118947) and the Govan Mbeki Research and Development Centre (GMRDC), University of Fort Hare, South Africa, for their financial support.

Data Availability Statement

Not applicable.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Agoro, M.A.; Meyer, E.L.; Mbese, J.Z.; Fuku, X.; Ahia, C.C. Aliphatic mixed ligands Sn(II) complexes as photon absorbers in quantum dots sensitized solar cell. J. Solid State Chem. 2022, 308, 122890. [Google Scholar] [CrossRef]
  2. Agoro, M.A.; Mbese, J.Z.; Meyer, E.L. Inorganic Pb(II)–P and Pb(II)–S Complexes as Photosensitizers from Primary and Secondary Amines in Dyes-Sensitized Solar Cells. ACS Omega 2021, 6, 23700–23709. [Google Scholar] [CrossRef]
  3. Gopi, C.V.; Rao, S.S.; Kim, S.K.; Punnoose, D.; Kim, H.J. Highly effective nickel sulfide counter electrode catalyst prepared by optimal hydrothermal treatment for quantum dot-sensitized solar cells. J. Power Sources 2015, 275, 547–556. [Google Scholar] [CrossRef]
  4. Zhu, L.; Zhang, M.; Zhong, W.; Leng, S.; Zhou, G.; Zou, Y.; Su, X.; Ding, H.; Gu, P.; Liu, F.; et al. Progress and prospects of the morphology of non-fullerene acceptor based high-efficiency organic solar cells. Energy Environ. Sci. 2021, 14, 4341–4357. [Google Scholar] [CrossRef]
  5. Ma, R.; Yan, C.; Yu, J.; Liu, T.; Liu, H.; Li, Y.; Chen, J.; Luo, Z.; Tang, B.; Lu, X.; et al. High-Efficiency Ternary Organic Solar Cells with a Good Figure-of-Merit Enabled by Two Low-Cost Donor Polymers. ACS Energy Lett. 2022, 7, 2547–2556. [Google Scholar] [CrossRef]
  6. Yang, X.; Yang, J.; Ullah, M.I.; Xia, Y.; Liang, G.; Wang, S.; Zhang, J.; Hsu, H.Y.; Song, H.; Tang, J. Enhanced passivation and carrier collection in ink-processed PbS quantum dot solar cells via a supplementary ligand strategy. ACS Appl. Mater. Interfaces 2020, 12, 42217–42225. [Google Scholar] [CrossRef] [PubMed]
  7. Chen, S.; Ishaq, M.; Xiong, W.; Ali Shah, U.; Farooq, U.; Luo, J.; Zheng, Z.; Su, Z.; Fan, P.; Zhang, X.; et al. Improved Open-Circuit Voltage of Sb2Se3 Thin-Film Solar Cells Via Interfacial Sulfur Diffusion-Induced Gradient Bandgap Engineering. Sol. RRL 2021, 5, 2100419. [Google Scholar] [CrossRef]
  8. Chen, S.; Zhang, Z.; Jiang, W.; Zhang, S.; Zhu, J.; Wang, L.; Ou, H.; Zaman, S.; Tan, L.; Zhu, P.; et al. Engineering Water Molecules Activation Center on Multisite Electrocatalysts for Enhanced CO2 Methanation. J. Am. Chem. Soc. 2022, 144, 12807–12815. [Google Scholar] [CrossRef] [PubMed]
  9. Ishaq, M.; Chen, S.; Farooq, U.; Azam, M.; Deng, H.; Su, Z.H.; Zheng, Z.H.; Fan, P.; Song, H.S.; Liang, G.X. High open-circuit voltage in full-inorganic Sb2S3 solar cell via modified Zn-doped TiO2 electron transport layer. Sol. RRL 2020, 4, 2000551. [Google Scholar] [CrossRef]
  10. Ali, H.; Zaman, S.; Majeed, I.; Kanodarwala, F.K.; Nadeem, M.A.; Stride, J.A.; Nadeem, M.A. Porous carbon/rGO composite: An ideal support material of highly efficient palladium electrocatalysts for the formic acid oxidation reaction. ChemElectroChem 2017, 4, 3126–3133. [Google Scholar] [CrossRef]
  11. Theerthagiri, J.; Karuppasamy, K.; Durai, G.; Rana, A.U.H.S.; Arunachalam, P.; Sangeetha, K.; Kuppusami, P.; Kim, H.S. Recent advances in metal chalcogenides (MX.; X = S, Se) nanostructures for electrochemical supercapacitor applications: A brief review. Nanomaterials 2018, 8, 256. [Google Scholar] [CrossRef]
  12. Iram, S.; Mahmood, A.; Ehsan, M.F.; Mumtaz, A.; Sohail, M.; Sitara, E.; Bukhari, S.A.B.; Gul, S.; Fatima, S.A.; Khan, M.Z.; et al. Impedance Spectroscopic Study of Nickel Sulfide Nanostructures Deposited by Aerosol Assisted Chemical Vapor Deposition Technique. Nanomaterials 2021, 11, 1105. [Google Scholar] [CrossRef]
  13. Huang, H.; Deng, X.; Yan, L.; Wei, G.; Zhou, W.; Liang, X.; Guo, J. One-step synthesis of self-supported Ni3S2/NiS composite film on Ni foam by electrodeposition for high-performance supercapacitors. Nanomaterials 2019, 9, 1718. [Google Scholar] [CrossRef]
  14. Tsai, C.H.; Lin, C.M.; Liu, Y.C. Increasing the efficiency of dye-sensitized solar cells by adding nickel oxide nanoparticles to titanium dioxide working electrodes. Coatings 2020, 10, 195. [Google Scholar] [CrossRef]
  15. Yoo, J.; Kwak, I.H.; Kwon, I.S.; Park, K.; Kim, D.; Lee, J.H.; Lim, S.A.; Cha, E.H.; Park, J. Nickel sulfide nanocrystals for electrochemical and photoelectrochemical hydrogen generation. J. Mater. Chem. C 2020, 8, 3240–3247. [Google Scholar] [CrossRef]
  16. Zhang, Z.; Lv, Q.; Chen, Y.; Yu, H.; Liu, H.; Cui, G.; Sun, X.; Li, L. NiS2@ rGO nanosheet wrapped with PPy aerogel: A sandwich-like structured composite for excellent microwave absorption. Nanomaterials 2019, 9, 833. [Google Scholar] [CrossRef]
  17. Guan, X.; Liu, X.; Xu, B.; Liu, X.; Kong, Z.; Song, M.; Fu, A.; Li, Y.; Guo, P.; Li, H. Carbon wrapped Ni3S2 nanocrystals anchored on graphene sheets as anode materials for lithium-ion battery and the study on their capacity evolution. Nanomaterials 2018, 8, 760. [Google Scholar] [CrossRef]
  18. Wang, L.; Zhu, Y.; Li, H.; Li, Q.; Qian, Y. Hydrothermal synthesis of NiS nanobelts and NiS2 microspheres constructed of cuboids architectures. J. Solid State Chem. 2010, 183, 223–227. [Google Scholar] [CrossRef]
  19. Sarkar, A.; Chakraborty, A.K.; Bera, S. NiS/rGO nanohybrid: An excellent counter electrode for dye sensitized solar cell. Sol. Energy Mater. Sol. Cells 2018, 182, 314–320. [Google Scholar] [CrossRef]
  20. Artal, R.; Serrà, A.; Michler, J.; Philippe, L.; Gómez, E. Electrodeposition of mesoporous Ni-Rich Ni-Pt films for highly efficient methanol oxidation. Nanomaterials 2020, 10, 1435. [Google Scholar] [CrossRef]
  21. Agoro, M.A.; Meyer, E.L.; Mbese, J.Z.; Manu, K. Electrochemical fingerprint of CuS-hexagonal chemistry from (bis(N-1,4-Phenyl-N-(4-morpholinedithiocarbamato)copper(II) complexes) as photon absorber in quantum-dot/dye-sensitised solar cells. Catalysts 2020, 10, 300. [Google Scholar] [CrossRef]
  22. Sathiyaraj, E.; Thirumaran, S.; Ciattini, S.; Selvanayagam, S. Synthesis and characterization of Ni(II) complexes with functionalized dithiocarbamates: New single source precursors for nickel sulfide and nickel-iron sulfide nanoparticles. Inorganica Chim. Acta 2019, 498, 119162. [Google Scholar] [CrossRef]
  23. Ma, R.; Yan, C.; Fong, P.W.K.; Yu, J.; Liu, H.; Yin, J.; Huang, J.; Lu, X.; Yan, H.; Li, G. In situ and ex situ investigations on ternary strategy and co-solvent effects towards high-efficiency organic solar cells. Energy Environ. Sci. 2022, 15, 2479–2488. [Google Scholar] [CrossRef]
  24. Ye, L.; Zhang, S.; Ma, W.; Fan, B.; Guo, X.; Huang, Y.; Ade, H.; Hou, J. From binary to ternary solvent: Morphology fine-tuning of D/A blends in PDPP3T-based polymer solar cells. Adv. Mater. 2012, 24, 6335–6341. [Google Scholar] [CrossRef]
  25. Wang, X.; Batter, B.; Xie, Y.; Pan, K.; Liao, Y.; Lv, C.; Li, M.; Sui, S.; Fu, H. Highly crystalline, small sized, monodisperse α-NiS nanocrystal ink as an efficient counter electrode for dye-sensitized solar cells. J. Mater. Chem. A 2015, 3, 15905–15912. [Google Scholar] [CrossRef]
  26. Harding, D.J.; Harding, P.; Dokmaisrijan, S.; Adams, H. Redox-active nickel and cobalt tris(pyrazolyl) borate dithiocarbamate complexes: Air-stable Co(II) dithiocarbamates. Dalton Trans. 2011, 40, 1313–1321. [Google Scholar] [CrossRef]
  27. Khalil, A.T.; Khan, M.D.; Razzaque, S.; Afridi, S.; Ullah, I.; Iqbal, J.; Tasneem, S.; Shah, A.; Shinwari, Z.K.; Revaprasadu, N.; et al. Single precursor-based synthesis of transition metal sulfide nanoparticles and evaluation of their antimicrobial, antioxidant and cytotoxic potentials. Appl. Nanosci. 2021, 11, 2489–2502. [Google Scholar] [CrossRef]
  28. Thangwane, C.S.; Xaba, T.; Moloto, M.J. The formation of the mixed morphology of nickel sulfide nanoparticles derived from substituted benzimidazole dithiocarbamate nickel(II) complexes. Chalcogenide Lett. 2017, 14, 407–417. [Google Scholar]
  29. Roffey, A.; Hollingsworth, N.; Islam, H.U.; Mercy, M.; Sankar, G.; Catlow, C.R.A.; Hogarth, G.; de Leeuw, N.H. Phase control during the synthesis of nickel sulfide nanoparticles from dithiocarbamate precursors. Nanoscale 2016, 8, 11067–11075. [Google Scholar] [CrossRef]
  30. Shombe, G.B.; Khan, M.D.; Zequine, C.; Zhao, C.; Gupta, R.K.; Revaprasadu, N. Direct solvent free synthesis of bare α-NiS, β-NiS and α-β-NiS composite as excellent electrocatalysts: Effect of self-capping on supercapacitance and overall water splitting activity. Sci. Rep. 2020, 10, 3260. [Google Scholar] [CrossRef]
  31. Nqombolo, A.; Ajibade, P.A. Synthesis and spectral studies of Ni(II) dithiocarbamate complexes and their use as precursors for nickel sulphides nanocrystals. J. Chem. 2016, 2016, 1293790. [Google Scholar] [CrossRef] [Green Version]
  32. Muhamed Shajudheen, V.P.; Senthil Kumar, V.; Anitha Rani, K.; Uma Maheswari, A.; Kumar, S. Structural and Optical Properties of NiS Nanoparticles Synthesized by Chemical Precipitation Method. IJIRSET 2016, 5, 15099–15103. [Google Scholar] [CrossRef]
  33. Raju, G.S.R.; Pavitra, E.; Nagaraju, G.; Sekhar, S.C.; Ghoreishian, S.M.; Kwak, C.H.; Yu, J.S.; Huh, Y.S.; Han, Y.K. Rational design of forest-like nickel sulfide hierarchical architectures with ultrahigh areal capacity as a binder-free cathode material for hybrid supercapacitors. J. Mater. Chem. A 2018, 6, 13178–13190. [Google Scholar] [CrossRef]
  34. Li, W.; Chen, Q.; Zhong, Q. One-pot fabrication of mesoporous g-C3N4/NiS co-catalyst counter electrodes for quantum-dot-sensitized solar cells. J. Mater. Sci. 2020, 55, 10712–10724. [Google Scholar] [CrossRef]
  35. Harish, S.; Naveen, A.N.; Abinaya, R.; Archana, J.; Ramesh, R.; Navaneethan, M.; Shimomura, M.; Hayakawa, Y. Enhanced performance on capacity retention of hierarchical NiS hexagonal nanoplate for highly stable asymmetric supercapacitor. Electrochim. Acta 2018, 283, 1053–1062. [Google Scholar] [CrossRef]
  36. Lehtinen, K.E.; Zachariah, M.R. Effect of coalescence energy release on the temporal shape evolution of nanoparticles. Phys. Rev. B 2001, 63, 205402. [Google Scholar] [CrossRef]
  37. Zheng, H.; Smith, R.K.; Jun, Y.W.; Kisielowski, C.; Dahmen, U.; Alivisatos, A.P. Observation of single colloidal platinum nanocrystal growth trajectories. Science 2009, 324, 1309–1312. [Google Scholar] [CrossRef]
  38. Londoño-Calderón, V.; Ospina, R.; Rodriguez-Pereira, J.; Rincón-Ortiz, S.A.; Restrepo-Parra, E. Molybdenum and Nickel Nanoparticles Synthesis by Laser Ablation towards the Preparation of a Hydrodesulfurization Catalyst. Catalysts 2020, 10, 1076. [Google Scholar] [CrossRef]
  39. Rajeshkhanna, G.; Singh, T.I.; Kim, N.H.; Lee, J.H. Remarkable bifunctional oxygen and hydrogen evolution electrocatalytic activities with trace-level Fe doping in Ni-and Co-layered double hydroxides for overall water-splitting. ACS Appl. Mater. Interfaces 2018, 10, 42453–42468. [Google Scholar] [CrossRef] [PubMed]
  40. Fazlali, F.; reza Mahjoub, A.; Abazari, R. A new route for synthesis of spherical NiO nanoparticles via emulsion nano-reactors with enhanced photocatalytic activity. Solid State Sci. 2015, 48, 263–269. [Google Scholar] [CrossRef]
  41. Zhou, E.; Tian, L.; Cheng, Z.; Fu, C. Design of NiO flakes@ CoMoO4 nanosheets core-shell architecture on Ni foam for high-performance supercapacitors. Nanoscale Res. Lett. 2019, 14, 221. [Google Scholar] [CrossRef] [PubMed]
  42. Ekeroth, S.; Ikeda, S.; Boyd, R.; Münger, P.; Shimizu, T.; Helmersson, U. Impact of nanoparticle magnetization on the 3D formation of dual-phase Ni/NiO nanoparticle-based nanotrusses. J. Nanoparticle Res. 2019, 21, 228. [Google Scholar] [CrossRef]
  43. Maafa, I.M. Synthesis and characterization of NiS Nanoparticles@ Carbon Nanofiber Composite as Electrocatalyst for Methanol Oxidation. Int. J. Electrochem. Sci. 2021, 16, 210431. [Google Scholar] [CrossRef]
  44. Amrani, M.A.; Alrafai, H.A.; Al-nami, S.Y.; Labhasetwar, N.K.; Qasem, A. Effect of mixing on nickel tartrate and Ni/NiO core/shell nanoparticles: Implications for morphology, magnetic, optical, dielectric and adsorption properties. Opt. Mater. 2022, 127, 112321. [Google Scholar] [CrossRef]
Nanomaterials 12 03409 sch001 550
Scheme 1. Synthesis of bis(NN-dibenzyl-N-p-anisldithiocarbamato)nickel(II) complexes.
Scheme 1. Synthesis of bis(NN-dibenzyl-N-p-anisldithiocarbamato)nickel(II) complexes.
Nanomaterials 12 03409 sch001
Nanomaterials 12 03409 g001 550
Figure 1. TGA (a–c) of [Ni[N,N-benz-N-p-anisldtc], [Ni[N,N-benzldtc], and [Ni[N-p-anisldtc] complexes as NiSa, NiSb, and NiSc and FTIR spectras (d) of NiSa, NiSb, and NiSc nanoparticles.
Figure 1. TGA (a–c) of [Ni[N,N-benz-N-p-anisldtc], [Ni[N,N-benzldtc], and [Ni[N-p-anisldtc] complexes as NiSa, NiSb, and NiSc and FTIR spectras (d) of NiSa, NiSb, and NiSc nanoparticles.
Nanomaterials 12 03409 g001
Nanomaterials 12 03409 g002 550
Figure 2. XRD spectra for NiSa, NiSb, and NiSc as (a) and inset Figure as (b) nanoparticles.
Figure 2. XRD spectra for NiSa, NiSb, and NiSc as (a) and inset Figure as (b) nanoparticles.
Nanomaterials 12 03409 g002
Nanomaterials 12 03409 g003 550
Figure 3. UV—Vis (a) and Tauc plot (b) spectra for NiSa, NiSb, and NiSc nanoparticles.
Figure 3. UV—Vis (a) and Tauc plot (b) spectra for NiSa, NiSb, and NiSc nanoparticles.
Nanomaterials 12 03409 g003
Nanomaterials 12 03409 g004 550
Figure 4. PL spectra for NiSa, NiSb, and NiSc nanoparticles.
Figure 4. PL spectra for NiSa, NiSb, and NiSc nanoparticles.
Nanomaterials 12 03409 g004
Nanomaterials 12 03409 g005a 550Nanomaterials 12 03409 g005b 550
Figure 5. TEM images, d-spacing, and SEAD for NiSa (a–d), NiSb (e–h), and NiSc (i–l) nanoparticles.
Figure 5. TEM images, d-spacing, and SEAD for NiSa (a–d), NiSb (e–h), and NiSc (i–l) nanoparticles.
Nanomaterials 12 03409 g005aNanomaterials 12 03409 g005b
Nanomaterials 12 03409 g006 550
Figure 6. AFM (a,d,g) and SEM images for the prepared NiSa (b,c), NiSb (e,f), and NiSc (h,i) nanoparticles.
Figure 6. AFM (a,d,g) and SEM images for the prepared NiSa (b,c), NiSb (e,f), and NiSc (h,i) nanoparticles.
Nanomaterials 12 03409 g006
Nanomaterials 12 03409 g007 550
Figure 7. EDS spectra of NiSa (a), NiSb (b), and NiSc (c) nanoparticles.
Figure 7. EDS spectra of NiSa (a), NiSb (b), and NiSc (c) nanoparticles.
Nanomaterials 12 03409 g007
Table
Table 1. Summary of NiSa, NiSb, and NiSc nanoparticles prepared by SSPs approach.
Table 1. Summary of NiSa, NiSb, and NiSc nanoparticles prepared by SSPs approach.
SamplesParticle Size (TEM Images (nm))d-Spacing (nm)PL Emission (nm)Band Gap from Taucs Plot (eV)Surface Roughness from AFM (nm)Atomic Percentage from EDS
NiS
NiSa19.69–24.320.304473.1246.814.121.37
NiSb9.08–16.630.256622.9549.16.420.83
NiSc9.37–10.490.304882.533412.811.93
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Agoro, M.A.; Meyer, E.L. Roles of TOPO Coordinating Solvent on Prepared Nano-Flower/Star and Nano-Rods Nickel Sulphides for Solar Cells Applications. Nanomaterials 2022, 12, 3409. https://doi.org/10.3390/nano12193409

AMA Style

Agoro MA, Meyer EL. Roles of TOPO Coordinating Solvent on Prepared Nano-Flower/Star and Nano-Rods Nickel Sulphides for Solar Cells Applications. Nanomaterials. 2022; 12(19):3409. https://doi.org/10.3390/nano12193409

Chicago/Turabian Style

Agoro, Mojeed A., and Edson L. Meyer. 2022. "Roles of TOPO Coordinating Solvent on Prepared Nano-Flower/Star and Nano-Rods Nickel Sulphides for Solar Cells Applications" Nanomaterials 12, no. 19: 3409. https://doi.org/10.3390/nano12193409

APA Style

Agoro, M. A., & Meyer, E. L. (2022). Roles of TOPO Coordinating Solvent on Prepared Nano-Flower/Star and Nano-Rods Nickel Sulphides for Solar Cells Applications. Nanomaterials, 12(19), 3409. https://doi.org/10.3390/nano12193409

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop