Next Article in Journal
Prevention in Thermal Crack Formation in Chabazite (CHA) Zeolite Membrane by Developing Thin Top Zeolite and Thick Intermediate Layers
Next Article in Special Issue
Effect of Amorphous Crosslinker on Phase Behavior and Electro-Optic Response of Polymer-Stabilized Blue Phase Liquid Crystals
Previous Article in Journal
Temperature-Dependent Superplasticity and Strengthening in CoNiCrFeMn High Entropy Alloy Nanowires Using Atomistic Simulations
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 11
Issue 8
10.3390/nano11082112
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Review

Unconventional Approaches to Prepare Triazine-Based Liquid Crystal Dendrimers

by
Yao-Chih Lu
1,
Hsiu-Fu Hsu
2 and
Long-Li Lai
1,*
1
Department of Applied Chemistry, National Chi Nan University, No. 1 University Rd., Puli, Nantou 545, Taiwan
2
Department of Chemistry, Tamkang University, No. 151, Yingzhuan Rd., New Taipei City 251, Taiwan
*
Author to whom correspondence should be addressed.
Nanomaterials 2021, 11(8), 2112; https://doi.org/10.3390/nano11082112
Submission received: 21 July 2021 / Revised: 13 August 2021 / Accepted: 17 August 2021 / Published: 19 August 2021
(This article belongs to the Special Issue Recent Advances in Nanostructured Liquid Crystals: From Supramolecular Order to Applications)
Browse Figures
Versions Notes

Abstract

:
Most triazine-based liquid crystalline (LC) dendrimers reported thus far are the main-chain LC macromolecules with long flexible chains at their periphery and attached to internal rigid or semi-rigid frameworks. Their formation of mesogenic phases often depends on the intermolecular face-to-face π–π interactions between dendritic molecules, which are unusual. Their mesogenic phases can also be formed by incorporation of mesogenic units to the dendritic skeletons through long flexible chains, as most side-chain LC dendrimers, in which the peripheral mesogenic units generally play the important roles. For main-chain triazine-based dendrimers, their morphology is maintained by restricted freedom of rigid or semi-rigid connecting units, and their formations of LC phases are therefore not straightforward to be controlled. In this review, we thus describe modulating of the intermolecular face-to-face π–π interactions between the triazine-based dendritic molecules, with the aim of forming LC phases through molecular design.

1. Introduction

Since the discovery of dendrimers in the late 1970s, [1] there has been substantial development in their synthesis and study of their physical properties. Dendrimers generally consist of a central core, linking bridges and peripheral groups. They can be efficiently prepared by iterative processes through convergent, divergent, and combined approaches as demonstrated in Scheme 1 [2]. Although dendrimers may have a branched architecture and three-dimensional spatial arrangement, their morphology is still predictable. Formed by controllable step-by-step and iterative processes, dendrimers are a class of macromolecules with several characteristics that polymers do not have, such as monodispersity, controllable sizes, and internal cavities [2]. In particular, various types of functionally designed groups can be attached at the periphery of dendrimers to give desired properties for this type of macromolecule. Therefore, dendrimers have been extensively investigated and are currently applied in various fields, including drug delivery [3,4,5,6,7,8,9], catalysis [10,11,12,13,14,15,16], light harvesting [17,18,19,20,21,22], and porous materials [23,24,25,26,27].
With mesogenic units in the dendritic framework, dendrimers have also been observed to exhibit liquid crystal (LC) behaviors on thermal treatment. Compared with traditional LC usually with low molecular weight, LC dendrimers often have a higher molecular weight and exhibit columnar mesophases on thermal treatment and are 2-D regular materials, thus yielding better self-assembling ability in a long-range domain and which have usefulness as solvating candidates in opto-electronic devices [28,29,30,31,32,33,34]. LC dendrimers can generally be divided into side-chain dendrimers in which the mesogenic units are incorporated at the periphery of molecules and main-chain dendrimers in which the mesogenic moieties are designed as linking moieties within the internal framework. Most LC dendrimers are side-chain LCs with flexible cores or linking units and peripheral mesogenic units linked to the internal dendritic structures through long flexible chains. The mesogenic units are important in inducing their LC behavior, and this type of LC dendrimer mostly consists of PMAMA (polyamidoamine), PPI (polypropylimine), Si-derivatives (siloxanes, carbosilanes, and carbosilazanes), and polyester as their dendritic network, all of which have been reviewed extensively [2,35,36,37,38]. Special functional moieties, such as fullerene and ferrocene, may be incorporated in side-chain LC dendrimers for particular properties as reported in literatures [2,36,39]. There are fewer main-chain LC dendrimers [40,41,42,43,44,45] than side-chain LC dendrimers because mesogenic moieties are used as bridging units in their internal structures, leading to a rigid or semi-rigid dendritic framework in the main-chain LC dendrimers in which flexible alkyl chains are frequently grafted at the periphery to increase their solubility in organic solvents. Therefore, in contrast to side-chain LC dendrimers in which the LC phases are mostly induced by the peripheral mesogenic units, both the rigid or semi-rigid internal frameworks and flexible peripheral chains are all important in inducing mesophases for the main-chain LC dendrimers [2,36,37], and this leads the formation of mesophases of the main-chain LC dendrimers to be difficult to control. As in the rod-like liquid crystals, the ionic, H-bond, and metallo interactions are also extensively employed in LC dendrimers, which also consist of side-chain and main-chain types of LC materials, depending on whether their mesogenic units are incorporated in the internal framework or at the periphery of dendritic network, which have been reviewed in the literature [46,47,48].
Cyanuric chloride, a simple heterocycle with three reactive sites on its ring, can be used as a branching unit for efficiently preparing dendrimers. For instance, the first chloro substituent can be replaced by alkylamines at 0 °C, and subsequently, the second and the third substituents can undergo similar substitutions at room temperature and above 60 °C, respectively (Scheme 2) [49,50]. The triazine-based dendrimers were first prepared by Takagi [51] and later investigated by others [52,53]. Little progress on LC dendrimers based on the triazine unit has been reported since then. To the best of our knowledge, in 2008, Lai and co-workers were the first to report LC dendrimers on the basis of the 1,3,5-triamino-s-triazine unit [54]. Kotha and colleagues also prepared 1,3,5-triphenyl-s-triazine-based dendrimers, which exhibited a columnar phase after being mixed with 1:1 molar ratio of trinitrofluorenone [55]. However, there has been less study of triazine-based LC dendrimers, and most are main-chain types of LC dendrimers. Induction of the LC phases of triazine-based dendrimers can be achieved by manipulating the molecular morphology of the dendrimer themselves or by adding extra components to form an LC dendritic mixture by intermolecular H-bond or face-to-face π–π interactions. By reviewing this system, we hope to guide future work in this field.

2. Formation of Triazine-Based LC Dendrimers by Manipulating Their Molecular Morphology

2.1. LC Dendrimers with C2 Symmetry

The LC dendrimer with a C2-symmetry on the basis of a 1,3,5-triamino-s-triazine unit was first reported by Lai and colleagues [54]. They prepared the fourth generation LC dendrimer 1 by the convergent approach (Figure 1), with a single molecular weight of ~12,479. Compound 1 is a monotropic material, showing no mesophase during heating but a columnar hexagonal phase between ~160 and ~143 °C on cooling. Additionally, compound 1 did not show any significant absorbance beyond 280 nm in the UV-vis spectrum and started to decompose at 300 °C under nitrogen by TGA analysis, which is an important characteristic required for opto- and electro-applications. However, the third generation triazine-based dendrimer 2 did not exhibit mesogenic behavior on thermal treatment, isotropic at ~133 °C on heating, and crystallized at ~98 °C on cooling. Computer simulations for the conformations of dendrimers 1 and 2 showed that the steric effect from the peripheral skeleton of 1 is more significant than that of 2 [54], i.e., the dendritic conformation of 1 is less coplanar due to congestion between the branched mainframe, thus reducing the face-to-face π–π interactions between dendritic molecules and forming the columnar phase on thermal treatment. Compared with traditional disk molecules, dendrimer 1 with a C2-symmetry having a columnar LC phase on cooling, is unusual. To exhibit columnar mesophases, the traditional C2-symmetry molecules may consist of a macrocyclic core [56,57]. Introducing a chiral core to result in helical stacking columns by modulating the intermolecular π–π interaction between molecules is another approach [58].

2.2. LC Dendrimers with C3 Symmetry

In addition, deforming the planarity of trigonal disk molecules to reduce face-to-face π–π interactions in traditional molecules can also lead to the formation of columnar mesophases [59]. Therefore, changing the shape of the rigid cores can be an efficient approach for preparing dendrimers with columnar LC phases, and thus two C3-symmetry dendrimers based on a triazine unit have been reported (Figure 2) [60]. Dendrimer 3, with a molecular weight of ~9248, is a monotropic material, which did not exhibit any mesogenic behavior on heating but showed a columnar phase between ~137 and ~100 °C on cooling. Dendrimer 4 exhibited a columnar phase from ~141 to ~173 °C on heating and from ~168 to ~136 °C on cooling.
As demonstrated by dendrimers 1 and 2, high molecular weight deforms the planar mainframe of dendritic molecules and leads to the formation of LC phases on thermal treatment. However, the molecular weight of dendrimer 4 (~4423) is much smaller than that of dendrimer 2 (~6034). Apparently, the C2-to-C3 approach significantly changes planarity of the internal mainframe of dendrimers. Thus 4 exhibits a columnar LC phase during the thermal process although there is less congestion from the dendritic mainframe when compared with that of 2.

2.3. LC Dendrimers with the Loss of C2 Symmetry by Changing the Peripheral Groups

Reducing the intermolecular face-to-face π–π interactions between the molecules of triazine-based dendrimer seems to be a good strategy for forming mesogenic phases on thermal treatment. According to literature [61], mixing two pure components can reduce the molecular interaction in the solid state, and thus lowers the melting point of the mixture. For example, the m.p. of (R)-(−)-2-amino-1-propanol is ~24–26 °C, which is the same as that of (S)-(+)-2-amino-1-propanol, but the m.p. of the 1:1 mixture of these two components drops to ~8–10 °C. Accordingly, four triazine-based LC dendrimers were prepared (Figure 3) [62]. Dendrimer 5, with the loss of the C2-symmetry, exhibited a columnar phase from ~95 to ~152 °C on heating and from ~147 to ~64 °C on cooling. Dendrimer 6, also with the loss of the C2-symmetry, is a monotropic material, only showing a columnar phase between ~123 and ~145 °C on heating. Dendrimers 7 and 8, with a C2-symmetry, did not exhibit any mesogenic phase on thermal treatment. Dendrimer 7 became isotropic at ~132 °C on heating and crystallized at ~117 °C on cooling; and dendrimer 8 became isotropic at ~229 °C on heating and solidified at ~221 °C on cooling. Dendrimers 5, 6, 7, and 8 all have similar molecular weights of ~2368, ~2030, ~2813, and ~2363, respectively. Based on the molecular simulation investigations [62], they are almost co-planar and the congestions between their dendritic frameworks are negligible. However, dendrimers 5 and 6 are isomeric. As shown in Figure 4, dendrimers 5 or 6, in principle, can be produced from the combination of the corresponding Cl-dendron and piperazino-dendron, respectively. Each dendron consists of at least four isomers, and therefore, dendrimers 5 and 6 have many isomers in their solid stackings, reducing their intermolecular face-to-face π–π interactions and forming LC phase during the thermal process.

2.4. LC Dendrimers with the Loss of C2 Symmetry by Changing the Central Cores

Partially changing the peripheral group to break C2-symmetry of molecules can lead dendrimers to contain isomers, and face-to-face π–π interactions between dendritic molecules are thus modulated to form the LC phase with thermal treatment. This strategy can also be applied to central linkers of dendrimers. With the peripheral group fixed by the dialkylamino units, the central linker is modulated as C5H10, C4H8, C3H6, and C2H4 (Figure 5) [63]. Dendrimers 9 and 11, with the odd-number carbon linker in the dendritic core, are LCs. Dendrimer 9 was observed to exhibit a columnar phase from ~109 to ~168 °C on heating and from ~146 to ~87 °C on cooling. Dendrimer 11 showed a columnar phase between ~107 and ~144 °C on heating and between ~115 and ~81 °C on cooling. Dendrimers 10 and 12 with the even-number carbon linker in the dendritic core are not liquid crystalline. The solid-phase-to-isotropic-phase (solid-to-iso) transition temperatures for dendrimers 10 and 12 are ~132 and ~147 °C, respectively, on heating, and the isotropic-phase-to-solid-phase (iso-to-solid) transition temperatures for 10 and 12 are ~100 and ~90 °C, respectively, on cooling.
Molecular weights for dendrimers 9–12 are similar: ~6050, ~6036, ~6022, and ~6008, respectively. A computer simulation for molecular conformations of dendrimers 9 and 10 showed that 9 is asymmetrical and 10 is symmetrical along with the central linkers, and a diagram can show their differences [63]. As shown in Figure 6, dendrimer 10, with a 4-carbon linker in the dendritic core, allows the dendronic halves to be located at the anti-position of the C4H8 linker to reduce repulsions between Hs (at C2 and C3) and the dendronic halves. Therefore, the molecular conformation of 10 is almost symmetrical. Accordingly, dendrimer 11 with a 3-carbon linker leads both the dendronic halves to exist in the syn-position of the C3H6 linker to reduce corresponding repulsions; in this conformation, two isomers of dendrimer 11 should exist since the left dendronic half may be on the top or bottom of the right dendronic half (Figure 6). Because of the isomeric effect, the intermolecular face-to-face π–π interactions are reduced in the solid stacking, and the columnar phases of dendrimers 9 and 11 are thus formed on thermal treatment. To further understand the isomeric effect on influencing their stackings in LC state, their molecular volumes (Vm) and cell volumes (Vcell) were calculated on the basis of powder-XRD data of dendrimers 9 and 11 [63]. Since the calculated volumes are temperature-dependent, and the XRD data for 9 and 11 were collected at different temperatures, the Vm/Vcell ratios, instead of Vm or Vcell, were compared to remove the temperature factor. The Vm/Vcell ratios of 9 and 11 were calculated to be ~1.03 and ~0.95, respectively. For the non-mesogenic compounds 10 and 12, crystalline XRD data were also used for calculation, assuming that both formed the columnar hexagonal crystalline phase; the Vm/Vcell ratios of 10 and 12 were estimated to be ~0.92 and ~0.87, respectively.
The ratios of Vm/Vcell for 9 and 11 are larger than those for 10 and 12, indicating that the stackings of 9 and 11 in the solid state are somewhat looser than those of 10 and 12. This further indicates that the isomeric effect on dendrimers can probably modulate the face-to-face π–π interactions between dendritic molecules.
As indicated previously, the repulsion between dendronic halves and the Hs (at C2 or C3) significantly influences the conformation of dendrimer 10. If the central linker of 10 was methylated on nitrogen, then the repulsion between Me and the Hs (at C2 or C3) should increase, although the repulsion should be smaller than that between the dendronic halves and the corresponding Hs (at C2 or C3). However, this should convert several of the dendronic halves at the anti-position of C4H8 linker to the syn-position. Specifically, dendrimer 13 should have three isomers in the solid state, as shown in Figure 7 [64], although most of the 13 exists as the form of isomer 13-I and, as expected, dendrimer 13 exhibited a columnar phase on thermal treatment (Figure 8). The mesogenic range is from ~111 to ~123 °C on heating and from ~115 to ~94 °C on cooling. Accordingly, dendrimer 14 has three isomers in the solid state but showed only a columnar phase between ~94 and ~72 °C on cooling without showing any mesogenic behavior on heating.
The solid-to-iso transition temperatures of dendrimers 10 and 12 on heating are ~132 and ~147 °C, respectively, which are higher than those of corresponding dendrimers 13 and 14 (~118 and 123 °C, respectively). This indicates that methylation of nitrogen in the central linker affects their molecular morphology and somewhat loosens their solid stacking. Based on the powder-XRD data of dendrimers 13 and 14, their ratios of Vm/Vcell were also calculated. The Vm/Vcell ratio of 13 was ~0.92, similar to that of 10 (~0.92) and the Vm/Vcell ratio of 14 was ~0.80, which is smaller to that of 12 (~0.87).
Although methylation of nitrogens in the central linker of dendrimers converts non-mesogenic 10 and 12 to become mesogenic 13 and 14, respectively, the isomeric effect seems to not be significant in reducing intermolecular face-to-face π–π interactions, allowing dendrimers 13 and 14 to be looser in the solid stacking than dendrimers 10 and 12. Based on the optimal conformation of 13 [64], it was discovered that four intramolecular H-bond interactions arise between Na (a = 7, 8, 9, 10) and H (at Cb; b = 1, 4, 5, 6), respectively, as shown in Figure 9. Accordingly, only two intramolecular H-bond interactions arise between Na (a = 5, 6) and H (at Cb; b = 1, 4,) in dendrimer 10. Therefore, dendrimer 13 that mostly exists in the form of 13-I should be more rigid and is less distorted than dendrimer 10, and therefore the void space inside the solid stacking of 10 should be larger than that inside the dendritic framework of 13-I. However, because of the isomeric effect, the face-to-face π–π interactions between dendritic molecules of 13 is reduced and therefore its dendritic framework is fluffier. As a result, dendrimers 10 and 13 have almost the same Vm/Vcell ratio (~0.92) on the basis of balancing the two conflicting factors. When the central linker is shortened, congestion from dendritic halves of 12 is more vigorous and the distortion allows dendrimer 12 to become more porous. Therefore, the Vm/Vcell ratio of 12 (~0.87) is larger than that of 14 (~0.80).
The central linkers in triazine-based dendrimers significantly influence their morphology and consequently affect the formation of the mesophase during the thermal process. Instead of N-alkylation of an even-number carbon central linker, this strategy was also undertaken to an odd-number carbon central linker. As dendrimer 11 has already been observed to exhibit a columnar phase on thermal treatment, a strong CN polar group was incorporated in the central linker to investigate its influence on the mesogenic behavior. Dendrimers 15 and 16 were therefore further prepared for studying their LC properties (Figure 10) [65]. Dendrimer 15 exhibited a columnar phase between ~102 and ~118 °C on heating and between ~115 and ~82 °C on cooling. Dendrimer 16 showed a columnar phase from ~88 to ~144 °C on heating and from ~138 to ~68 °C on cooling. Compared with the DSC behaviors of 11, the solid-to-iso transition temperature of 15 (~118 °C) was lower than that of 11 (~144 °C) on heating, indicating that the alkylation on N in the central linker increased the steric congestion of triazine-based dendrimer and somewhat loosened their solid stacking as shown in the study of dendrimers 10, 12, 13 and 14. The solid-to-iso transition temperature of 16 (~144 °C) was similar to that of 11 (~144 °C), and the mesogenic range of 16 on cooling (from ~138 to ~68 °C) was broader than that of 11 (from ~115 to ~81 °C). The CN group in the central linker not only lowered the solidifying temperature but also raised the isotropic-phase-to-columnar-mesophase (iso-to-col) transition temperature on cooling. In principle, the steric congestion from benzyl moiety in the central linker of dendrimers 15 should not differ from and 4-cyanobenzyl moiety in 16, but their mesogenic behaviors on thermal treatment are significantly different. The strong polarity of the CN group strengthens intermolecular interactions between face-to-face dendritic molecules. For further understanding, the Vm/Vcell ratios of 15 and 16 were estimated on the basis of their powder-XRD data as ~0.80 and ~0.98, respectively. The Vm/Vcell ratio of dendrimer 16 was larger than that of 11 (~0.95), but that of dendrimer 15 was smaller, indicating that the loose order of their stacking is 16 > 11 > 15. As dendrimers 11, 15, and 16 all show a columnar phase in the mesogenic range, the face-to-face distances between two dendritic molecules (dslice) for 11, 15, and 16 can be obtained from the powder-XRD data in a similar manner and are calculated to be 13.14, 13.28, and 13.68 Å, respectively. The Vm/Vcell ratios and dslice distances show that the strong polarity of CN group significantly increased the face-to-face distance between dendritic molecules within columns. This reasonably explains that the col-to-solid transition temperature on cooling of 16 is lower than those of 11 and 15. However, as indicated previously, the solid-to-iso transition temperature of 16 (~144 °C) is similar to that of 11 (~144 °C) on heating, which can also be ascribed to the strong polarity of the CN group. During the heating process, the strong intermolecular polar-to-polar interactions within columns led dendrimer 16 to have the same solid-to-iso transition temperature as 11, although the stacking of 16 was looser. Neither dendrimer 11 nor 15 contains any functional group in the central linker, but the dslice distance of 15 within columns is 13.28 Å, only slightly larger than that of 11 (13.14 Å). The more void space between dendritic molecules of 15 is occupied by the benzyl group, which results in the lower Vm/Vcell ratio of 15 (0.80) versus that of 11 (0.95). Since the dslice distances of 11 and 15 do not differ from each other, the mesophase ranges of both dendrimer are also similar to each other.

3. Formation of Triazine-Based LC Dendrimers by Adding Extra Components

3.1. Formation of LC Dendrimers by Intermolecular π–π Interaction

In addition to manipulating the morphology of dendritic molecules to form their LC phase, mixing extra components to non-liquid-crystalline (non-LC) triazine-based dendrimers can lead to the mesophase formation. Dendrimers 17 and 18 were reported to be non-LC on thermal treatment (Figure 11) [55]. Compound 17 became isotropic at ~66 °C on heating but no transition was observed on cooling. Compound 18 became isotropic at ~57 °C on heating and crystallized at ~32 °C on cooling. After mixing with 1:1 molar ratio of trinitrofluorenone (TNF), the mixture of 17-TNF showed a columnar phase between ~56 and ~78 °C on heating but still no transition was observed on cooling. The mixture of 18-TNF exhibited a columnar phase from ~51 to ~102 °C on heating and from ~97 °C to room temperature on cooling [55]. It is believed that TNF forms a complex mixture with 17 or 18 through the face-to-face π-π interactions, thereby adjusting the distance between dendritic molecules and showing LC phases on thermal treatment.

3.2. Formation of LC Dendrimers by Intermolecular H-Bond Interaction

Apart from the face-to-face π–π interactions, the LC dendritic mixtures can also be formed by the intermolecular H-bond interaction. Mixing 2,4-diamino-6-dodecyl-1,3,4- triazine with carboxylic acid-containing dendron in a 1:3 ratio generates H-bonded dendrimers 19 and 20, as shown in Figure 12 [66]. The acid-containing dendrons 21 and 22 did not exhibit any mesophase on thermal treatment. Compound 21 showed only a glass-phase-to-isotropic-phase (glass-to-iso) transition temperature at ~52 °C on heating, and compound 22 showed a glass-to-iso transition temperature at ~46 °C on heating. Instead of a columnar phase, dendrimer 19 exhibited a nematic phase between ~4 and ~35 °C on heating, and dendrimer 20 was observed to exhibit a SmA phase from ~43 and ~70 °C on heating. Neither dendrimers nor dendrons were reported to show any mesophase on cooling. A carbazole unit was incorporated in dendrimers and dendrons for studying their photoconductivities, but the performances of dendrons 21 and 22 were slightly better than those of dendrimers 19 and 20, respectively.

4. Possible Applications

As shown in the literature, the triazine-based LC dendrimers are thermally stable and nearly transparent beyond 280 nm in the UV/Vis range [54]. Moreover, these dendrimers are electrochemically stable in solution and can survive in acidic media for a period of time [52]. These characteristics are important and are often required for opto- and electro-applications. In addition, LC dendrimers often have a high molecular weight, exhibiting columnar phases on thermal treatment and thus exhibiting good self-assembling ability in a long-range domain. In solvating guest materials, such as carbon nanotubes and nano-size catalysts, the LC dendrimers can lead the physical properties of guest molecules to be significantly displayed [28,29,30,31,32,33,34]. As shown in the introduction, dendrimers have been shown to be useful in the fields of catalysis [10,11,12,13,14,15,16] and light harvesting [17,18,19,20,21,22]. With the assistance of LC dendrimers, the guest molecules should be more regularly arranged, thus exhibiting their physical characteristics significantly.

5. Conclusions and Prospect

Three approaches have been described to prepare triazine-based dendrimers with mesogenic phase on thermal treatment. The first is to properly incorporate mesogenic units onto triazine and piperazine framework in a straightforward manner by molecular design.
The second approach is to mix components to form LC dendritic mixtures by adjusting intermolecular face-to-face π–π interactions, which is valuable for 1,3,5-triamino-s-triazine-based LC dendrimers. The mixing approach allows versatile preparation of 1,3,5-triamino-s-triazine-based dendrimers, which were observed to form strong π–π interactions with tetrafluorbenzoquinone (TFB) in CH2Cl2, and the red shift of absorbance from the dendrimer-TFB complexes in the UV-Vis spectra can be up to ~180 nm [67].
Intermolecular H-bond interactions can also be applied to prepare 1,3,5-triamino-s-triazine-based dendrimers with the columnar phase. Figure 13 shows an example of a central core with a C2 symmetry that can be efficiently prepared according to the literatures [62,63,64,65,66,67]. Incorporating special functional groups at the periphery of dendrons can give desired physical properties to the LC triazine-based dendritic mixtures. Although the photoconductivity of the resulting dendrimers from the mixtures of 2,4-diamino-6-dodecyl-1,3,4-triazine and the corresponding dendrons is not better than those of dendrons alone, this property may be improved if columnar phases are formed on the thermal treatment of the dendritic mixtures since these columnar mesogens show better long-range self-assembling ability. Compound 23 may be likely to form columnar mesophases when treated with proper acid-containing dendrons.

Author Contributions

Conceptualization, methodology, writing—original draft preparation, L.-L.L.; writing—review and editing, L.-L.L., H.-F.H., and Y.-C.L.; software, formal analysis, investigation visualization, validation, data curation, Y.-C.L.; supervision, funding acquisition and project administration, L.-L.L. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by the National Chi Nan University and the Ministry of Science and Technology, Taiwan (108-2113-M-260-008- and 109-2113-M-260 -001).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The data presented in this study are available on request from the corresponding author.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Tomalia, D.A.; Fréchet, J.M.J. Discovery of dendrimers and dendritic polymers: A brief historical perspective. J. Polym. Sci. A Polym. Chem. 2002, 40, 2719–2728. [Google Scholar] [CrossRef]
  2. Caminade, A.-M.; Turrin, C.-O.; Laurent, R.; Ouali, A.; Delavaux-Nicot, B. Dendrimers: Towards Catalytic, Material and Biomedical Uses; Wiley: New York, NY, USA, 2011. [Google Scholar]
  3. Janaszewska, A.; Lazniewska, J.; Trzepiński, P.; Marcinkowska, M.; Klajnert-Maculewicz, B. Cytotoxicity of Dendrimers. Biomolecules 2019, 9, 330. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  4. Chauhan, A.S. Dendrimers for Drug Delivery. Molecules 2018, 23, 938. [Google Scholar] [CrossRef] [Green Version]
  5. Sherje, A.P.; Jadhav, M.; Dravyakar, B.R.; Kadam, D. Dendrimers: A versatile nanocarrier for drug delivery and targeting. Int. J. Pharm. 2018, 548, 707–720. [Google Scholar] [CrossRef]
  6. Kaur, D.; Jain, K.; Mehra, N.K.; Kesharwani, P.; Jain, N.K. A review on comparative study of PPI and PAMAM dendrimers. J. Nanopart. Res. 2016, 18, 146. [Google Scholar] [CrossRef]
  7. Kesharwani, P.; Jain, K.; Jain, N.K. Dendrimer as nanocarrier for drug delivery. Prog. Polym. Sci. 2014, 39, 268–307. [Google Scholar] [CrossRef]
  8. Madaan, K.; Kumar, S.; Poonia, N.; Lather, V.; Pandita, D. Dendrimers in drug delivery and targeting: Drug-dendrimer interactions and toxicity issues. J. Pharm. Bioallied Sci. 2014, 6, 139–150. [Google Scholar] [PubMed]
  9. Mignani, S.; El Kazzouli, S.; Bousmina, M.; Majoral, J.-P. Expand classical drug administration ways by emerging routes using dendrimer drug delivery systems: A concise overview. Adv. Drug Deliv. Rev. 2013, 65, 1316–1330. [Google Scholar] [CrossRef]
  10. Liu, Y.; Lopes, R.P.; Lüdtke, T.; Di Silvio, D.; Moya, S.; Hamon, J.-R.; Astruc, D. “Click” dendrimer-Pd nanoparticle assemblies as enzyme mimics: Catalytic o-phenylenediamine oxidation and application in colorimetric H2O2 detection. Inorg. Chem. Front. 2021, 8, 3301–3307. [Google Scholar] [CrossRef]
  11. Yamamoto, K.; Imaoka, T.; Tanabe, M.; Kambe, T. New Horizon of Nanoparticle and Cluster Catalysis with Dendrimers. Chem. Rev. 2020, 120, 1397–1437. [Google Scholar] [CrossRef] [PubMed]
  12. Tang, Y.-H.; Cangiotti, M.; Kao, C.-L.; Ottaviani, M.F. EPR Characterization of Copper(II) Complexes of PAMAM-Py Dendrimers for Biocatalysis in the Absence and Presence of Reducing Agents and a Spin Trap. J. Phys. Chem. B 2017, 121, 10498–10507. [Google Scholar] [CrossRef]
  13. Neumann, P.; Dib, H.; Caminade, A.-M.; Hey-Hawkins, E. Redox Control of a Dendritic Ferrocenyl-Based Homogeneous Catalyst. Angew. Chem. Int. Ed. 2015, 54, 311–314. [Google Scholar] [CrossRef] [PubMed]
  14. Twyman, L.J.; King, A.S.H.; Martin, I.K. Catalysis inside dendrimers. Chem. Soc. Rev. 2002, 31, 69–82. [Google Scholar] [CrossRef]
  15. Astruc, D.; Chardac, F. Dendritic Catalysts and Dendrimers in Catalysis. Chem. Rev. 2001, 101, 2991–3024. [Google Scholar] [CrossRef]
  16. Crooks, R.M.; Zhao, M.; Sun, L.; Chechik, V.; Yeung, L.K. Dendrimer-Encapsulated Metal Nanoparticles:  Synthesis, Characterization, and Applications to Catalysis. Acc. Chem. Res. 2001, 34, 181–190. [Google Scholar] [CrossRef] [Green Version]
  17. Concellón, A.; Termine, R.; Golemme, A.; Romero, P.; Marcos, M.; Serrano, J.L. High hole mobility and light-harvesting in discotic nematic dendrimers prepared via ‘click’ chemistry. J. Mater. Chem. C 2019, 7, 2911–2918. [Google Scholar] [CrossRef]
  18. Yim, D.; Sung, J.; Kim, S.; Oh, J.; Yoon, H.; Sung, Y.M.; Kim, D.; Jang, W.-D. Guest-Induced Modulation of the Energy Transfer Process in Porphyrin-Based Artificial Light Harvesting Dendrimers. J. Am. Chem. Soc. 2017, 139, 993–1002. [Google Scholar] [CrossRef] [PubMed]
  19. Nantalaksakul, A.; Reddy, D.R.; Bardeen, C.J.; Thayumanavan, S. Light Harvesting Dendrimers. Photosyn. Res. 2006, 87, 133–150. [Google Scholar] [CrossRef]
  20. Balzani, V.; Ceroni, P.; Maestri, M.; Vicinelli, V. Light-harvesting dendrimers. Curr. Opin. Chem. Biol. 2003, 7, 657–665. [Google Scholar] [CrossRef] [PubMed]
  21. Adronov, A.; Fréchet, J.M.J. Light-harvesting dendrimers. Chem. Comm. 2000, 18, 1701–1710. [Google Scholar] [CrossRef]
  22. Gilat, S.L.; Adronov, A.; Fréchet, J.M.J. Light Harvesting and Energy Transfer in Novel Convergently Constructed Dendrimers. Angew. Chem. Int. Ed. 1999, 38, 1422–1427. [Google Scholar] [CrossRef]
  23. Wang, Y.; He, X.; Lu, Q. Polyamidoamine dendrimer functionalized cellulose nanocrystals for CO2 capture. Cellulose 2021, 28, 4241–4251. [Google Scholar] [CrossRef]
  24. El Kadib, A.; Katir, N.; Bousmina, M.; Majoral, J.P. Dendrimer–Silica hybrid mesoporous materials. New J. Chem. 2012, 36, 241–255. [Google Scholar] [CrossRef]
  25. Bonaccorsi, L.; Lombardo, D.; Longo, A.; Proverbio, E.; Triolo, A. Dendrimer Template Directed Self-Assembly during Zeolite Formation. Macromolecules 2009, 42, 1239–1243. [Google Scholar] [CrossRef]
  26. Yoo, S.; Lunn, J.D.; Gonzalez, S.; Ristich, J.A.; Simanek, E.E.; Shantz, D.F. Engineering Nanospaces:  OMS/Dendrimer Hybrids Possessing Controllable Chemistry and Porosity. Chem. Mater. 2006, 18, 2935–2942. [Google Scholar] [CrossRef]
  27. Kriesel, J.W.; Tilley, T.D. Dendrimers as Building Blocks for Nanostructured Materials:  Micro- and Mesoporosity in Dendrimer-Based Xerogels. Chem. Mater. 1999, 11, 1190–1193. [Google Scholar] [CrossRef]
  28. Martínez, N.P.; Inostroza-Rivera, R.; Durán, B.; Molero, L.; Bonardd, S.; Ramírez, O.; Isaacs, M.; Díaz Díaz, D.; Leiva, A.; Saldías, C. Exploring the Effect of the Irradiation Time on Photosensitized Dendrimer-Based Nanoaggregates for Potential Applications in Light-Driven Water Photoreduction. Nanomaterials 2019, 9, 1316. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  29. Avila-Salas, F.; Pereira, A.; Rojas, M.A.; Saavedra-Torres, M.; Montecinos, R.; Bonardd, S.; Quezada, C.; Saldías, S.; Díaz Díaz, D.; Leiva, A.; et al. An experimental and theoretical comparative study of the entrapment and release of dexamethasone from micellar and vesicular aggregates of PAMAM-PCL dendrimers. Eur. Polym. J. 2017, 93, 507–520. [Google Scholar] [CrossRef]
  30. Axenov, K.V.; Laschat, S. Thermotropic Ionic Liquid Crystals. Materials 2011, 4, 206–259. [Google Scholar] [CrossRef] [PubMed]
  31. Rosen, B.M.; Wilson, C.J.; Wilson, D.A.; Peterca, M.; Imam, M.R.; Percec, V. Dendron-Mediated Self-Assembly, Disassembly, and Self-Organization of Complex Systems. Chem. Rev. 2009, 109, 6275–6540. [Google Scholar] [CrossRef]
  32. Goodby, J.W.; Saez, I.M.; Cowling, S.J.; Görtz, V.; Draper, M.; Hall, A.W.; Sia, S.; Cosquer, G.; Lee, S.-E.; Raynes, E.P. Transmission and Amplification of Information and Properties in Nanostructured Liquid Crystals. Angew. Chem. Int. Ed. 2008, 47, 2754–2787. [Google Scholar] [CrossRef]
  33. Kim, H.-J.; Jung, E.-Y.; Jin, L.Y.; Lee, M. Solution Behavior of Dendrimer-Coated Rodlike Coordination Polymers. Macromolecules 2008, 41, 6066–6072. [Google Scholar] [CrossRef]
  34. Inoue, K. Functional dendrimers, hyperbranched and star polymers. Prog. Polym. Sci. 2000, 25, 453–571. [Google Scholar] [CrossRef]
  35. Hernández-Ainsa, S.; Barberá, J. Fluorinated liquid crystalline dendrimers. J. Fluor. Chem 2015, 177, 37–45. [Google Scholar] [CrossRef]
  36. Donnio, B.; Buathong, S.; Bury, I.; Guillon, D. Liquid crystalline dendrimers. Chem. Soc. Rev. 2007, 36, 1495–1513. [Google Scholar] [CrossRef] [PubMed]
  37. Marcos, M.; Martín-Rapún, R.; Omenat, A.; Serrano, J.L. Highly congested liquid crystal structures: Dendrimers, dendrons, dendronized and hyperbranched polymers. Chem. Soc. Rev. 2007, 36, 1889–1901. [Google Scholar] [CrossRef] [PubMed]
  38. Saez, I.M.; Goodby, J.W. Supermolecular liquid crystals. J. Mater. Chem. 2005, 15, 26–40. [Google Scholar] [CrossRef]
  39. Deschenaux, R.; Donnio, B.; Guillon, D. Liquid-crystalline fullerodendrimers. New J. Chem. 2007, 31, 1064–1073. [Google Scholar] [CrossRef] [Green Version]
  40. Gehringer, L.; Bourgogne, C.; Guillon, D.; Donnio, B. Liquid-Crystalline Octopus Dendrimers:  Block Molecules with Unusual Mesophase Morphologies. J. Am. Chem. Soc. 2004, 126, 3856–3867. [Google Scholar] [CrossRef]
  41. Gehringer, L.; Guillon, D.; Donnio, B. Liquid Crystalline Octopus: An Alternative Class of Mesomorphic Dendrimers. Macromolecules 2003, 36, 5593–5601. [Google Scholar] [CrossRef]
  42. Meier, H.; Lehmann, M. Stilbenoid Dendrimers. Angew. Chem. Int. Ed. 1998, 37, 643–645. [Google Scholar] [CrossRef]
  43. Pesak, D.J.; Moore, J.S. Columnar Liquid Crystals from Shape-Persistent Dendritic Molecules. Angew. Chem. Int. Ed. Engl. 1997, 36, 1636–1639. [Google Scholar] [CrossRef]
  44. Li, J.-F.; Crandall, K.A.; Chu, P.; Percec, V.; Petschek, R.G.; Rosenblatt, C. Dendrimeric Liquid Crystals:  Isotropic−Nematic Pretransitional Behavior. Macromolecules 1996, 29, 7813–7819. [Google Scholar] [CrossRef]
  45. Percec, V.; Chu, P.; Ungar, G.; Zhou, J. Rational Design of the First Nonspherical Dendrimer Which Displays Calamitic Nematic and Smectic Thermotropic Liquid Crystalline Phases. J. Am. Chem. Soc. 1995, 117, 11441–11454. [Google Scholar] [CrossRef]
  46. Goossens, K.; Lava, K.; Bielawski, C.W.; Binnemans, K. Ionic Liquid Crystals: Versatile Materials. Chem. Rev. 2016, 116, 4643–4807. [Google Scholar] [CrossRef] [PubMed]
  47. Donnio, B. Liquid–crystalline metallodendrimers. Inorg. Chim. Acta 2014, 409, 53–67. [Google Scholar] [CrossRef]
  48. Kato, T.; Mizoshita, N.; Kishimoto, K. Functional Liquid-Crystalline Assemblies: Self-Organized Soft Materials. Angew. Chem. Int. Ed. 2006, 45, 38–68. [Google Scholar] [CrossRef]
  49. Schnabel, W.J.; Rätz, R.; Kober, E. The Synthesis of Substituted Melams. J. Org. Chem. 1962, 27, 2514–2519. [Google Scholar] [CrossRef]
  50. Thurston, J.T.; Dudley, J.R.; Kaiser, D.W.; Hechenbleikner, I.; Schaefer, F.C.; Holm-Hansen, D. Cyanuric Chloride Derivatives. I. Aminochloro-s-triazines. J. Am. Chem. Soc. 1951, 73, 2981–2983. [Google Scholar] [CrossRef]
  51. Takagi, K.; Hattori, T.; Kunisada, H.; Yuki, Y. Triazine dendrimers by divergent and convergent methods. J. Polym. Sci. A Polym. Chem. 2000, 38, 4385–4395. [Google Scholar] [CrossRef]
  52. Lai, L.-L.; Wang, L.-Y.; Lee, C.-H.; Lin, Y.-C.; Cheng, K.-L. Nanomaterials of Triazine-Based Dendrons:  Convergent Synthesis and Their Physical Studies. Org. Lett. 2006, 8, 1541–1544. [Google Scholar] [CrossRef] [PubMed]
  53. Steffensen, M.B.; Hollink, E.; Kuschel, F.; Bauer, M.; Simanek, E.E. Dendrimers based on [1,3,5]-triazines. J. Polym. Sci. A Polym. Chem. 2006, 44, 3411–3433. [Google Scholar] [CrossRef] [Green Version]
  54. Lai, L.-L.; Lee, C.-H.; Wang, L.-Y.; Cheng, K.-L.; Hsu, H.-F. Star-Shaped Mesogens of Triazine-Based Dendrons and Dendrimers as Unconventional Columnar Liquid Crystals. J. Org. Chem. 2008, 73, 485–490. [Google Scholar] [CrossRef] [PubMed]
  55. Kotha, S.; Kashinath, D.; Kumar, S. Synthesis of liquid crystalline materials based on 1,3,5-triphenylbenzene and 2,4,6-triphenyl-1,3,5-s-triazine. Tetrahedron Lett. 2008, 49, 5419–5423. [Google Scholar] [CrossRef]
  56. Thiebaut, O.; Bock, H.; Grelet, E. Face-on Oriented Bilayer of Two Discotic Columnar Liquid Crystals for Organic Donor−Acceptor Heterojunction. J. Am. Chem. Soc. 2010, 132, 6886–6887. [Google Scholar] [CrossRef]
  57. Shearman, G.C.; Yahioglu, G.; Kirstein, J.; Milgrom, L.R.; Seddon, J.M. Synthesis and phase behaviour of β-octaalkyl porphyrins. J. Mater. Chem. 2009, 19, 598–604. [Google Scholar] [CrossRef]
  58. Yang, C.-W.; Hsia, T.-H.; Chen, C.-C.; Lai, C.-K.; Liu, R.-S. Synthesis and Columnar Mesophase of Fluorescent Liquid Crystals Bearing a C2-Symmetric Chiral Core. Org. Lett. 2008, 10, 4069–4072. [Google Scholar] [CrossRef]
  59. Li, Z.; Zhi, L.; Lucas, N.T.; Wang, Z. Triangle-shaped polycyclic aromatics based on tribenzocoronene: Facile synthesis and physical properties. Tetrahedron 2009, 65, 3417–3424. [Google Scholar] [CrossRef]
  60. Lai, L.-L.; Hsu, S.-J.; Hsu, H.-C.; Wang, S.-W.; Cheng, K.-L.; Chen, C.-J.; Wang, T.-H.; Hsu, H.-F. Formation of Columnar Liquid Crystals on the Basis of Unconventional Triazine-Based Dendrimers by the C3-Symmetric Approach. Chem. Eur. J. 2012, 18, 6542–6547. [Google Scholar] [CrossRef]
  61. Alfa Aesar. Research Chemicals, Metals and Materials; Alfa Aesar: Ward Hill, MA, USA, 2011; p. 124. [Google Scholar]
  62. Lai, L.L.; Wang, S.W.; Cheng, K.L.; Lee, J.J.; Wang, T.H.; Hsu, H.F. Induction of the columnar phase of unconventional dendrimers by breaking the C2 symmetry of molecules. Chem. Eur. J. 2012, 18, 15361–15367. [Google Scholar] [CrossRef] [PubMed]
  63. Lai, L.-L.; Hsieh, J.-W.; Cheng, K.-L.; Liu, S.-H.; Lee, J.-J.; Hsu, H.-F. A Small Change in Central Linker Has a Profound Effect in Inducing Columnar Phases of Triazine-Based Unconventional Dendrimers. Chem. Eur. J. 2014, 20, 5160–5166. [Google Scholar] [CrossRef] [PubMed]
  64. Tsai, M.-J.; Hsieh, J.-W.; Lai, L.-L.; Cheng, K.-L.; Liu, S.-H.; Lee, J.-J.; Hsu, H.-F. Converting Nonliquid Crystals into Liquid Crystals by N-Methylation in the Central Linker of Triazine-Based Dendrimers. J. Org. Chem. 2016, 81, 5007–5013. [Google Scholar] [CrossRef]
  65. Lee, C.-H.; Huang, C.-C.; Li, C.-Y.; Lai, L.-L.; Lee, J.-J.; Hsu, H.-F. Both increasing the Iso-to-Col transition and lowering the solidifying temperatures of a triazine-based dendrimer by introducing CN polar groups in the dendritic core. J. Mater. Chem. C 2019, 7, 14232–14238. [Google Scholar] [CrossRef]
  66. Castelar, S.; Barberá, J.; Marcos, M.; Romero, P.; Serrano, J.-L.; Golemme, A.; Termine, R. Supramolecular dendrimers based on the self-assembly of carbazole-derived dendrons and triazine rings: Liquid crystal, photophysical and electrochemical properties. J. Mater. Chem. C 2013, 1, 7321–7332. [Google Scholar] [CrossRef]
  67. Lai, L.-L.; Hsu, H.-C.; Hsu, S.-J.; Cheng, K.-L. A Convenient Synthesis of Triazine-Based Dendrons and Dendrimers via a Convergent Approach and a Study of Their Interactions with Tetrafluorobenzoquinone. Synthesis 2010, 2010, 3576–3582. [Google Scholar] [CrossRef]
Nanomaterials 11 02112 sch001 550
Scheme 1. Preparation of dendrimers by the convergent, divergent, and combined approaches.
Scheme 1. Preparation of dendrimers by the convergent, divergent, and combined approaches.
Nanomaterials 11 02112 sch001
Nanomaterials 11 02112 sch002 550
Scheme 2. Reaction of amines with cyanuric chlorides at different temperatures.
Scheme 2. Reaction of amines with cyanuric chlorides at different temperatures.
Nanomaterials 11 02112 sch002
Nanomaterials 11 02112 g001 550
Figure 1. Structures of dendrimers (1) and (2) with C2-symmetry.
Figure 1. Structures of dendrimers (1) and (2) with C2-symmetry.
Nanomaterials 11 02112 g001
Nanomaterials 11 02112 g002 550
Figure 2. Structures of dendrimers (3) and (4) with C3-symmetry.
Figure 2. Structures of dendrimers (3) and (4) with C3-symmetry.
Nanomaterials 11 02112 g002
Nanomaterials 11 02112 g003 550
Figure 3. Structures of dendrimers (5) and (6) without a C2-symmetry and structures of dendrimers (7) and (8) with a C2-symmetry.
Figure 3. Structures of dendrimers (5) and (6) without a C2-symmetry and structures of dendrimers (7) and (8) with a C2-symmetry.
Nanomaterials 11 02112 g003
Nanomaterials 11 02112 g004 550
Figure 4. Structural isomers of dendrons to form dendrimers (5) and (6).
Figure 4. Structural isomers of dendrons to form dendrimers (5) and (6).
Nanomaterials 11 02112 g004
Nanomaterials 11 02112 g005 550
Figure 5. Structures of dendrimers (9–12).
Figure 5. Structures of dendrimers (9–12).
Nanomaterials 11 02112 g005
Nanomaterials 11 02112 g006 550
Figure 6. Isomers of dendrimers (10) and (11).
Figure 6. Isomers of dendrimers (10) and (11).
Nanomaterials 11 02112 g006
Nanomaterials 11 02112 g007 550
Figure 7. Isomers of dendrimers (13-I), (13-II), and (13-III).
Figure 7. Isomers of dendrimers (13-I), (13-II), and (13-III).
Nanomaterials 11 02112 g007
Nanomaterials 11 02112 g008 550
Figure 8. Structures of dendrimers (13) and (14).
Figure 8. Structures of dendrimers (13) and (14).
Nanomaterials 11 02112 g008
Nanomaterials 11 02112 g009 550
Figure 9. The numbering on carbons for indicating intramolecular H-bond interactions between H and N of dendrimers (10) and (13).
Figure 9. The numbering on carbons for indicating intramolecular H-bond interactions between H and N of dendrimers (10) and (13).
Nanomaterials 11 02112 g009
Nanomaterials 11 02112 g010 550
Figure 10. Structures of dendrimers (15) and (16).
Figure 10. Structures of dendrimers (15) and (16).
Nanomaterials 11 02112 g010
Nanomaterials 11 02112 g011 550
Figure 11. Structures of dendrimers (17) and (18).
Figure 11. Structures of dendrimers (17) and (18).
Nanomaterials 11 02112 g011
Nanomaterials 11 02112 g012 550
Figure 12. Structures of dendrimers (19) and (20) and and dendrons (21) and (22).
Figure 12. Structures of dendrimers (19) and (20) and and dendrons (21) and (22).
Nanomaterials 11 02112 g012
Nanomaterials 11 02112 g013 550
Figure 13. Structure of molecule (23).
Figure 13. Structure of molecule (23).
Nanomaterials 11 02112 g013
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Lu, Y.-C.; Hsu, H.-F.; Lai, L.-L. Unconventional Approaches to Prepare Triazine-Based Liquid Crystal Dendrimers. Nanomaterials 2021, 11, 2112. https://doi.org/10.3390/nano11082112

AMA Style

Lu Y-C, Hsu H-F, Lai L-L. Unconventional Approaches to Prepare Triazine-Based Liquid Crystal Dendrimers. Nanomaterials. 2021; 11(8):2112. https://doi.org/10.3390/nano11082112

Chicago/Turabian Style

Lu, Yao-Chih, Hsiu-Fu Hsu, and Long-Li Lai. 2021. "Unconventional Approaches to Prepare Triazine-Based Liquid Crystal Dendrimers" Nanomaterials 11, no. 8: 2112. https://doi.org/10.3390/nano11082112

APA Style

Lu, Y.-C., Hsu, H.-F., & Lai, L.-L. (2021). Unconventional Approaches to Prepare Triazine-Based Liquid Crystal Dendrimers. Nanomaterials, 11(8), 2112. https://doi.org/10.3390/nano11082112

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop